CN103467906A - 阻燃增强pom/ptfe组合物及其制备方法 - Google Patents

阻燃增强pom/ptfe组合物及其制备方法 Download PDF

Info

Publication number
CN103467906A
CN103467906A CN2013103911327A CN201310391132A CN103467906A CN 103467906 A CN103467906 A CN 103467906A CN 2013103911327 A CN2013103911327 A CN 2013103911327A CN 201310391132 A CN201310391132 A CN 201310391132A CN 103467906 A CN103467906 A CN 103467906A
Authority
CN
China
Prior art keywords
pom
ptfe
fire
inflaming
retarding
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Withdrawn
Application number
CN2013103911327A
Other languages
English (en)
Inventor
庄亚东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Original Assignee
WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd filed Critical WUJIANG WUHUA HARDWARE PRODUCTS CO Ltd
Priority to CN2013103911327A priority Critical patent/CN103467906A/zh
Publication of CN103467906A publication Critical patent/CN103467906A/zh
Withdrawn legal-status Critical Current

Abstract

阻燃增强POM/PTFE组合物及其制备方法，阻燃增强POM/PTFE组合物包括如下质量份数的原料：POM树脂78-84份、PTFE25-30份、无卤阻燃剂Exolit?OP9350.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。本发明将无卤阻燃剂Exolit?OP935、双氰胺和铝酸锌复配作为阻燃剂，具有良好的阻燃效果；本发明具有良好的机械性能，拉伸强度可达50MPa，弯曲强度可达78MPa，且所得材料流动性好，易于加工成型。

