CN103265750B - 一种乙烯-丙烯酸甲酯电缆护套料及其制备方法 - Google Patents

一种乙烯-丙烯酸甲酯电缆护套料及其制备方法 Download PDF

Info

Publication number
CN103265750B
CN103265750B CN201310197332.9A CN201310197332A CN103265750B CN 103265750 B CN103265750 B CN 103265750B CN 201310197332 A CN201310197332 A CN 201310197332A CN 103265750 B CN103265750 B CN 103265750B
Authority
CN
China
Prior art keywords
ethylene
methyl acrylate
magnesium hydroxide
cable sheath
agent
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310197332.9A
Other languages
English (en)
Other versions
CN103265750A (zh
Inventor
莫连松
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Changyuan Zhihao Electric Power Science & Technology Co Ltd
Original Assignee
Anhui Changyuan Zhihao Electric Power Science & Technology Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Changyuan Zhihao Electric Power Science & Technology Co Ltd filed Critical Anhui Changyuan Zhihao Electric Power Science & Technology Co Ltd
Priority to CN201310197332.9A priority Critical patent/CN103265750B/zh
Publication of CN103265750A publication Critical patent/CN103265750A/zh
Application granted granted Critical
Publication of CN103265750B publication Critical patent/CN103265750B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种乙烯-丙烯酸甲酯电缆护套料及其制备方法，其组成原料为：乙烯-丙烯酸甲酯、顺丁橡胶、三氧化二铝、硅酸钠粉、改性氢氧化镁、异氰酸酯、防焦剂CTP、钛酸酯偶联剂TMC-TTS、氧化锌、抗氧剂DSTP、抗滴落剂TN3500和甘油三醋酸酯；本发明采用乙烯-丙烯酸甲酯作为主料，具有优良的拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率等性能，以三氧化二铝为补强剂，而且通过对阻燃剂氢氧化镁的改性处理，可以大大提高电缆护套的阻燃性，阻燃效果明显。

Description

一种乙烯-丙烯酸甲酯电缆护套料及其制备方法
技术领域
本发明涉及一种乙烯-丙烯酸甲酯电缆护套料及其制备方法，属于电缆护套料制造领域。
背景技术
随着经济的迅速发展，电线电缆在各个行业、领域中都得到广泛的应用，电气火灾事故的频繁发生，电线电缆的阻燃问题逐渐引起世界各国的重视，电缆燃烧时释放出大量烟雾和有毒的、腐蚀性的气体是火灾中危险因素，在火灾中妨碍了人们的安全撤离和灭火工作，使生命财产遭到严重损失，同时随着通讯事业、汽车工业和计算机工业的发展，对电缆护套料的质量要求日益增加，本发明提供一种乙烯-丙烯酸甲酯电缆护套料及其制备方法。
发明内容
本发明的目的在于提供一种乙烯-丙烯酸甲酯电缆护套料及其制备方法。
为了实现上述目的，本发明采用如下技术方案：
乙烯-丙烯酸甲酯电缆护套料，其组成原料的重量份为：乙烯-丙烯酸甲酯40-50、顺丁橡胶15-20、三氧化二铝3.0-4.0、硅酸钠粉17-23、改性氢氧化镁10-15、异氰酸酯1.1-1.3、防焦剂CTP1.9-2.1、钛酸酯偶联剂TMC-TTS2.3-2.8、氧化锌0.4-0.6、抗氧剂DSTP2.3-2.5、抗滴落剂TN35000.25-0.35和甘油三醋酸酯1.0-1.5。
乙烯-丙烯酸甲酯电缆护套料，其组成原料的重量份为：乙烯-丙烯酸甲酯45、顺丁橡胶18、三氧化二铝3.5、硅酸钠粉20、改性氢氧化镁12、异氰酸酯1.2、防焦剂CTP2.0、钛酸酯偶联剂TMC-TTS2.5、氧化锌0.5、抗氧剂DSTP2.4、抗滴落剂TN35000.30和甘油三醋酸酯1.2。
乙烯-丙烯酸甲酯电缆护套料的制备方法，包括以下步骤：
（1）制备：按组成原料的重量份称取氢氧化镁，粉碎成150-200nm之间，然后加入氢氧化镁总重量的0.4-0.6%脂肪醇聚氧乙烯醚、0.7-1.0%交联剂TAC和1.3-1.5%纳米混凝土粉末，均匀搅拌，控制压力1.0Mpa-1.2Mpa，得到改性氢氧化镁；
（2）按组成原料的重量份称取步骤（1）的改性氢氧化镁和其他剩余各原料，然后在温度135-150℃在密炼8-10分钟后，加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度155-170℃，得到成品。
本发明的有益效果：
本发明采用乙烯-丙烯酸甲酯作为主料，具有优良的拉伸强度、断裂延伸率、老化后的拉伸强度保持率及断裂伸出保持率等性能，以三氧化二铝为补强剂，而且通过对阻燃剂氢氧化镁的改性处理，可以大大提高电缆护套的阻燃性，阻燃效果明显。
具体实施方式
实施例1：乙烯-丙烯酸甲酯电缆护套料，其组成原料的重量份（kg）为：乙烯-丙烯酸甲酯45、顺丁橡胶18、三氧化二铝3.5、硅酸钠粉20、改性氢氧化镁12、异氰酸酯1.2、防焦剂CTP2.0、钛酸酯偶联剂TMC-TTS2.5、氧化锌0.5、抗氧剂DSTP2.4、抗滴落剂TN35000.30和甘油三醋酸酯1.2。
乙烯-丙烯酸甲酯电缆护套料的制备方法，包括以下步骤：
（1）制备：按组成原料的重量份称取氢氧化镁，粉碎成180nm之间，然后加入氢氧化镁总重量的0.5%脂肪醇聚氧乙烯醚、0.85%交联剂TAC和1.4%纳米混凝土粉末，均匀搅拌，控制压力1.1Mpa，得到改性氢氧化镁；
（2）按组成原料的重量份称取步骤（1）的改性氢氧化镁和其他剩余各原料，然后在温度145℃在密炼9分钟后，加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度160℃，得到成品。
通过本发明的实施例1制得的电缆料性能数据：
拉伸强度为16.1-173Mpa，断裂伸出率为715-740%，老化后拉伸强度保持率（120℃，96h）90.2%，老化后断裂伸出保持率（120℃，96h）81.9%；氧指数28.7.6-32.6%，烟密度为70-73，垂直燃烧试验通过UL-94V0级。

