CN103397278A - 多元低合金耐磨铸钢及其制备方法 - Google Patents
多元低合金耐磨铸钢及其制备方法 Download PDFInfo
- Publication number
- CN103397278A CN103397278A CN201310271443XA CN201310271443A CN103397278A CN 103397278 A CN103397278 A CN 103397278A CN 201310271443X A CN201310271443X A CN 201310271443XA CN 201310271443 A CN201310271443 A CN 201310271443A CN 103397278 A CN103397278 A CN 103397278A
- Authority
- CN
- China
- Prior art keywords
- hour
- cast steel
- insulation
- wear resistant
- low alloy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种多元低合金耐磨铸钢，其特征在于所述铸钢的化学成分及其质量百分比为：碳0.20-0.26、锰1.15-1.35、硅1.75-1.90、磷≤0.040、硫≤0.040、镍0.60-0.75、钒0.25-0.35、Mo0.03-0.05、Zn0.58-0.91、In0.2-0.3、As0.15-0.18、Sb0.05-0.06、Bi0.09-0.12，基质为铁。本发明具有较好的机械力学性能，以低价硅、锰为主要合金元素，可制造球磨机衬板、挖掘机斗齿等抗磨部件。
Description
技术领域
本发明属于钢铁铸造技术，具体是一种铸钢及制备方法。
背景技术
铸钢是在凝固过程中不经历共晶转变的用于生产铸件的铁基合金的总称。铸钢分为铸造碳钢、铸造低合金钢和铸造特种钢3类。对于强度、塑性和韧性要求更高的机器零件，需要采用铸钢件，现有铸钢存在屈服强度、抗拉强度均较低、抗冲击性等机械力学性能指标较低，已不能满足产品对材料力学性能的要求。
发明内容
本发明的目的是提供一种多元低合金耐磨铸钢及其制备方法，具有较好的机械力学性能。
本发明的技术方案如下：
多元低合金耐磨铸钢，其特征在于所述铸钢的化学成分及其质量百分比为：碳0.20-0.26、锰1.15-1.35、硅1.75-1.90、磷≤0.040、硫≤0.040、镍0.60-0.75、钒0.25-0.35、Mo0.03-0.05、Zn0.58-0.91、In0.2-0.3、As0.15-0.18、Sb0.05-0.06、Bi0.09-0.12，基质为铁。
所述的多元低合金耐磨铸钢的制备方法，其特征在于：将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1590-1650℃ ；然后进行铸件的后续热处理：先由室温以160-190℃/小时速率升温至915-945℃，保温3-4小时；再以120-140℃/小时速率降温至420-440℃，保温1-2小时；再以120-130℃/小时速率降温至180-230℃，保温2-3小时；再以150-170℃/小时速率升温至520-540℃，保温2-3小时；再以再以110-130℃/小时速率升温至720-740℃，保温2-3小时，取出放入200-240℃淬火油中，随油冷却即得。
所述的精炼剂由下列重量份原料混合压块而成：碳酸钡3-3.2、四硼酸钠2.3-2.6、海泡石粉5-6、氟化铝钠1.3-1.5、明矾3-4、SnO21.1-1.3、Bi2O34.1-4.3、二硼化钒1.6-1.8、碳化铌2.3-2.5。
本发明具有较好的机械力学性能，以低价硅、锰为主要合金元素，可制造球磨机衬板、挖掘机斗齿等抗磨部件。
具体实施方式
多元低合金耐磨铸钢，所述铸钢的化学成分及其质量百分比为：碳0.20-0.26、锰1.15-1.35、硅1.75-1.90、磷≤0.040、硫≤0.040、镍0.60-0.75、钒0.25-0.35、Mo0.03-0.05、Zn0.58-0.91、In0.2-0.3、As0.15-0.18、Sb0.05-0.06、Bi0.09-0.12，基质为铁。
制备方法，将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1590-1650℃ ；然后进行铸件的后续热处理：先由室温以160-190℃/小时速率升温至915-945℃，保温3-4小时；再以120-140℃/小时速率降温至420-440℃，保温1-2小时；再以120-130℃/小时速率降温至180-230℃，保温2-3小时；再以150-170℃/小时速率升温至520-540℃，保温2-3小时；再以再以110-130℃/小时速率升温至720-740℃，保温2-3小时，取出放入200-240℃淬火油中，随油冷却即得。
所述的精炼剂由下列重量份（公斤）原料混合压块而成：碳酸钡3、四硼酸钠2.3、海泡石粉6、氟化铝钠1.3、明矾3、SnO21.1、Bi2O34.1、二硼化钒1.6、碳化铌2.3。
本发明超高强度铸钢的机械性能为：拉伸强度1380MPa，屈服强度893MPa，延伸率12％，断面收缩率23％，冲击吸收功66J，冲击韧性76J/cm2，硬度295HB。
Claims (2)
1.一种多元低合金耐磨铸钢，其特征在于所述铸钢的化学成分及其质量百分比为：碳0.20-0.26、锰1.15-1.35、硅1.75-1.90、磷≤0.040、硫≤0.040、镍0.60-0.75、钒0.25-0.35、Mo0.03-0.05、Zn0.58-0.91、In0.2-0.3、As0.15-0.18、Sb0.05-0.06、Bi0.09-0.12，基质为铁。
2.根据权利要求1所述的多元低合金耐磨铸钢的制备方法，其特征在于：将各配料放入于工业电弧炉中进行熔炼，检测合金成分含量并添加相应成分至达标，加入精炼剂精炼，搅拌10-15分钟，扒渣，并浇注成铸件，浇注温度为1590-1650℃ ；然后进行铸件的后续热处理：先由室温以160-190℃/小时速率升温至915-945℃，保温3-4小时；再以120-140℃/小时速率降温至420-440℃，保温1-2小时；再以120-130℃/小时速率降温至180-230℃，保温2-3小时；再以150-170℃/小时速率升温至520-540℃，保温2-3小时；再以110-130℃/小时速率升温至720-740℃，保温2-3小时，取出放入200-240℃淬火油中，随油冷却即得。