CN103333555A - Waterproof coating capable of chemical crosslinking and physical mortise and tenon with cement - Google Patents
Waterproof coating capable of chemical crosslinking and physical mortise and tenon with cement Download PDFInfo
- Publication number
- CN103333555A CN103333555A CN2013102768124A CN201310276812A CN103333555A CN 103333555 A CN103333555 A CN 103333555A CN 2013102768124 A CN2013102768124 A CN 2013102768124A CN 201310276812 A CN201310276812 A CN 201310276812A CN 103333555 A CN103333555 A CN 103333555A
- Authority
- CN
- China
- Prior art keywords
- parts
- tenon
- waterproof
- waterproof paint
- chemically crosslinked
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention provides a waterproof coating capable of chemical crosslinking and physical mortise and tenon with cement. The waterproof coating is characterized by comprising the following raw materials by weight: 20-50 parts of a synthetic rubber latex, 20-50 parts of emulsified asphalt, 0.5-2 parts of a functional additive and 0.5-2 parts of a dispersant, 20-40 parts of a filler and 10-25 parts of water. The principle is that through coupling effect of the functional additive, part of the molecules in the synthetic rubber and most molecules in the asphalt couple into large molecules with reaction activity; when the large molecules contact with a base plane, the non-reactive molecule segments of the rubber and asphalt and the base plane form physical adsorption, and the molecular segments with reaction activity conduct react with the base plane to form chemical bond effect, so as to generate strong adhesive force; and after bonding, the coating is hardly influenced by environmental factors. Therefore, the waterproof coating provided by the invention has excellent waterproof performance.
Description
Technical field
The present invention relates to a kind of waterproof paint, particularly can be with cement and concrete generation chemical reaction and the coating that bonds.
Background technology
The waterproof paint brushing is on building surface, and the chemical reaction of component forms thin film at building surface after the volatilization of solvent or moisture or in two kinds of coating, and the protection building surface completely cuts off with water, thereby plays waterproof, dampproof effect.The water resistance of waterproof paint is relevant with cohesiveness, extensibility, elastoplasticity, splitting resistance, impermeability and the weathering resistance of the film of its formation.The cohesive strength of film and basal plane is an important indicator of check waterproof paint water resistance, and cohesive force is strong, good water-proof effect.At present, conventional waterproof coating on the market mainly relies on physical adsorption and basal plane bonding, and this cohesive force is smaller, is subjected to the influence of external environment factor easily and disappears.For example be subjected to expanding with heat and contract with cold of hydraulic pressure effect, soda acid salt corrosion, basal plane etc. and do the time spent, waterproof layer easily separates with basal plane, the situation of scurrying water, leaking occurs.Application of paints is in smooth interface, as plastics tubing, ceramic tile glaze etc., because the cohesive force of waterproof layer and smooth surface is little, and easier coming off and cause the phenomenon of scurrying water, leaking.
Summary of the invention
The objective of the invention is to develop a kind of waterproof paint, its molecule can with cement and the effect of concrete surface generation chemical bonding, by physical adsorption and chemical bonding effect, improved the cohesive force of waterproof layer and basal plane, waterproof layer and basal plane form the waterproof construction of skin-type, have strengthened the water resistance of coating.
Technical scheme of the present invention is:
With the waterproof paint of cement generation chemically crosslinked and physics mortise and tenon, comprise the raw material of following parts by weight:
Synthetic rubber latex 20～50; Emulsified bitumen 20～50; Functional aid 0.5～2; Dispersion agent 0.5～2; Filler 20～40; Water 10～25;
Described synthetic rubber latex solid content is the composition of any or they in 40～60% styrene butadiene rubber latex, chloroprene rubber latex, SBS rubber latex or the polyacrylate(s);
To be petroleum pitch, emulsifying agent and water through high-speed emulsifying machine handle described emulsified bitumen that to obtain solid content be that 40～70% emulsion or solid content are any in 40～60% SBS modified emulsifying asphalt, styrene-butadiene rubber(SBR) modified emulsifying asphalt or the chloroprene rubber modified emulsifying asphalt.
Described functional aid is the coupling agent with hydroxyl, vinyl, amino or carboxyl isoreactivity group.
