CN103289438A - 一种抗氧化氧化铁黑颗粒的制备方法 - Google Patents

一种抗氧化氧化铁黑颗粒的制备方法 Download PDF

Info

Publication number
CN103289438A
CN103289438A CN2013101945776A CN201310194577A CN103289438A CN 103289438 A CN103289438 A CN 103289438A CN 2013101945776 A CN2013101945776 A CN 2013101945776A CN 201310194577 A CN201310194577 A CN 201310194577A CN 103289438 A CN103289438 A CN 103289438A
Authority
CN
China
Prior art keywords
iron oxide
oxide black
viscous liquid
antioxidant
preparation
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013101945776A
Other languages
English (en)
Other versions
CN103289438B (zh
Inventor
孙晓庆
章志海
曹阳
黄忠达
杜松松
刘凡
缪志剑
黎镇
沃承立
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING RELY TECHNOLOGY Co Ltd
Original Assignee
TONGLING RELY TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING RELY TECHNOLOGY Co Ltd filed Critical TONGLING RELY TECHNOLOGY Co Ltd
Priority to CN201310194577.6A priority Critical patent/CN103289438B/zh
Publication of CN103289438A publication Critical patent/CN103289438A/zh
Application granted granted Critical
Publication of CN103289438B publication Critical patent/CN103289438B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种抗氧化氧化铁黑颗粒的制备方法，具体步骤如下：按一定重量比将硅烷偶联剂KH570、儿茶酚和司盘-80溶解于去离子水中，得粘性液体；再在上述制得的粘性液体中加入抗氧剂1010和炭黑进行改性；取氧化铁黑加入造粒机中进行造粒，同时将改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒，烘干，过筛，即得成品。本发明所生产的氧化铁黑具有优越的耐温性能，良好的耐酸、抗氧化性能以及吸光性强、着色力高、相容性好、分散性好等特点，具有巨大的市场前景。

Description

一种抗氧化氧化铁黑颗粒的制备方法
技术领域
本发明涉及一种氧化铁黑的制备方法，具体涉及一种抗氧化氧化铁黑颗粒的制备方法。
背景技术
    氧化铁黑，分子式为Fe3O4，为黑色粉末，是Fe2O3和FeO的加成物，不溶于水，具有磁性，着色力和遮盖力很高。氧化铁黑作为铁系颜料中的一种，由于其无毒、无嗅、无污染等特点，广泛用于建筑行业中酚醛防锈漆填料、重防腐涂料底漆等；在用于橡胶、塑料的着色时，有补强老化的作用，同时保护有机物被紫外光降解的特点；此外，也用于人造大理石、陶瓷及水泥地面的着色。但是氧化铁黑在较高温度下会发生褪色、变色等现象，耐热稳定性差，从而限制了氧化铁黑的使用范围。
发明内容
本发明的目的在于提供一种抗氧化氧化铁黑颗粒的制备方法，提高氧化铁黑的高温稳定性。
本发明采用的技术方案如下：
    一种抗氧化氧化铁黑颗粒的制备方法，包括以下步骤：
    （1）按重量比3-4:2-3:1称取硅烷偶联剂KH570、儿茶酚和司盘-80加入10-12倍去离子水中，水浴加热至55-60℃，超声分散25-30分钟，得粘性液体；
    （2）在上述制得的粘性液体中加入2-3%的抗氧剂1010和1-3%的高耐磨炭黑，2000-3000rpm高速剪切分散10-20分钟，得抗氧剂1010和炭黑改性的粘性液体；
    （3）按重量份取100-150份氧化铁黑加入造粒机中进行造粒，同时将50-80份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
    （4）将步骤（3）制得的氧化铁黑颗粒于85-95℃下烘干，然后过50-60目筛，即得成品。
    步骤（1）中所述的超声功率为700-800W，超声频率为20-25KHz。
    步骤（3）中所述的造粒机的转速为1500-2000rpm。
 
本发明有益效果：
本发明将氧化铁黑粉末制造成表面覆盖有含有抗氧剂1010、硅烷偶联剂KH570等组分，可以明显提高氧化铁黑的抗氧化性能，并提高了其与其它成分的复配特性，扩大使用范围，同时也提高了氧化铁黑颜料的流动性和分散性；本发明所生产的氧化铁黑具有优越的耐温性能，良好的耐酸、抗氧化性能以及吸光性强、着色力高、相容性好、分散性好等特点，具有巨大的市场前景。
具体实施方式
    一种抗氧化氧化铁黑颗粒的制备方法，包括以下步骤：
    （1）按重量比3:2:1称取硅烷偶联剂KH570、儿茶酚和司盘-80加入10倍去离子水中，水浴加热至60℃，超声分散25分钟，得粘性液体；
    （2）在上述制得的粘性液体中加入2。5%的抗氧剂1010和2%的高耐磨炭黑，3000rpm高速剪切分散10分钟，得抗氧剂1010和炭黑改性的粘性液体；
    （3）按重量份取120份氧化铁黑加入造粒机中进行造粒，同时将60份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
    （4）将步骤（3）制得的氧化铁黑颗粒于90℃下烘干，然后过50目筛，即得成品。
    步骤（1）中所述的超声功率为800W，超声频率为20KHz。
    步骤（3）中所述的造粒机的转速为2000rpm。
本实施例生产出来的氧化铁黑产品性能分析数据如下表：
项目 指标 检测结果
水溶物（%） ≤1.0  0.68
105℃挥发物（%） ≤1.0 0.71
吸油量（%） 15-25 21.1
着色强度（%） 95-105 99.9
耐200℃/30min （△E） ≤1.0 0.72

Claims (3)

1.一种抗氧化氧化铁黑颗粒的制备方法，其特征在于包括以下步骤：
（1）按重量比3-4:2-3:1称取硅烷偶联剂KH570、儿茶酚和司盘-80加入10-12倍去离子水中，水浴加热至55-60℃，超声分散25-30分钟，得粘性液体；
（2）在上述制得的粘性液体中加入2-3%的抗氧剂1010和1-3%的高耐磨炭黑，2000-3000rpm高速剪切分散10-20分钟，得抗氧剂1010和炭黑改性的粘性液体；
（3）按重量份取100-150份氧化铁黑加入造粒机中进行造粒，同时将50-80份步骤（2）制得的改性粘性液体均匀地喷淋到氧化铁黑粉料上，形成氧化铁黑小颗粒；
（4）将步骤（3）制得的氧化铁黑颗粒于85-95℃下烘干，然后过50-60目筛，即得成品。
2.根据权利要求1所述的一种抗氧化氧化铁黑颗粒的制备方法，其特征在于，步骤（1）中所述的超声功率为700-800W，超声频率为20-25KHz。
3.根据权利要求1所述的一种抗氧化氧化铁黑颗粒的制备方法，其特征在于，步骤（3）中所述的造粒机的转速为1500-2000rpm。
CN201310194577.6A 2013-05-23 2013-05-23 一种抗氧化氧化铁黑颗粒的制备方法 Active CN103289438B (zh)