CN103254693B - 一种混凝土内墙用防水隔热保温涂料 - Google Patents
一种混凝土内墙用防水隔热保温涂料 Download PDFInfo
- Publication number
- CN103254693B CN103254693B CN201310208161.5A CN201310208161A CN103254693B CN 103254693 B CN103254693 B CN 103254693B CN 201310208161 A CN201310208161 A CN 201310208161A CN 103254693 B CN103254693 B CN 103254693B
- Authority
- CN
- China
- Prior art keywords
- parts
- paint
- water
- intermediate coat
- emulsion
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种混凝土内墙用防水隔热保温涂料,由面漆、中间漆和底漆组成,其中,面漆含有粘土15~25份、天然橡胶乳液20~40份、丁苯橡胶5~10份、苯丙乳液5~10份、颜填料25~40份、助剂5~16份、水15~25份;中间漆含有粘土10~20份、EVA乳液20~35份、E44环氧树脂3~10份、颜填料30~50份、助剂2~8、水20~25份;底漆含有天然橡胶乳液15~30份、丁苯乳液5~10份、苯丙乳液5~10份、颜填料20~30、助剂4~8、水15~20份,按重量份计。本发明的防水隔热保温涂料是由耐擦洗面漆、中间漆和底漆构成,可隔绝来自外部环境的大部分热量,环保节能,以外墙面积500平方的别墅为例,涂刷本发明的防水隔热涂料后,全年可节省电耗15-20%。且涂料中不含有有机溶剂等易致癌物质,健康环保。
Description
技术领域
本发明涉及一种涂料,具体涉及一种混凝土内墙用防水隔热保温涂料。
背景技术
据统计,建筑能耗占全社会总能耗的30%,我国建筑能耗是发达国家的2-4倍。我国地域辽阔,有严寒寒冷地区、冬冷夏热地区,冬冷夏暖地区。冬天取暖,夏天降温,使得居住建筑成为能耗最多的建筑类型。以广东省为例,2009年全省新竣工商品住宅面积666.5万平方米,都是高能耗建筑。若按50%节能计算,这些住宅我耗能源折合电力为2.9亿度.
按照全国每年新增6亿平方米建筑的建设规模,且实现建筑节能50%目标,则每年全国可节约建筑能261亿度电。为全面推进建筑节能工作,国家建设部、广东省建设厅已确定:今后建筑节能目标与工作重点为墙体节能。因而,开发一种高效环保的混凝土内墙用防水隔热保温涂料,对于墙体节能工作具有重要意义。
发明内容
本发明的目的在于提供一种混凝土内墙用防水隔热保温涂料。
本发明所采取的技术方案是:
一种混凝土内墙用防水隔热保温涂料,由面漆、中间漆和底漆组成,其中:
面漆含有以下重量份比的组分:粘土15~25份、天然橡胶乳液20~40份、丁苯橡胶5~10份、苯丙乳液5~10份、颜填料25~40份、助剂5~16份、水15~25份;
中间漆含有以下重量份比的组分:粘土10~20份、EVA乳液20~35份、E44环氧树脂3~10份、颜填料30~50份、助剂2~8、水20~25份;
底漆含有以下重量份比的组分:天然橡胶乳液15~30份、丁苯乳液5~10份、苯丙乳液5~10份、颜填料20~30、助剂4~8、水15~20份。
面漆中所用颜填料为金红石钛白粉、硅灰石粉、沉淀硫酸钡中的至少两种。
面漆中所用助剂为邻苯二甲酸二丁酯、三乙醇胺中的至少一种。
中间漆中所用颜填料为金红石钛白粉、有机膨润土、纳米级氧化镁、氧化锌中的至少一种。
中间漆中所用助剂为邻苯二甲酸二丁酯。
底漆所用颜填料为滑石粉、锐钛型钛白粉、纳米级氧化镁、沉淀硫酸钡、硅灰石粉中的至少两种。
底漆所用助剂为邻苯二甲酸二丁酯、六偏磷酸钠中的至少一种。
一种混凝土内墙用防水隔热保温涂料,由面漆、中间漆和底漆组成,其中:
面漆由粘土15~25份、天然橡胶乳液20~40份、丁苯橡胶5~10份、苯丙乳液5~10份、金红石钛白粉15~25份、硅灰石粉10~20份、邻苯二甲酸二丁酯2~8份、三乙醇胺3~8份、水15~25份组成;
