CN103319124A - 一种建筑保温干粉砂浆 - Google Patents
一种建筑保温干粉砂浆 Download PDFInfo
- Publication number
- CN103319124A CN103319124A CN2012100855509A CN201210085550A CN103319124A CN 103319124 A CN103319124 A CN 103319124A CN 2012100855509 A CN2012100855509 A CN 2012100855509A CN 201210085550 A CN201210085550 A CN 201210085550A CN 103319124 A CN103319124 A CN 103319124A
- Authority
- CN
- China
- Prior art keywords
- parts
- mass
- powder
- dry powder
- cement
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种建筑保温干粉砂浆,属于一种建筑保温隔热材料。其干粉与水的重量比为1∶1.5。干粉由普通硅酸盐水泥、煅烧石膏粉、可再分散乳胶粉、细木质纤维、聚丙烯短纤维、熟石灰、灰钙、重钙、羟丙基甲基纤维素、煅烧膨胀珍珠岩、预混助剂混合而成,干粉的各原料所占质量份数为:普通硅酸盐水泥450份、煅烧石膏粉70份、可再分散乳胶粉37.5份、细木质纤维15份、聚丙烯短纤维13份、熟石灰10份、灰钙10份、重钙10份、羟丙基甲基纤维素3份、煅烧膨胀珍珠岩364份、预混助剂17.5份。具有保温隔热性强、与墙体粘结牢固、抗压强度高、拉拔力强、耐候性优越、环保、防火、防裂、防渗水、防潮、抗滑坠、抗震等优点。
Description
技术领域
本发明属于建筑保温隔热材料,具体涉及一种建筑保温干粉砂浆。
背景技术
近年来,建筑行业在建筑物墙体层面采用粉刷保温材料,以保证建筑物具备密封、透气、保温隔热、节能性能的方法得到了越来越广泛的应用。现有无机保温砂浆材料,如中国专利申请200610072751.X(一种墙体保温胶料材料及其备制方法和使用方法)和中国专利申请200810047858.8(建筑保温砂浆)。他们主要采用了改性水泥、粉煤灰、脱硫石膏、玻化微珠、闭孔珍珠岩、蛭石、纤维等材料,但其保温隔热性能、耐候性、抗压、防冻、抗裂、干密度、抗震性能、线收缩率以及对设计要求的(节能65%)抹灰厚度等有待提高。
发明内容
本发明的目的在于提供一种建筑保温干粉砂浆,该建筑保温干粉砂浆具有良好的保温隔热性能,密封会呼吸功能,与墙体粘结牢固(属胶凝材料,分子结构为多元共聚)抗压、抗冲击、拉拔力强、耐候性优越、环保无污染、无毒、无味、抗渗水、抗线收缩率、抗震性能好,施工可与水泥砂灰同步进行,两种材料隔时一次性施工,施工性能优越。
为了实现上述目的,本发明提供的方案是:建筑保温干粉砂浆,其特征在于:它由干粉和水组成,干粉与水的重量比为1∶1.5,使用时干粉加入水搅拌(采用平口立式砂浆搅拌机)均匀后即可使用,即可得到建筑保温干粉浆体砂浆。
