CN103274675A - Manufacturing method of art ceramics - Google Patents
Manufacturing method of art ceramics Download PDFInfo
- Publication number
- CN103274675A CN103274675A CN 201310175269 CN201310175269A CN103274675A CN 103274675 A CN103274675 A CN 103274675A CN 201310175269 CN201310175269 CN 201310175269 CN 201310175269 A CN201310175269 A CN 201310175269A CN 103274675 A CN103274675 A CN 103274675A
- Authority
- CN
- China
- Prior art keywords
- ceramic
- art pottery
- art
- earth base
- pottery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the technical field of ceramics, and discloses a manufacturing method of art ceramics. The manufacturing method is characterized in that the art ceramics is ceramic with aesthetic felling composed of different figures. The method comprises the following steps of: pulping the ceramic clay into slurry by using a beating machine, adding the slurry in a stirrer and uniformly stirring to form ceramic slurry, smearing ceramic glaze on manufactured dry art ceramics clay blank, placing the manufactured dry art ceramics clay blank with ceramic glaze in a kiln for firing, cooling to manufacture the art ceramics. A ceramic lamp manufactured by the method disclosed by the invention is low in production cost and high in production efficiency.
Description
Technical field
The present invention relates to the ceramic technology field, be specifically related to the ceramic making method.
Background technology
People's living standard improves, and people more and more pursue the enjoyment of aesthetic feeling to pottery, and the art pottery is liked because its plain quality is subjected to the human consumer deeply, usually as putting artwork.
Chinese invention patent number is: 201010562408.X discloses a kind of production method of Attapulgite art pottery slurry, (1) stirs in the batching adding stirrer with Attapulgite art pottery slurry, stir and carry out that sodium is old to be treated to moistening shape mixture in the old pond of back input, the old time control of sodium was at 1～15 day; (2) will be pressed into flap in the moistening shape mixture input twin rollers, the thickness of flap is less than 3 millimeters; (3) flap is imported be squeezed into cylindrical strip thing in the forcing machine, the diameter control of cylindrical strip thing is at 2～10 millimeters, and (4) are input to the cement threshing ground with cylindrical strip thing and carry out airing, and the cylindrical strip thing water content after the airing is less than 15%; (5) will carry out abrasive dust in the cylindrical strip thing input grinding machine after the airing, and in the meal outlet access pipeline self-discharging type permanent-magnetic iron expeller with grinding machine, meal to abrasive dust output carries out being work in-process after the deironing, half-finished particle fineness is less than 0.044 millimeter, (6) stir adding water in the input of the work in-process after the deironing vacuum mixer, the water ratio control of Attapulgite art pottery slurry finished product is 25%～50%, and the slurry that stirs back output is the finished product of Attapulgite art pottery slurry; The raw-material batching of described Attapulgite art pottery slurry is made up of following component by weight percentage: paste attapulgite clay 55～75%, white bentonite in powder 5～25%, ripe flint clay powder 5～20%, kaolin powder 5～15%, yellow soda ash 0.1～2%, alkali lignin 0.1～2% and water 1～30%; The production technique of described paste attapulgite clay: will stir in the Attapulgite ore deposit input stirrer, after forcing machine is squeezed into sheet, import again in the stirrer and stir, natural drying after forcing machine is squeezed into sheet, the Attapulgite ore deposit of drying is transported in the feed reservoir soaks, dash with air pump and to turn over, post precipitation is emitted immersion water, the sieve decon in the input work in-process pond, is soaked again, dash with air pump and to turn over, post precipitation is emitted immersion water, and the slurry transportation of post precipitation is arrived in the finished product pond, is paste attapulgite clay; Described paste attapulgite clay is made up of following component by weight percentage: attapulgite clay 25～60%, water 40～75%.
The art pottery of above-mentioned this structure, production cost are extremely high, unstable product quality, because structure is complicated especially, manufacture difficulty is big, and manufacturing cost is extremely high, and production process is many, increases labour intensity, and production efficiency is low.
