CN103373812B - 一种组合物及其用途 - Google Patents

一种组合物及其用途 Download PDF

Info

Publication number
CN103373812B
CN103373812B CN201210122540.8A CN201210122540A CN103373812B CN 103373812 B CN103373812 B CN 103373812B CN 201210122540 A CN201210122540 A CN 201210122540A CN 103373812 B CN103373812 B CN 103373812B
Authority
CN
China
Prior art keywords
composition
present
glass
brush
vehicles
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201210122540.8A
Other languages
English (en)
Other versions
CN103373812A (zh
Inventor
杨伟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201210122540.8A priority Critical patent/CN103373812B/zh
Publication of CN103373812A publication Critical patent/CN103373812A/zh
Application granted granted Critical
Publication of CN103373812B publication Critical patent/CN103373812B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种组合物及其应用，所述组合物包括50-99wt％的玻璃以及1-50wt％的石英-长石斑岩或磁铁矿。本发明的组合物不需使用对人体有害的砷、硒氧化物等，制备、使用简单，并且明显改善交通工具的燃油性能，可广泛、有效地应用于各种交通工具。

Description

一种组合物及其用途
技术领域
本发明属于化学材料领域，更具体地，本发明涉及含有石英-长石斑岩或磁铁矿的玻璃组合物及其用途。
背景技术
传统的苏打石灰玻璃一般以SiO2为主要原料，添加R2O(Li2O、Na2O、K2O)、RO(MgO、CaO、BaO)、B2O3、P2O5、Al2O3、ZnO以及硝酸盐制成。然而，为了得到透明澄清的玻璃，常常需要另外添加As2O3、Sb2O3等对人体有害的物质。
在世界各国油价飞涨，并且人们日益追求环境保护的今天，亟需能够简单、低成本地降低油耗并减少污染物排放的产品。
发明内容
本发明的一个目的是提供一种组合物，包括：50-99wt％的玻璃以及1-50wt％的石英-长石斑岩或磁铁矿。
根据本发明的一个方面，所述玻璃为现有技术的玻璃，包括SiO2、R2O(Li2O、Na2O、K2O)、RO(MgO、CaO、BaO)、B2O3、P2O5、Al2O3、ZnO等，即，所述玻璃包括SiO2、Na2CO3、CaCO3、Na2B2O4·5H2O、NaNO3、Al(OH)3、TiO2、ZnO、Fe2O3、Li2CO3、K2CO3、KNO3、AlPO4、H3BO3中的一种或多种。
根据本发明的又一个方面，所述组合物包括：65.2-79wt％的玻璃以及21-34.8wt％的石英-长石斑岩，其中所述玻璃包括38-41wt％的SiO2、20-23wt％的Na2CO3、4-6wt％的CaCO3、1-3wt％的Na2B2O4·5H2O、1-2wt％的NaNO3、1-2wt％的Al(OH)3、0.1-1wt％的TiO2以及0.1-1wt％的ZnO，并且所述玻璃优选进一步包括3-5wt％的Fe2O3或0.1-1wt％的Li2CO3。
根据本发明的又一个方面，所述组合物包括：72-85wt％的玻璃以及15-28wt％的石英-长石斑岩，其中所述玻璃包括49-53wt％的SiO2、3-6wt％的Al(OH)3、19-23wt％的Li2CO3以及1-3wt％的AlPO4。
根据本发明的又一个方面，所述组合物包括：61-88wt％的玻璃以及12-39wt％的石英-长石斑岩，其中所述玻璃包括39-53wt％的SiO2、3-7wt％的Na2CO3、1-5wt％的CaCO3、6-10wt％的Na2B2O4·5H2O、1-5wt％的KNO3、8-12wt％的K2CO3以及3-6wt％的ZnO。
根据本发明的又一个方面，所述组合物包括：68.1-96wt％的玻璃以及4-31.9wt％的石英-长石斑岩，其中所述玻璃包括37-41wt％的SiO2、1-3wt％的Na2CO3、20-25wt％的Na2B2O4·5H2O、1-5wt％的Al(OH)3、1-5wt％的ZnO、7-11wt％的H3BO3、0.1-1wt％的Li2CO3、1-5wt％的Fe2O3。
根据本发明的又一个方面，所述组合物包括：74.4-99wt％的玻璃以及1-25.6wt％的磁铁矿，其中所述玻璃包括46-50wt％的SiO2、21-25wt％的Na2CO3、4-6.5wt％的CaCO3、2-4wt％的Na2B2O4·5H2O、0.1-2.5wt％的NaNO3、1-3.5wt％的Al(OH)3、0.1-2.5wt％的TiO2、0.1-2wt％的ZnO、0.1-3wt％的KNO3。
本发明的组合物由于使用石英-长石斑岩或磁铁矿，因此大大降低了玻璃制品中的钾、钠离子等的表面溶出，从而提高了玻璃内部构造的稳定性，此外，本发明避免了对人体有害的As2O3、Sb2O3等物质的使用。
另外，不局限于任何理论，本发明发明人出人意料地发现，本发明的玻璃组合物经过普通技术人员已知的加工方法进行简单加工后，能够显著地改善交通工具的燃油性能。
