CN103450763A - Paint capable of releasing negative oxygen ions and processing method thereof - Google Patents
Paint capable of releasing negative oxygen ions and processing method thereof Download PDFInfo
- Publication number
- CN103450763A CN103450763A CN 201210171128 CN201210171128A CN103450763A CN 103450763 A CN103450763 A CN 103450763A CN 201210171128 CN201210171128 CN 201210171128 CN 201210171128 A CN201210171128 A CN 201210171128A CN 103450763 A CN103450763 A CN 103450763A
- Authority
- CN
- China
- Prior art keywords
- negative oxygen
- releasing negative
- melamine resin
- processing method
- oxygen ions
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a kind of paint capable of releasing negative oxygen ions and a processing method thereof. The paint comprises following materials in percentage by weight: 15% to 20% of acrylic resin, 10 to 15% of diatom ooze, 5% to 10% of polyol polymer, 12% to 18% of tourmalinite powder, 15% to 20% of titanium dioxide, 5% to 8% of melamine resin, and 15% to 25% of purified water. The processing method of the paint capable of releasing negative oxygen ions comprises following steps: (1) adding acrylic resin, polyol polymer, diatom ooze, tourmalinite powder, titanium dioxide, and melamine resin into a container according to the ratio mentioned above, and then evenly mixing; (2) heating to the temperature of 75 to 80 DEG C, and evenly mixing so as to obtain the paint capable of releasing negative oxygen ions. The processing method has the advantages of capability of direct using, simple technology, and low cost.
Description
Technical field
The present invention relates to a kind of coating, particularly relate to a kind of energy releasing negative oxygen ion coating and working method.
Background technology
Polypropylene (PP) plastic cement is in the industrial fields such as automobile, electrical equipment, sports equipment, toy that are widely used in, due to polypropylene surface static electrification ion not, can't direct spraying in plastic surface, mostly producer adopts is to beat at the bottom of PP the method for water to carry out polypropylene (PP) plastic surface and process, spray again afterwards acrylic coating, make process complications, produce repetition, waste a large amount of human and material resources and time.
Summary of the invention
Purpose of the present invention overcomes the deficiencies in the prior art exactly, and a kind of energy releasing negative oxygen ion coating and working method are provided.
For achieving the above object, the present invention adopts following technical scheme:
A kind of can releasing negative oxygen ion coating, comprise the material of following weight part:
Acrylic resin: 15%-20%;
Diatom ooze: 10%-15%;
Polyhydric alcohol polymer: 5%-10%;
Tourmaline powder: 12%-18%;
Titanium dioxide 15%-20%;
Melamine resin: 5%-8%;
Pure water: 15%-25%.
A kind of working method of negative oxygen ion coating comprises following procedure of processing:
(1) by said ratio by acrylic resin, polyhydric alcohol polymer, diatom ooze, tourmaline powder, titanium dioxide, melamine resin, that melamine resin is put into container for stirring is even;
(2) 75-80 degree centigrade of heating stir and make negative oxygen ion coating.
Advantage of the present invention: can directly use, technique is simple, and cost is low.
Embodiment
Embodiment 1:
A kind of can releasing negative oxygen ion coating, comprise the material of following weight part:
Acrylic resin: 18%
Diatom ooze: 15%;
Polyhydric alcohol polymer: 8%;
Tourmaline powder: 15%;
Titanium dioxide 17%;
Melamine resin: 7%;
Pure water: 20%.
A kind of working method of energy releasing negative oxygen ion coating comprises following procedure of processing:
(1), by said ratio by acrylic resin, polyhydric alcohol polymer, diatom ooze, tourmaline powder, titanium dioxide, melamine resin, that melamine resin is put into container for stirring is even;
(2), above-mentioned mixed solution is heated to 76 degrees centigrade, the cold energy releasing negative oxygen ion coating that both must make.
Embodiment 2:
A kind of can releasing negative oxygen ion coating, comprise the material of following weight part:
Acrylic resin: 16%
Diatom ooze: 18%;
Polyhydric alcohol polymer: 7%;
Tourmaline powder: 15%;
Titanium dioxide 18%;
Melamine resin: 8%;
Pure water: 18%.
A kind of working method of energy releasing negative oxygen ion coating comprises following procedure of processing:
(1), by said ratio by acrylic resin, polyhydric alcohol polymer, diatom ooze, tourmaline powder, titanium dioxide, melamine resin, that melamine resin is put into container for stirring is even;
(2), by 76 degrees centigrade of above-mentioned mixed solution heating, cold both must having made can releasing negative oxygen ion coating, adds pigment during use.
Embodiment 3:
A kind of can releasing negative oxygen ion coating, comprise the material of following weight part:
Acrylic resin: 19%
Diatom ooze: 15%;
Polyhydric alcohol polymer: 8%;
Tourmaline powder: 14%;
Titanium dioxide 17%;
Melamine resin: 9%;
Pure water: 18%.
A kind of working method of energy releasing negative oxygen ion coating comprises following procedure of processing:
(1), by said ratio by acrylic resin, polyhydric alcohol polymer, diatom ooze, tourmaline powder, titanium dioxide, melamine resin, that melamine resin is put into container for stirring is even;
(2), by 76 degrees centigrade of above-mentioned mixed solution heating, cold both must having made can releasing negative oxygen ion coating, adds pigment during use.
Claims (2)
1. an energy releasing negative oxygen ion coating is characterized in that comprising the material of following weight part:
Acrylic resin: 15%-20%;
Diatom ooze: 10%-15%;
Polyhydric alcohol polymer: 5%-10%;
Tourmaline powder: 12%-18%;
Titanium dioxide 15%-20%;
Melamine resin: 5%-8%;
Pure water: 15%-25%.
2. the working method of an energy releasing negative oxygen ion coating comprises following procedure of processing:
(1) by said ratio by acrylic resin, polyhydric alcohol polymer, diatom ooze, tourmaline powder, titanium dioxide, melamine resin, that melamine resin is put into container for stirring is even;
(2) 75-80 degree centigrade of heating stir and make negative oxygen ion coating.