CN103386702A - Composite stone-grain sandstone plate manufacturing method by using phosphorus ore tailing sand - Google Patents
Composite stone-grain sandstone plate manufacturing method by using phosphorus ore tailing sand Download PDFInfo
- Publication number
- CN103386702A CN103386702A CN2013103623194A CN201310362319A CN103386702A CN 103386702 A CN103386702 A CN 103386702A CN 2013103623194 A CN2013103623194 A CN 2013103623194A CN 201310362319 A CN201310362319 A CN 201310362319A CN 103386702 A CN103386702 A CN 103386702A
- Authority
- CN
- China
- Prior art keywords
- sandstone
- color matching
- layer
- top layer
- face brick
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A composite stone-grain sandstone plate manufacturing method by using phosphorus ore tailing sand comprises the steps related to a basement layer face brick, a middle color matching layer and a sandstone surface layer, i.e. unsaturated polyester resin is arranged on the surface of the basement layer face brick with a brush in a coating manner, then middle matched color materials are poured on the basement layer face brick to manufacture the middle color matching layer, sandstone surface layer materials are poured on the middle color matching layer to manufacture the sandstone surface layer, salt particles are poured on the surface of the sandstone surface layer and are slicked by a machine, coarse grinding is performed, and finally washing is performed with water to wash away salt adhered to the surface and expose specific micropores of a sandstone plate. A product manufactured by the method is most characterized in that the grain of serpeggiante sandstone is clear, and has the advantages of fine and smooth texture, truth, naturality,corrosion resistance, compact resistance and the like. The product can be widely applied to various plate products, various irregular-shaped plate products and complicated building veneers, and is a cheap and fine product for decorating inner and outer eaves of large hotels, airports, railway stations and office buildings.
Description
Technical field
The present invention relates to a kind of manufacturing technology of wall surface decorative plate, particularly a kind of preparation method that adopts the compound bag sand rock plate of phosphorite tailings sand material.
Background technology
Sandstone sheet material adopts characteristic earth to make as special raw material or on marble surface in the market.Weak point is: texture is unintelligible, nature, corrosion-resistant, poor impact resistance, and also large tracts of land digs to adopt and causes vegetation deterioration, causes soil erosion, and cost is low high.
Summary of the invention
The technical problem to be solved in the present invention is for the deficiencies in the prior art, has proposed a kind of clean mark, exquisite in texture, true nature, the preparation method of the compound bag sand rock plate of corrosion-resistant, impact-resistant employing phosphorite tailings sand material.
The technical problem to be solved in the present invention is achieved through the following technical solutions, and a kind of preparation method that adopts the compound bag sand rock plate of phosphorite tailings sand material, be characterized in, comprises basic unit's face brick, middle color matching layer and sandstone top layer,
Middle color matching layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 30%, 80 ~ 200 purpose phosphorite tailings sands 60%,
Different cobalt green 2 ~ 3%, methyl ethyl ketone peroxide 1 ~ 6%,
Pigment 0.2 ~ 5.5%,
Color matching material in the middle of said ratio raw material mixing and stirring is made;
The sandstone top layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 21 ~ 36%, 80 ~ 100 orders buildings fine sands 5 ~ 25%,
80 ~ 200 purpose phosphorite tailings sands 40 ~ 55%, different cobalt green 2 ~ 5%,
Methyl ethyl ketone peroxide 1 ~ 6%, pigment 0.2 ~ 5.5%,
Said ratio raw material mixing and stirring is made sandstone top layer material;
Unsaturated-resin is brushed on surface at basic unit's face brick, then centre color matching material is poured on basic unit's face brick and makes middle color matching layer, then in the middle of sandstone top layer material being poured on, the color matching layer is made the sandstone top layer, the salt particle is gone up on surface on the sandstone top layer, strike off with machine, then roughly grind, final rinse water, the salt that is bonded at surface is rinsed out, spill the distinctive micropore of sand rock plate.
The present invention compared with prior art, be not earth as raw material, prevent erosion, the protection vegetation.Adopt the outstanding feature of product that the present invention makes to be the clean mark of grain mudstone, product also has exquisite in texture simultaneously, true nature, the advantage such as corrosion-resistant, shock-resistant, the present invention can be widely used in all kinds of sheet materials, Special-shaped Plates material products, complicated architectural coating is large hotel, aircraft factory, railway station, Office Building decoration inner and outer eaves better quality products at good values.
The specific embodiment
A kind of preparation method that adopts the compound bag sand rock plate of phosphorite tailings sand material, be characterized in, comprises basic unit's face brick, middle color matching layer and sandstone top layer,
Middle color matching layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 30%, 80 ~ 200 purpose phosphorite tailings sands 60%,
Different cobalt green 2 ~ 3%, methyl ethyl ketone peroxide 1 ~ 6%,
Grey cyan serial pigment 0.2 ~ 5.5%,
Color matching material in the middle of said ratio raw material mixing and stirring is made;
The sandstone top layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 21 ~ 36%, 80 ~ 100 orders buildings fine sands 5 ~ 25%,
80 ~ 200 purpose phosphorite tailings sands 40 ~ 55%, different cobalt green 2 ~ 5%,
Methyl ethyl ketone peroxide 1 ~ 6%, pigment 0.2 ~ 5.5%,
Said ratio raw material mixing and stirring is made sandstone top layer material;
Unsaturated-resin is brushed on surface at basic unit's face brick, then centre color matching material is poured on basic unit's face brick and makes middle color matching layer, then in the middle of sandstone top layer material being poured on, the color matching layer is made the sandstone top layer, the salt particle is gone up on surface on the sandstone top layer, strike off with machine, then roughly grind, final rinse water, the salt that is bonded at surface is rinsed out, spill the distinctive micropore of sand rock plate.The transition on middle color matching layer and sandstone top layer will, by pouring how much completing of grey, cyan series into,, according to customer requirement,, according to the size of face brick, can be made the sheet material of all size model.Cut into the packaging products in boxes packing according to the actual size of sandstone sheet material finally.
Claims (1)
1. preparation method that adopts the compound bag sand rock plate of phosphorite tailings sand material is characterized in that: comprise basic unit's face brick, middle color matching layer and sandstone top layer,
Middle color matching layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 30%, 80 ~ 200 purpose phosphorite tailings sands 60%,
Different cobalt green 2 ~ 3%, methyl ethyl ketone peroxide 1 ~ 6%,
Pigment 0.2 ~ 5.5%,
Color matching material in the middle of said ratio raw material mixing and stirring is made;
The sandstone top layer is to be made by the raw material of following weight percent proportioning:
Unsaturated-resin 21 ~ 36%, 80 ~ 100 orders buildings fine sands 5 ~ 25%,
80 ~ 200 purpose phosphorite tailings sands 40 ~ 55%, different cobalt green 2 ~ 5%,
Methyl ethyl ketone peroxide 1 ~ 6%, pigment 0.2 ~ 5.5%,
Said ratio raw material mixing and stirring is made sandstone top layer material;
Unsaturated-resin is brushed on surface at basic unit's face brick, then centre color matching material is poured on basic unit's face brick and makes middle color matching layer, then in the middle of sandstone top layer material being poured on, the color matching layer is made the sandstone top layer, the salt particle is gone up on surface on the sandstone top layer, strike off with machine, then roughly grind, final rinse water, the salt that is bonded at surface is rinsed out, spill the distinctive micropore of sand rock plate.