CN103387369A - 一种防水型富冰土质注浆材料 - Google Patents

一种防水型富冰土质注浆材料 Download PDF

Info

Publication number
CN103387369A
CN103387369A CN201310333552XA CN201310333552A CN103387369A CN 103387369 A CN103387369 A CN 103387369A CN 201310333552X A CN201310333552X A CN 201310333552XA CN 201310333552 A CN201310333552 A CN 201310333552A CN 103387369 A CN103387369 A CN 103387369A
Authority
CN
China
Prior art keywords
cao
grog
grouting material
essential mineral
ice
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310333552XA
Other languages
English (en)
Other versions
CN103387369B (zh
Inventor
宫振鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
MINGYUAN NEW MATERIALS TECHNOLOGY DEVELOPMENT CO., LTD.
Original Assignee
DALIAN MINGYUANQUAN BUILDING MATERIALS Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by DALIAN MINGYUANQUAN BUILDING MATERIALS Co Ltd filed Critical DALIAN MINGYUANQUAN BUILDING MATERIALS Co Ltd
Priority to CN201310333552.XA priority Critical patent/CN103387369B/zh
Publication of CN103387369A publication Critical patent/CN103387369A/zh
Application granted granted Critical
Publication of CN103387369B publication Critical patent/CN103387369B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种防水型富冰土质注浆材料,以C3S-C2S-
Figure 201310333552X100004DEST_PATH_IMAGE002
-CaO为主要矿物熟料、石膏、工业尾矿共同粉磨制成胶凝材料母料,然后加入粒径为6~10μm细砂或者尾矿砂加水搅拌而成。本发明的有益效果为:本发明的防水型富冰土质注浆材料采用以C3S-C2S-

Description

一种防水型富冰土质注浆材料
技术领域
本发明涉及一种建筑胶凝材料,具体是一种防水型富冰土质注浆材料。 
背景技术
传统的冬施喷射技术常采用OPC水泥加防冻剂、引气剂、速凝剂等达到降低液相冰点温度、缩短凝结时间、提高抗冻能力和获得早期强度,但在-30℃超低温的情况下,由于普通水泥的水化硬化慢,抵御超低温冻害的能力极差,必须加入大量防冻引气剂,防冻而不增强,快凝而不快硬,混凝土气泡多、抗渗差,因此混凝土的后期强度和耐久性大幅度降低。常出现开裂、酥碎、剥落、冒水、渗漏、挂冰、潮湿等隧道病害,极大影响工程质量。 
例如:在中央西部开发决策下,大批工程项目进入西部。公路、铁路、桥梁、河床、山坡均需要建设治理。国家重点项目青藏铁路格拉段需穿越547公里多年永冻土地段,除水冻土铁路路基固化,沿线海拔近5000米破碎断面、风化岩层、富(饱)冰土质、滑坡等均需支护处理外,两座全长3024米的水冻土层隧道急需超低温注浆、喷射。然而传统的材料和冬施技术不能完全满足严寒地区的施工要求,例如牙林线、嫩林线、南弱线等,永冻土层、南寒隧道由于气候严寒,隧道内普遍发生开裂、酥碎、剥落、挂冰、冒水、积水、结冰等隧道病害,严重威胁行东安全和使用寿命,养护工作繁重,治理十分困难。这主要是由于气温低,砼微结构破坏,渗透、陈融恶性循环等所致。 
发明内容
本发明的目的是提供一种防水型富冰土质注浆材料,特别适合地下工程初支后的渗漏水防治。 
本发明的技术方案是这样实现的:一种防水型富冰土质注浆材料,以C3S- C2S - 
Figure 201310333552X100002DEST_PATH_IMAGE002
-CaO为主要矿物熟料、石膏、工业尾矿共同粉磨制成胶凝材料母料,然后加入粒径为6~10μm细砂或者尾矿砂加水搅拌而成。 
母料的制法有两种,方法1:以C3S-C2S-
Figure 983741DEST_PATH_IMAGE002
-CaO为主要矿物熟料30~50%、石膏5~15%和工业尾矿15~70%。方法2:加入CAS熟料、OPC熟料混配,配比为:以C3S-C2S-
Figure 868521DEST_PATH_IMAGE002
-CaO为主要矿物熟料10~15%、CAS熟料15~25%、OPC熟料5~10%、石膏5~15%和工业尾矿15~70%。 
防水型富冰土质注浆材料 是1份胶凝材料母料加入1~3份细砂或者尾矿砂,加水量保证水灰比为0.8~1.2。 
以C3S- C2S --CaO为主要矿物熟料的制法是:在CaO-SiO2-Al2O3-Fe2O3-SO3五元系统的水泥生料中,超量引入了CaO,过量氧化钙的含量在b-CaO=5~8%之间,控制碱度系数Km=1.0~1.3范围内,在1200℃~1300℃的烧成温度下煅烧制成熟料。 
本发明的有益效果为:本发明的防水型富冰土质注浆材料采用以C3S-C2S-
Figure 648968DEST_PATH_IMAGE002
-CaO为主要矿物熟料配置而成,一般控制砂浆流动度在350mm左右,凝结时间在30~60分钟之间,28d抗压强度25Mpa以上,特别适合地下工程初支后的渗漏水防治。 
具体实施方式
下面结合具体实施例对本发明做进一步解释说明。 
实施例1以C3S-C2S--CaO为主要矿物熟料30%、石膏5%和工业尾矿65%制成凝胶材料母料,然后加入超细为尾矿粉再加水搅拌而成。原料用料为:1份胶凝材料母料加入1份超细为尾矿粉,加水量保证水灰比为0.8。 
以C3S- C2S -
Figure 311211DEST_PATH_IMAGE002
-CaO为主要矿物熟料的制法是:在CaO-SiO2-Al2O3-Fe2O3-SO3五元系统的水泥生料中,超量引入了CaO,过量氧化钙的含量在b-CaO=5~8%之间,控制碱度系数Km=1.0~1.3范围内,在1200℃~1300℃的烧成温度下煅烧制成熟料。 
实施例2以C3S-C2S-
Figure 127857DEST_PATH_IMAGE002
-CaO为主要矿物熟料10~15%、CAS熟料15~25%、OPC熟料5~10%、石膏5~15%和工业尾矿15~70%制成凝胶材料母料,然后加入超细为尾矿粉再加水搅拌而成。原料用料为:1份胶凝材料母料加入3份超细尾矿粉,加水量保证水灰比为1.1。 
以C3S-C2S-
Figure 864869DEST_PATH_IMAGE002
-CaO为主要矿物熟料的制法是:在CaO-SiO2-Al2O3-Fe2O3-SO3五元系统的水泥生料中,超量引入了CaO,过量氧化钙的含量在b-CaO=5~8%之间,控制碱度系数Km=1.0~1.3范围内,在1200℃~1300℃的烧成温度下煅烧制成熟料。 
    以上所述,仅为本发明较佳的具体实施方式,但本发明的保护范围并不局限于此,任何熟悉本技术领域的技术人员在本发明披露的技术范围内,根据本发明的技术方案及其发明构思加以等同替换或改变,都应涵盖在本发明的保护范围之内。 

