CN103333470A - A kind of heat conduction polyester resin material and preparation method thereof - Google Patents
A kind of heat conduction polyester resin material and preparation method thereof Download PDFInfo
- Publication number
- CN103333470A CN103333470A CN2013102602542A CN201310260254A CN103333470A CN 103333470 A CN103333470 A CN 103333470A CN 2013102602542 A CN2013102602542 A CN 2013102602542A CN 201310260254 A CN201310260254 A CN 201310260254A CN 103333470 A CN103333470 A CN 103333470A
- Authority
- CN
- China
- Prior art keywords
- heat conduction
- polyester resin
- pet
- described heat
- master batch
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of heat conduction polyester resin (being called for short PET) material and preparation method thereof, this heat conduction PET material comprises mass ratio and is respectively: 1: 6-9.5: 0.003: 0.003: 0.003-0.02: 0.005-0.025: 0.01-0.05: agent, compatible toughening agents, fortifying fibre are improved in 1.5 PET resin, heat conduction master batch, oxidation inhibitor, lubricant, nucleator, crystallization.Its preparation method is heat conduction master batch and PET matrix resin, oxidation inhibitor, and lubricant, nucleator, agent is improved in crystallization, and compatible toughening agents is extruded through twin screw after mixing, air-cooled thermal conductivity height, the short PET material of shaping cycle earnestly prepared.This thermally conductive material not only has good heat-conducting, possesses good mechanical property again simultaneously, has taken into account thermal conductivity, mechanical property and later stage processability.
Description
Technical field
The invention belongs to functionalized macromolecular material field, be specifically related to a kind of heat conduction polyester resin (hereinafter to be referred as PET) material and preparation method thereof.
Background technology
At electronic technology field, because the degree of integration of electronic circuit is more and more higher, the gathering of heat is more and more.The gathering of heat causes electronic device temperature to raise, and job stability reduces.Temperature and electric device have following relation work-ing life: every rising 10 degree of temperature, the life-span of electron device reduces by 1/2nd.Thermally conductive material generally is heat conductivility preferred metal material, but proportion of metal material is bigger, and moulding is difficulty relatively, and plastics can pass through the injection molding way moulding, but traditional plastics do not possess the characteristic of heat conduction.The heat-conducting plastic that exploitation has a heat conductivility not only can replace traditional aluminium and make scatterer, and because the density of heat-conducting plastic is lighter than aluminium, similar is half of aluminium, so the quality of plastic tank radiators has only 1/2nd of aluminium radiator, thereby plays the effect of loss of weight.In addition, plastic tank radiators can be processed with injection molding, and its shaping cycle can shorten 20%~50%.
PET has low price, anti-creep, antifatigue, abrasion are little and the hardness height, has toughness maximum in the thermoplastics; Advantages such as electrical insulation capability is good, but PET resin crystallization velocity is slow, shaping cycle is long, and the big grade of molding shrinkage has limited use.
Summary of the invention
In order to solve the dispersion of heat conductive filler in PET, balance toughness causes degradation with high the filling, and the problem that shortens the PET shaping cycle.The invention provides a kind of high thermal conductivity, can use the PET material of injection molding later stage use.
A kind of heat conduction PET material comprises mass ratio and is respectively: 1: 6-9.5: 0.003: 0.003: 0.003-0.02: 0.005-0.025: 0.01-0.05: agent, compatible toughening agents, fortifying fibre are improved in 1.5 PET resin, heat conduction master batch, oxidation inhibitor, lubricant, nucleator, crystallization.
Wherein the heat conduction master batch is respectively by mass ratio: 80-100: 1400-1450: the Resins, epoxy of 10-20, heat conductive filler, solidifying agent are prepared from.Viscosity during 25 ℃ of described Resins, epoxy is 100-300mpa.s, heat conductive filler is: one or more in aluminium nitride, aluminum oxide, boron nitride, the silicon carbide, prepare heat conduction master batch A (aluminum oxide), B (aluminium nitride), C (aluminium nitride 50%+ aluminum oxide 50%), D (aluminium nitride 40%+30% aluminum oxide+silicon carbide 30%) respectively; Solidifying agent is: the low molecular polyether amine hardener.