Description

阻燃增强 POM/PTFE 组合物及其制备方法
技术领域
本发明属于高分子材料技术领域，具体涉及一种阻燃增强POM/PTFE组合物及其制备方法。
背景技术
POM是第三大通用塑料，均具有优异的耐摩擦性能和钢性，物理性能、机械性能和化学性能良好，但是其热稳定性和阻燃性较差；PTFE具有优良的耐腐蚀性和自润滑性，还具有良好的电学性能，其电绝缘性不受温度影响，素有“塑料王”之称，但是其流动性较差，不易加工成型。目前有关改性POM的报道屡见不鲜，但是改性后的POM虽然其某一方面的性能得到的提升，但是其物理性能和机械性能在一定程度上受到了影响，使其应用受到了很大限制。
综上所述如何提升POM的综合性能成为该领域亟待解决的技术难题。
发明内容
本发明的目的在于克服现有技术的不足而提供一种阻燃增强POM/PTFE组合物及其制备方法，本发明成品具有良好的阻燃性，机械性能良好，且加工成型性良好。
本发明的技术方案：
阻燃增强POM/PTFE组合物，包括如下质量份数的原料： POM树脂78-84份、PTFE 25-30份、无卤阻燃剂Exolit™ OP935 0.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。
所述抗氧剂为受阻酚类抗氧剂。
所述受阻酚类抗氧剂为2，6-叔丁基-4-甲基苯酚、双（3，5-叔丁基-4-羟基苯基）硫醚或四〔β-(3，5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯。
阻燃增强POM/PTFE组合物的制备方法，包括以下步骤：按照质量配比称取各原料，将POM树脂、PTFE粉碎至100目与抗氧剂混合搅拌均匀，后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌，混合搅拌均匀后出料至双螺杆挤出机中挤出，各段温度控制150-155℃，造粒即可得。
有益效果：本发明将无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌复配作为阻燃剂，具有良好的阻燃效果；本发明具有良好的机械性能，拉伸强度可达50 MPa，弯曲强度可达78 MPa，且所得材料流动性好，易于加工成型。
具体实施方式
下面结合实施例对本发明作进一步的详细描述。
实施例1
阻燃增强POM/PTFE组合物，包括如下质量份数的原料： POM树脂78份、PTFE 25份、无卤阻燃剂Exolit™ OP935 0.2份、双氰胺0.1份、铝酸锌0.1份、2，6-叔丁基-4-甲基苯酚0.5份、马来酸酐接枝聚乙烯0.2份。
本发明制备方法：按照质量配比称取各原料，将POM树脂、PTFE粉碎至100目与抗氧剂2，6-叔丁基-4-甲基苯酚混合搅拌均匀，后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌，混合搅拌均匀后出料至双螺杆挤出机中挤出，各段温度控制150℃，造粒即可得。
实施例2
阻燃增强POM/PTFE组合物，包括如下质量份数的原料： POM树脂84份、PTFE 30份、无卤阻燃剂Exolit™ OP935 0.5份、双氰胺0.3份、铝酸锌0.2份、双（3，5-叔丁基-4-羟基苯基）硫醚1份、马来酸酐接枝聚乙烯0.6份。
本发明制备方法：按照质量配比称取各原料，将POM树脂、PTFE粉碎至100目与抗氧剂双（3，5-叔丁基-4-羟基苯基）硫醚混合搅拌均匀，后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌，混合搅拌均匀后出料至双螺杆挤出机中挤出，各段温度控制155℃，造粒即可得。
实施例3
阻燃增强POM/PTFE组合物，包括如下质量份数的原料： POM树脂82份、PTFE 28份、无卤阻燃剂Exolit™ OP935 0.3份、双氰胺0.2份、铝酸锌0.15份、四〔β-(3，5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯0.8份、马来酸酐接枝聚乙烯0.4份。
本发明制备方法，包括以下步骤：按照质量配比称取各原料，将POM树脂、PTFE粉碎至100目与抗氧剂四〔β-(3，5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯混合搅拌均匀，后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌，混合搅拌均匀后出料至双螺杆挤出机中挤出，各段温度控制155℃，造粒即可得。
将实施例1-3所得材料按照国际标准注塑成型为测试样条，进行性能测试，测试结果见下表1。
表1 实施例1-3所得材料性能测试数据
性能 实施例1 实施例2 实施例3
拉伸强度，MPa 42.8 50 48
弯曲强度，MPa 75 78 74
缺口冲击强度，kJ/m2 13.6 15.6 14
UL-94 V0 V0 V0
由上表可见本发明成品具有良好的阻燃性，阻燃性能为V0级，具有优良的冲击强度、拉伸强度和弯曲强度。

Claims (4)

1.阻燃增强POM/PTFE组合物，其特征在于，包括如下质量份数的原料： POM树脂78-84份、PTFE 25-30份、无卤阻燃剂Exolit™ OP935 0.2-0.5份、双氰胺0.1-0.3份、铝酸锌0.1-0.2份、抗氧剂0.5-1份、马来酸酐接枝聚乙烯0.2-0.6份。
2.根据权利要求1所述的阻燃增强POM/PTFE组合物，其特征在于，所述抗氧剂为受阻酚类抗氧剂。
3.根据权利要求2所述的阻燃增强POM/PTFE组合物，其特征在于，所述受阻酚类抗氧剂为2，6-叔丁基-4-甲基苯酚、双（3，5-叔丁基-4-羟基苯基）硫醚或四〔β-(3，5-叔丁基-4-羟基苯基)丙酸〕季戊四醇酯。
4.如权利要求1所述的阻燃增强POM/PTFE组合物的制备方法，其特征在于，包括以下步骤：按照质量配比称取各原料，将POM树脂、PTFE粉碎至100目与抗氧剂混合搅拌均匀，后依次加入马来酸酐接枝聚乙烯、无卤阻燃剂Exolit™ OP935、双氰胺和铝酸锌，混合搅拌均匀后出料至双螺杆挤出机中挤出，各段温度控制150-155℃，造粒即可得。
CN2013103911327A 2013-09-02 2013-09-02 阻燃增强pom/ptfe组合物及其制备方法 Withdrawn CN103467906A (zh)