所述的干粉由普通硅酸盐水泥、煅烧石膏粉、可再分散乳胶粉、细木质纤维、聚丙烯短纤维、熟石灰、灰钙、重钙、羟丙基甲基纤维素、煅烧膨胀珍珠岩、预混助剂混合而成,干粉的各原料所占质量份数为: 普通硅酸盐水泥450份、煅烧石膏粉70份、可再分散乳胶粉37.5份、细木质纤维15份、聚丙烯短纤维13份、熟石灰10份、灰钙10份、重钙10份、羟丙基甲基纤维素3份、煅烧膨胀珍珠岩364份、预混助剂17.5份;
所述的普通硅酸盐水泥由强度等级为P042.5水泥和强度等级为PC32.5水泥组成,普通硅酸盐水泥的各原料所占质量百分比为:强度等级为P042.5水泥44.44%、PC32.5水泥55.56%;
所述的煅烧膨胀珍珠岩由粗颗粒珍珠岩石砂和细粉沫珍珠岩粉组成,煅烧膨胀珍珠岩各原料所占质量百分比为:粗颗粒珍珠岩石砂54.95%、细粉沫珍珠岩粉45.05%;
所述的预混助剂由早强减水剂、膨胀剂、聚丙烯酰胺、六偏磷酸钠、早强防冻剂混合组成,预混助剂的各原料所占质量百分比为:早强减水剂2.85%,膨胀剂2.85%,聚丙烯酰胺5.71%,六偏磷酸钠11.42%,早强防冻剂65.75%,硼砂11.42%。
本发明的有益效果是:
1、采用两种普通硅酸盐水泥混合使用可降低碱性,防止饰面层出现花斑现象,加强耐候性,料的备制可就地取材,成本低,经济效益好。
2、采用煅烧石膏粉增加了抗压强度和补充了胶凝材料的质量,增加了保温隔热效果及施工性能,缩短了过长的凝结时间。
3、采用熟石灰促进低温成膜性,干粉状态下的干燥、防潮、抗冻融,有效节PH值酸碱度。
4、采用灰钙、重钙,加快产品短期表面钙化,保持长期整体钙化,提高抗压强度。
5、采用可再分散乳胶粉,增强了材料与墙体的压剪粘结强度,粘结牢固,提高了韧性、抗冲击性和抗压强度,起到了阻渗水和不热桥的保塑作用,提高了耐候性。
6、采用聚丙烯短纤维,增强了抗裂、拉拔力、材料与墙体的附着力。
7、采用细木质纤维,改善了分子结构,抗龟裂、抗滑坠功能有效 提高,混合加工时易操作,物料均匀。
8、采用羟丙基甲基纤维素,增强保水性、合易性,提高强度,改善了分子结构,促进物料之间的相溶性。
9、特配制预混助剂,由于配方内采用了一定量的防冻、阻水、增稠、阻燃、合易、分散、保塑等功能添加剂,改善了分子结构,防渗水、防火、防冻、抗裂、增稠、抗空鼓、抗氧化、抗风化、给力防震、抗滑坠功能大大提高,确保耐候性及延长建筑墙体寿命。
10、采用煅烧膨胀珍珠岩,提升了保温隔热性能,降低了导热系数与蓄热系数,提高了抹灰厚度和增加了干粉的吨/m3容重,粗细颗粒结构配置合理,提高了施工合易性与抹灰后表面光洁度。
本发明在干粉状态下,加水搅拌相互作用,充分发挥无机活性,柔性渐变,多元共聚的特点,使用该建筑保温干粉砂浆具有:保温隔热性强、与墙体粘结牢固(防脱落)抗压强度高、拉拔力强、耐候性优越、环保性好(无毒、无味,放射性比活度核素镭、钾、钍等元素大大低于国家标准),A级阻燃防火功能,同时具有良好的防裂、防渗水、防潮性能、抗滑坠、抗震的功能,运输方便快捷,袋装25公斤/包,简易运至工地即可,材料成本适宜,性价比优越。
本发明的建筑保温干粉砂浆适用建筑类别为:外墙保温隔热系统;外墙内保温隔热系统;外墙内外结合或分户保温隔热系统;涂料饰面和面砖饰面保温隔热系统;车库、楼道、消防通道、走廊的保温隔热系统;广泛用于严寒、寒冷、夏热冬冷和夏热冬暖地区,气候不同抹灰厚度不同。
本发明的建筑保温干粉砂浆适应各类墙体如:钢筋混凝土、混凝土空心砌砖、各类空心砖、烧结实心砖、烧结多孔砖、加气混凝土砌块、陶粒砌块、灰砂砖、粉煤灰及火山灰砖。