Oxidation inhibitor is one or more of 1076,1010,168;
Lubricant is: one or more in stearic acid, polyamide wax class, the polyethylene wax class;
Nucleator is: one or more among Surlyn8920, NAV101, the P250;
Agent is improved in crystallization: H302;
Compatible toughening agents is: one or several of POE-MAH, EPDM-MAH, AX8900 etc.;
Fortifying fibre is: glass fibre, metallic aluminium fiber, carbon fiber.
The present invention also provides the high shaping cycle of a kind of thermal conductivity short PET preparation methods, and its step is as follows:
1, heat conductive filler was dried by the fire 4 hours when 100 spend;
2, heat conductive filler is added in the kneader, add Resins, epoxy, airtight stirring is 1-3 hour under the normal temperature, adds solidifying agent, heats up after the curing, gets material and is broken for little bulk at crusher;
3, the PET pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min discharging then, after will be behind the material that mixes add in the twin screw extruder master loading hopper, add fortifying fibre at the side spout, the material of extruding is prepared a kind of heat conduction PET through earnestly air-cooled.
Beneficial effect of the present invention is:
1, heat conductive filler carries out the heat conduction master batch that high heat conductive filler content is prepared in the surface coating, and the interpolation component of heat conductive filler is greatly increased, and can realize the effect of high heat conduction.
2, adopt fortifying fibre to strengthen, the mechanical property of material is higher relatively.
3, agent is improved in the employing crystallization, nucleator is accelerated the crystallization velocity of PET, and shaping cycle shortened dramatically when the later stage used,, heat-drawn wire is higher simultaneously.
4, it is higher relatively that the interpolation of compatible toughening agents makes the toughness of material, realized the balance of high filler loading capacity and excellent toughness.
5, heat conductive filler cooperates with fortifying fibre and can form the more thermal conducting path of high thermal conductivity.
Specific embodiment
Embodiment 1
PET material prescription that the high shaping cycle of a kind of thermal conductivity is short and preparation method thereof, composition of raw materials:
PET:100 part
Heat conduction master batch A:600 part
Antioxidant 1076: 0.3 part, 168:0.3 part
Lubricant stearic acid: 0.3 part
Nucleator Surlyn8920:2 part
Agent H302:1 part is improved in crystallization
Compatible toughening agents AX8900:2 part
Glass fibre: 150 parts
Its preparation method: earlier the PET pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min then, add after the discharging in the twin screw extruder master loading hopper, extrusion temperature is: 260 degree, add fiberglass fiber at the side spout, the material of extruding is at the die head place, earnestly air-cooledly prepares a kind of heat conduction PET.
The thermal conductivity of this material is 2.1W/m.k after tested, and shock strength is: 4.1KJ/m2, shaping cycle is: 27s, heat-drawn wire is: 242 ℃.
Embodiment 2
PET material prescription that the high shaping cycle of a kind of thermal conductivity is short and preparation method thereof, composition of raw materials:
PET:100 part
Heat conduction mother particle B: 750 parts
Antioxidant 1076: 0.3 part, 168:0.3 part
Lubricant polyethylene wax: 0.3 part
Nucleator Surlyn8920:1.5 part
Agent H302:1 part is improved in crystallization
Compatible toughening agents EPDM-MAH:3 part
Metallic aluminium fiber: 150 parts
Its preparation method: earlier the PET pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min then, add after the discharging in the twin screw extruder master loading hopper, extrusion temperature is: 260 degree, add the metallic aluminium fiber at the side spout, the material of extruding is at the die head place, earnestly air-cooledly prepares a kind of heat conduction PET.
The thermal conductivity of this material is 2.8W/m.k after tested, and shock strength is: 3.9KJ/m2, shaping cycle is: 28s, heat-drawn wire is: 245 ℃.
Embodiment 3
PET material prescription that the high shaping cycle of a kind of thermal conductivity is short and preparation method thereof, composition of raw materials:
PET:100 part
Heat conduction master batch C:850 part
Antioxidant 1010: 0.3 part, 168:0.3 part
Lubricant polyamide wax: 0.3 part
Nucleator NAV101:0.5 part
Agent H302:1 part is improved in crystallization
Compatible toughening agents POE-MAH:5 part
Carbon fiber: 150 parts
Its preparation method: earlier the PET pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min then, add after the discharging in the twin screw extruder master loading hopper, extrusion temperature is: 260 degree, add fortifying fibre at the side spout, the material of extruding is at the die head place, earnestly air-cooledly prepares a kind of heat conduction PET.