Described functional aid is to have vinyl, hydroxyl, the coupling agent of amino or carboxyl isoreactivity group, hydroxyl is particularly arranged, the polysiloxane coupling agent of amino or carboxyl-reactive functional group, poly-naphthaldehyde sulfonate sodium or their mixture, polysiloxane coupling agent comprises: the hydroxyl alkyl polysiloxane, the carboxyl polysiloxane, the derivative of dimethyl siloxane or cyclohexyl methyl siloxanes, as poly-methyl ethoxy silane, the fatty amide alkyl silane, two kinds of amino third Trimethoxy silane of carboxyl polysiloxane or 3-or they, two or more mixtures, the active group that produces after their hydrolysis can play synergistic effect (the Chemical Bonding and Physical Crosslinking Synergism of chemically crosslinked-physics mortise and tenon with cement or concrete, be called for short CPS) additive (Chinese patent of inventor's application: application (patent) number: CN200910114456.X, title: carry out the waterproof roll of chemically crosslinked and the collaborative bonding of physics mortise and tenon with concrete; Open (bulletin) number: CN101694114A applies for (patent right) people: Guangxi Jiyusan Waterproof Decoration Co., Ltd. address: WangZhou Road, Nanning City, Guangxi Zhuang Autonomous nationality District 267-1 contriver: Lu Guicai; Wu Shengjiang; Zhu Fangwu; Guo Wenxiong) disclose wherein two kinds: poly-methyl ethoxy silane and poly-naphthaldehyde sulfonate sodium.Through overtesting, we find except these two kinds of compounds, coupling agent with hydroxyl, amino or carboxyl, particularly the polysiloxane coupling agent of responding property functional group all has or partly has and can carry out chemically crosslinked and the collaborative cohesive action of physics mortise and tenon with cement and concrete, as isobutyl-triethoxyl silane, 3-aminopropyl triethoxysilane, distearyl acyl-oxygen sec.-propyl aluminic acid ester, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester.
Described dispersion agent is a kind of in polyacrylamide, cellulose ethers, sodium polyacrylate, gelatin or the polyoxyethylene or their composition.
Described filler is any one or more mixture of white carbon black, titanium dioxide, kaolin, barium sulfate, talcum powder, light calcium carbonate or water-ground limestone.
The waterproof paint of of the present invention and cement generation chemically crosslinked and physics mortise and tenon also comprises the antifreezing agent of 0～0.5 parts by weight, and described antifreezing agent is glycerine, ethylene glycol, 1, the mixture of any one or more of ammediol or calcium chloride.
Principle of the present invention is to be raw material with synthetic rubber latex and modified rubber emulsified bitumen, add functional aid, make synthetic rubber molecule, the asphaltene molecule macromole that coupling becomes to have reactive behavior with the functional aid molecule, when this macromole contacts with basal plane, rubber molecule and asphaltene molecule section and basal plane form physical adsorption, and macromole and the adsorption of basal plane generation chemical bonding with reactive behavior, produce chemical action power, therefore the cohesive force of the waterproof layer that forms and basal plane just strengthens greatly, is difficult to by extraneous such environmental effects.Waterproof paint of the present invention is water-borne coatings, in order to make the layering of the stable difficult segregation of product, also needs to add dispersion agent, filler, antifreezing agent etc.
Above-mentioned preparation method with waterproof paint cement generation chemically crosslinked and physics mortise and tenon is:
(1) normal temperature is respectively put into a jar to two kinds of emulsions, stirs earlier;
(2) synthetic rubber latex stirs and adds the modified rubber emulsified bitumen down, add functional aid after adding the modified rubber emulsified bitumen, add softening agent, stir, add filler at last, dispersion agent is according to the environment for use needs interpolation antifreezing agent of product, stir, namely obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
The positively effect that the present invention produces: by the coupled action of functional aid, the macromole that makes synthetic rubber molecule and asphaltene molecule coupling become to have reactive behavior, when this macromole contacts with basal plane, rubber molecule and asphaltene molecule section and basal plane form physical adsorption, and macromole and the effect of basal plane generation chemical bonding with reactive behavior, and the cohesiveness of coating rete, extensibility, elastoplasticity, splitting resistance are very outstanding, waterproof layer and basal plane have formed the waterproof construction of skin-type, good water-proof effect like this.
