CN102676958A - 一种高性能粉末冶金耐热铝合金的制备方法 - Google Patents

一种高性能粉末冶金耐热铝合金的制备方法 Download PDF

Info

Publication number
CN102676958A
CN102676958A CN2012101125170A CN201210112517A CN102676958A CN 102676958 A CN102676958 A CN 102676958A CN 2012101125170 A CN2012101125170 A CN 2012101125170A CN 201210112517 A CN201210112517 A CN 201210112517A CN 102676958 A CN102676958 A CN 102676958A
Authority
CN
China
Prior art keywords
aluminum alloy
powder metallurgy
alloy
preparation
elements
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2012101125170A
Other languages
English (en)
Other versions
CN102676958B (zh
Inventor
曲选辉
原现杰
尹海清
关佳
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
University of Science and Technology Beijing USTB
Original Assignee
University of Science and Technology Beijing USTB
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by University of Science and Technology Beijing USTB filed Critical University of Science and Technology Beijing USTB
Priority to CN201210112517.0A priority Critical patent/CN102676958B/zh
Publication of CN102676958A publication Critical patent/CN102676958A/zh
Application granted granted Critical
Publication of CN102676958B publication Critical patent/CN102676958B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

一种粉末冶金耐热铝合金的制备方法，属于粉末冶金新成形工艺和铝合金相结合的材料成形领域。采用用粉末冶金新工艺-高速压制成形方法，制备铝合金，有效降低合金中元素的偏析，提高材料的性能，通过加入过渡族元素来提高铝合金的耐热性能。主要用于汽车零件，如齿轮、活塞等。雾化粉经过高速压制强大的冲击能量，可以有效的提高合金的生坯密度，降低合金元素的偏析。液相烧结使得合金元素扩散充分，Cr、Ti有助于细化晶粒，铁提高合金的热稳定性。制备方法简单，高效，合金比传统合金有很好的拉伸强度、延展性、耐热性能。

