CN103408281A - 一种保温隔热材料 - Google Patents

一种保温隔热材料 Download PDF

Info

Publication number
CN103408281A
CN103408281A CN2013102834060A CN201310283406A CN103408281A CN 103408281 A CN103408281 A CN 103408281A CN 2013102834060 A CN2013102834060 A CN 2013102834060A CN 201310283406 A CN201310283406 A CN 201310283406A CN 103408281 A CN103408281 A CN 103408281A
Authority
CN
China
Prior art keywords
parts
thermal insulation
sepiolite
grams
insulation material
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102834060A
Other languages
English (en)
Inventor
陆静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN2013102834060A priority Critical patent/CN103408281A/zh
Publication of CN103408281A publication Critical patent/CN103408281A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种保温隔热材料，该材料组分按重量份为：复合海泡石100-120份；珍珠岩30-40份；玻缕石12-15份；碳酸镁18-22份；水镁石6-8份；硅酸铝纤维棉1-3份；硅酸锂5-8份；羧甲基纤维素5-8份；聚乙烯醇2-3份。本发明的优点是：在上述配方中玻缕石、复合海泡石、水镁石都含有纤维状的硅酸镁，特性之一是可吸附自身重量150％的水分，水分干燥后留下含微孔的纤维，硅酸铝纤维棉也是纤维状，此类纤维状材料构成了本发明保温材料的骨架结构，配方中珍珠岩是颗粒(带微孔)状，填充在材料的纤维骨架中，使得本发明保温材料能够有效隔阻热传导、对流和辐射。

Description

一种保温隔热材料
技术领域
本发明涉及一种隔热材料，尤其涉及一种保温隔热材料。
背景技术
目前保温材料多处于单一结构，如岩棉、玻璃纤维、陶瓷纤维等及制品属纤维状结构，珍珠岩、陶瓷微珠等属于颗粒微孔结构。这些单一结构的保温材料使用过程中都存在着保温性能因材料结构和施工而大大降低的问题。因此，需要提供一种新的技术方案来解决上述问题。
发明内容
本发明的目的是提供一种保温性能好的保温隔热材料。
本发明采用的技术方案：
一种保温隔热材料，该材料组分按重量份为： 
复合海泡石        100-120份；
珍珠岩              30-40份；
玻缕石              12-15份；
碳酸镁              18-22份；
水镁石               6-8份；
硅酸铝纤维棉         1-3份； 
硅酸锂               5-8份；
羧甲基纤维素         5-8份；
聚乙烯醇             2-3份。
所述复合海泡石为一级海泡石、二级海泡石与三级海泡石按质量比为1:3-5:10-12。
硅酸铝纤维棉中加入60-80℃的热水，在合成釜内，搅拌20-30分钟，待用。
对玻缕石表面采用质量浓度5%稀硫酸进行活化处理。
本发明的优点是：在上述配方中玻缕石、复合海泡石、水镁石都含有纤维状的硅酸镁，特性之一是可吸附自身重量150％的水分，水分干燥后留下含微孔的纤维，硅酸铝纤维棉也是纤维状，此类纤维状材料构成了本发明保温材料的骨架结构，配方中珍珠岩是颗粒( 带微孔) 状，填充在材料的纤维骨架中，使得本发明保温材料能够有效隔阻热传导、对流和辐射。
具体实施方式
下述实施例仅用于说明本发明，但并不能限定本发明的保护范围。
实施例1
一种保温隔热材料，该材料组分为： 
复合海泡石            100克；
珍珠岩                 30克；
玻缕石                 12克；
碳酸镁                 18克；
水镁石                  6克；
硅酸铝纤维棉           1克； 
硅酸锂                 5克；
羧甲基纤维素           5克；
聚乙烯醇               2克。
复合海泡石为一级海泡石、二级海泡石与三级海泡石按质量比为1:3:10；硅酸铝纤维棉中加入60℃的热水，在合成釜内，搅拌20分钟，待用；对玻缕石表面采用质量浓度5%稀硫酸进行活化处理。
实施例2
一种保温隔热材料，该材料组分为： 
复合海泡石            110克；
珍珠岩                 35克；
玻缕石                 13克；
碳酸镁                 20克；
水镁石                  7克；
硅酸铝纤维棉            2克； 
硅酸锂                  6克；
羧甲基纤维素            6克；
聚乙烯醇                2克。
复合海泡石为一级海泡石、二级海泡石与三级海泡石按质量比为1:4:11；硅酸铝纤维棉中加入70℃的热水，在合成釜内，搅拌25分钟，待用；对玻缕石表面采用质量浓度5%稀硫酸进行活化处理。
实施例3
一种保温隔热材料，该材料组分为： 
复合海泡石            120克；
珍珠岩                 40克；
玻缕石                 15克；
碳酸镁                 22克；
水镁石                  8克；
硅酸铝纤维棉            3克； 
硅酸锂                  8克；
羧甲基纤维素            8克；
聚乙烯醇                3克。
复合海泡石为一级海泡石、二级海泡石与三级海泡石按质量比为1:5:12；硅酸铝纤维棉中加入80℃的热水，在合成釜内，搅拌30分钟，待用；对玻缕石表面采用质量浓度5%稀硫酸进行活化处理。
采用复合海泡石，复合海泡石分为一级海泡石、二级海泡石与三级海泡石，是一种高效节能保温材料，五毒、无味，对环境和人体无害，经济，可节约成本。
在上述配方中玻缕石、复合海泡石、水镁石都含有纤维状的硅酸镁，特性之一是可吸附自身重量150％的水分，水分干燥后留下含微孔的纤维，硅酸铝纤维棉也是纤维状，此类纤维状材料构成了本发明保温材料的骨架结构，配方中珍珠岩是颗粒( 带微孔) 状，填充在材料的纤维骨架中，使得本发明保温材料能够有效隔阻热传导、对流和辐射。

Claims (4)

1.一种保温隔热材料，其特征在于：该材料组分按重量份为： 
复合海泡石        100-120份；
珍珠岩              30-40份；
玻缕石              12-15份；
碳酸镁              18-22份；
水镁石               6-8份；
硅酸铝纤维棉         1-3份； 
硅酸锂               5-8份；
羧甲基纤维素         5-8份；
聚乙烯醇             2-3份。
2.根据权利要求1所述的一种保温隔热材料，其特征在于：所述复合海泡石为一级海泡石、二级海泡石与三级海泡石按质量比为1:3-5:10-12。
3.根据权利要求1所述的一种保温隔热材料，其特征在于：硅酸铝纤维棉中加入60-80℃的热水，在合成釜内，搅拌20-30分钟，待用。
4.根据权利要求1所述的一种保温隔热材料，其特征在于：对玻缕石表面采用质量浓度5%稀硫酸进行活化处理。
CN2013102834060A 2013-07-08 2013-07-08 一种保温隔热材料 Pending CN103408281A (zh)