Embodiment
Embodiment 1
(1) in two jars, takes by weighing 40 parts of neoprene latex latex rubbers and 20 parts of SBS modified emulsifying asphalts respectively, stir;
(2) stirring joins 20 parts of SBS modified emulsifying asphalts in 40 parts of neoprene latex latex rubbers down, add 1 part of isobutyl-triethoxyl silane then, stir, add 30 parts of white carbon blacks, 0.5 part Xylo-Mucine, 0.1 part ethylene glycol and 10 parts of water stir, and obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon
Embodiment 2
(1) in two jars, takes by weighing 50 parts of styrene butadiene rubber latexes and 20 parts of styrene-butadiene rubber(SBR) modified emulsifying asphalts respectively, stir;
(2) 50 parts of styrene butadiene rubber latexes stir and add 25 parts of styrene-butadiene rubber(SBR) modified emulsifying asphalts down, add 1.5 parts of 3-aminopropyl triethoxysilanes then, stir, add 25 parts of light calcium carbonates at last, 0.4 part glycerine, 12 parts of water, 0.75 part of sodium polyacrylate, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 3
(1) in two jars, takes by weighing 30 parts of SBS rubber latexs and 30 parts of modified rubber emulsified bitumens respectively, stir;
(2) 30 parts of SBS rubber latexs stir and add 30 parts of modified rubber emulsified bitumens down, add 2 parts of distearyl acyl-oxygen sec.-propyl aluminic acid esters then, stir, add 30 parts of water-ground limestones at last, 1 part of gelatin, 20 parts of water and 0.5 part of calcium chloride stir, and obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 4
(1) in two jars, takes by weighing 42 parts of butyl polyacrylate emulsions and 30 parts of modified rubber emulsified bitumens respectively, stir;
(2) 42 parts of butyl polyacrylate emulsions stir down and add 24 parts of modified rubber emulsified bitumens, add 1.6 parts of sec.-propyls three (dioctylphyrophosphoric acid acyloxy) titanic acid ester then, stir, add the feed liquid that step (1) obtains, stir, add 0.3 part 1, ammediol, add 30 parts of kaolin at last, 0.8 part polyoxyethylene, 18 parts of water and 0.3 part 1, ammediol, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 5
(1) in two jars, takes by weighing 20 parts of neoprene latex latex rubbers and 50 parts of emulsified bitumens respectively, stir;
(2) 50 parts of emulsified bitumens stir and add 20 parts of neoprene latex latex rubbers down, add 0.5 part of isobutyl-triethoxyl silane then, stir, 0.1 part antifreezing agent ethylene glycol, add 30 parts of kaolin at last, 1 part of Xylo-Mucine, 15 parts of water, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 6
(1) in two jars, takes by weighing 25 parts of styrene butadiene rubber latexes and 40 parts of emulsified bitumens respectively, stir;
(2) 25 parts of styrene butadiene rubber latexes stir and add 40 parts of emulsified bitumens down, add 1 part of distearyl acyl-oxygen sec.-propyl aluminic acid ester then, stir, add 35 parts of talcum powder, 1.5 parts of sodium polyacrylates and 20 parts of water at last, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 7
(1) in two jars, takes by weighing 30 parts of SBS rubber latexs and 30 parts of emulsified bitumens respectively, stir in 25 parts of water;
(2) 30 parts of SBS rubber latexs stir and add 30 parts of emulsified bitumens down, add 2 parts of 3-aminopropyl triethoxysilanes then, stir, add 0.3 part of calcium chloride and 0.2 part 1, ammediol adds 2 parts of gelatin and 25 parts of water, stir, add 40 parts of barium sulfate at last, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
Embodiment 8
(1) in two jars, take by weighing 24 parts of butyl polyacrylate emulsions and 36 parts of chloroprene rubber modified emulsifying asphalts respectively, in stir;
(2) 24 parts of butyl polyacrylate emulsions stir and add 36 parts of chloroprene rubber modified emulsifying asphalts down, add 1.6 parts of poly-naphthaldehyde sulfonate sodiums then, stir, add 1.4 parts of polyacrylamides and 18 parts of water, stir, add 32 parts of titanium dioxides at last, stir, obtain the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon.
According to JC/T 408-2005 standard the waterproof paint with cement generation chemically crosslinked and physics mortise and tenon of the present invention is carried out the detection of each index, the result is as shown in table 1:
The detected result of table 1 waterproof paint with cement generation chemically crosslinked and physics mortise and tenon of the present invention
| Project | Solid content/% | Thermal stability/℃ | Watertightness | Cohesive strength/Mpa | The time do time/h | Low-temperature tenderness (standard conditions)/℃ | Extension at break degree/% |
| Embodiment 1 | 55.2 | 115 | 0.3MPa 30min is waterproof | 0.58 | 15 | -25 | 1000 |
| Embodiment 2 | 56.5 | 118 | 0.3MPa 30min is waterproof | 0.61 | 13 | -25 | 1060 |
| Embodiment 3 | 47.7 | 90 | 0.3MPa 30min is waterproof | 0.42 | 20 | -20 | 800 |
| Embodiment 4 | 57.3 | 122 | 0.3MPa 30min is waterproof | 0.66 | 12 | -30 | 1200 |
| Embodiment 5 | 57.1 | 85 | 0.3MPa 30min is waterproof | 0.38 | 15 | -15 | 650 |
| Embodiment 6 | 56.8 | 90 | 0.3MPa 30min is waterproof | 0.45 | 13 | -20 | 780 |
| Embodiment 7 | 57.3 | 105 | 0.3MPa 30min is waterproof | 0.46 | 20 | -20 | 920 |
| Embodiment 8 | 57.5 | 100 | 0.3MPa 30min is waterproof | 0.52 | 12 | -20 | 860 |
Table 2 performance with the waterproof paint of cement generation chemically crosslinked and physics mortise and tenon and fast-selling on the market waterproof paint of the present invention relatively
| Project | Execution conditions | Watertightness | Cohesive strength/Mpa with basal plane | Extension at break degree/% |
| The waterproof paint of of the present invention and cement generation chemically crosslinked and physics mortise and tenon | But construct under the wet environment, basal plane needn't clean | 0.3MPa 30min is waterproof | 0.5～0.7 | 1000～1200 |
| Polyurethane water-proof paint | Basal plane must be dry, and cleaning | 0.3MPa 30min is waterproof | 0.3～0.5 | 600～800 |
| 208-Wet Patch of U.S. Henry company | Basal plane must be dry, and cleaning | 0.10MPa 30min is waterproof | 0.35～0.45 | 10-30 |
| The JS waterproof paint | But construct under the wet environment, basal plane needn't clean | 0.2MPa 30min is waterproof | 0.3～0.4 | 80～120 |
As seen from Table 1 and Table 2, the waterproof paint of of the present invention and cement generation chemically crosslinked and physics mortise and tenon since with basal plane generation chemisorption power, cohesive strength is stronger than the waterproof paint that has only physical adsorption, the waterproof layer of formation can be waterproof under high hydraulic pressure.The waterproof layer extension at break degree height that waterproof paint of the present invention and cement generation chemically crosslinked and physics mortise and tenon forms, low temperature flexibility is good, even basal plane ruptures, waterproof layer also is not easy to be damaged, and still keeps good watertightness, the water resistance excellence.
