CN103436104A - Water-based UV (ultraviolet) woodware adhesion colorant mother solution and preparation method thereof - Google Patents
Water-based UV (ultraviolet) woodware adhesion colorant mother solution and preparation method thereof Download PDFInfo
- Publication number
- CN103436104A CN103436104A CN2013104222139A CN201310422213A CN103436104A CN 103436104 A CN103436104 A CN 103436104A CN 2013104222139 A CN2013104222139 A CN 2013104222139A CN 201310422213 A CN201310422213 A CN 201310422213A CN 103436104 A CN103436104 A CN 103436104A
- Authority
- CN
- China
- Prior art keywords
- water
- woodenware
- mother liquor
- adheres
- tinting material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a water-based UV (ultraviolet) woodware adhesion colorant mother solution and a preparation method thereof. The colorant mother solution is prepared from 70-80 parts of water-based UV polyurethane acrylate emulsion, 1-1.5 parts of photoinitiator, 2-4 parts of cosolvent, 0.2-0.5 part of defoaming agent, 1-2 parts of wetting and dispersing agent, 1-2 parts of thickener, 0.2-0.5 part of amine neutralizer and 10-15 parts of deionized pure water. The colorant mother solution has higher adhesive force between the coating and the substrate, and favorable compatibility and dispersity with water-based dyes and water-based pigments, highlights the layered sensation of the colored wood grains, can perform mechanical application operation to enhance the coloring efficiency of the produced board, is green, environment-friendly and pollution-free for the environment, and ensures the safety of the production enterprise and user.
Description
Technical field
The present invention relates to the painted chemical material technical field of woodenware, particularly relate to a kind of water-based UV woodenware and adhere to tinting material mother liquor and preparation method thereof.
Background technology
The paint that furniture industry is generally used is conventional solvent type complexing metal dyestuff, and solvent based coating exists smell large and to be dried of long duration and stain for wood effect lines is unintelligible, the undesirable shortcoming of sticking power effect of colored film; In addition, conventional solvent type tinting material is by spraying application, and efficiency is low, and cost is high, contaminate environment, affects workmen's health; Conventional solvent type coating lacquer contains solvent (as toluene, acetone, vinyl acetic monomer solidifying agent etc.) inflammable, explosive, organic volatile simultaneously, and these solvents very easily bring fire hazard to manufacturing concern; Finally, the product after the solvent based coating film forming does not have the fire protection flame retarding effect yet, meets spark and very easily burns, and the shortcoming of above existence all works the mischief to people's life, production.
Summary of the invention
In order to overcome above-mentioned the deficiencies in the prior art, the invention provides a kind of water-based UV woodenware and adhere to tinting material mother liquor and preparation method thereof, large and to be dried of long duration and stain for wood effect lines is unintelligible, the undesirable shortcoming of sticking power effect of colored film to solve smell that current woodenware coloured material exists, the use that guarantees material is to enterprise, to people's security.
The technical solution adopted in the present invention is: the invention provides a kind of water-based UV woodenware and adhere to the tinting material mother liquor, its important component part forms containing following important substance and amount part ratio.
As preferably, water-based UV polyurethane-acrylate emulsion adopts cyanogen specialization product 7177 product types, solid content is 40%, outward appearance emulsus transparent liquid, molecular weight are 5500 dalton, but but has the wettability of remarkable sticking power and timber good, emulsification before low viscosity mechanical cycles coating decoration, photocuring, paint film flexibility is good.
As preferably, the water-based solubility promoter adopts 1-Methoxy-2-propyl acetate (PMA), is the low toxicity advanced industrial solvent molecule amount 132.16 of excellent property, transparent liquid, polarity and nonpolar material is all had to very strong dissolving power.
As preferably, water-based wetting dispersing agent 4 adopts the high Dispers760w of enlightening, the wetting dispersing agent for water-based printing ink and coating system, the aqueous solution containing high pigment affinity groups polymkeric substance and surface-active substance of 35% active quantities is transparent in slight haze liquid; The characteristic of the high Dispers760w of enlightening is for water prescription, is specially adapted to carbon black and pigment dyestuff; Have strong reduction and grind viscosity, the main recommendation, for resiniferous grinding, has excellent tinting strength.
As preferably, water-based thickener adopts chemical DSX 3551, is superpower non-ionic associative type thickening material, containing organic solvent, and the various types of resins emulsion systems such as application urethane.
