CN102746750A - Gloss emulsion paint - Google Patents
Gloss emulsion paint Download PDFInfo
- Publication number
- CN102746750A CN102746750A CN 201110098871 CN201110098871A CN102746750A CN 102746750 A CN102746750 A CN 102746750A CN 201110098871 CN201110098871 CN 201110098871 CN 201110098871 A CN201110098871 A CN 201110098871A CN 102746750 A CN102746750 A CN 102746750A
- Authority
- CN
- China
- Prior art keywords
- sodium
- water
- emulsion paint
- light
- kilogram
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses gloss emulsion paint. The gloss emulsion paint comprises: by mass, 35 to 55% of an ethylene-propylene copolymer emulsion, 25 to 45% of titanium dioxide, 1.0 to 1.8% of sodium hexametaphosphate, 5 to 7% of glycol, 0.15 to 0.2% of tributyl phosphate, 1.5 to 2.5% of dibutyl phthalate, 0.05 to 0.08% of sodium benzoate, 0.03 to 0.06% of sodium pentachlorophenate, 0.01 to 0.03% of sodium nitrite, 1 to 2% of ammonia water and 15 to 30% of water. The gloss emulsion paint has the advantages of construction convenience, bright coating, strong color retention, good water resistance and good weatherability.
Description
Technical field
The present invention relates to a kind of trade sales coating, be specifically related to a kind of light emulsion coatings that has.
Background technology
Emulsion coatings is to be one type of coating of main film forming substance with the high molecular synthetic resin emulsion, and emulsion particle diameter is thin more, and gloss is high more, when emulsion particle diameter carefully again during wider distribution, can obtain the gloss height and cut flowability the light emulsion coatings is arranged preferably.Existing have the light emulsion coatings to be mainly the alkyd emulsion gloss paint, and such coating gloss is better, but poor-performings such as its preservative property, water tolerance.
Summary of the invention
Goal of the invention: the present invention is in order to solve the deficiency of prior art, a kind of easy construction is provided, the light of filming, water-tolerant the light emulsion coatings arranged.
The technical scheme that the present invention adopts: a kind of have a light emulsion coatings; Formulated by b-propylene copolymer emulsion, white titanium pigment, Sodium hexametaphosphate 99, terepthaloyl moietie, tributyl phosphate, Witcizer 300, Sodium Benzoate, sodium pentachlorophenate, Sodium Nitrite, ammoniacal liquor, water, the mass percent of its each component is:
B-propylene copolymer emulsion 35-55%
White titanium pigment 25-45%
Sodium hexametaphosphate 99 1.0-1.8%
Terepthaloyl moietie 5-7%
Tributyl phosphate 0.15-0.2%
Witcizer 300 1.5-2.5%
Sodium Benzoate 0.05-0.08%
Sodium pentachlorophenate 0.03-0.06%
Sodium Nitrite 0.01-0.03%
Ammoniacal liquor 1-2%
Water 15-30%.
As preferably, described white titanium pigment is a Rutile type Titanium Dioxide.
Provided by the invention have the light emulsion coatings when construction, is main with brushing and roller coat, and the base material light requirement is sliding, smooth, and the construction environment temperature must not be lower than the coating minimum film-forming temperature.
Beneficial effect: the present invention compared with prior art, its remarkable advantage is: provided by the invention have that the easy construction of light emulsion coatings, the light of filming, tint retention are strong, fast drying, and this coating also has excellent water tolerance and weathering resistance simultaneously.
Embodiment
Embodiment 1
For use with stirring after 0.03 kilogram of sodium pentachlorophenate, 0.05 kilogram of Sodium Benzoate and 0.02 kilogram of adding of the Sodium Nitrite water dissolution; With 25 kilograms of white titanium pigments, 1 kilogram of Sodium hexametaphosphate 99,5 kilograms of terepthaloyl moietie, 0.15 kilogram of tributyl phosphate, 1.75 kilograms of Witcizer 300s and 20 kg water add to carry out in the impeller pre-dispersed; After impeller making beating, grind through sand mill, it is for use to grind to form slurry again; Using ammoniacal liquor to be neutralized to the pH value 48 kilograms of b-propylene copolymer emulsions is 8; Add the mixture of the sodium pentachlorophenate, Sodium Benzoate and the Sodium Nitrite that stir after the dissolving in the above-mentioned steps and ground slurry then; Under low speed, stir, promptly made the light emulsion coatings after filtering.
Embodiment 2
For use with stirring after 0.05 kilogram of sodium pentachlorophenate, 0.08 kilogram of Sodium Benzoate and 0.02 kilogram of adding of the Sodium Nitrite water dissolution; With 35 kilograms of white titanium pigments, 1 kilogram of Sodium hexametaphosphate 99,6 kilograms of terepthaloyl moietie, 0.15 kilogram of tributyl phosphate, 1.7 kilograms of Witcizer 300s and 20 kg water add to carry out in the impeller pre-dispersed; After impeller making beating, grind through sand mill, it is for use to grind to form slurry again; Using ammoniacal liquor to be neutralized to the pH value 36 kilograms of b-propylene copolymer emulsions is 8; Add the mixture of the sodium pentachlorophenate, Sodium Benzoate and the Sodium Nitrite that stir after the dissolving in the above-mentioned steps and ground slurry then; Under low speed, stir, promptly made the light emulsion coatings after filtering.
Embodiment 3
For use with stirring after 0.06 kilogram of sodium pentachlorophenate, 0.08 kilogram of Sodium Benzoate and 0.03 kilogram of adding of the Sodium Nitrite water dissolution; With 40 kilograms of white titanium pigments, 1.63 kilograms of Sodium hexametaphosphate 99s, 7 kilograms of terepthaloyl moietie, 0.2 kilogram of tributyl phosphate, 1.7 kilograms of Witcizer 300s and 20 kg water, it is for use to grind to form slurry; Using ammoniacal liquor to be neutralized to the pH value 31 kilograms of b-propylene copolymer emulsions is 8; Add the mixture of the sodium pentachlorophenate, Sodium Benzoate and the Sodium Nitrite that stir after the dissolving in the above-mentioned steps and ground slurry then; Under low speed, stir, promptly made the light emulsion coatings after filtering.
Claims (2)
1. one kind has the light emulsion coatings; It is characterized in that: described have the light emulsion coatings formulated by b-propylene copolymer emulsion, white titanium pigment, Sodium hexametaphosphate 99, terepthaloyl moietie, tributyl phosphate, Witcizer 300, Sodium Benzoate, sodium pentachlorophenate, Sodium Nitrite, ammoniacal liquor, water, and the mass percent of its each component is:
B-propylene copolymer emulsion 35-55%
White titanium pigment 25-45%
Sodium hexametaphosphate 99 1.0-1.8%
Terepthaloyl moietie 5-7%
Tributyl phosphate 0.15-0.2%
Witcizer 300 1.5-2.5%
Sodium Benzoate 0.05-0.08%
Sodium pentachlorophenate 0.03-0.06%
Sodium Nitrite 0.01-0.03%
Ammoniacal liquor 1-2%
Water 15-30%.
2. according to claim 1 have a light emulsion coatings, and it is characterized in that: described white titanium pigment is a Rutile type Titanium Dioxide.