具体实施方式
为了更好地理解本发明,下面结合实施例进一步说明本发明的内容,但本发明的内容不仅局限于下面实施例。
实施例1:
建筑保温干粉砂浆它由干粉和水组成,干粉与水的重量比为:1∶1.5,使用时干粉加入水搅拌(采用平口立式砂浆搅拌机)稠稀适宜后即可使用。
所述的干粉由普通硅酸盐水泥、煅烧石膏粉、可再分散乳胶粉、细木质纤维、聚丙烯短纤维、熟石灰、灰钙、重钙、羟丙基甲基纤维素、煅烧膨胀珍珠岩、预混助剂混合而成,干粉的各原料所占质量份数为:普通硅酸盐水泥450份、煅烧石膏粉70份、可再分散乳胶粉37.5份、细木质纤维15份、聚丙烯短纤维13份、熟石灰10份、灰钙10份、重钙10份、羟丙基甲基纤维素3份、煅烧膨胀珍珠岩364份、预混助剂17.5份;
所述的普通硅酸盐水泥由强度等级为P042.5水泥和强度等级为PC32.5水泥组成,普通硅酸盐水泥的各原料所占质量百分比为:强度等级为P042.5水泥44.44%、PC32.5水泥55.56%;
所述的煅烧膨胀珍珠岩由粗颗粒珍珠岩石砂和细粉沫珍珠岩粉组成,煅烧膨胀珍珠岩各原料所占质量百分比为:粗颗粒珍珠岩石砂54.95%、细粉沫珍珠岩粉45.05%;
所述的预混助剂由早强减水剂、膨胀剂、聚丙烯酰胺、六偏磷酸钠、早强防冻剂混合组成,预混助剂的各原料所占质量百分比为:早强减水剂2.85%,膨胀剂2.85%,聚丙烯酰胺5.71%,六偏磷酸钠11.42%,早强防冻剂65.75%,硼砂11.42%
所述普通硅酸盐水泥强度等级为P042.5水泥与PC32.5水泥为内蒙古蒙西水泥集团生产;
所述煅烧石膏粉为内蒙古鹏远石膏厂生产(II级天然石膏粉,含特殊陶瓷土);
所述可再分散乳胶粉为山东宜佳BONNER公司研制生产;
所述细木质纤维为江苏LVJIAN木质纤维厂生产,型号为TC300;
所述聚丙烯短纤维为济南豪建科技有限公司生产;
所述熟石灰为巴彦淖尔市临河区雄伟白灰厂生产;
所述灰钙(多功能)为北京鹏程浩野工贸有限公司监制生产;
所述重钙为巴彦淖尔市玉力石粉厂生产;
所述羟丙基甲基纤维素(HPMC)为济南铭仕臣工贸有限公司(卓俊)生产;
所述煅烧膨胀珍珠岩为内蒙临河万花珍珠岩厂生产;
所述预混助剂由本发明人自己研发配制而成,由膨胀剂、早强减水剂、聚丙烯酰胺、六偏磷酸钠、早强防冻剂、硼砂混合组成,预混助剂各原料所占质量百分比为:膨胀剂2.85%,早强减水剂2.85%。聚丙烯酰胺5.71%,六偏磷酸钠11.42%、早强防冻剂65.75%,硼砂11.42%;
所述膨胀剂、早强减水剂为巴彦淖尔市顺鑫混凝土外加剂有限公司(FTM)生产;
所述聚丙烯酰胺为大庆石油管理局石油化工厂生产(证1126159号);
所述六偏磷酸钠为山东久恒化工有限公司生产;
所述早强防冻剂为中国北京迈克龙力化工产品有限公司(龙力牌P-85型)生产;
所述硼砂为大石桥市华信化工有限公司(雁落牌CB537-97)生产。
预混助剂的备制过程为:将所述各原料投入到干粉搅拌机中搅拌15分钟即可使用。
上述建筑保温干粉砂浆的制备方法,采取如下步骤:
1、干粉的制备:按干粉的各原料所占质量份额为:普通硅酸盐水泥强度等级P042.5水泥200份、PC 32.5水泥250份;煅烧石膏粉70份;可再分散乳胶粉37.5份;细木质纤维15份;聚丙烯短纤维13份;熟石灰10份;灰钙10份;重钙10份;羟丙基甲基纤维素3份;预混助剂17.5份;煅烧膨胀珍珠岩粗颗粒200份、细粉沫164份;各原料混合搅拌,得建筑保温干粉砂浆。