The working procedure of the waterproof paint of of the present invention and cement generation chemically crosslinked and physics mortise and tenon is as follows:
(1) base treatment: solid smooth, the no floating dust of basal plane, no greasy dirt.Dry basal plane water in advance wetting effect is better, or at the basal plane lean concrete grout of filming, just can when treating the lean concrete grout initial set.Pipe root limit or drain gully etc. will be smeared into circular arc with the basic unit seam crossing, and arc radius is preferably 5cm.
(2) brushing waterproof paint: sealing compound evenly is applied in node positions such as crack, pipe root, gutter, eaves gutter, negative and positive angle with hairbrush or slurry cutter, generally brushes 2-3 all over finishing, gauge control is at 1.5～2.5mm; Wide 10cm is smeared at pipe root node circumference place, and the pipe root is smeared high 5cm, but reinforcement tire sills such as brushing process paving grid cloth, non-woven fabrics are made enhancement process, and brushing should adopt the method for scumbling multipass to carry out;
(3) maintenance: the construction back guarantees to ventilate, drying, and solidified in general 2-3 days fully the brushing back, stuffy or wet environment, and then can prolong set time.
(4) follow-up construction: when the water-tight layer is done follow-up construction, must after coating is solidified fully, carry out.
Claims (5)
1. with the waterproof paint of cement generation chemically crosslinked and physics mortise and tenon, it is characterized in that, comprise the raw material of following parts by weight:
Synthetic rubber latex 20～50; Emulsified bitumen 20～50; Functional aid 0.5～2; Dispersion agent 0.5～2; Filler 20～40; Water 10～25;
Described synthetic rubber latex solid content is the composition of any or they in 40～60% styrene butadiene rubber latex, chloroprene rubber latex, SBS rubber latex or the polyacrylate(s);
To be petroleum pitch, emulsifying agent and water through high-speed emulsifying machine handle described emulsified bitumen that to obtain solid content be that 40～70% emulsion or solid content are any in 40～60% SBS modified emulsifying asphalt, styrene-butadiene rubber(SBR) modified emulsifying asphalt or the chloroprene rubber modified emulsifying asphalt;
Described functional aid is the coupling agent with hydroxyl, vinyl, amino or carboxyl active group.
2. the waterproof paint of according to claim 1 and cement generation chemically crosslinked and physics mortise and tenon, it is characterized in that, the antifreezing agent that also comprises 0～0.5 parts by weight, described antifreezing agent are glycerine, ethylene glycol, 1, the mixture of any one or more of ammediol or calcium chloride.
3. the waterproof paint of according to claim 1 and cement generation chemically crosslinked and physics mortise and tenon, it is characterized in that described coupling agent is any in isobutyl-triethoxyl silane, 3-aminopropyl triethoxysilane, distearyl acyl-oxygen sec.-propyl aluminic acid ester, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester or the poly-naphthaldehyde sulfonate sodium.
4. the waterproof paint of according to claim 1 and cement generation chemically crosslinked and physics mortise and tenon, it is characterized in that described dispersion agent is any one or more the mixture in polyacrylamide, Xylo-Mucine, sodium polyacrylate, gelatin or the polyoxyethylene.
5. the waterproof paint of according to claim 1 and cement generation chemically crosslinked and physics mortise and tenon, it is characterized in that described filler is any one or more mixture of white carbon black, titanium dioxide, kaolin, barium sulfate, talcum powder, light calcium carbonate or water-ground limestone.