CN103396166A - 一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法 - Google Patents

一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法 Download PDF

Info

Publication number
CN103396166A
CN103396166A CN2013103363500A CN201310336350A CN103396166A CN 103396166 A CN103396166 A CN 103396166A CN 2013103363500 A CN2013103363500 A CN 2013103363500A CN 201310336350 A CN201310336350 A CN 201310336350A CN 103396166 A CN103396166 A CN 103396166A
Authority
CN
China
Prior art keywords
glaze
raw material
crystal
zinc oxide
granite
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013103363500A
Other languages
English (en)
Inventor
蔣述兴
刘丹阳
秦志东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guilin University of Technology
Original Assignee
Guilin University of Technology
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guilin University of Technology filed Critical Guilin University of Technology
Priority to CN2013103363500A priority Critical patent/CN103396166A/zh
Publication of CN103396166A publication Critical patent/CN103396166A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法。添加助熔物质滑石、成晶物质氧化锌、熔融石英以及着色剂二氧化锰，并进行湿法球磨；运用非定向成核方法——在坯体上人工点种40～50目（0.300～0.425㎜）经煅烧的氧化锌颗粒作为晶种，使产品晶花在点种晶种位置上定位生长，解决了传统结晶釉产品晶花杂乱无序的现象；并在合理的烧成制度下制备出了硅酸锌结晶釉产品。本发明用料简单，生产方法简单易行，能节省原料成本，利用人工点种晶核的成核方法，真正做到了晶体的定位生长，利用花岗岩为主要原料制备较为名贵的结晶釉产品，提高了花岗岩废料的利用价值。

