CN103290605A - Dyeing and printing technology for corduroy fabric - Google Patents
Dyeing and printing technology for corduroy fabric Download PDFInfo
- Publication number
- CN103290605A CN103290605A CN201310141288XA CN201310141288A CN103290605A CN 103290605 A CN103290605 A CN 103290605A CN 201310141288X A CN201310141288X A CN 201310141288XA CN 201310141288 A CN201310141288 A CN 201310141288A CN 103290605 A CN103290605 A CN 103290605A
- Authority
- CN
- China
- Prior art keywords
- dyeing
- corduroy fabric
- adopt
- temperature
- fabric
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a dyeing and printing technology for corduroy fabric. The dyeing and printing technology particularly optimizes the pile cutting technology, adds a pre-alkali-rolling treatment technology before pile cutting and a natronite desizing technology after pile cutting, adopts hot-cold water continuous flushing for desizing, and improves the mellowness and smoothness of the corduroy fabric, thereby guaranteeing that the dyeing is easier and the phenomena of breakpoints and dislocations are not liable to happen during printing in the follow-up dyeing and printing procedure. The whole dyeing and printing technology is convenient and simple, is easy to operate and low in cost, improves the dyeing and printing quality of the corduroy fabric, and increases the economic benefits of industrial production.
Description
Technical field
The present invention relates to the coloration of textile materials printing technology, relate in particular to a kind of dyeing and printing technology of corduroy fabric.
Background technology
That corduroy fabric has is soft, abundant, the suede bar is clear, plentiful as wick-like characteristics, because fabric is organized with suede with having and organized two parts, service life, general COTTON FABRIC was significantly increased, and printed corduroy is because its intrinsic fabric characteristics, be equipped with style elegant in appearance and colourful color and luster, can be used as clothes, cap, gum shoes surfacing material, be subjected to consumer's welcome deeply, in addition, also can be used on furniture, decoration aspect, purposes is comparatively extensive.But because the design feature of corduroy fabric causes the dyeing and printing technological effect of existing corduroy fabric unsatisfactory, dislocation appears in stamp usually, fault, discontinuous problem are arranged, influenced the quality of product and attractive in appearance, also limited its large-scale application.
Therefore, need a kind of new technical scheme to address the above problem.
Summary of the invention
Goal of the invention: in order to solve the existing in prior technology problem, it is few to the invention provides a kind of stamp fault, and pattern is successively put the dyeing and printing technology of the corduroy fabric of dislocation.
Technical scheme: for achieving the above object, the dyeing and printing technology of a kind of corduroy fabric of the present invention may further comprise the steps:
(1) grey cloth margin to seam;
(2) clipping pre-treatment: roll alkali treatment, concentration of lye is 8-12g/L, adds the bleeding agent of 2%-4%, and treatment temperature is 80-100 ℃, and the processing time is 20-40min;
(3) clipping: adopt the corduroy fabric after wi77569 type cutting machines are handled step (2) to carry out clipping processing, speed of a motor vehicle 3-7m/min, blade axis rotary speed 1000-1400r/min;
(4) natron destarch: concentration of lye is 5-10g/L, after temperature is the 60-80 ℃ of 40-50min that banks up, adopt 60-80 ℃ water washing 2-3 time after, adopt water washing 2-3 time of room temperature;
(5) oven dry: temperature 60-80 ℃, 7-9 becomes to do;
(6) bristle: the corduroy fabric that obtains after adopting MM series carbon fiber roughing-up machine to step (5) oven dry carries out bristle, speed of a motor vehicle 5-15m/min, humidity 10%-15%;
(7) dyeing: corduroy fabric is immersed dye solution dye, adopt REACTIVE DYES Sumifix HF8-10g/L, dye leveller 0.5-1.5g/L, pH are 5-5.5, and dyeing temperature rises to 100-120 ℃ with 1 ℃/min, retention time 20-30min;
(8) typing stamp: adopt zy750 type thermal transfer printing machine to carry out stamp to the corduroy fabric typing back that step (7) obtains, temperature 220-250 ℃, humidity 30%-40%;
(9) finished product inspection: the corduroy fabric that step (8) gained stamp is finished carries out the examination and test of products, rejects faulty materials.
