CN103306261B - 一种以废弃塑料和沙子为原料制备憎水沙的方法 - Google Patents
一种以废弃塑料和沙子为原料制备憎水沙的方法 Download PDFInfo
- Publication number
- CN103306261B CN103306261B CN201310274211.XA CN201310274211A CN103306261B CN 103306261 B CN103306261 B CN 103306261B CN 201310274211 A CN201310274211 A CN 201310274211A CN 103306261 B CN103306261 B CN 103306261B
- Authority
- CN
- China
- Prior art keywords
- sand
- waste plastic
- fine sand
- waste
- temperature
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种以细沙和废弃塑料为原料制备憎水沙的方法。主要工艺过程是将废弃塑料加热下形成粘液,加入细沙搅拌使废弃塑料粘液均匀分布在沙的表面即得憎水沙。本方法制备的憎水沙性能很好。本方法制备的憎水沙可用于城市绿化的节水,干旱地区土壤的水分保持及沙漠防治等方面,并有望发挥很大的作用。
Description
技术领域
本发明涉及可用于城市园林、治沙及供其他节水领域应用的一种憎水沙的制备方法,特别指以废弃塑料和细沙为主要原料来制备憎水沙的方法。
背景技术
本发明主要针对目前水资源短缺、灌溉用水严重浪费;荒漠化日益严重等方面的问题。利用废弃塑料及成本很低的细沙为原料制备一种表面由塑料覆盖的细沙,由于该沙的表面为塑料,因此不会保留水分,而且不亲水,可以使雨水或者灌溉水顺利渗入地下;同时由于细沙表面不亲水,可以有效降低水分通过土壤以毛细现象吸水,然后再蒸发造成土壤失水。
由于本发明是利用废弃塑料和沙子为主要原料,制备的憎水沙成本低廉,目前还未见该方面的相关报道,而其独特的性能使其在荒漠化防治和城市绿化及景观美化(如果制备时在沙的表面附着不同颜色)方面将有广阔的应用前景。
发明内容
本发明要解决的技术问题是提供一种憎水沙的制备方法,这种制备方法以细沙、废弃塑料为原料,经合理配比,通过一定的工艺过程而制得憎水沙。
本发明要解决的技术问题是由如下方案解决的:一种以废弃塑料和沙子为原料制备憎水沙的方法,其特征是:将废弃塑料加热到190℃,加入预热到250℃的细沙,加热下搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品,其中废弃塑料与细沙的质量比为1:9-23。
上述一种以废弃塑料和沙子为原料制备憎水沙的方法中的废弃塑料是指:废弃聚乙烯塑料、废弃聚丙烯塑料及废弃聚氯乙烯塑料。
上述一种以废弃塑料和沙子为原料制备憎水沙的方法中的细沙是指:海沙、河沙及其他来源的沙子。
本发明的优点是:1、用本方法制备的憎水沙成本很低。2、沙子表面由塑料覆盖,因而不亲水。3、将其应用于城市绿化或者荒漠化防治可以节约灌溉用水、减少蒸发以抑制荒漠化的进程,以达到节水和治理荒漠化的目的。
附图说明
图1是以废弃塑料和沙子为原料制备憎水沙的工艺流程图。
具体实施方式
实施例1:
将10 g废弃塑料加热到190℃形成塑料粘液,称取230g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例2:
将10 g废弃塑料加热到190℃形成塑料粘液,称取210g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例3:
将10 g废弃塑料加热到190℃形成塑料粘液,称取190g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例4:
将10 g废弃塑料加热到190℃形成塑料粘液,称取170g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例5:
将10 g废弃塑料加热到190℃形成塑料粘液,称取150g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例6:
将10 g废弃塑料加热到190℃形成塑料粘液,称取130g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例7:
将10 g废弃塑料加热到190℃形成塑料粘液,称取110g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
实施例8:
将10 g废弃塑料加热到190℃形成塑料粘液,称取90g细沙加热到250℃,将该温度下的细沙搅拌下与上述废弃塑料粘液混合,继续加热并搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品。
Claims (3)
1.一种以废弃塑料和沙子为原料制备憎水沙的方法,其特征是:将废弃塑料加热到190℃,加入预热到250℃的细沙,加热下搅拌,当温度达到250℃时,继续在该温度下搅拌10分钟,使其拌和均匀,冷却后出料,包装即得产品,其中废弃塑料与细沙的质量比为1:9-23。
2.权利要求1中的废弃塑料是指:废弃聚乙烯塑料、废弃聚丙烯塑料及废弃聚氯乙烯塑料。
3.权利要求1中的细沙是指:海沙、河沙及其他来源的沙子。