The thermal conductivity of this material is 3.5W/m.k after tested, and shock strength is: 4.2KJ/m2, shaping cycle is: 32s, heat-drawn wire is: 243 ℃.
Embodiment 4
PET material prescription that the high shaping cycle of a kind of thermal conductivity is short and preparation method thereof, composition of raw materials:
PET:100 part
Heat conduction master batch D:950 part
Antioxidant 1010: 0.3 part, 168:0.3 part
Lubricant polyethylene wax: 0.3 part
Nucleator P250:0.5 part
Agent H302:1 part is improved in crystallization
Compatible toughening agents AX8900:5 part
Carbon fiber: 150 parts
Its preparation method: earlier the PET pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min then, add after the discharging in the twin screw extruder master loading hopper, extrusion temperature is: 260 degree, add fortifying fibre at the side spout, the material of extruding is at the die head place, earnestly air-cooledly prepares a kind of heat conduction PET.
The thermal conductivity of this material is 4.3W/m.k after tested, and shock strength is: 5.5KJ/m2, the moulding rental period is: 32s, heat-drawn wire is: 246 ℃.
Above-mentioned example only is explanation technical conceive of the present invention and characteristics, and its purpose is to allow the people who is familiar with this technology can understand content of the present invention and enforcement according to this, can not limit protection scope of the present invention with this.All equivalent transformations that spirit is done according to the present invention or modification all should be encompassed within protection scope of the present invention.
Claims (10)
1. heat conduction polyester resin material and preparation method thereof, it is characterized in that comprising mass ratio is respectively: 1: 6-9.5: 0.003: 0.003: 0.003-0.02: 0.005-0.025: 0.01-0.05: agent, compatible toughening agents, fortifying fibre are improved in 1.5 polyester resin, heat conduction master batch, oxidation inhibitor, lubricant, nucleator, crystallization.
2. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described heat conduction master batch is respectively by mass ratio: the Resins, epoxy of 80-100: 1400-1450: 10-20, heat conductive filler, solidifying agent are prepared from.
3. according to the described heat conduction polyester resin of claim 2 material, viscosity when it is characterized in that 25 ℃ of described Resins, epoxy is 100-300mpa.s, heat conductive filler is one or more in aluminium nitride, aluminum oxide, boron nitride, the silicon carbide, and solidifying agent is the low molecular polyether amine hardener.
4. according to the described heat conduction polyester resin of claim 2 material, it is characterized in that the used heat conductive filler of described heat conduction master batch is a kind of in aluminum oxide, aluminium nitride, aluminium nitride 50%+ aluminum oxide 50%, the aluminium nitride 40%+30% aluminum oxide+silicon carbide 30%.
5. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described oxidation inhibitor is one or more of 1076,1010,168.
6. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described lubricant is one or more in stearic acid, polyamide wax class, the polyethylene wax class.
7. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described nucleator is: one or more among Surlyn8920, NAV101, the P250.
8. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described crystallization improves agent and be: H302.
9. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that described compatible toughening agents is: one or several of POE-MAH, EPDM-MAH, AX8900 etc., described fortifying fibre are a kind of in glass fibre, metallic aluminium fiber, the carbon fiber.
10. according to the described heat conduction polyester resin of claim 1 material, it is characterized in that comprising following steps: dry by the fire heat conductive filler 4 hours when 100 spend (1); (2) heat conductive filler is added in the kneader, add Resins, epoxy, airtight stirring is 1-3 hour under the normal temperature, adds solidifying agent, heats up after the curing, gets material and is broken for little bulk at crusher; (3) the polyester resin pellet is added blender, add auxiliary agent, heat conduction master batch stirring 2min discharging then, after will be behind the material that mixes add in the twin screw extruder master loading hopper, add fortifying fibre at the side spout, the material of extruding is prepared a kind of heat conduction polyester resin through earnestly air-cooled.