本发明的又一目的是提供所述组合物在改善交通工具燃油性能上的应用。
根据本发明一个方面，所述交通工具包括任何以汽油、柴油为燃料的交通工具，例如飞机、火车、汽车、摩托车，但不限于此。
根据本发明另一方面，所述改善交通工具燃油性能包括增大发动机的动力利用、提高空气过滤效率、增大燃料的燃烧率、降低污染物排放、节省耗油量等。
根据本发明的又一方面，所述组合物以多个直径约为0.5mm的圆形或椭圆形玻璃颗粒的形式封装于具有多个直径小于该颗粒直径的孔的筒体中使用。
具体地，对于汽车，将20-25g本发明的组合物颗粒封装到一个圆柱形金属筒体内，所述圆柱形金属筒体的柱面和两底面均设有多个直径小于上述颗粒直径的孔。所述筒体的直径小于汽车水箱与发动机的接管(上水管)的直径。将带有本发明组合物的不锈钢筒体装入连接汽车水箱与发动机的接管(上水管)中靠近水箱一侧即可。显然，本领域技术人员能够根据使用所述组合物的工具的体积、常规耗油量等来选择本发明组合物的用量。
根据本方面的又一方面，所述组合物以刷的形式装入空气滤清器中使用。
本发明的组合物在用于改善交通工具燃油性能应用方面的加工工艺简单、成本低廉、效果明显。
具体实施方式
通过下面的实施例进一步说明本发明，然而实施例只用于说明本发明，不应以任何方式将所述实施例理解为对本发明范围进行限制。除另有说明外，本发明所用的各成份原料均为市购可得的。
实施例1
采用下表所列出组分及用量(单位：Kg)，均匀混合，在1300-1400℃融化，冷却至室温，得到本发明的组合物。
实例1 实例2 实例3 实例4 实例5 实例6 实例7
SiO2 56.81 51.00 60.10 62.00 78.04 60.00 62.30
Na2CO3 32.00 28.80 33.00 - 9.56 2.50 30.05
CaCO3 7.33 6.57 7.50 - 5.50 - 7.25
Na2B2O4·5H2O 3.18 2.85 3.22 - 15.23 35.00 4.21
NaNO3 2.05 1.83 2.20 - - - 1.60
Al(OH)3 2.05 1.83 2.55 5.10 - 4.92 3.20
TiO2 1.11 1.02 1.00 - - - 2.00
ZnO 1.11 1.02 1.00 - 8.50 4.00 1.00
Li2CO3 - 1.20 - 25.90 - 0.50 -
K2CO3 - - - - 18.90 - -
KNO3 - - - - 6.00 - 2.30
Fe2O3 - - 5.20 - - 2.00 -
AlPO4 - - - 2.22 - - -
H3BO3 - - - - - 13.00 -
石英-长石斑岩 35.30 77.10 1.20 25.00 46.62 30.00 -
磁铁矿 - - - - - - 15.00
实施例2
将本发明的组合物成型为直径约为0.5cm的圆形或椭圆形颗粒。取20-25g封装到一个圆柱形金属筒体内，所述圆柱形金属筒体的柱面和两底面均设有多个直径小于上述颗粒直径的孔，并且所述圆柱形金属筒体例如是不锈钢筒体。所述筒体的直径小于汽车水箱与发动机的接管(上水管)的直径。将带有本发明组合物的不锈钢筒体装入连接汽车水箱与发动机的接管中靠近水箱一侧即可。
实施例3
以一汽大众公司产捷达车为试验对象，根据“轻型汽车污染物排放限值及测量方法(III)(GB18352.3-2005)规定的方法进行冷启动排放实验。对照未加装本发明组合物。实验对象燃烧市售93#汽油。
实验用仪器主要包括汽车尾气分析仪，美国Rosemount公司；CVS系统，美国PEI公司；以及底盘测功机，日本小野测器。
实验结果如下表所示：
污染物(g·km-1) 对照 本发明
CO 7.864 5.741
HC 0.799 0.603
NOx 1.864 0.886
由上表可以看出，本发明的组合物可显著抑制汽车尾气污染物的产生。
实施例4
以北京汽车制造厂的陆霸2.7L汽车为实验对象，根据汽车燃料消耗量试验方法(GB/T12545-1990)规定的方法进行实验。对照未加装本发明组合物。实验对象燃烧市售93#汽油。
实验用仪器主要包括底盘测功机、数字流量计以及油耗传感器，均为日本小野测器。
实验结果如下表所示：
由上表可以看出，本发明的组合物可显著降低燃油消耗。
实施例5
将本发明的组合物成型为长约10-20cm的刷子的形式，该刷子的刷毛的横向(即，与刷子整体长度垂直的方向)长度为约3-5cm。将所述刷子放入交通工具的空气滤清器中，实验表明，本发明的组合物可以有助于净化空气，进而有助于改善交通工具的燃油性能(数据未示出)。
其它实施例
利用其他品牌型号的汽车、摩托车，采用本发明记载的其他配比重复实施例3-4的实验，得到相同的结论，即本发明的组合物有助于改善交通工具的燃油性能(数据未示出)。
本发明仅以上述实施例为示例来进行阐述，实施例中示出的具体配比以及未示出的本发明组合物的其他配比均可用于本发明并且它们可在各种燃烧汽油、柴油的交通工具中均实现本发明的技术效果。

Claims (2)

1.玻璃组合物在改善交通工具燃油性能上的应用，所述玻璃组合物包括：50-99wt％的玻璃以及1-50wt％的石英-长石斑岩或磁铁矿，其中所述玻璃包括SiO2、Na2CO3、CaCO3、Na2B2O4·5H2O、NaNO3、Al(OH)3、TiO2、ZnO、Fe2O3、Li2CO3、K2CO3、KNO3、AlPO4、H3BO3中的一种或多种；其特征在于将所述玻璃组合物成型为刷子形式，将所述刷子放入交通工具的空气滤清器中。
2.根据权利要求1所述的玻璃组合物，其特征在于所述刷子长度为10-20cm，该刷子的刷毛的横向长度为3-5cm，所述横向是指与刷子整体长度垂直的方向。
CN201210122540.8A 2012-04-25 2012-04-25 一种组合物及其用途 Expired - Fee Related CN103373812B (zh)