CN103409102A - 一种夹层玻璃用胶粘剂及其制备方法 - Google Patents

一种夹层玻璃用胶粘剂及其制备方法 Download PDF

Info

Publication number
CN103409102A
CN103409102A CN2013103202091A CN201310320209A CN103409102A CN 103409102 A CN103409102 A CN 103409102A CN 2013103202091 A CN2013103202091 A CN 2013103202091A CN 201310320209 A CN201310320209 A CN 201310320209A CN 103409102 A CN103409102 A CN 103409102A
Authority
CN
China
Prior art keywords
laminated glass
silicone resin
adhesion agent
agent
tackiness agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013103202091A
Other languages
English (en)
Other versions
CN103409102B (zh
Inventor
余剑军
胡小刚
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
JUN YI CHEMICAL TECHNOLOGY Co Ltd
Original Assignee
JUN YI CHEMICAL TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by JUN YI CHEMICAL TECHNOLOGY Co Ltd filed Critical JUN YI CHEMICAL TECHNOLOGY Co Ltd
Priority to CN201310320209.1A priority Critical patent/CN103409102B/zh
Publication of CN103409102A publication Critical patent/CN103409102A/zh
Application granted granted Critical
Publication of CN103409102B publication Critical patent/CN103409102B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种夹层玻璃用胶粘剂及其制备方法，夹层玻璃用胶粘剂，按重量百分比包括以下组分：有机硅树脂70-95％；增稠剂5-10％；促进剂1-3％；催化剂1-6％。6、夹层玻璃用胶粘剂制备方法，包括步骤：(1)在分散缸中先加入有机硅树脂190-200份，开启搅拌；(2)分别加入5-8份纤维素，2份钛酸正丁酯和3-4份有机锡；(3)澄清若干分钟。本发明胶粘剂粘接力强，玻璃层间不易结集水气，透明性好，溶剂挥发少，吸潮，接近100％固体份，是一种理想的环保型粘结剂。

Description

一种夹层玻璃用胶粘剂及其制备方法
技术领域
本发明涉及一种胶粘剂，具体涉及一种夹层玻璃用胶粘剂及其制备方法。 
背景技术
玻璃大面积粘接时都需要用胶粘剂，市场迫切需要粘接力强、层间不易有水气、透明性好且环保的胶粘剂。 
发明内容
本发明要解决的技术问题是提供一种夹层玻璃用胶粘剂及其制备方法。 
本发明为解决上述技术问题所采用的技术方案为： 
一种夹层玻璃用胶粘剂，按重量百分比包括以下组分： 
Figure BDA00003573353100011
Figure BDA00003573353100021
根据本发明的实施例，所述有机硅树脂设为含甲氧基的有机硅树脂。 
根据本发明的实施例，所述增稠剂设为纤维素。 
根据本发明的实施例，所述促进剂设为钛酸正丁酯。 
根据本发明的实施例，所述催化剂设为有机锡。 
一种夹层玻璃用胶粘剂制备方法，包括步骤： 
(1)在分散缸中先加入有机硅树脂190-200份，开启搅拌； 
(2)分别加入5-8份纤维素，2份钛酸正丁酯和3-4份有机锡； 
(3)澄清若干分钟。 
根据本发明的实施例，所述步骤(3)包括步骤：澄清20分钟至透明。 
根据本发明的实施例，还包括步骤： 
(4)检测； 
(5)包装。 
根据本发明的实施例，所述有机硅树脂设为含甲氧基的有机硅树脂。 
本发明的有益效果：本发明胶粘剂粘接力强，玻璃层间不易结集水 气，透明性好，溶剂挥发少，吸潮，接近100％固体份，是一种理想的环保型粘结剂。 
具体实施方式
下面根据实施例对本发明作进一步详细说明： 
本发明夹层玻璃用胶粘剂，按重量百分比包括以下组分： 
实施例1： 
(1)在分散缸中先加入含甲氧基的有机硅树脂190公斤，开启搅拌； 
(2)分别加入5公斤纤维素，2公斤钛酸正丁酯和3公斤有机锡； 
(3)澄清20分钟至透明； 
(4)检测； 
(5)包装。 
实施例2： 
(1)在分散缸中先加入含甲氧基的有机硅树脂200公斤，开启搅 拌； 
(2)分别加入8公斤纤维素，2公斤钛酸正丁酯和4公斤有机锡； 
(3)澄清20分钟至透明； 
(4)检测； 
(5)包装。 
本领域技术人员不脱离本发明的实质和精神，可以有多种变形方案实现本发明，以上所述仅为本发明较佳可行的实施例而已，并非因此局限本发明的权利范围，凡运用本发明说明书内容所作的等效结构变化，均包含于本发明的权利范围之内。 

Claims (9)

1.一种夹层玻璃用胶粘剂，其特征在于，按重量百分比包括以下组分：
有机硅树脂    70-95%
增稠剂        5-10%
促进剂        1-3%
 催化剂        1-6% 。
2.根据权利要求1所述的夹层玻璃用胶粘剂，其特征在于：所述有机硅树脂设为含甲氧基的有机硅树脂。
3.根据权利要求1所述的夹层玻璃用胶粘剂，其特征在于：所述增稠剂设为纤维素。
4.根据权利要求1所述的夹层玻璃用胶粘剂，其特征在于：所述促进剂设为钛酸正丁酯。
5.根据权利要求1所述的夹层玻璃用胶粘剂，其特征在于：所述催化剂设为有机锡。
6.一种夹层玻璃用胶粘剂制备方法，其特征在于，包括步骤：
（1）在分散缸中先加入有机硅树脂190-200份，开启搅拌；
（2）分别加入5-8份纤维素，2份钛酸正丁酯和3-4份有机锡；
（3）澄清若干分钟。
7.根据权利要求6所述的夹层玻璃用胶粘剂制备方法，其特征在于，所述步骤（3）包括步骤：澄清20分钟至透明。
8.根据权利要求6所述的夹层玻璃用胶粘剂制备方法，其特征在于，还包括步骤：
（4）检测；
（5）包装。
9.根据权利要求6所述的夹层玻璃用胶粘剂制备方法，其特征在于：所述有机硅树脂设为含甲氧基的有机硅树脂。
CN201310320209.1A 2013-07-26 2013-07-26 一种夹层玻璃用胶粘剂及其制备方法 Active CN103409102B (zh)