Beneficial effect: the dyeing and printing technology of a kind of corduroy fabric provided by the present invention, the clipping technology of re-optimization, before clipping, increased and rolled the alkali pre-treatment process, increased the natron desizing after the clipping, and adopt hot cold water to wash destarch continuously, improved the mellow and full of corduroy fabric, smooth degree, thereby guaranteed easier colouring on follow-up dyeing and printing operation, stamp is not prone to the breakpoint inconsistent phenomenon, whole technology is convenient and simple, and operation is with low cost easily, improve dyeing and the printing quality of corduroy fabric, increased industrial economic benefit.
The specific embodiment
Below in conjunction with the specific embodiment, further illustrate the present invention, should understand the following specific embodiment only is used for explanation the present invention and is not used in and limits the scope of the invention, after having read the present invention, those skilled in the art all fall within the application's claims institute restricted portion to the modification of the various equivalent form of values of the present invention.
Embodiment 1:
A kind of dyeing and printing technology of corduroy fabric may further comprise the steps:
(1) grey cloth margin to seam;
(2) clipping pre-treatment: roll alkali treatment, concentration of lye is 8g/L, adds 2% bleeding agent, and treatment temperature is 80 ℃, and the processing time is 40min;
(3) clipping: adopt the corduroy fabric after wi77569 type cutting machines are handled step (2) to carry out clipping processing, speed of a motor vehicle 3m/min, blade axis rotary speed 1400r/min;
(4) natron destarch: concentration of lye is 5g/L, after temperature is 60 ℃ of 40min that bank up, adopt 60 ℃ water washing 2 times after, adopt the water washing 3 times of room temperature;
(5) oven dry: 60 ℃ of temperature, do for 7 one-tenth;
(6) bristle: the corduroy fabric that obtains after adopting MM series carbon fiber roughing-up machine to step (5) oven dry carries out bristle, speed of a motor vehicle 5m/min, humidity 10%;
(7) dyeing: corduroy fabric is immersed dye solution dye, adopt REACTIVE DYES Sumifix HF8g/L, dye leveller 0.5g/L, pH are 5, and dyeing temperature rises to 100 ℃ with 1 ℃/min, retention time 30min;
(8) typing stamp: adopt zy750 type thermal transfer printing machine to carry out stamp, 220 ℃ of temperature, humidity 30% to the corduroy fabric typing back that step (7) obtains;
(9) finished product inspection: the corduroy fabric that step (8) gained stamp is finished carries out the examination and test of products, rejects faulty materials.
Embodiment 2:
A kind of dyeing and printing technology of corduroy fabric may further comprise the steps:
(1) grey cloth margin to seam;
(2) clipping pre-treatment: roll alkali treatment, concentration of lye is 12g/L, adds 4% bleeding agent, and treatment temperature is 100 ℃, and the processing time is 20min;
(3) clipping: adopt the corduroy fabric after wi77569 type cutting machines are handled step (2) to carry out clipping processing, speed of a motor vehicle 7m/min, blade axis rotary speed 1000r/min;
(4) natron destarch: concentration of lye is 10g/L, after temperature is 80 ℃ of 50min that bank up, adopt 80 ℃ water washing 3 times after, adopt the water washing 2 times of room temperature;
(5) oven dry: 80 ℃ of temperature, do for 9 one-tenth;
(6) bristle: the corduroy fabric that obtains after adopting MM series carbon fiber roughing-up machine to step (5) oven dry carries out bristle, speed of a motor vehicle 15m/min, humidity 15%;
(7) dyeing: corduroy fabric is immersed dye solution dye, adopt REACTIVE DYES Sumifix HF10g/L, dye leveller 1.5g/L, pH are 5.5, and dyeing temperature rises to 120 ℃ with 1 ℃/min, retention time 20min;
(8) typing stamp: adopt zy750 type thermal transfer printing machine to carry out stamp, 250 ℃ of temperature, humidity 40% to the corduroy fabric typing back that step (7) obtains;
(9) finished product inspection: the corduroy fabric that step (8) gained stamp is finished carries out the examination and test of products, rejects faulty materials.
