CN103381324B - 一种电气石功能陶瓷滤芯及其制备方法 - Google Patents

一种电气石功能陶瓷滤芯及其制备方法 Download PDF

Info

Publication number
CN103381324B
CN103381324B CN201310255194.5A CN201310255194A CN103381324B CN 103381324 B CN103381324 B CN 103381324B CN 201310255194 A CN201310255194 A CN 201310255194A CN 103381324 B CN103381324 B CN 103381324B
Authority
CN
China
Prior art keywords
parts
powder
tourmaline
hour
ceramic filter
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310255194.5A
Other languages
English (en)
Other versions
CN103381324A (zh
Inventor
陈登宇
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI PHOENIX FILTER Co Ltd
Original Assignee
ANHUI PHOENIX FILTER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI PHOENIX FILTER Co Ltd filed Critical ANHUI PHOENIX FILTER Co Ltd
Priority to CN201310255194.5A priority Critical patent/CN103381324B/zh
Publication of CN103381324A publication Critical patent/CN103381324A/zh
Application granted granted Critical
Publication of CN103381324B publication Critical patent/CN103381324B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种电气石功能陶瓷滤芯及其制备方法，其特征在于由下列重量份的原料制成：电气石粉40-45、竹炭粉12-14、麦饭石粉6-8、钾长石粉7-9、聚乙烯醇4-6、沸石粉3-4、过硫酸钠2-3、尿素12-13、改性膨润土20-25、水适量。本发明电气石粉粒与过滤物充分接触，大大提高了接触面积，充分发挥出电气石的辐射红外线、释放负离子，对人体有益的。具有净化效率高、耐高温、耐腐蚀、使用寿命长、除去空气中的微尘等突出优点。

Description

一种电气石功能陶瓷滤芯及其制备方法
技术领域
    本发明属于过滤材料技术领域，具体是一种电气石功能陶瓷滤芯及其制备方法。
背景技术
过滤材料用途极为广泛，广泛应用在化工、电力、冶金、石油、电子电器、机械等工业；最常见的有汽车空气滤清器，用于过滤进入发动机的空气，将空气中的颗粒物、微粒等机械杂质成分阻挡，防止这些成分进入汽油、柴油或机油中，保证发动机正常工作。还有大量的过滤材料用于空气调节系统，现在环境大气污染十分严重，极大危害人体健康，空气过滤材料能将空气的各种有害颗粒物吸附，防止进入人们的生活或工作环境，减少人体肺部对颗粒物等有害物质的吸入，提高人们的生活质量，减少疾病的发生。还有一部分用于水过滤与污水处理，用于分离水中的重金属或有害成分。现有过滤材料主要有蜂窝陶瓷、滤纸、钢丝网等。现有蜂窝陶瓷过滤材料原料配功能单一，不能满足技术不断发展的要求。
发明内容
本发明的目的是提供一种电气石功能陶瓷滤芯及其制备方法，本发明具有净化效率高、耐高温、耐腐蚀、使用寿命长、除去空气中的微尘等突出优点。
本发明所采用的技术方案是：
    一种电气石功能陶瓷滤芯，其特征在于由下列重量份的原料制成：
    电气石粉40-45、竹炭粉12-14、麦饭石粉6-8、钾长石粉7-9、聚乙烯醇4-6、沸石粉3-4、过硫酸钠2-3、尿素12-13、改性膨润土20-25、水适量。
所述的改性膨润土由以下方法制得：
    将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量35-40%的氮化铝、16-18%的罗布麻粉末、2-3%的红糖、2-3%的硼化铬、3-4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量5-7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得。
所述的电气石功能陶瓷滤芯的制备方法，其特征在于包括以下步骤：
    将各物料混合均匀后，真空练泥，压制成型，送入烧结炉中分区烧结，一区：温度200-220℃，时间1-2小时；二区340-360℃，时间2-3小时；三区：950-1050℃，时间3-4小时；冷却后，取出送10-14%的双氧水中浸泡1-2小时，再送入400-500ppm的高锰酸钾溶液中浸泡1-2天，取出，用清水洗净，烘干即可。
   本发明电气石粉粒与过滤物充分接触，大大提高了接触面积，充分发挥出电气石的辐射红外线、释放负离子，对人体有益的。具有净化效率高、耐高温、耐腐蚀、使用寿命长、除去空气中的微尘等突出优点，本发明可以用于空气调节系统的空气过滤、也可以用于水过滤、还可以用于汽车滤清器吸气过滤，适用于各种环境恶劣的场所。
具体实施方式
    一种电气石功能陶瓷滤芯，由下列重量份（公斤）的原料制成：
    电气石粉40、竹炭粉14、麦饭石粉8、钾长石粉9、聚乙烯醇6、沸石粉3、过硫酸钠3、尿素13、改性膨润土20、水适量。
    所述的改性膨润土由以下方法制得：
    将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量40%的氮化铝、18%的罗布麻粉末、3%的红糖、3%的硼化铬、4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得。
    电气石功能陶瓷滤芯的制备方法，包括以下步骤：
    将各物料混合均匀后，真空练泥，压制成型，送入烧结炉中分区烧结，一区：温度200-220℃，时间1-2小时；二区340-360℃，时间2-3小时；三区：950-1050℃，时间3-4小时；冷却后，取出送10-14%的双氧水中浸泡1-2小时，再送入400-500ppm的高锰酸钾溶液中浸泡1-2天，取出，用清水洗净，烘干即可。
本发明样品主要技术参数为：抗热冲击：950℃-20℃风冷一次不裂；最高使用温度1250℃。废气净化处理装置的技术指标为：处理气体最高温度550℃；捕集微尘效率≥ 99％；出口排放烟尘颗粒物浓度≤ 30mg/m3；捕获的粉尘颗粒最小粒径范围1-10μm。

Claims (1)

1.一种电气石功能陶瓷滤芯，其特征在于由下列重量份的原料制成：
   电气石粉40-45、竹炭粉12-14、麦饭石粉6-8、钾长石粉7-9、聚乙烯醇4-6、沸石粉3-4、过硫酸钠2-3、尿素12-13、改性膨润土20-25、水适量；
    所述的改性膨润土由以下方法制得：
将膨润土放入520-540℃煅烧3-4小时，取出，冷却，放入10-12%盐酸溶液中浸泡2-3小时，再放入10-12%氢氧化钠溶液中浸泡1-2小时，取出，用纯净水洗净，烘干研成粉末；再加入相当于膨润土重量35-40%的氮化铝、16-18%的罗布麻粉末、2-3%的红糖、2-3%的硼化铬、3-4%的碳化钨粉，混合搅拌30-40分钟，然后再喷入相当于膨润土重量5-7%的交联剂 TAC，在12000-15000转/分下搅拌40-50分钟，即得；
所述的电气石功能陶瓷滤芯的制备方法包括以下步骤：
将各物料混合均匀后，真空练泥，压制成型，送入烧结炉中分区烧结，一区：温度200-220℃，时间1-2小时；二区340-360℃，时间2-3小时；三区：950-1050℃，时间3-4小时；冷却后，取出送10-14%的双氧水中浸泡1-2小时，再送入400-500ppm的高锰酸钾溶液中浸泡1-2天，取出，用清水洗净，烘干即可。
CN201310255194.5A 2013-06-25 2013-06-25 一种电气石功能陶瓷滤芯及其制备方法 Active CN103381324B (zh)