CN103382319A - Epoxy impregnated resin and preparation method thereof - Google Patents
Epoxy impregnated resin and preparation method thereof Download PDFInfo
- Publication number
- CN103382319A CN103382319A CN2013102614959A CN201310261495A CN103382319A CN 103382319 A CN103382319 A CN 103382319A CN 2013102614959 A CN2013102614959 A CN 2013102614959A CN 201310261495 A CN201310261495 A CN 201310261495A CN 103382319 A CN103382319 A CN 103382319A
- Authority
- CN
- China
- Prior art keywords
- parts
- resin
- epoxy
- impregnated resin
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An epoxy impregnated resin and a preparation method thereof are disclosed. The epoxy impregnated resin is characterized by being composed of following raw materials in parts by weight: 32 to 35 parts of epoxy resin, 12 to 14 parts of terpolycyantoamino-formaldehyde resin, 2 to 3 parts of benzene dimethylamine tripolymer, 6 to 8 parts of phthalic anhydride, 1 to 2 parts of hydroquinone, 1 to 2 parts of tert-butyl hydroperoxide, 8 to 10 parts of methyltrichlorosilane, 1 to 2 parts of methyl tin mercaptide, 5 to 7 parts of styrene, 3 to 4 parts of vinyl carboxylate, 1 to 2 parts of nitrodracylic acid, 40 to 45 parts of xylene and 4 to 5 parts of film forming agent. The impregnated paint has the advantages of high temperature and high damp resistance, good electric insulation property, good toughness, high heatproof grade, and high mechanic strength. Heat conductivity of the impregnated resin is improved, so the expoxy impregnated resin can work at the temperature of 200 DEG C for a long term, and work at the temperature of 220 DEG C for a short term. The expoxy impregnated resin can be applied to the insulation systems, which have high requirements on heatproof grade, of motor train units motors and subway motors.
Description
Technical field
The invention belongs to the insulating material field, relate to a kind of epoxy impregnation resin and preparation method thereof.
Background technology
Pressure impregnation technique is generally adopted in the productions such as motor, transformer, wire.The workpiece preliminary drying is gone after tide cooling, be placed in vacuum environment, get rid of inner air and volatile matter, rely on paint liquid gravity in vacuum, apply the effect of certain pressure, make paint liquid rapid permeability and be full of the insulation system internal layer.This technique can obtain the paint film of continuous densification, free of pinholes.
Existing impregnating varnish is to be solidifying agent by epoxy resin as matrix resin, acid anhydrides.But the temperature resistant grade of this system cured product and toughness are not enough, need to carry out modification to epoxy anhydride impregnating varnish system, are the requirements that impregnating varnish system cured article satisfies temperature resistant grade and mechanical property simultaneously.
Summary of the invention
The purpose of this invention is to provide a kind of epoxy impregnation resin and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of epoxy impregnation resin is characterized in that being made by the raw material of following weight part:
E-44 epoxy resin 32-35, terpolycyantoamino-formaldehyde resin 12-14, benzene dimethylamine tripolymer 2-3, Tetra hydro Phthalic anhydride 6-8, Resorcinol 1-2, tertbutyl peroxide 1-2, METHYL TRICHLORO SILANE 8-10, Methyl stannum mercaptide 1-2, vinylbenzene 5-7, vinyl carboxylate 3-4, p-nitrobenzoic acid 1-2, dimethylbenzene 40-45, membrane-forming agent 4-5.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of described epoxy impregnation resin, it is characterized in that comprising the following steps: Tetra hydro Phthalic anhydride, Resorcinol, METHYL TRICHLORO SILANE, Methyl stannum mercaptide, vinylbenzene, vinyl carboxylate, p-nitrobenzoic acid, dimethylbenzene are mixed, be heated to 100-110 ℃, drip tertbutyl peroxide, stirring reaction 2-3 hour, then, add other remaining component, be warming up to 130-145 ℃, continue to stir 3-4 hour, and get final product.
High temperature resistant, the high humidity of impregnating varnish energy of the present invention, electrical insulation capability is good, good toughness, temperature resistant grade is high.Physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, 220 ℃ of short-terms, the present invention can be used for the EMUs motor, iron machine etc. to the demanding insulation system of temperature resistant grade.
Embodiment
A kind of epoxy impregnation resin, made by the raw material (kilogram) of following weight part:
E-44 epoxy resin 35, terpolycyantoamino-formaldehyde resin 14, benzene dimethylamine tripolymer 3, Tetra hydro Phthalic anhydride 8, Resorcinol 2, tertbutyl peroxide 2, METHYL TRICHLORO SILANE 10, Methyl stannum mercaptide 2, vinylbenzene 5, vinyl carboxylate 3, p-nitrobenzoic acid 2, dimethylbenzene 45, membrane-forming agent 5.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 4,582-2 aminoresin 16, polyisobutene 4, cobalt naphthenate 2, sec.-propyl distearyl acyl-oxygen base Aluminate 2, two ten four carbon alcohols esters 5, aluminium nitride 2, nano-attapulgite 2, epoxy soybean oil 4, morpholine 2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of epoxy impregnation resin, comprise the following steps: Tetra hydro Phthalic anhydride, Resorcinol, METHYL TRICHLORO SILANE, Methyl stannum mercaptide, vinylbenzene, vinyl carboxylate, p-nitrobenzoic acid, dimethylbenzene are mixed, be heated to 100-110 ℃, drip tertbutyl peroxide, stirring reaction 2-3 hour, then, add other remaining component, be warming up to 130-145 ℃, continue to stir 3-4 hour, and get final product.
Curing process: smoked under 110 ~ 150 ℃ 3-5 hour;
After it solidifies, cohesive strength is greater than 25N, and temperature classification is the H level, and volume specific resistance is not less than 1 * 1014 Ω m, and surface resistivity is not less than 1 * 1014 Ω, and after immersion, volume specific resistance is not less than 1 * 1012 Ω m, and surface resistivity is not less than 1 * 1012 Ω.Impregnating varnish of the present invention can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, and 220 ℃ of short-terms have satisfied design requirements.
Claims (2)
1. epoxy impregnation resin is characterized in that being made by the raw material of following weight part:
E-44 epoxy resin 32-35, terpolycyantoamino-formaldehyde resin 12-14, benzene dimethylamine tripolymer 2-3, Tetra hydro Phthalic anhydride 6-8, Resorcinol 1-2, tertbutyl peroxide 1-2, METHYL TRICHLORO SILANE 8-10, Methyl stannum mercaptide 1-2, vinylbenzene 5-7, vinyl carboxylate 3-4, p-nitrobenzoic acid 1-2, dimethylbenzene 40-45, membrane-forming agent 4-5;
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
2. the preparation method of epoxy impregnation resin according to claim 1, it is characterized in that comprising the following steps: Tetra hydro Phthalic anhydride, Resorcinol, METHYL TRICHLORO SILANE, Methyl stannum mercaptide, vinylbenzene, vinyl carboxylate, p-nitrobenzoic acid, dimethylbenzene are mixed, be heated to 100-110 ℃, drip tertbutyl peroxide, stirring reaction 2-3 hour, then, add other remaining component, be warming up to 130-145 ℃, continue to stir 3-4 hour, and get final product.