Embodiment 3:
A kind of dyeing and printing technology of corduroy fabric may further comprise the steps:
(1) grey cloth margin to seam;
(2) clipping pre-treatment: roll alkali treatment, concentration of lye is 10g/L, adds 3% bleeding agent, and treatment temperature is 90 ℃, and the processing time is 30min;
(3) clipping: adopt the corduroy fabric after wi77569 type cutting machines are handled step (2) to carry out clipping processing, speed of a motor vehicle 5m/min, blade axis rotary speed 1200r/min;
(4) natron destarch: concentration of lye is 7g/L, after temperature is 70 ℃ of 45min that bank up, adopt 70 ℃ water washing 3 times after, adopt the water washing 2 times of room temperature;
(5) oven dry: 70 ℃ of temperature, do for 8 one-tenth;
(6) bristle: the corduroy fabric that obtains after adopting MM series carbon fiber roughing-up machine to step (5) oven dry carries out bristle, speed of a motor vehicle 10m/min, humidity 15%;
(7) dyeing: corduroy fabric is immersed dye solution dye, adopt REACTIVE DYES Sumifix HF9g/L, dye leveller 1.0g/L, pH are 5, and dyeing temperature rises to 110 ℃ with 1 ℃/min, retention time 25min;
(8) typing stamp: adopt zy750 type thermal transfer printing machine to carry out stamp, 230 ℃ of temperature, humidity 35% to the corduroy fabric typing back that step (7) obtains;
(9) finished product inspection: the corduroy fabric that step (8) gained stamp is finished carries out the examination and test of products, rejects faulty materials.
Claims (1)
1. the dyeing and printing technology of a corduroy fabric is characterized in that may further comprise the steps:
(1) grey cloth margin to seam;
(2) clipping pre-treatment: roll alkali treatment, concentration of lye is 8-12g/L, adds the bleeding agent of 2%-4%, and treatment temperature is 80-100 ℃, and the processing time is 20-40min;
(3) clipping: adopt the corduroy fabric after wi77569 type cutting machines are handled step (2) to carry out clipping processing, speed of a motor vehicle 3-7m/min, blade axis rotary speed 1000-1400r/min;
(4) natron destarch: concentration of lye is 5-10g/L, after temperature is the 60-80 ℃ of 40-50min that banks up, adopt 60-80 ℃ water washing 2-3 time after, adopt water washing 2-3 time of room temperature;
(5) oven dry: temperature 60-80 ℃, 7-9 becomes to do;
(6) bristle: the corduroy fabric that obtains after adopting MM series carbon fiber roughing-up machine to step (5) oven dry carries out bristle, speed of a motor vehicle 5-15m/min, humidity 10%-15%;
(7) dyeing: corduroy fabric is immersed dye solution dye, adopt REACTIVE DYES Sumifix HF8-10g/L, dye leveller 0.5-1.5g/L, pH are 5-5.5, and dyeing temperature rises to 100-120 ℃ with 1 ℃/min, retention time 20-30min;
(8) typing stamp: adopt zy750 type thermal transfer printing machine to carry out stamp to the corduroy fabric typing back that step (7) obtains, temperature 220-250 ℃, humidity 30%-40%;
(9) finished product inspection: the corduroy fabric that step (8) gained stamp is finished carries out the examination and test of products, rejects faulty materials.