Claims (2)

1.一种乙烯-丙烯酸甲酯电缆护套料，其特征在于其组成原料的重量份为：乙烯-丙烯酸甲酯40-50、顺丁橡胶15-20、三氧化二铝3.0-4.0、硅酸钠粉17-23、改性氢氧化镁10-15、异氰酸酯1.1-1.3、防焦剂CTP1.9-2.1、钛酸酯偶联剂TMC-TTS2.3-2.8、氧化锌0.4-0.6、抗氧剂DSTP2.3-2.5、抗滴落剂TN35000.25-0.35和甘油三醋酸酯1.0-1.5；
所述的乙烯-丙烯酸甲酯电缆护套料的制备方法，包括以下步骤：
（1）制备：按组成原料的重量份称取氢氧化镁，粉碎成150-200nm之间，然后加入氢氧化镁总重量的0.4-0.6%脂肪醇聚氧乙烯醚、0.7-1.0%交联剂TAC和1.3-1.5%纳米混凝土粉末，均匀搅拌，控制压力1.0MPa-1.2MPa，得到改性氢氧化镁；
（2）按组成原料的重量份称取步骤（1）的改性氢氧化镁和其他剩余各原料，然后在温度135-150℃在密炼8-10分钟后，加入开炼机和密炼机或双螺杆挤出机混炼、造粒，控制温度155-170℃，得到成品。
2.根据权利要求1所述的乙烯-丙烯酸甲酯电缆护套料，其特征在于其组成原料的重量份为：乙烯-丙烯酸甲酯45、顺丁橡胶18、三氧化二铝3.5、硅酸钠粉20、改性氢氧化镁12、异氰酸酯1.2、防焦剂CTP2.0、钛酸酯偶联剂TMC-TTS2.5、氧化锌0.5、抗氧剂DSTP2.4、抗滴落剂TN35000.30和甘油三醋酸酯1.2。
CN201310197332.9A 2013-05-24 2013-05-24 一种乙烯-丙烯酸甲酯电缆护套料及其制备方法 Expired - Fee Related CN103265750B (zh)