Summary of the invention
Create art pottery production cost height for solving existing production technique, production efficiency is low, the purpose of this invention is to provide a kind of making method of the art pottery.The art pottery production cost that this method is made is low, production efficiency height, constant product quality.
Purpose of the present invention is achieved through the following technical solutions:
A kind of making method of the art pottery, this method may further comprise the steps:
A kind of making method of the art pottery, the described art pottery is formed the pottery with aesthetic feeling by different decorative patterns, and this method may further comprise the steps:
The ceramic material of making the art pottery is encased in the hollander, ceramic earth is broken into mud with hollander, to break into mud and join evenly stirring in the stirrer, back one-tenth ceramic mud stirs, wherein the chemical ingredients of ceramic material is: silicon-dioxide 68-73%, ferric oxide 0.5-1%, calcium oxide 17-23%, magnesium oxide 3-8%, zinc oxide 2-8%;
To accomplish fluently ceramic mud is injected into and designs art pottery mould, through drying automatically, evenly transpiring moisture dries the back demoulding, produces art pottery earth base, will be at the art pottery earth base of making through drying automatically 24-48 hour, art pottery earth base is put in the barn again and dried, the problem in the barn is the 40-60 degree, and carrying out art pottery earth base storing time in the barn is 48-58 hour, produce dry art pottery earth base
To smear ceramic glaze at the art pottery earth base of making drying, smear the ceramic glaze of different thickness according to the decorative pattern of art pottery earth base, wherein the composition of ceramic glaze is: ceramic glaze contains: silicon 59-69.4%, aluminium 2.5-12%, iron 0.08-3.30%, titanium 0.01-2.10%, calcium 6.90-8.90%, sodium 2.05-2.80%
The ceramic glaze ceramic disc earth base of making that smears is put into kiln and is fired, and the temperature of firing is the 1200-1290 degree, and the time of firing is 7-8 hour, after overcooling, is made into the art pottery.
A kind of preferred, the temperature that described kiln is fired is the 1250-1300 degree.
With respect to prior art, the present invention has following advantage and beneficial effect:
The produced art pottery quality of this method is very stable, and appearance looks elegant is good-looking.The quality that this method is made ceramic lamp is good, and the art pottery made from this method can keep ceramic decorative pattern for a long time, thereby the art pottery can preserve for a long time, and it is very attractive in appearance that such ceramic lamp seems.The art pottery uses the glaze amount bigger, the variable thickness sample that ceramic glaze is wiped, and the color of the decorative pattern that presents is different, and such art pottery is taken a fancy to very attractive in appearance.The mould of this art pottery has separated manufacturing, saves a lot of operations like this, has reduced human cost.For the manufacturing provides great convenience.So it is low that the making method of this ceramic lamp is production cost, the production efficiency height.
Embodiment
The present invention is described in further detail below in conjunction with embodiment, but embodiments of the present invention are not limited thereto.
Embodiment 1
A kind of making method of the art pottery, the described art pottery is formed the pottery with aesthetic feeling by different decorative patterns, and this method may further comprise the steps:
The ceramic material of making the art pottery is encased in the hollander, ceramic earth is broken into mud with hollander, to break into mud and join evenly stirring in the stirrer, back one-tenth ceramic mud stirs, wherein the chemical ingredients of ceramic material is: silicon-dioxide 71%, ferric oxide 1%, calcium oxide 21%, magnesium oxide 4%, zinc oxide 3%;
To accomplish fluently ceramic mud is injected into and designs art pottery mould, through drying automatically, evenly transpiring moisture dries the back demoulding, produces art pottery earth base, will be at the art pottery earth base of making through drying automatically 30 hours, art pottery earth base is put in the barn again and dried, the problem in the barn is 52 degree, and carrying out art pottery earth base storing time in the barn is 50 hours, produce dry art pottery earth base
To smear ceramic glaze at the art pottery earth base of making drying, smear the ceramic glaze of different thickness according to the decorative pattern of art pottery earth base, wherein the composition of ceramic glaze is: ceramic glaze contains: silicon 59-69.4%, aluminium 2.5-12%, iron 0.08-3.30%, titanium 0.01-2.10%, calcium 6.90-8.90%, sodium 2.05-2.80%
The ceramic glaze ceramic disc earth base of making that smears is put into kiln and is fired, and the temperature of firing is 1280 degree, and the time of firing is 8 hours, after overcooling, is made into the art pottery.