Claims (6)

1.一种防水型富冰土质注浆材料,其特征在于,以C3S- C2S - 
Figure 201310333552X100001DEST_PATH_IMAGE002
-CaO为主要矿物熟料、石膏、工业尾矿共同粉磨制成胶凝材料母料,然后加入超细尾矿粉加水搅拌而成。
2.根据权利要求1所述的防水型富冰土质注浆材料,其特征在于,以C3S- C2S -
Figure 769569DEST_PATH_IMAGE002
-CaO为主要矿物熟料30~50%、石膏5~15%和工业尾矿15~70%。
3.根据权利要求1所述的超低温喷射胶凝材料,其特征在于,加入CAS熟料、OPC熟料混配,配比为:以C3S- C2S -
Figure 549306DEST_PATH_IMAGE002
-CaO为主要矿物熟料10~15%、CAS熟料15~25%、OPC熟料5~10%、石膏5~15%和工业尾矿15~70%。
4.根据权利要求1所述的防水型富冰土质注浆材料,其特征在于,所述1份胶凝材料母料加入1~3份超细尾矿粉。
5.根据权利要求1所述的防水型富冰土质注浆材料,其特征在于,加水量保证水灰比为0.8~1.1。
6.根据权利要求1所述的防水型富冰土质注浆材料,其特征在于,以C3S- C2S -
Figure 6832DEST_PATH_IMAGE002
-CaO为主要矿物熟料是在CaO-SiO2-Al2O3-Fe2O3-SO3五元系统的水泥生料中,超量引入了CaO,过量氧化钙的含量在b-CaO=5~8%之间,控制碱度系数Km=1.0~1.3范围内,在1200℃~1300℃的烧成温度下煅烧制成熟料。
CN201310333552.XA 2013-08-02 2013-08-02 一种防水型富冰土质注浆材料 Expired - Fee Related CN103387369B (zh)