中间漆由粘土10~20份、EVA乳液20~35份、E44环氧树脂3~10份、金红石钛白粉10~15份、有机膨润土3~10份、纳米级氧化镁10~20份、氧化锌5~10份、邻苯二甲酸二丁酯2~8份、水20~25份组成;
底漆由天然橡胶乳液15~30份、丁苯乳液5~10份、苯丙乳液5~10份、滑石粉5~10份、锐钛型钛白粉5~10份、纳米级氧化镁5~10份、邻苯二甲酸二丁酯2~5份、六偏磷酸钠1~3份、水15~20份组成。
本发明的有益效果是:
(1)本发明的防水隔热保温涂料是由耐擦洗面漆、中间漆和底漆构成,可隔绝来自外部环境的大部分热量,环保节能,以外墙面积500平方的别墅为例,涂刷本发明的防水隔热涂料后,全年可节省电耗15-20%;
(2)本发明的隔热涂料为水性涂料,溶剂为水,因而不含有有机溶剂等易致癌物质,健康环保;
(3)本发明的防水隔热保温涂料具有良好的防水功能,对墙体的粘结强度高,大大提高了墙体的保温防水及抗侵蚀功能,延长墙体使用寿命。
具体实施方式
下面结合实施例对本发明作进一步的说明,但并不局限于此。
实施例1
表1为本发明一种混凝土内墙用防水隔热涂料的一个优选方案。
表1
实施例2
表2为本发明一种混凝土内墙用防水隔热涂料的一个优选方案。
表2
实施例3
表3为本发明一种混凝土内墙用防水隔热涂料的一个优选方案。
表3
实施例4
表4为本发明一种混凝土内墙用防水隔热涂料的一个优选方案。
表4
实施例5
表5为本发明一种混凝土外墙用防水隔热涂料的一个优选方案。
表5
将上述1-5实施例的面漆的各组分经溶解、混合、研磨、过滤后,得到本发明隔热涂料的面漆;将上述1-5实施例的中间漆的各组分经溶解、混合、研磨、过滤后,得到本发明隔热涂料的中间漆;将上述1-5实施例的底漆的各组分经溶解、混合、改性、研磨、过滤后,得到本发明隔热涂料的底漆。
对实施例1-5制备的混凝土外墙用防水隔热涂料进行性能测试,测试结果见表6。
表6
隔热温差测试:把实施例1-5所得到的涂料涂在10×10mm的混凝土板上,漆膜厚度为100微米。把涂刷的测试样板和参考样板(涂刷普通内墙涂料)放在测试箱,对两种样品同时加热,分别同时记录加热箱温度,测试完毕后,测试样板后箱温度比参考样板后箱温度低20℃。说明测试样板有明显的隔热保温效果。
Claims (6)
1.一种混凝土内墙用防水隔热保温涂料,由面漆、中间漆和底漆组成,其中:
面漆含有以下重量份比的组分:粘土15~25份、天然橡胶乳液20~40份、丁苯橡胶5~10份、苯丙乳液5~10份、颜填料25~40份、助剂5~16份、水15~25份;
中间漆含有以下重量份比的组分:粘土10~20份、EVA乳液20~35份、E44环氧树脂3~10份、颜填料30~50份、助剂2~8、水20~25份;
底漆含有以下重量份比的组分:天然橡胶乳液15~30份、丁苯乳液5~10份、苯丙乳液5~10份、颜填料20~30、助剂4~8、水15~20份;
面漆中所用颜填料为金红石钛白粉、硅灰石粉、沉淀硫酸钡中的至少两种;
面漆中所用助剂为邻苯二甲酸二丁酯、三乙醇胺中的至少一种。
2.根据权利要求1所述的混凝土内墙用防水隔热保温涂料,其特征在于,中间漆中所用颜填料为金红石钛白粉、有机膨润土、纳米级氧化镁、氧化锌中的至少一种。
3.根据权利要求1所述的混凝土内墙用防水隔热保温涂料,其特征在于,中间漆中所用助剂为邻苯二甲酸二丁酯。
4.根据权利要求1所述的混凝土内墙用防水隔热保温涂料,其特征在于,底漆所用颜填料为滑石粉、锐钛型钛白粉、纳米级氧化镁、沉淀硫酸钡、硅灰石粉中的至少两种。
5.根据权利要求1所述的混凝土内墙用防水隔热保温涂料,其特征在于,底漆所用助剂为邻苯二甲酸二丁酯、六偏磷酸钠中的至少一种。
6.一种混凝土内墙用防水隔热保温涂料,由面漆、中间漆和底漆组成,其中:面漆由粘土15~25份、天然橡胶乳液20~40份、丁苯橡胶5~10份、苯丙乳液5~10份、金红石钛白粉15~25份、硅灰石粉10~20份、邻苯二甲酸二丁酯2~8份、三乙醇胺3~8份、水15~25份组成;
中间漆由粘土10~20份、EVA乳液20~35份、E44环氧树脂3~10份、金红石钛白粉10~15份、有机膨润土3~10份、纳米级氧化镁10~20份、氧化锌5~10份、邻苯二甲酸二丁酯2~8份、水20~25份组成;
底漆由天然橡胶乳液15~30份、丁苯乳液5~10份、苯丙乳液5~10份、滑石粉5~10份、锐钛型钛白粉5~10份、纳米级氧化镁5~10份、邻苯二甲酸二丁酯2~5份、六偏磷酸钠1~3份、水15~20份组成。