CN103382117B - 一种去除饮用水中苯的结构滤芯及其制备方法 - Google Patents

一种去除饮用水中苯的结构滤芯及其制备方法 Download PDF

Info

Publication number
CN103382117B
CN103382117B CN201310255123.5A CN201310255123A CN103382117B CN 103382117 B CN103382117 B CN 103382117B CN 201310255123 A CN201310255123 A CN 201310255123A CN 103382117 B CN103382117 B CN 103382117B
Authority
CN
China
Prior art keywords
parts
hour
filter core
water
benzene
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310255123.5A
Other languages
English (en)
Other versions
CN103382117A (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Bengbu Phoenix International Co Ltd
Original Assignee
Bengbu Phoenix International Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Bengbu Phoenix International Co Ltd filed Critical Bengbu Phoenix International Co Ltd
Priority to CN201310255123.5A priority Critical patent/CN103382117B/zh
Publication of CN103382117A publication Critical patent/CN103382117A/zh
Application granted granted Critical
Publication of CN103382117B publication Critical patent/CN103382117B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种去除饮用水中苯的结构滤芯及其制备方法，其特征在于由下列重量份的原料制成：膨润土24-26、硫化钠4-6、硝酸银1-2、红糖3-5、沸石粉5-7、柠檬酸三丁酯1-2、有机硅树脂4-6、硅烷偶联剂KH550？3-4、纳米二氧化硅3-5、改性膨润土25-35、水适量。本发明具有杀菌效果，且对于空气与水中的重金属颗粒有较好的吸附作用，具有净化效率高、耐高温、压力损失小、耐腐蚀、使用寿命长、除去空气中的微尘等突出优点。

Description

一种去除饮用水中苯的结构滤芯及其制备方法
技术领域
    本发明属于过滤材料技术领域，具体是一种去除饮用水中苯的结构滤芯及其制备方法。
背景技术
过滤材料用途极为广泛，广泛应用在化工、电力、冶金、石油、电子电器、机械等工业；最常见的有汽车空气滤清器，用于过滤进入发动机的空气，将空气中的颗粒物、微粒等机械杂质成分阻挡，防止这些成分进入汽油、柴油或机油中，保证发动机正常工作。还有大量的过滤材料用于空气调节系统，现在环境大气污染十分严重，极大危害人体健康，空气过滤材料能将空气的各种有害颗粒物吸附，防止进入人们的生活或工作环境，减少人体肺部对颗粒物等有害物质的吸入，提高人们的生活质量，减少疾病的发生。还有一部分用于水过滤与污水处理，用于分离水中的重金属或有害成分。现有过滤材料主要有蜂窝陶瓷、滤纸、钢丝网等。现有蜂窝陶瓷过滤材料原料配功能单一，不能满足技术不断发展的要求。
发明内容
本发明的目的是提供一种去除饮用水中苯的结构滤芯及其制备方法，本发明具有净化效率高、耐高温、使用寿命长、除去空气中的微尘等突出优点。
本发明所采用的技术方案是：
    一种去除饮用水中苯的结构滤芯，其特征在于由下列重量份的原料制成：
膨润土24-26、硫化钠4-6、硝酸银1-2、红糖3-5、沸石粉5-7、柠檬酸三丁酯1-2、有机硅树脂4-6、硅烷偶联剂KH550  3-4、纳米二氧化硅3-5、改性膨润土25-35、水适量。
所述的改性膨润土由以下方法制得：
    将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量35-40%的氮化铝、16-18%的罗布麻粉末、2-3%的红糖、2-3%的沸石粉、3-4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量5-7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得。
    所述的去除饮用水中苯的结构滤芯的制备方法，其特征在于包括以下步骤：
    将各物料混合均匀，真空练泥，压制成型，送入隧道式炉中分区烧结，一区：温度340-380℃，时间2-3小时；二区：温度570-590℃，时间2-3小时；三区：温度1070-1090℃，时间3-4小时；冷却后取出，送入4-6%的碳酸氢钠的溶液中浸泡1-2天，用清水洗净后，烘干即得。
   本发明具有杀菌效果，且对于空气与水中的重金属颗粒有较好的吸附作用，具有净化效率高、耐高温、压力损失小、耐腐蚀、使用寿命长、除去空气中的微尘等突出优点。 本发明可以用于空气调节系统的空气过滤、也可以用于水过滤、还可以用于汽车滤清器吸气过滤，适用于各种环境恶劣的场所。
具体实施方式
   一种去除饮用水中苯的结构滤芯，由下列重量份（公斤）的原料制成：
   膨润土24、硫化钠6、硝酸银1、红糖5、沸石粉7、柠檬酸三丁酯1、有机硅树脂4、硅烷偶联剂KH550 4、纳米二氧化硅5、改性膨润土35、水适量。
    所述的改性膨润土由以下方法制得：
    将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量40%的氮化铝、18%的罗布麻粉末、3%的红糖、3%的沸石粉、4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得。
    去除饮用水中苯的结构滤芯的制备方法，包括以下步骤：
将各物料混合均匀，真空练泥，压制成型，送入隧道式炉中分区烧结，一区：温度340-380℃，时间2-3小时；二区：温度570-590℃，时间2-3小时；三区：温度1070-1090℃，时间3-4小时；冷却后取出，送入4-6%的碳酸氢钠的溶液中浸泡1-2天，用清水洗净后，烘干即得。
     本发明样品主要技术参数为：抗热冲击：950℃-20℃风冷一次不裂；最高使用温度1250℃。废气净化处理装置的技术指标为：处理气体最高温度550℃；捕集微尘效率≥ 99％；出口排放烟尘颗粒物浓度≤ 30mg/m3；捕获的粉尘颗粒最小粒径范围1-10μm。

Claims (1)

1.一种去除饮用水中苯的结构滤芯，其特征在于由下列重量份的原料制成：膨润土24-26、硫化钠4-6、硝酸银1-2、红糖3-5、沸石粉5-7、柠檬酸三丁酯1-2、有机硅树脂4-6、硅烷偶联剂KH550  3-4、纳米二氧化硅3-5、改性膨润土25-35、水适量；
所述的改性膨润土由以下方法制得：
将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量35-40%的氮化铝、16-18%的罗布麻粉末、2-3%的红糖、2-3%的沸石粉、3-4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量5-7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得；
所述的去除饮用水中苯的结构滤芯的制备方法，包括以下步骤：将各物料混合均匀，真空练泥，压制成型，送入隧道式炉中分区烧结，一区：温度340-380℃，时间2-3小时；二区：温度570-590℃，时间2-3小时；三区：温度1070-1090℃，时间3-4小时；冷却后取出，送入4-6%的碳酸氢钠的溶液中浸泡1-2天，用清水洗净后，烘干即得。
CN201310255123.5A 2013-06-25 2013-06-25 一种去除饮用水中苯的结构滤芯及其制备方法 Active CN103382117B (zh)