CN103254637A - 苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料 - Google Patents

苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料 Download PDF

Info

Publication number
CN103254637A
CN103254637A CN2013101594873A CN201310159487A CN103254637A CN 103254637 A CN103254637 A CN 103254637A CN 2013101594873 A CN2013101594873 A CN 2013101594873A CN 201310159487 A CN201310159487 A CN 201310159487A CN 103254637 A CN103254637 A CN 103254637A
Authority
CN
China
Prior art keywords
styrene
acrylonitrile copolymer
parts
alloy material
copolymer modified
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101594873A
Other languages
English (en)
Inventor
周洪保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Changshu Kangbao Medical Appliance Factory
Original Assignee
Changshu Kangbao Medical Appliance Factory
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Changshu Kangbao Medical Appliance Factory filed Critical Changshu Kangbao Medical Appliance Factory
Priority to CN2013101594873A priority Critical patent/CN103254637A/zh
Publication of CN103254637A publication Critical patent/CN103254637A/zh
Pending legal-status Critical Current

Abstract

一种苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，属于高分子材料技术领域。其是由以下重量份数的原料组成：聚酰胺6树脂100～112份；橡胶8～15份；苯乙烯-丙烯腈共聚物6～12份；增韧剂6～10份；磷酸盐23～32份；抗氧剂0.7～1.2份；磨碎玻璃纤维21～28份；炭黑2.1～2.7份。提供的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料经测试具有如下性能指标：拉伸强度123～145MPa，弯曲强度210～235MPa，缺口冲击强度10.5～14.0kj/m2，阻燃性达到V-0(UL-94-3.0mm)，在200℃放置24小时，无开裂；由于配方中不含有损环境的助剂、卤素和重金属，因而具有良好的环保效果。

Description

苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料
技术领域
本发明属于高分子材料技术领域，具体涉及一种苯乙烯-丙烯腈共聚物改性聚酰胺合金材料。
背景技术
聚酰胺是一类很重要的工程塑料，广泛用于汽车、建筑、电子等领域。随着热塑性工程塑料应用越来越广，但是工程塑料废弃也越来普遍。塑料制品添加剂的污染也呈扩大趋势，很多助剂，卤素、铅、铬等都随着塑料制品的丢弃而不断扩散，影响水体、自然环境，最终影响人类健康。因此如何避免工程塑料在废弃后损及环境的问题越来越为人们关注。
发明内容
本发明的任务是要提供一种有助于避免在废弃后对环境产生影响的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料。
本发明的任务是这样来完成的，一种苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其是由以下重量份数的原料组成：
在本发明的一个实施例中，所述的聚酰胺6树脂为熔点在210℃以上，特性黏度指数为2.4 的聚己内酰胺树脂。
在本发明的另一个实施例中，所述的橡胶为三元乙丙橡胶。
在本发明的又一个实施例中，所述的苯乙烯-丙烯腈共聚物为苯乙烯含量为75%苯乙烯-丙烯腈共聚物。
在本发明的再一个实施例中，所述的增韧剂为马来酸酐接枝的三元乙丙橡胶。
在本发明的还有一个实施例中，所述的磷酸盐为次磷酸铝。
在本发明的更而一个实施例中，所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
在本发明的进而一个实施例中，所述的磨碎玻璃纤维为长度为150～220微米的乱玻璃纤维。
在本发明的又更而一个实施例中，所述的炭黑为炉法炭黑。
本发明提供的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料经测试具有如下性能指标：拉伸强度123～145MPa，弯曲强度210～235MPa ,缺口冲击强度10.5～14.0kj/m2,阻燃性达到V-0(UL-94-3.0mm)，在200℃放置24小时，无开裂；由于配方中不含有损环境的助剂、卤素和重金属，因而具有良好的环保效果。
具体实施方式
实施例1：
实施例2：
Figure BDA0000313887283
实施例3：
Figure BDA0000313887284
Figure BDA0000313887285
实施例4：
Figure BDA0000313887286
由上述实施例1至4得到的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料经测试具有如下技术效果：
测试项目 实施例1 实施例2 实施例3 实施例4
拉伸强度MPa 125 131 138 144
弯曲强度MPa 212 218 225 234
悬臂梁缺口冲击强度kj/m2 10.7 11．6 12.3 13.8
阻燃性(UL-94-3.0mm) V-0 V-0 V-0 V-0
200℃放置24小时 不开裂 不开裂 不开裂 不开裂

Claims (9)

1.一种苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于其是由以下重量份数的原料组成：
                  聚酰胺6树脂          100～112份；
          橡胶                 8~15份；
          苯乙烯-丙烯腈共聚物     6～12份；
          增韧剂               6~10份；
          磷酸盐               23~32份；
          抗氧剂               0.7~1.2份；
          磨碎玻璃纤维         21~28份；
           炭黑                2.1~2.7份。
2.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的聚酰胺6树脂为熔点在210℃以上，特性黏度指数为2.4 的聚己内酰胺树脂。
3.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的橡胶为三元乙丙橡胶。
4.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的苯乙烯-丙烯腈共聚物为苯乙烯含量为75%苯乙烯-丙烯腈共聚物。
5.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的增韧剂为马来酸酐接枝的三元乙丙橡胶。
6.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的磷酸盐为次磷酸铝。
7.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的抗氧剂为双（2，4-二叔丁基苯基）季戊四醇双二亚磷酸酯。
8.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的磨碎玻璃纤维为长度为150～220微米的乱玻璃纤维。
9.根据权利要求1所述的苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料，其特征在于所述的炭黑为炉法炭黑。
CN2013101594873A 2013-05-03 2013-05-03 苯乙烯-丙烯腈共聚物改性环保聚酰胺合金材料 Pending CN103254637A (zh)