2、按干粉与水的重量比为1∶1.5选取干粉和水,使用时干粉加入清水搅拌稀稠适宜后即可使用。
本发明建筑保温干粉砂浆施工工艺及方法:
使用建筑保温干粉砂浆,当基层墙体非水泥砂灰抹面时,可先用水泥砂灰打底找平,拉毛处理即可,若墙体为水泥砂灰基面时,光面必须用素灰拉毛处理,方可抹建筑保温干粉砂浆,一次性隔时配套成活,省工、省时、省料。
建筑保温干粉砂浆,现场采用平口直式砂浆拌搅机直接加水搅拌,抹于要求墙体基面。
使用建筑保温干粉砂浆,施工前先用滚刷湿润清洁墙体表面(现抹水泥砂灰不需湿润),再将搅拌好的建筑保温干粉砂浆抹于墙面上,第一遍厚度掌握在15mm左右,其后,初凝时每遍厚度掌握在15-20mm左右,直至完成设计要求的厚度即可。建筑保温干粉砂浆,从拌和起初凝时间为4小时左右,终凝时间为8小时。建筑保温干粉砂浆经过自然干涸,七天后粘贴面砖,十天后可做涂料等。
使用建筑保温干粉砂浆,一般采用加强型,工序为:水泥砂灰打底找平-直接抹建筑保温干粉砂浆-抗裂摸面砂浆(同时抹贴耐碱网格布)-柔性耐水腻子-饰面(贴瓷砖,做涂料等)。
使用建筑保温干粉砂浆施工时,一律不许添加其它任何材料,搅拌好的浆料尽快用完,不允许凝结后反复使用,同时做好施完工墙壁的保护,避免雨淋、浸泡和碰撞,内保温应注意施工现场通风干燥,施工期间注意防冻和大风,环境温度不低于5℃,5级以上大风、扬沙及沙尘天气不得施工。
使用建筑保温干粉砂浆,施工流程为:加水搅拌-直接抹面-抹平收光-饰面(包括冲筋、贴饼、整形)。
使用建筑保温砂浆,设计结构及施工验收:参照墙体保温隔热系统设计结构及施工验收图集进行。
虽然以上已经对按照本发明目的的构思和实例作了详尽说明,但本领域普通技术人员可以认识到,在没有脱离权利要求限定范围的前提条件下,仍然可以对本发明作出各种改进和变换,而这种改进和变换仍然应当属于本发明的保护范围。
Claims (1)
1.一种建筑保温干粉砂浆,包括干粉和水,其特征在于:干粉与水的重量比为1∶1.5,使用时干粉加入水搅拌均匀后即可使用;
所述的干粉由普通硅酸盐水泥、煅烧石膏粉、可再分散乳胶粉、细木质纤维、聚丙烯短纤维、熟石灰、灰钙、重钙、羟丙基甲基纤维素、煅烧膨胀珍珠岩、预混助剂混合而成,干粉的各原料所占质量份数为:普通硅酸盐水泥450份、煅烧石膏粉70份、可再分散乳胶粉37.5份、细木质纤维15份、聚丙烯短纤维13份、熟石灰10份、灰钙10份、重钙10份、羟丙基甲基纤维素3份、煅烧膨胀珍珠岩364份、预混助剂17.5份;
所述的普通硅酸盐水泥由强度等级为P042.5水泥和强度等级为PC32.5水泥组成,普通硅酸盐水泥的各原料所占质量百分比为:强度等级为P042.5水泥44.44%、PC 32.5水泥55.56%;
所述的煅烧膨胀珍珠岩由粗颗粒珍珠岩石砂和细粉沫珍珠岩粉组成,煅烧膨胀珍珠岩各原料所占质量百分比为:粗颗粒珍珠岩石砂54.95%、细粉沫珍珠岩粉45.05%;
所述的预混助剂由早强减水剂、膨胀剂、聚丙烯酰胺、六偏磷酸钠、早强防冻剂混合组成,预混助剂的各原料所占质量百分比为:早强减水剂2.85%,膨胀剂2.85%,聚丙烯酰胺5.71%,六偏磷酸钠11.42%,早强防冻剂65.75%,硼砂11.42%。