CN102827579A - 一种相变温度为36℃的无机相变材料(pcm-36) - Google Patents
一种相变温度为36℃的无机相变材料(pcm-36) Download PDFInfo
- Publication number
- CN102827579A CN102827579A CN201110163554XA CN201110163554A CN102827579A CN 102827579 A CN102827579 A CN 102827579A CN 201110163554X A CN201110163554X A CN 201110163554XA CN 201110163554 A CN201110163554 A CN 201110163554A CN 102827579 A CN102827579 A CN 102827579A
- Authority
- CN
- China
- Prior art keywords
- phase
- change
- temperature
- inorganic
- pcm
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
一种相变温度为36℃的无机相变材料(PCM-36)本发明涉及一种无机相变恒温材料,含有质量比25%的六水氯化钙、20%的六水氯化锶、10%的马来酸酐、8%的甲酸钠、8%的氯化钠、2%的过硫酸钾和27%的水。本发明所提供的相变材料相变温度在36℃,过冷度为0.5℃,相变潜热为218KJ/KG,相变过程可逆,可循环使用次数为10000次以上,原材料均为规模生产,无毒无腐蚀,易于推广。此相变材料在常温时为无色透明雪化状晶体,便于各储能领域开发利用。
Description
技术领域:
本发明涉及一种无机相变恒温材料及其制备方法,特别设计一种相变温度在36℃的相变材料。
背景技术:
在食品保温、电炉、电暖气、化工、物流、医疗应用、军事、电子等众多行业中,普遍利用加热装置来对环境或储藏需要的特定温度进行恒温。加热装置停电时,因而温度下降的快、无法维持最佳的环境温度。在无相变恒温材料的恒温系统中,提供恒温环境时,加热装置工作启动频繁,因而降低了其使用寿命,耗电量多。
相变恒温材料即潜热蓄能材料,是相变恒温系统中存储能量的功能材料。在夜间用电低谷期利用“物质潜热”将热能储存在相变恒温材料中,在白天用电高峰时将热量释放出来,温度低时将热量释放出来从而满足环境或生活、生产所需要温度。这样的制热系统,大部分时间运行在夜间用电低谷峰期,而在白天用电高峰期只有辅助设备运行,从而实现电网“错峰用冷、移峰填谷”,有利于缓解能量双方供求矛盾。
在无机相变恒温材料的恒温系统中,提供恒温环境时,加热装置工作启动频繁,因而降低了其使用寿命,耗电量多。停电后环境温度骤变,无法维持所需的温度,给生产、生活造成一定的影响。在使用无机相变恒温材料的加制热系统中,利用无机相变恒温材料储存热量,加热装置停止运行后,无机相变恒温材料释放热量维持所需环境温度,从而减少制热系统的启动的次数,延长设备使用寿命。在停电时或无源保温系统中仍可维持所需的环境温度。
目前国内外对相变蓄热材料的研究还比较少,但在食品保温、电炉、电暖气、化工、物流、医疗应用、军事、电子等众多行业,对保温材料有着巨大的需求。因此研究相变恒温保温材料,研制出相变温度为36℃,相变潜热大,过冷度小,无相分离、性能稳定的新型、相变恒温材料,显得尤为重要。
本发明所提供的相变材料性能稳定,相变温度在36℃,过冷度为0.5℃,相变潜热为218KJ/KG,相变过程可逆,可循环使用次数为10000次以上,原材料均为规模生产,无毒无腐蚀,易于推广。此相变材料在常温时为结晶雪花状,便于各储能领域开发利用。
发明内容:
本发明的目的在于提供一种由无机盐类物质合成,性能稳定,相变潜热大,无毒无腐蚀,易塑性好的无机相变恒温材料。
本发明的无机相变恒温材料,按重量百分比由以下组成:
具体的制备方法:
1、在45~80℃条件下在配置皿中将总配置量为8%的甲酸钠与总配置量为10%水配成水溶液;
2、将总配置量为20%的六水氯化锶加入到步骤1的水溶液中,混合均匀,制成混合溶液;
3、向步骤2的混合溶液中加入总配置量为10%的马来酸酐,再加总配置比例为5%的水,搅拌均匀,加热1小时,温度保持在60℃左右让其充分反应。
4、将总配置量为8%的氯化钠放到总配置量为5%水中,混合均匀,制成混合溶液;
5、向步骤4的混合溶液中总配置量为2%过硫酸钾,搅拌均匀;
6、将步骤3的溶液与步骤5中溶液进行搅拌均匀;
7、向步骤6的混合溶液里加入总配置量为25%六水氯化钙,在60~70℃、常压条件下反应0.5~1.5小时。
8、将步骤7制备的高分子材料中加入剩余总配置比例为7%的水,搅拌均匀,放置10~15分钟即可。
9、最终化学成份“无机相变液体高分子材料”
附图一本发明的制备工艺流程图
A为25%的六水氯化钙
B为20%的六水氯化锶
C为10%马来酸酐
D为8%的甲酸钠
E为8%的氯化钠
F为2%羟过硫酸钾
G为10%的水
H为5%的水
I为5%的水
J为7%的水
K为步骤一产生的水溶液
L为步骤二产生的混合溶液
M为步骤三产生的混合溶液
N为步骤四产生的混合溶液
O为步骤五产生的混合溶液
P为步骤六产生的混合溶液
Q为步骤七产生的混合溶液
R为本发明相变恒温材料
1在45~80℃条件下混合
2搅拌加热1小时,温度保持在60℃左右
3在60~70℃、常压条件下反应0.5~1.5小时
4搅拌均匀,放置10~15分钟
本发明的无机相变材料产品规格为
密度: | 1.37g/cm3(25℃) |
相变点: | 36℃ |
潜热: | 218kJ/kg |
导热系数: | 0.55W/m.k |
过冷度: | 0.5℃ |
使用次数 | 10000此次以上 |
本发明的无机相变材料重新融化的温度与时间的关系
重新融化是使相变材料的再融化以便开始另一个能量吸收-释放循环。
本无机相变恒温材料在高于36℃开始融化吸热,当36.5℃时,融化时间为4.5小时, 随着温度的升高,融化时间也相应缩短,40℃时融化时间为3小时,43℃时凝结时间为2小时,45℃时凝结时间为1.5小时,48℃时凝结时间为1小时。
结果表明:重新融化吸热的时间随着温度的变大而迅速减少。
附图二为本发明的无机相变材料重新融化的温度与时间的关系
本发明的无机相变材料控制温度与时间的关系
相变材料控制温度能力与时间成反比,随着时间的增加,相变材料释放的热量开始减小,环境温度低于36℃时开始释放热量,并可保持温度时间为12小时,然后才会逐渐升温,直至相变材料完全凝结热量释放完毕。
附图三为相变材料控制温度时间曲线。
Claims (3)