CN103468181A - 碳材料用高温粘结剂 - Google Patents

碳材料用高温粘结剂 Download PDF

Info

Publication number
CN103468181A
CN103468181A CN201310414357XA CN201310414357A CN103468181A CN 103468181 A CN103468181 A CN 103468181A CN 201310414357X A CN201310414357X A CN 201310414357XA CN 201310414357 A CN201310414357 A CN 201310414357A CN 103468181 A CN103468181 A CN 103468181A
Authority
CN
China
Prior art keywords
temperature
carbon material
alcohol
weight
accounts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310414357XA
Other languages
English (en)
Inventor
郭祥和
刘传福
马秋分
周帅
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JINING XINYUAN CARBON Co Ltd
Original Assignee
JINING XINYUAN CARBON Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JINING XINYUAN CARBON Co Ltd filed Critical JINING XINYUAN CARBON Co Ltd
Priority to CN201310414357XA priority Critical patent/CN103468181A/zh
Publication of CN103468181A publication Critical patent/CN103468181A/zh
Pending legal-status Critical Current

Abstract

碳材料用高温粘结剂，其特征是取一定重量的酒精，向其中加入酒精重量20～70%的热塑性酚醛树脂，搅拌使其完全溶解，然后，再加入酚醛树脂重量5～15%的乌洛托品、酒精重量1～5%的硬脂酸和酒精重量0.5～1.5%的乙酸乙酯，充分搅拌，混合均匀，制成溶液，根据粘结对象不同，也可在上述溶液中加入酒精重量5～30%碳化硅或细颗粒石墨粉，混合均匀，即制得碳材料用高温粘结剂，本发明的有益效果是碳材料用高温粘结剂能够较好地解决高温热场用品的粘结，有效地延长固化碳毡、石墨及石墨纸热场用品在高温下的使用寿命，节能降耗，提高生产效率。