As preferably, water-soluble photoinitiator adopts chemical 819DW, is applicable to solidifying of UV aqueous polyurethane dispersion system, also can be used for the day photocuring system of UV aqueous polyurethane dispersion. and the thick coating curing system of UV water-based.
As preferably, the water-based defoamer adopts Foamex3062, and it is the defoamer for water-based system, 100% slight haze liquid, and polyether siloxane copolymer, containing aerosil.Foamex3062 is applicable in colored paint, grinding stage defoaming effect excellence, is applied to building coating, pigment concentrate slurry, flexo and gravure ink, woodenware and coatings for furniture, industrial coating.
As preferably, water-based amine neutralizing agent adopts chemical MA-95, is low smell, multifunction amine neutralizing agent, and the potential of hydrogen of holding concurrently is regulated and stablely promoted that gloss of film represents.
A kind of water-based UV woodenware adheres to the preparation method of tinting material mother liquor:
(1) first solubility promoter 1-Methoxy-2-propyl acetate 50g is added in cup beforehand dilution after slowly adding 819DW light trigger 15g to add water-based 760W dispersion agent 50 to add 3g water-based defoamer Foamex3062 to splash into more than MA-95g to add to stir, be controlled at 500r/min slowly splashing into aqueous polyurethane acrylate 700g mixing speed in cup, deionized water 154g and thickening material 20g dilution are stirred, slowly splash into again in the aqueous polyurethane acrylate emulsion, add rear stirring within 30 minutes, to obtain a kind of novel aqueous UV woodenware later and adhere to the tinting material mother liquor,
(2) added rear control rotating speed 500r/min to disperse 30 minutes, detection paint liquid particle diameter fineness≤25um, the paint fluid viscosity: rotational viscosimeter 4# pin tested viscosity is:
600 ± 100maps/25 ℃, emulsion ultraviolet photo-curing energy: wavelength 280-450nm, curing energy is 250-350mj/cm2.
Compared with prior art, the invention has the beneficial effects as follows that waterborne UV wood paint tinting material mother liquor is 60 ℃ by IR infrared drying volatilization moisture film forming, roller coat coloring process IR infrared drying temperature, the conveying belt speed control is at 15m/min, and the bake drying time is 30 seconds.
Impel decomposition of initiator under the irradiation that ultraviolet photo-curing is 260-450nm at ultraviolet wavelength, produce free radical, cause the emulsion reaction, the instantaneous solidification film forming.Compare directly direct coloring and coating on timber element plate of ultraviolet photo-curing aqueous wooden ware tinting material with conventional solvent type colorants for paints; The application mode: roller coat, showering, spraying, obliterating coloring effect can mechanical application circulation painting operations, improve enterprises production efficiency, reduce organic volatile to the pollution of atmosphere simultaneously and affect the health of human body.
Embodiment
Below in conjunction with the painted embodiment of concrete 3 timber element plate, the present invention is described in detail.
A kind of water-based UV woodenware adheres to the tinting material mother liquor, and this product is comprised of following formula.
A kind of water-based UV woodenware adheres to the preparation method of tinting material mother liquor:
(1) first solubility promoter 1-Methoxy-2-propyl acetate 50g is added in cup beforehand dilution after slowly adding 819DW light trigger 15g to add water-based 760W dispersion agent 50 to add 3g water-based defoamer Foamex3062 to splash into more than MA-95g to add to stir.Be controlled at 500r/min slowly splashing into aqueous polyurethane acrylate 700g mixing speed in cup, deionized water 154g and thickening material 20g dilution are stirred, slowly splash in the aqueous polyurethane acrylate emulsion again, add rear stirring within 30 minutes, to obtain a kind of novel aqueous UV woodenware later and adhere to the tinting material mother liquor;
(2) added rear control rotating speed 500r/min to disperse 30 minutes, detection paint liquid particle diameter fineness≤25um, the paint fluid viscosity: rotational viscosimeter 4# pin tested viscosity is:
600 ± 100maps/25 ℃, emulsion ultraviolet photo-curing energy: wavelength 280-450nm, curing energy is 250-350mj/cm2.
