CN103265866A - Epoxy resin wear-resistant paint for wood floor - Google Patents
Epoxy resin wear-resistant paint for wood floor Download PDFInfo
- Publication number
- CN103265866A CN103265866A CN 201310196570 CN201310196570A CN103265866A CN 103265866 A CN103265866 A CN 103265866A CN 201310196570 CN201310196570 CN 201310196570 CN 201310196570 A CN201310196570 A CN 201310196570A CN 103265866 A CN103265866 A CN 103265866A
- Authority
- CN
- China
- Prior art keywords
- parts
- resistant paint
- wear
- epoxy resin
- resins
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an epoxy resin wear-resistant paint for a wood floor, wherein the paint is mainly prepared from the following raw materials in a stirring manner according to the weight ratio: 110-115 parts of epoxy resin, 40-45 parts of polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamine, 10-13 parts of quartz sand, 5-6 parts of calcium caprylate, 4 parts of aluminum stearate, 10-12 parts of polyterephthalyl alcohol, 6-8 parts of trisodium phosphate and 15-18 parts of urea. The epoxy resin wear-resistant paint prepared by the invention can provide a firm protective coating with high wear resistance, high shock resistance and high adhesive force for the wood floor.
Description
Technical field
The present invention relates to a kind of timber floor Resins, epoxy wear-resistant paint.
Technical background
Multiple novel building structured material and finishing material although the world today has developed production, because timber has its unique good characteristic, wooden facing is given a kind of special graceful impression, this is that other finishing material can't be by comparison.So timber is remaining consequence in construction work especially decoration field.Along with
Construction industryDevelopment, interior decoration industry will have bigger development, and timber floor also will develop as one of important materials of interior decoration thereupon.And on the existing timber floor in order to prevent from making moist distortion, so can apply the enamelled coating with water-proof function on its surface, but this class enamelled coating is not wear-resisting, is easy to be wiped off; Simultaneously after floor coating wearing and tearing, its surface smoothness also can variation, influences attractive in appearance and can shorten the work-ing life on floor.So also need to apply one deck wear-resistant paint on its surface, be used for protecting the enamelled coating on the floor, avoid paint film damaged or peel off.
Summary of the invention
The present invention seeks to provides a kind of timber floor Resins, epoxy wear-resistant paint in order to overcome the deficiencies in the prior art.
For addressing the above problem, technical scheme provided by the invention is: a kind of timber floor Resins, epoxy wear-resistant paint, it mainly is to be stirred according to weight proportion by following raw materials according to make: 110-115 part Resins, epoxy, 40-45 part polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamines, 10-13 part quartz sand, 5-6 part calcium octoate, 4 parts of aluminum stearates, 10-12 part is gathered terephthalyl alcohol, 6-8 part tertiary sodium phosphate and 15-18 part urea.
Also comprise 15-17 part Natvosol.
Also comprise 5-7 part glycerine.
Beneficial effect of the present invention: the Resins, epoxy wear-resistant paint that the present invention makes can be timber floor and provides a kind of and have than high-wearing feature, shock resistance, high adhesive force, tough and tensile supercoat.Sticking to be coated with technology simple, generally only need prepare coating in proportion, stirs to be coated on floor surface and to get final product, and the workmen is not had higher technical requirements, and easy construction is low to site requirements.
Embodiment
Embodiment 1
A kind of timber floor stirs by the stirrer high speed dispersion according to weight proportion by following raw material with the Resins, epoxy wear-resistant paint and makes: 110-115 part Resins, epoxy, 40-45 part polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamines, 10-13 part quartz sand, 5-6 part calcium octoate, 4 parts of aluminum stearates, 10-12 part is gathered terephthalyl alcohol, 6-8 part tertiary sodium phosphate and 15-18 part urea.
Embodiment 2
A kind of timber floor stirs by the stirrer high speed dispersion according to weight proportion by following raw material with the Resins, epoxy wear-resistant paint and makes: 110-115 part Resins, epoxy, 40-45 part polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamines, 10-13 part quartz sand, 5-6 part calcium octoate, 4 parts of aluminum stearates, 10-12 part is gathered terephthalyl alcohol, 6-8 part tertiary sodium phosphate, 15-18 part urea and 15-17 part Natvosol.
Embodiment 3
A kind of timber floor stirs by the stirrer high speed dispersion according to weight proportion by following raw material with the Resins, epoxy wear-resistant paint and makes: 110-115 part Resins, epoxy, 40-45 part polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamines, 10-13 part quartz sand, 5-6 part calcium octoate, 4 parts of aluminum stearates, 10-12 part is gathered terephthalyl alcohol, 6-8 part tertiary sodium phosphate, 15-18 part urea, 15-17 part Natvosol and 5-7 part glycerine.
Embodiment 4
Basic mechanical design feature such as the table 1 of the product of the present invention's preparation:
Table 1
| Project | Technical indicator |
| Mean particle size, μ m | 79-85 |
| Water regain/(g/10mi n) | ≤1.5 |
| Alkali resistance (48h) | No abnormal |
| Sticking power | 1 grade |
| Water tolerance (96h) | No abnormal |
| Cohesive strength/MPa | Standard state |
| Hardness | 9H (Mohs) |
| Viscosity | 3400-3600mPa.s |
| Surface drying time | Greater than 30 minutes |
| Wearability | ?0.010 |
Claims (3)
1. timber floor Resins, epoxy wear-resistant paint, it is characterized in that it mainly is to be stirred according to weight proportion by following raw materials according to make: 110-115 part Resins, epoxy, 40-45 part polyamide resin, 25 parts of dimethylbenzene, 10 parts of diethylenetriamines, 10-13 part quartz sand, 5-6 part calcium octoate, 4 parts of aluminum stearates, 10-12 part is gathered terephthalyl alcohol, 6-8 part tertiary sodium phosphate and 15-18 part urea.
2. a kind of timber floor Resins, epoxy wear-resistant paint according to claim 1 is characterized in that: also comprise 15-17 part Natvosol.
3. a kind of timber floor Resins, epoxy wear-resistant paint according to claim 1 and 2 is characterized in that: also comprise 5-7 part glycerine.