CN103408286B - A kind of preparation method of large-scale jade construction material - Google Patents
A kind of preparation method of large-scale jade construction material Download PDFInfo
- Publication number
- CN103408286B CN103408286B CN201310250230.9A CN201310250230A CN103408286B CN 103408286 B CN103408286 B CN 103408286B CN 201310250230 A CN201310250230 A CN 201310250230A CN 103408286 B CN103408286 B CN 103408286B
- Authority
- CN
- China
- Prior art keywords
- jade
- high temperature
- temperature furnace
- preparation
- raw material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
1), collect the rejectable waste of jade the invention discloses a kind of preparation method of large-scale jade construction material, include following operating procedure:, select to go to give up, clean decontamination processing; 2), get the raw material of following mass fraction: only expect jade material 15%, calcite in powder 33%, quartz powder 50%, other pigments 2%, mixed raw material is dropped into high temperature furnace, heating-up temperature remains on 2100 DEG C, and pressure is controlled at 4200Pa; 3), treat the fusing clarification of high temperature furnace solution, all change into water slurry shape, pour mould molding into, after 1 hour, put into cold water and soak more than 4 hours annealing; 4), the blank after annealing is carried out to Seiko is chiseled and carved again, sanding and polishing, inspection finished product. Jade carving rejectable waste is collected and added the physics mode such as calcite, quartz powder and other painted elements that their fusing is become to the generous jade building decorative material of natural beauty, can need to produce qualified products by building and ornament materials specification.
Description
Technical field
The present invention relates to waste material and be reduced into the materials such as natural large-scale jade building decorative material by physical technique, specifically belong to a kind of preparation method of large-scale jade construction material.
Background technology
There is great change several times in China from ancient times to the present building and ornament materials. Utilize from the beginning that stone riprap base, branch leaf etc. are original develops into civil construction, reinforced concrete construction frosted etc., then to granite and marble and pottery. So far ceramic tile remains main building and ornament materials, but they more or less contain the harmful substance such as radiation and lead, are unfavorable for people's health, and prolonged application is caused carninomatosis and occurred.
Because most love life person wants to seek a kind of new, radiationless, unleaded innocuous substance, beautiful generous building and ornament materials.
Summary of the invention
The object of this invention is to provide a kind of preparation method of large-scale jade construction material, jade carving rejectable waste is collected and added the physics mode such as calcite, quartz powder and other painted elements that their fusing is become to the generous jade building decorative material of natural beauty, can need to produce qualified products by building and ornament materials specification.
The technical solution used in the present invention is as follows:
A preparation method for large-scale jade construction material, includes following operating procedure:
1), collect the rejectable waste of jade, select to go to give up, clean decontamination processing;
2), get the raw material of following mass fraction: only expect jade material 15%, calcite in powder 33%, quartz powder 50%, other pigments 2%, mixed raw material is dropped into high temperature furnace, heating-up temperature remains on 2000-2200 DEG C, and pressure is controlled at 4200Pa left and right;
3), treat the fusing clarification of high temperature furnace solution, all change into water slurry shape, pour mould molding into, after 1 hour, put into cold water and soak more than 4 hours annealing;
4), the blank after annealing is carried out to Seiko is chiseled and carved again, sanding and polishing, inspection finished product.
The heating-up temperature of described high temperature furnace remains on 2100 DEG C, and pressure is controlled at 4200Pa.
Beneficial effect of the present invention is as follows: 1, turn waste into wealth, improve the added value of non-metallic ore, walk the Road of Cyclic Economy; 2, press building decoration color needs, make desirable material elegant in appearance; 3, radiationless, prevent that the harmful substances such as lead from entering building decorative product, improves people's living standard; 4, after this patented technology application, change existing building ornament materials, can need to produce qualified products by building and ornament materials specification; 5, can export goods and earn foreign currency; 6, prospect potentiality are large.
Detailed description of the invention
A preparation method for large-scale jade construction material, includes following operating procedure:
1), collect the rejectable waste of jade, select to go to give up, clean decontamination processing;
2), get the raw material of following mass fraction: only expect jade material 15%, calcite in powder 33%, quartz powder 50%, other pigments 2%, mixed raw material is dropped into high temperature furnace, heating-up temperature remains on 2100 DEG C, and pressure is controlled at 4200Pa;
3), treat the fusing clarification of high temperature furnace solution, all change into water slurry shape, pour mould molding into, after 1 hour, put into cold water and soak more than 4 hours annealing;
4), the blank after annealing is carried out to Seiko is chiseled and carved again, sanding and polishing, inspection finished product.
Claims (2)
1. a preparation method for large-scale jade construction material, is characterized in that, includes following operating procedure:
1), collect the rejectable waste of jade, select to go to give up, clean decontamination processing;
2), get the raw material of following mass fraction: only expect jade material 15%, calcite in powder 33%, quartz powder 50%, other pigments 2%, mixed raw material is dropped into high temperature furnace, heating-up temperature remains on 2000-2200 DEG C, and pressure is controlled at 4200Pa;
3), treat the fusing clarification of high temperature furnace solution, all change into water slurry shape, pour mould molding into, after 1 hour, put into cold water and soak more than 4 hours annealing;
4), the blank after annealing is carried out to Seiko is chiseled and carved again, sanding and polishing, inspection finished product.
2. the preparation method of large-scale jade construction material according to claim 1, is characterized in that, the heating-up temperature of described high temperature furnace remains on 2100 DEG C, and pressure is controlled at 4200Pa.