Below by experiment production technique obtain a kind of water-based UV woodenware adhere to tinting material mother liquor, minutes three parts each 300g again, water soluble dyestuffs yellow 30g red 30 with water soluble dyestuffs palm fibre 30g, water soluble dyestuffs, to add in cup, the roller coat painted by roller coating technology of stirring be that sponge rubber roll roller coat is painted.
| Title | Deionized water | Water-based UV mother liquor | The water soluble dyestuffs palm fibre | Water soluble dyestuffs is red | The water soluble dyestuffs Huang |
| Proportioning quantity 1 | 30g | 300g | 30g | - | - |
| Proportioning quantity 2 | 30g | 300g | - | 30g | - |
| Proportioning quantity 3 | 30g | 300g | - | - | 30g |
Cortex Fraxini mandshuricae element plate experiment coloring and coating technique:
Sponge rubber roll roller coat is painted, and to cross IR infrared drying volatilization moisture, IR Temperature Setting be that IR infrared drying temperature is that 60 ℃ of conveying belt speed control are 30 seconds in the 15m/min bake drying time, cross UV-lamp and solidify, solidify energy for >=260mj/cm 2.
Above Cortex Fraxini mandshuricae material roller coat coating process is done following performance test to 3 kinds of water soluble dyestuffs application sheet material and conventional solvent type tinting material application sheet material after timber element plate is unified coating process test, film forming respectively.
Claims (8)
1. a water-based UV woodenware adheres to the tinting material mother liquor, and its important component part forms containing following important substance and amount part ratio:
Its characteristics are: described water-based UV polyurethane-acrylate emulsion adopts cyanogen specialization product 7177 product types, solid content is 40%, outward appearance emulsus transparent liquid, molecular weight are 5500 dalton, but but has the wettability of remarkable sticking power and timber good, emulsification before low viscosity mechanical cycles coating decoration, photocuring, paint film flexibility is good.
2. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-based solubility promoter adopts 1-Methoxy-2-propyl acetate (PMA), be the low toxicity advanced industrial solvent molecule amount 132.16 of excellent property, transparent liquid, polarity and nonpolar material all had to very strong dissolving power.
3. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-based wetting dispersing agent 4 adopts the high Dispers760w of enlightening, it is the wetting dispersing agent for water-based printing ink and coating system, the aqueous solution containing high pigment affinity groups polymkeric substance and surface-active substance of 35% active quantities is transparent in slight haze liquid; The characteristic of the high Dispers760w of enlightening is for water prescription, is specially adapted to carbon black and pigment dyestuff; Have strong reduction and grind viscosity, the main recommendation, for resiniferous grinding, has excellent tinting strength.
4. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-based thickener adopts chemical DSX 3551, is superpower non-ionic associative type thickening material, not containing organic solvent, and the various types of resins emulsion systems such as application urethane.
5. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-soluble photoinitiator adopts chemical 819DW, be applicable to solidifying of UV aqueous polyurethane dispersion system, also can be used for the day photocuring system of UV aqueous polyurethane dispersion. and the thick coating curing system of UV water-based.
6. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-based defoamer adopts Foamex3062, and it is the defoamer for water-based system, 100% slight haze liquid, polyether siloxane copolymer, containing aerosil, Foamex3062 is applicable in colored paint, grinding stage defoaming effect excellence, be applied to building coating, pigment concentrate slurry, flexo and gravure ink, woodenware and coatings for furniture, industrial coating.
7. water-based UV woodenware according to claim 1 adheres to the tinting material mother liquor, it is characterized in that: described water-based amine neutralizing agent adopts chemical MA-95, is low smell, multifunction amine neutralizing agent, and the potential of hydrogen of holding concurrently is regulated and stable promotion gloss of film represents.
8. a water-based UV woodenware adheres to the preparation method of tinting material mother liquor, and its characteristics are, the preparation method comprises following content:
(1) first solubility promoter 1-Methoxy-2-propyl acetate 50g is added in cup beforehand dilution after slowly adding 819DW light trigger 15g to add water-based 760W dispersion agent 50 to add 3g water-based defoamer Foamex3062 to splash into more than MA-95g to add to stir, be controlled at 500r/min slowly splashing into aqueous polyurethane acrylate 700g mixing speed in cup, deionized water 154g and thickening material 20g dilution are stirred, slowly splash into again in the aqueous polyurethane acrylate emulsion, add rear stirring within 30 minutes, to obtain a kind of novel aqueous UV woodenware later and adhere to the tinting material mother liquor,
(2) added rear control rotating speed 500r/min to disperse 30 minutes, detection paint liquid particle diameter fineness≤25um, the paint fluid viscosity: rotational viscosimeter 4# pin tested viscosity is:
600 ± 100maps/25 ℃, emulsion ultraviolet photo-curing energy: wavelength 280-450nm, curing energy is 250-350mj/cm2.