Description

一种高性能粉末冶金耐热铝合金的制备方法
 
技术领域
本发明属于粉末冶金新成形工艺和铝合金相结合的材料成形领域。用高速压制的成形方法与粉末冶金铝合金热处理工艺相结合，制备Al-Fe-Cr-Ti耐热铝合金。本发明主要用于汽车零件，如齿轮、活塞等。提供高速压制工艺、粉末冶金铝合金材料成分和热处理工艺的设计方案。涉及耐热铝合金各组成成分的设计以及粉末冶金铝合金热处理工艺。
背景技术
随着汽油价格的上涨和人们环保意识的增强，汽车轻量化越来越多的引起人们的关注，汽车上的一些铁基材料正在被铝基材料所取代。汽车轻量化为高比强度的铝基合金件的应用提供了工业化前景。特别是在发动机传送系统方面，零部件的轻量能显著改善汽车的性能，并降低能耗。传统铸造铝基合金由于存在成分偏析，无法满足材料高性能的要求，而粉末冶金件普遍具有以下几个优点：①能够避免成分的偏析，保证合金具有均匀的组织和稳定的性能；②能利用金属和金属、金属和非金属(包括一些高熔点的材料)的组合效果，生产各种特殊性能的材料。粉末冶金铝合金件除具有上述优点之外，还具有如下特性：①密度低(Al的密度为2.70 g/cm3)，约为Fe(7.874 g/cm3)和Cu(8.96 g/cm3)的1/3；②不需要做防锈处理，因为A1表面极易形成一层氧化膜，进而起到防护作用，相对于需要防护涂层的零件节省了生产成本；③有较强的吸能性，在撞车时比钢制零件多吸收50％以上的冲击能，从而减少对人员的伤害，同时提高安全性和乘坐舒适性。由于粉末冶金铝合金具有低密度、高比强、高耐磨性和耐腐蚀性的特点，表现出广阔的应用前景。然而由于各种因素的影响,其开发利用远远落后于Fe 、Cu 系合金。这些制约因素主要包括：①Al 活性高，在快速凝固制粉的过程中，不可避免地形成一层致密的氧化膜，在压制和烧结过程中，这层氧化膜使合金元素的相互扩散受到阻碍，不利于其冶金粘结；②粉末价格高、缺少专有生产技术。这些制约因素，曾经限制了粉末冶金的铝合金的发展，粉末冶金铝合金经过几十年的发展，已经取得了许多新的突破。在材料种类上有Al-Si-X耐磨合金、Al-Fe-X耐热合金、高强合金、铝复合材料等等。粉末冶金铝合金整体水平有了很大的提高，在成形方法上有喷射成形、压制烧结、热挤压、冷等静压等等。目前主要存在的问题是缺少商业粉末冶金铝合金牌号，所以提高适用的铝基粉末冶金件的性能并有效地降低其成本，开发出商业可用的粉末冶金铝合金牌号，是研究发展的方向。当前压制烧结由于工艺简单，降低了成本，材料性能优越，显现出很强的优势。D P Bishop研究了用传统压制方法制备了铝硅合金，取得了一定成果，只是合金密度还待提高[W.G.E. Mosher, G.J. Kippouros, W.F. Caley, I.W. Donaldson, D.P. Bishop, On hot deformation of aluminium–silicon powder metallurgy alloys. Powder Metal., 54(2011), No. 3, P.366.]。高速压制主要的优点就是有效提高生坯密度，在这种情况下，研究粉末冶金铝合金高速压制及烧结工艺，对于汽车工业用高效节能粉末冶金铝合金件的发展具有重要意义。
发明内容
本发明的目的在于：采用用粉末冶金新工艺-高速压制成形方法，制备铝合金，有效降低合金中元素的偏析，提高材料的性能，通过加入过渡族元素来提高铝合金的耐热性能。
一种高性能粉末冶金耐热铝合金的制备方法,其特征是采用粉末冶金高速压制，然后进行烧结和热处理。具体工艺步骤为：
1 采用快速凝固的方法制备铝合金粉，各种元素的成分含量分别是：铁4.0-5.8%、铬3.6-5.0%、Ti3.3-4.8%，余量为铝。
2压制采用粉末冶金高速压制，压制成形设备为HYP35-2型高速冲击成形压机，压制能量为600-2000J，生坯压制密度最高可达2.76g/cm3。
3烧结温度为610℃～650℃，保温时间为20min ～60min。
4 烧结气氛采用氮气、氩气和真空。
5 固溶处理温度为480℃～520℃。
6 淬火采用水淬、空冷、随炉冷
7 退火
8 时效处理采用自然时效。
本发明的优点在于：雾化粉经过高速压制强大的冲击能量，可以有效的提高合金的生坯密度，降低合金元素的偏析。液相烧结使得合金元素扩散充分，Cr、Ti有助于细化晶粒，铁提高合金的热稳定性。制备方法简单，高效，合金比传统合金有很好的拉伸强度、延展性、耐热性能。
附图说明
图1为本发明设计的耐热铝合金组织形貌。
图 2 为本发明设计的铝合金粉末的形貌。
具体实施方式
实验过程中，用到的原料粉为气雾化方法制备。 
高速压制成形设备为HYP35-2型高速冲击成形压机。   
实施例1  
将雾化铝合金粉末加入高速压机的料穴中，采用自动模式的单次压制，压制能量为2000J，压坯在620℃的烧结温度下进行烧结并保温30min，烧结气氛选择高纯氮气，然后随炉冷却至室温。按照T6工艺进行热处理。
实施例2
将雾化铝合金粉末加入高速压机的料穴中，采用自动模式的单次压制，压制能量为2000J，压坯真空状态下在620℃的烧结温度下进行烧结并保温30min，然后随炉冷却至室温。按照T6工艺进行热处理。
实施例3
将雾化铝合金粉末加入高速压机的料穴中，采用自动模式的单次压制，压制能量为2000J，压坯在620℃的烧结温度下进行烧结并保温30min，在氢气气氛保护下。然后随炉冷却至室温。按照T6工艺进行热处理。
实施例4    
将雾化铝合金粉末加入高速压机的料穴中，采用自动模式的单次压制，压制能量为2000J，在高纯氮气气氛的保护下，压坯在600℃的烧结温度下进行烧结并保温30min，然后随炉冷却至室温。按照T6工艺进行热处理。

Claims (1)

1.一种粉末冶金耐热铝合金的制备方法，其特征是具体工艺步骤为：
1）、采用快速凝固的方法制备铝合金粉，各种元素的成分含量分别是：铁4.0-5.8%、铬3.6-5.0%、Ti3.3-4.8%，余量为铝；
2）、压制采用粉末冶金高速压制，压制成形设备为HYP35-2型高速冲击成形压机，压制能量为600-2000J，生坯压制密度最高达2.783g/cm3；
3）、烧结温度为610℃～650℃，保温时间为20min ～60min；
4）、烧结气氛采用氮气、氩气和真空；
5）、固溶处理温度为480℃～520℃；
6）、淬火采用水淬、空冷、随炉冷；
7）、退火；
8）、时效处理采用自然时效。
CN201210112517.0A 2012-04-17 2012-04-17 一种高性能粉末冶金耐热铝合金的制备方法 Expired - Fee Related CN102676958B (zh)