CN103410020A - White pigment with good weather resistance - Google Patents
White pigment with good weather resistance Download PDFInfo
- Publication number
- CN103410020A CN103410020A CN2013102857560A CN201310285756A CN103410020A CN 103410020 A CN103410020 A CN 103410020A CN 2013102857560 A CN2013102857560 A CN 2013102857560A CN 201310285756 A CN201310285756 A CN 201310285756A CN 103410020 A CN103410020 A CN 103410020A
- Authority
- CN
- China
- Prior art keywords
- parts
- good weatherability
- chinese white
- starch
- white pigment
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a white pigment with good weather resistance. The white pigment is prepared from the following components in parts by weight: 20-30 parts of titanium dioxide, 5-10 parts of arabic gum, 5-10 parts of pectin, 5-10 parts of sulphate starch, 5-10 parts of starch stearate, 1-3 parts of sodium lactate, 5-10 parts of polyethylene glycol, and 3-5 parts of magnesium sulfate. The prepared white pigment is good in weather resistance.
Description
Technical field
The present invention relates to a kind of pigment, particularly relate to a kind of Chinese white with good weatherability properties.
Background technology
The purposes of pigment is very extensive, can be applied to the every aspect in life.Some pigment is behind the surface that is sprayed on some vessel or other materials, do not have good weatherability, as there will be color to shoal after placing a period of time, after drenching with rain with regard to unsettled problem, if can overcome the weatherability problem under mal-condition, will greatly expand so Application Areas and the scope of pigment.The Chinese white that has possessed good weatherability properties can be applied to a plurality of fields, as machine surface, fabric face etc.
Summary of the invention
The technical problem solved: Chinese white does not have the problem of good weatherability properties.
Technical scheme: technical solution of the present invention is a kind of Chinese white with good weatherability properties, is comprised of according to weight ratio following composition: 20～30 parts of titanium dioxides, 5～10 parts of Arabic gums, 5～10 parts of pectin, 5～10 parts of starch sulfates, 5～10 parts of starch stearates, 1～3 part of sodium lactate, 5～10 parts of polyethylene glycol, 3～5 parts, magnesium sulfate.The preparation method of Chinese white who possesses good weatherability properties is as follows:
At first take titanium dioxide 20～30kg, Arabic gum 5～10kg, pectin 5～10kg, starch sulfate 5～10kg, starch stearate 5～10kg, sodium lactate 1～3kg, polyethylene glycol 5～10kg, magnesium sulfate 3～5kg.Wherein magnesium sulfate purity is more than 99%.Mentioned component is dropped in reactor, with electronic stirring arm, stir 1h, until mix.
Beneficial effect: the Chinese white of preparation has good weatherability.
The specific embodiment
Preparation method: at first take titanium dioxide, Arabic gum, pectin, starch sulfate, starch stearate, sodium lactate, polyethylene glycol, magnesium sulfate.Wherein magnesium sulfate purity is more than 99%.Mentioned component is dropped in reactor, with electronic stirring arm, stir 1h, until mix.
Weatherability method of testing: carry out the weatherability test after the product of embodiment acquisition is evenly spread upon to the linen surface.High temperature test: probe temperature is 50 ℃, and the time is 5h.It is also 5h that water drenches test, and high temperature test and water drench the test alternate cycles, and cycle-index is 80 times.After test finishes, use color difference meter to carry out color difference measurement to product appearance.
The weatherability test result:
Embodiment 1: value of chromatism is 0.21, and the pigment outward appearance does not change, and has good weatherability.
Embodiment 2: value of chromatism is 0.17, and the pigment outward appearance does not change, and has good weatherability.
Embodiment 1: value of chromatism is 0.14, and the pigment outward appearance does not change, and has good weatherability.
Claims (5)
1. the Chinese white with good weatherability properties, is characterized in that being comprised of according to weight ratio following composition: 20～30 parts of titanium dioxides, 5～10 parts of Arabic gums, 5～10 parts of pectin, 5～10 parts of starch sulfates, 5～10 parts of starch stearates, 1～3 part of sodium lactate, 5～10 parts of polyethylene glycol, 3～5 parts, magnesium sulfate.
2. a kind of Chinese white with good weatherability properties according to claim 1, is characterized in that in the pigment composition, titanium dioxide is 20 parts.
3. a kind of Chinese white with good weatherability properties according to claim 1, is characterized in that in the pigment composition, Arabic gum is 10 parts.
4. a kind of Chinese white with good weatherability properties according to claim 1, is characterized in that in the pigment composition, pectin is 10 parts.
5. a kind of Chinese white with good weatherability properties according to claim 1, is characterized in that in the pigment composition, starch sulfate is 5 parts.