CN103382360A - Alkyd resin impregnating varnish and preparation method thereof - Google Patents
Alkyd resin impregnating varnish and preparation method thereof Download PDFInfo
- Publication number
- CN103382360A CN103382360A CN2013102613369A CN201310261336A CN103382360A CN 103382360 A CN103382360 A CN 103382360A CN 2013102613369 A CN2013102613369 A CN 2013102613369A CN 201310261336 A CN201310261336 A CN 201310261336A CN 103382360 A CN103382360 A CN 103382360A
- Authority
- CN
- China
- Prior art keywords
- parts
- varnish
- vinyl
- impregnating varnish
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
An alkyd impregnating varnish and a preparation method thereof are disclosed. The varnish is characterized by being composed of following raw materials in parts by weight: 40 to 45 parts of medium-oil-length alkyd resin, 24 to 26 parts of terpolycyantoamino-formaldehyde resin, 12 to 14 parts of m-phenylenediamine, 6 to 8 parts of diaminodiphenyl-methane, 3 to 4 parts of calcium naphthenate, 4 to 6 parts of dimethicone, 1 to 2 parts of triphenethylphenoxypoly(ethyleneoxy)ethanol, 2 to 3 parts of ricinoleic acid, 4 to 5 parts of vinyl tri(beta-metoxyethoxy) silane, 3 to 4 parts of styrene, 8 to 10 parts of vinyl carboxylic ester, 2 to 3 parts of tributyltin chloride and 4 to 5 parts of film forming agent. The alkyd resin impregnating varnish has the advantages of compact coating membrane, fast drying, high-temperature resistance, high dampness resistance, good electric insulation property and high mechanic performance. The heat conductivity of the varnish is improved, so the varnish can work at the temperature of 200 DEG C for a long period and at the temperature of 220 DEG C for a short period. The design requirements are fulfilled.
Description
Technical field
The invention belongs to the insulating material field, relate to a kind of Synolac impregnating varnish and preparation method thereof.
Background technology
Pressure impregnation technique is generally adopted in the productions such as motor, transformer, wire.The workpiece preliminary drying is gone after tide cooling, be placed in vacuum environment, get rid of inner air and volatile matter, rely on paint liquid gravity in vacuum, apply the effect of certain pressure, make paint liquid rapid permeability and be full of the insulation system internal layer.This technique can obtain the paint film of continuous densification, free of pinholes.
Existing Synolac impregnating varnish is to be solidifying agent by epoxy resin as matrix resin, acid anhydrides.But the temperature resistant grade of this system cured product and toughness are not enough, need to carry out modification to epoxy anhydride Synolac impregnating varnish system, are the requirements that Synolac impregnating varnish system cured article satisfies temperature resistant grade and mechanical property simultaneously.
Summary of the invention
The purpose of this invention is to provide a kind of Synolac impregnating varnish and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of Synolac impregnating varnish is characterized in that being made by the raw material of following weight part:
Medium oil alkyd 40-45, terpolycyantoamino-formaldehyde resin 24-26,
Mphenylenediamine 12-14, diaminodiphenyl-methane 6-8, calcium naphthenate 3-4, dimethyl silicone oil 4-6,Triphen ethyl phenol Soxylat A 25-7 1-2, ricinolic acid 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 4-5, vinylbenzene 3-4, vinyl carboxylate 8-10, tributyl tin trichloride 2-3, membrane-forming agent 4-5.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of described Synolac impregnating varnish is characterized in that comprising the following steps:
With dimethyl silicone oil,Triphen ethyl phenol Soxylat A 25-7, ricinolic acid, vinyl three ('beta '-methoxy oxyethyl group) silane, vinylbenzene, vinyl carboxylate mix, and are heated to 110-130 ℃, stir 2-3 hour; Then, add other remaining component, be cooled to 65-75 ℃, stirred 3-4 hour, and get final product.