Description

碳材料用高温粘结剂
技术领域
 本发明属于保温材料技术领域，更具体的说是一种碳材料用高温粘结剂。
背景技术
随着科技发展的需要，一些材料部件经常需要在高温真空状态下使用，现有技术的粘结剂多只能应用在200～300℃的范围内，目前，新型固化碳毡需要在1000℃以上甚至2500℃以上的高温环境下使用，由于使用温度高，该制品变得易碎，容易出现开裂、分层、脱落等现象，造成保温热场的破坏，对节能降耗，生产效率带来很大损失，为解决该难题，可将固化碳毡的表层喷刷涂层、粘结柔性石墨纸进行增强，这就需要耐高温的粘结剂。
现有技术的粘结剂大多以有机粘结剂为主，虽然比无机粘结剂在性能和耐高温方面有很大的改进，但有些粘结剂因添加的改性剂不同，在应用领域上受到很大的局限，如钼酸、硼酸钠、硼酸、硼酸锌、磷酸、三氯氧磷、碳化硼、二氧化硅等在1000oC以上高温时，挥发产生的蒸汽会对单晶硅和多晶硅造成污染，影响单晶硅和多晶硅的纯度，所以在单晶炉和多晶炉热场制品中严禁使用，同时，上述改性剂挥发所产生的蒸汽多为有毒气体，对环境会产生污染，特别是对操作人员的身心会造成很大伤害，同时，在高温环境下，随着其挥发性的增强，其粘接强度会大大降低，变得易碎、脱落，起不到粘结剂的作用。
发明内容
为了解决上述问题，本发明提供了一种可在高温环境下使用的碳材料用高温粘结剂，其具体方案是：本发明所述的碳材料用高温粘结剂，其特征是：取一定重量的酒精，向其中加入酒精重量20～70%的热塑性酚醛树脂，搅拌使其完全溶解，然后，再加入酚醛树脂重量5～15%的乌洛托品、酒精重量1～5%的硬脂酸和酒精重量0.5～1.5%的乙酸乙酯，充分搅拌，混合均匀，制成溶液，根据粘结对象不同，也可在上述溶液中加入酒精重量5～30%碳化硅或细颗粒石墨粉，混合均匀，即制得碳材料用高温粘结剂。
使用时，把碳材料用粘结剂均匀的喷涂或涂刷在需粘结制品的表面，待5～20分钟，将两者黏贴在一起并压实，进行固化，温度控制在180～250℃，然后放入高温炉进行1000℃以上的碳化，达到能够在高温下长期使用的目的。
本发明的有益效果是碳材料用高温粘结剂能够较好地解决高温热场用品的粘结，有效地延长固化碳毡、石墨及石墨纸热场用品在高温下的使用寿命，节能降耗，提高生产效率。
具体实施方式
下面通过具体实施例进一步详细说明本发明的实施方案，以便公众更好地掌握本发明的具体实施方法。
实施例1
固化碳毡与石墨纸之间的粘结：
取1000g工业酒精，加入200g的热塑性酚醛树脂，充分溶解后，再加入10g乌洛托品、50g硬脂酸、15g乙酸乙酯，充分混合，搅拌均匀，再加入50g的细颗粒石墨粉，充分搅拌，使石墨粉处于溶液的悬浮状态，碳材料用高温粘结剂即制备完毕，使用时，将粘结剂均匀的涂刷在固化保温碳毡和石墨纸的表面，待10分钟，将其二者黏贴在一起并压实，然后进行固化，温度控制在180℃，最后入真空高温炉碳化，温度控制在1000℃以上，达到长期在高温下使用的目的。
实施例2
石墨纸之间的粘结：
取1000g工业酒精，加入500g的热塑性酚醛树脂充分搅拌完全溶解后，再加入50g乌洛托品、30g硬脂酸、10g乙酸乙酯,充分混合，搅拌均匀，制备高温粘结剂，把粘结剂均匀的喷涂在石墨纸粘结面的表面，待10分钟，将其二者均匀的黏贴在一起，然后进行固化，温度控制在200℃，最后入真空高温炉，温度控制在1000℃以上，使酚醛树脂充分碳化，达到能够在高温下长期使用的目的。。
实施例3
石墨之间的粘结：
取1000g工业酒精，加入700g的热塑性酚醛树脂充分溶解后，再加入105g乌洛托品、10g硬脂酸、5g乙酸乙酯，充分混合，搅拌均匀，制备高温粘结剂，把粘结剂制均匀的喷涂在石墨之间的粘结面上，待10分钟，将其二者黏贴在一起并压实，然后进行固化，温度控制在250℃，最后入真空高温炉碳化，温度控制在1000℃以上，达到能够在高温下长期使用的目的。
本发明的有益效果是碳材料用高温粘结剂能够较好地解决高温热场用品的粘结，有效地延长固化碳毡、石墨及石墨纸热场用品在高温下的使用寿命，节能降耗，提高生产效率。

Claims (3)

1.碳材料用高温粘结剂，其特征是：取一定重量的酒精，向其中加入酒精重量20～70%的热塑性酚醛树脂，搅拌使其完全溶解，然后，再加入酚醛树脂重量5～15%的乌洛托品、酒精重量1～5%的硬脂酸和酒精重量0.5～1.5%的乙酸乙酯，充分搅拌，混合均匀，即制成碳材料用高温粘结剂。
2. 根据权利要求1所述的碳材料用高温粘结剂，其特征在于可选择性地加入酒精重量5～30%碳化硅或细颗粒石墨粉，混合均匀，即制得碳材料用高温粘结剂。
3. 根据权利要求1所述的碳材料用高温粘结剂，其特征在于所述的碳材料用高温粘结剂的粘结方法是：将碳材料用粘结剂均匀的喷涂或涂刷在需粘结制品的表面，待5～20分钟，将两者黏贴在一起并压实，进行固化，温度控制在180～250℃，然后放入高温炉进行1000℃以上的碳化，达到能够在高温下长期使用的目的。
CN201310414357XA 2013-09-12 2013-09-12 碳材料用高温粘结剂 Pending CN103468181A (zh)