CN103352152A - 空调散热器翅片用铝合金及其制造方法 - Google Patents

空调散热器翅片用铝合金及其制造方法 Download PDF

Info

Publication number
CN103352152A
CN103352152A CN2013102739422A CN201310273942A CN103352152A CN 103352152 A CN103352152 A CN 103352152A CN 2013102739422 A CN2013102739422 A CN 2013102739422A CN 201310273942 A CN201310273942 A CN 201310273942A CN 103352152 A CN103352152 A CN 103352152A
Authority
CN
China
Prior art keywords
hour
air conditioner
incubated
cooled
speed again
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013102739422A
Other languages
English (en)
Inventor
骆宣佐
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Original Assignee
ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd filed Critical ANHUI TIANXIANG AIR-CONDITIONER SCIENCE AND TECHNOLOGY Co Ltd
Priority to CN2013102739422A priority Critical patent/CN103352152A/zh
Publication of CN103352152A publication Critical patent/CN103352152A/zh
Pending legal-status Critical Current

Abstract

空调散热器翅片用铝合金，其特征在于其组成元素的重量百分含量为：Si 5.3-5.6、Fe 1.2-1.4、Cu 0.8-1.0、Mn 2.1-2.3、Mg 1.4-1.6、Cr 4.5-4.8、Zn 0.2-0.4、Nb 0.06-0.08、V 0.5-0.6、Zr 0.16-0.19、Li 0.2-0.4、余量为铝。本发明的铝合金材料具有较高的强度特性、钎焊性、耐蚀性优异并具有良好的可加工性能，特别适合用作散热器翅片。

Description

空调散热器翅片用铝合金及其制造方法
技术领域
本发明属于一种铝合金，具体是一种空调散热器用铝合金材料。
背景技术
空调散热结构件大多是由铝合金制成，包括铸造件、挤型件、冲压件及锻造件等。铝合金铸造件成本较低，但一般铸造成形的铝合金结构件其导热系数并不高，通常在90 W/m·K 左右，以至于导热性能差，目前常用纯铝（纯度＞ 99% 以上），虽然导热系数很高（＞ 220 W/m·K），但其流动性及铸造性不好，且太软，不易加工，且易变形。目前，研究热传导率高、强度高的铸造用铝合金，对空调散热器至关重要。
发明内容
本发明的目的在于提供一种空调散热器翅片用铝合金及其制造方法。
本发明所采取的技术方案为：
空调散热器翅片用铝合金，其特征在于其组成元素的重量百分含量为：Si5.3-5.6、Fe1.2-1.4、Cu0.8-1.0、Mn2.1-2.3、Mg1.4-1.6、Cr4.5-4.8、Zn0.2-0.4、Nb0.06-0.08、V0.5-0.6、Zr0.16-0.19、Li0.2-0.4、余量为铝。
所述的空调散热器翅片用铝合金的制造方法，包括熔炼、扒渣、检测合金成分并调整、加入精炼剂精炼、浇铸，其特征在于：包括熔炼、扒渣、检测合金成分并调整、精炼、浇铸，其特征在于：浇铸后以110-120℃/小时速率降温至480-540℃，存放1-2小时；然后，再以130-150℃/小时速率降温至260-270℃，保温2-3小时；再以50-70℃/小时速率升温至480-520℃，保温2-3小时；再以40-60℃/小时速率降温至120-140℃，保温14-16小时；再以120-140℃/小时速率升温至280-310℃，保温2-3小时；再以70-90℃/小时速率冷却至室温；
所述的精炼剂由下列重量份的原料组分混合压块而成：蛭石粉6-7、氟化铝钠2.3-2.5、SnO22.2-2.5、氟化钙2.2-2.4、活性炭2.5-2.8、氯化钠2-3、Bi2O31.1-1.3、二硼化钒2.1-2.4、铝矾土2.1-2.5、纳米二氧化硅1-2。
本发明经过上述的精炼剂处理，得到高品质的铝合金熔液，这样的铝合金熔液用于铸造生产，明显提高成品率，特别是铸件中的气孔度降低1-2度，得到有效的控制，不会在铸件表面产生气孔，夹杂氧化物也明显降低，氧化夹杂物在2级左右。
本发明的铝合金材料具有较高的强度特性、钎焊性、耐蚀性优异并具有良好的可加工性能，特别适合用作散热器翅片。
具体实施方式
空调散热器翅片用铝合金，其组成元素的重量百分含量为：Si5.3-5.6、Fe1.2-1.4、Cu0.8-1.0、Mn2.1-2.3、Mg1.4-1.6、Cr4.5-4.8、Zn0.2-0.4、Nb0.06-0.08、V0.5-0.6、Zr0.16-0.19、Li0.2-0.4、余量为铝。
空调散热器翅片用铝合金的制造方法，包括熔炼、扒渣、检测合金成分并调整、加入精炼剂精炼、浇铸，包括熔炼、扒渣、检测合金成分并调整、精炼、浇铸，其特征在于：浇铸后以110-120℃/小时速率降温至480-540℃，存放1-2小时；然后，再以130-150℃/小时速率降温至260-270℃，保温2-3小时；再以50-70℃/小时速率升温至480-520℃，保温2-3小时；再以40-60℃/小时速率降温至120-140℃，保温14-16小时；再以120-140℃/小时速率升温至280-310℃，保温2-3小时；再以70-90℃/小时速率冷却至室温；
所述的精炼剂由下列重量份（公斤）的原料组分混合压块而成：蛭石粉7、氟化铝钠2.3、SnO22.5、氟化钙2.4、活性炭2.8、氯化钠2、Bi2O31.1、二硼化钒2.4、铝矾土2.5、纳米二氧化硅1。
本发明铝合金强度达到250Mpa-280MPa，硬度可达到130HB～145HB，延伸率4-9%，其盐雾试验的腐蚀率仅为0.1-0.2毫克/厘米2.天。导热系数210 -250W/m·K。

Claims (2)

1.空调散热器翅片用铝合金，其特征在于其组成元素的重量百分含量为：Si5.3-5.6、Fe1.2-1.4、Cu0.8-1.0、Mn2.1-2.3、Mg1.4-1.6、Cr4.5-4.8、Zn0.2-0.4、Nb0.06-0.08、V0.5-0.6、Zr0.16-0.19、Li0.2-0.4、余量为铝。
2.根据权利要求1所述的空调散热器翅片用铝合金的制造方法，包括熔炼、扒渣、检测合金成分并调整、加入精炼剂精炼、浇铸，其特征在于：包括熔炼、扒渣、检测合金成分并调整、精炼、浇铸，其特征在于：浇铸后以110-120℃/小时速率降温至480-540℃，存放1-2小时；然后，再以130-150℃/小时速率降温至260-270℃，保温2-3小时；再以50-70℃/小时速率升温至480-520℃，保温2-3小时；再以40-60℃/小时速率降温至120-140℃，保温14-16小时；再以120-140℃/小时速率升温至280-310℃，保温2-3小时；再以70-90℃/小时速率冷却至室温；
所述的精炼剂由下列重量份的原料组分混合压块而成：蛭石粉6-7、氟化铝钠2.3-2.5、SnO22.2-2.5、氟化钙2.2-2.4、活性炭2.5-2.8、氯化钠2-3、Bi2O31.1-1.3、二硼化钒2.1-2.4、铝矾土2.1-2.5、纳米二氧化硅1-2。
CN2013102739422A 2013-07-02 2013-07-02 空调散热器翅片用铝合金及其制造方法 Pending CN103352152A (zh)