Description

一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法
技术领域
本发明涉及陶瓷结晶釉的制备方法，特别是利用花岗岩废料为基础釉原料制备陶瓷硅酸锌结晶釉的方法。
背景技术
结晶釉作为一种装饰性很强的艺术釉，很受消费者的青睐。随着现代社会的发展，陶瓷釉需求量与日俱增，传统釉料中所需的长石、石英的矿源日益减少，急需其它矿源的取代。花岗岩废料广泛存在于生产开采、加工成形、日常装修产生的废弃边角料中，目前没有得到较好的利用，特别是作为废渣形式存在的花岗岩，目前只作为废弃物丢弃处理。花岗岩的主要矿物成分为长石和石英以及少量的杂质元素，能够用来替代传统长石和石英，以制备陶瓷釉料。这样既解决了花岗岩浪费问题，又降低了制釉工业的生产成本。传统硅酸锌结晶釉的制备需要用到多种矿物原料，基础釉用的原料有石英、长石、粘土、碳酸钙、玻璃粉等矿物原料，一般要经过选矿提纯或加工处理才能获得这些原料，这样就增加了原料成本。
发明内容[0003] 本发明的目的是提供一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法。
具体步骤为：
（1）原料的质量百分比分别为：花岗岩50%～58%、滑石7%～13%、熔融石英7%～13%、氧化锌17%～22%和着色剂1%～2%，将上述原料混合湿法球磨得釉料，氧化铝球、原料和水的质量比为2:1:0.8。
（2）以先刷釉后浸釉的方法将步骤（1）所得釉料施于坯体表面，刷釉使用毛刷刷两层釉，待釉片干燥后浸釉两次。
（3）将步骤（2）所得产物在指定位置点种40～50目（0.300～0.425㎜）的氧化锌颗粒作为晶种，人工点种在指定位置，以达到晶花定位生长的效果。
（4）将步骤（3）所得产物烘干后放入硅钼炉中进行烧制，烧成制度为：室温～1000℃用时3.2小时，1000℃～1350℃用时2小时，1350℃保温20分钟，1350℃～1230℃用时60分钟，1230℃保温2.5小时，最后随炉温冷却至室温。
所述着剂为二氧化锰。
所述氧化锌、作为晶种的氧化锌颗粒和二氧化锰均为分析纯。
本发明基础釉原料不需要高品质的长石、粘土等矿物，因此省去了矿物原料的选矿提纯或加工处理工艺，还省去了基础釉原料中长石、粘土等矿物的配料计算和混合这样的烦杂过程，并可以克服对基础釉原料难以混合均匀的缺点。基础釉原料只用花岗岩废料矿石和少量石英，原料易得，价格低廉，配料品种简单，所制的生釉料不含有毒物质，对坯体适应性强，熔融性较好。还具有产品釉面光亮、机械性能好的优点。
而本发明只需球磨花岗岩、石英与滑石，能节省原料成本。本发明利用人工点种晶核的成核方法，真正做到了晶体的定位生长。利用花岗岩为主要原料制备较为名贵的结晶釉产品，提高了花岗岩的利用价值。
附图说明
图1为本发明实施例的产品照片。
具体实施方式
实施例：
（1）原料的质量百分比分别为：花岗岩55.8%、滑石11.9%、氧化锌20.5%、熔融石英10.8%和着色剂二氧化锰1%，将上述原料混合湿法球磨（各原料化学成分见表1，氧化锌和二氧化锰为分析纯）得釉料，氧化铝球、原料和水的质量比为2:1:0.8；釉浆的粒度参数为：D10=1.93μm，D50=12.24μm，D97=34.79μm。
（2）以先刷釉后浸釉的方法将步骤（1）所得釉料施于坯体表面（坯体化学成分见表2），刷釉使用毛刷刷两层釉，待釉片干燥后浸釉两次。
（3）将步骤（2）所得产物在指定位置点种40～50目（0.300～0.425㎜）的氧化锌颗粒作为晶种，人工点种在指定位置，以达到晶花定位生长的效果。
（4）将步骤（3）所得产物烘干后放入硅钼炉中进行烧制，烧成制度为：室温～1000℃用时3.2小时，1000℃～1350℃用时2小时，1350℃保温20分钟，1350℃～1230℃用时60分钟，1230℃保温2.5小时，最后随炉温冷却至室温。取出样品可得到精美的结晶釉产品，见附图。
表1：花岗岩、滑石和石英的化学成分（质量百分比）/%
原料 SiO 2 TiO 2 Al 2 O3 Fe 2 O 3 FeO MgO CaO Na 2 O K 2 O I.L
花岗岩 72.18 0.34 13.31  0.85 2.43 0.33 1.18 3.33 1.80 —
滑石 58.03 0.035 0.42 0.082 — 31.03 2.08 0.026 0.099 7.64
熔融石英 99.5 — — — — — — — — —
表2：坯体的化学成分（质量百分比）/%
名称 SiO 2 Al 2 O 3 CaO MgO Fe 2 O3 K 2 O Na 2 O TiO 2 I.L
坯体 63.67 22.67 0.72 1.01 0.71 4.16 1.80 0.23 4.84

Claims (1)

1.一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法，其特征在于具体步骤为：
（1）原料的质量百分比分别为：花岗岩50%～58%、滑石7%～13%、熔融石英7%～13%、氧化锌17%～22%和着色剂1%～2%，将上述原料混合湿法球磨得釉料，氧化铝球、原料和水的质量比为2:1:0.8；
（2）以先刷釉后浸釉的方法将步骤（1）所得釉料施于坯体表面，刷釉使用毛刷刷两层釉，待釉片干燥后浸釉两次；
（3）将步骤（2）所得产物在指定位置点种40～50目即0.300～0.425㎜的氧化锌颗粒作为晶种；
（4）将步骤（3）所得产物烘干后放入硅钼炉中进行烧制，烧成制度为：室温～1000℃用时3.2小时，1000℃～1350℃用时2小时，1350℃保温20分钟，1350℃～1230℃用时60分钟，1230℃保温2.5小时，最后随炉温冷却至室温；
所述着色剂为二氧化锰；
所述氧化锌、作为晶种的氧化锌颗粒和二氧化锰均为分析纯。
CN2013103363500A 2013-08-05 2013-08-05 一种以花岗岩为基础釉原料制备硅酸锌结晶釉的方法 Pending CN103396166A (zh)