It is fine and close that rational formula of the present invention, Synolac impregnating varnish form paint film, and fast drying can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, and 220 ℃ of short-terms have satisfied design requirements.
Embodiment
A kind of Synolac impregnating varnish, made by the raw material (kilogram) of following weight part:
Medium oil alkyd 45, terpolycyantoamino-formaldehyde resin 26,
Mphenylenediamine 14, diaminodiphenyl-methane 6, calcium naphthenate 4, dimethyl silicone oil 6,Triphen ethyl phenol Soxylat A 25-7 2, ricinolic acid 2, vinyl three ('beta '-methoxy oxyethyl group) silane 5, vinylbenzene 4, vinyl carboxylate 8, tributyl tin trichloride 3, membrane-forming agent 4.
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 4,582-2 aminoresin 16, polyisobutene 4, cobalt naphthenate 2, sec.-propyl distearyl acyl-oxygen base Aluminate 2, two ten four carbon alcohols esters 5, aluminium nitride 2, nano-attapulgite 2, epoxy soybean oil 4, morpholine 2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
The preparation method of Synolac impregnating varnish comprises the following steps:
With dimethyl silicone oil,Triphen ethyl phenol Soxylat A 25-7, ricinolic acid, vinyl three ('beta '-methoxy oxyethyl group) silane, vinylbenzene, vinyl carboxylate mix, and are heated to 110-130 ℃, stir 2-3 hour; Then, add other remaining component, be cooled to 65-75 ℃, stirred 3-4 hour, and get final product.
Curing process: smoked under 110 ~ 150 ℃ 3-5 hour;
After it solidifies, cohesive strength is greater than 25N, and temperature classification is the H level, and volume specific resistance is not less than 1 * 1014 Ω m, and surface resistivity is not less than 1 * 1014 Ω, and after immersion, volume specific resistance is not less than 1 * 1012 Ω m, and surface resistivity is not less than 1 * 1012 Ω.Synolac impregnating varnish of the present invention can high temperature resistant, high humidity, and electrical insulation capability is good, and physical strength is high, has improved thermal conductivity, but 200 ℃ of long term operations, and 220 ℃ of short-terms have satisfied design requirements.
Claims (2)
1. Synolac impregnating varnish is characterized in that being made by the raw material of following weight part:
Medium oil alkyd 40-45, terpolycyantoamino-formaldehyde resin 24-26, mphenylenediamine 12-14, diaminodiphenyl-methane 6-8, calcium naphthenate 3-4, dimethyl silicone oil 4-6, triphen ethyl phenol Soxylat A 25-7 1-2, ricinolic acid 2-3, vinyl three ('beta '-methoxy oxyethyl group) silane 4-5, vinylbenzene 3-4, vinyl carboxylate 8-10, tributyl tin trichloride 2-3, membrane-forming agent 4-5;
Described membrane-forming agent is made by the raw material of following weight part: Silane coupling agent KH550 2-4,582-2 aminoresin 16-21, polyisobutene 3-4, cobalt naphthenate 1-2, sec.-propyl distearyl acyl-oxygen base Aluminate 1-2, two ten four carbon alcohols ester 4-5, aluminium nitride 1-2, nano-attapulgite 1-2, epoxy soybean oil 4-5, morpholine 1-2;
The preparation method is: with each mixing of materials, be heated to 105-110 ℃, stirring reaction 2-3 hour, grinding removes slag obtained.
2. the preparation method of Synolac impregnating varnish according to claim 1, it is characterized in that comprising the following steps: dimethyl silicone oil, triphen ethyl phenol Soxylat A 25-7, ricinolic acid, vinyl three ('beta '-methoxy oxyethyl group) silane, vinylbenzene, vinyl carboxylate are mixed, be heated to 110-130 ℃, stirred 2-3 hour; Then, add other remaining component, be cooled to 65-75 ℃, stirred 3-4 hour, and get final product.