CN103374334B - 一种相变温度为17℃的无机相变材料(pcm-17) - Google Patents
一种相变温度为17℃的无机相变材料(pcm-17) Download PDFInfo
- Publication number
- CN103374334B CN103374334B CN201210127585.4A CN201210127585A CN103374334B CN 103374334 B CN103374334 B CN 103374334B CN 201210127585 A CN201210127585 A CN 201210127585A CN 103374334 B CN103374334 B CN 103374334B
- Authority
- CN
- China
- Prior art keywords
- phase
- temperature
- inorganic
- phase change
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
Description
密度: | 1.37g/cm3(25℃) |
相变点: | 17℃ |
潜热: | 172kJ/kg |
导热系数: | 0.55W/m.k |
过冷度: | 0.5℃ |
使用次数 | 10000此次以上 |
Claims (1)