Select 6 mass parameters that detect of the produced art pottery arbitrarily, as follows through detecting data, table 1
Embodiment 2
A kind of making method of the art pottery, the described art pottery is formed the pottery with aesthetic feeling by different decorative patterns, and this method may further comprise the steps:
The ceramic material of making the art pottery is encased in the hollander, ceramic earth is broken into mud with hollander, to break into mud and join evenly stirring in the stirrer, back one-tenth ceramic mud stirs, wherein the chemical ingredients of ceramic material is: silicon-dioxide 72%, ferric oxide 1%, calcium oxide 20%, magnesium oxide 3%, zinc oxide 4%;
To accomplish fluently ceramic mud is injected into and designs art pottery mould, through drying automatically, evenly transpiring moisture dries the back demoulding, produces art pottery earth base, will be at the art pottery earth base of making through drying automatically 31 hours, art pottery earth base is put in the barn again and dried, the problem in the barn is 53 degree, and carrying out art pottery earth base storing time in the barn is 51 hours, produce dry art pottery earth base
To smear ceramic glaze at the art pottery earth base of making drying, smear the ceramic glaze of different thickness according to the decorative pattern of art pottery earth base, wherein the composition of ceramic glaze is: ceramic glaze contains: silicon 59-69.4%, aluminium 2.5-12%, iron 0.08-3.30%, titanium 0.01-2.10%, calcium 6.90-8.90%, sodium 2.05-2.80%
The ceramic glaze ceramic disc earth base of making that smears is put into kiln and is fired, and the temperature of firing is 1278 degree, and the time of firing is 7.5 hours, after overcooling, is made into the art pottery.
Select 6 mass parameters that detect of the produced art pottery arbitrarily, as follows through detecting data, table 2
More than technical scheme that the embodiment of the invention is provided be described in detail, used specific case herein principle and the embodiment of the embodiment of the invention are set forth, the explanation of above embodiment only is applicable to the principle that helps to understand the embodiment of the invention; Simultaneously, for one of ordinary skill in the art, according to the embodiment of the invention, the part that on embodiment and range of application, all can change, in sum, this description should not be construed as limitation of the present invention.
Claims (2)
1. the making method of an art pottery is characterized in that, the described art pottery is formed the pottery with aesthetic feeling by different decorative patterns, and this method may further comprise the steps:
The ceramic material of making the art pottery is encased in the hollander, ceramic earth is broken into mud with hollander, to break into mud and join evenly stirring in the stirrer, back one-tenth ceramic mud stirs, wherein the chemical ingredients of ceramic material is: silicon-dioxide 68-73%, ferric oxide 0.5-1%, calcium oxide 17-23%, magnesium oxide 3-8%, zinc oxide 2-8%;
To accomplish fluently ceramic mud is injected into and designs art pottery mould, through drying automatically, evenly transpiring moisture dries the back demoulding, produces art pottery earth base, will be at the art pottery earth base of making through drying automatically 24-48 hour, art pottery earth base is put in the barn again and dried, the problem in the barn is the 40-60 degree, and carrying out art pottery earth base storing time in the barn is 48-58 hour, produce dry art pottery earth base
To smear ceramic glaze at the art pottery earth base of making drying, smear the ceramic glaze of different thickness according to the decorative pattern of art pottery earth base, wherein the composition of ceramic glaze is: ceramic glaze contains: silicon 59-69.4%, aluminium 2.5-12%, iron 0.08-3.30%, titanium 0.01-2.10%, calcium 6.90-8.90%, sodium 2.05-2.80%
The ceramic glaze ceramic disc earth base of making that smears is put into kiln and is fired, and the temperature of firing is the 1200-1290 degree, and the time of firing is 7-8 hour, after overcooling, is made into the art pottery.
2. a kind of making method of the art pottery according to claim 1 is characterized in that the temperature that described kiln is fired is the 1250-1300 degree.