CN103243893A - Production method for six-layer environment-friendly composite floor - Google Patents
Production method for six-layer environment-friendly composite floor Download PDFInfo
- Publication number
- CN103243893A CN103243893A CN2012100296872A CN201210029687A CN103243893A CN 103243893 A CN103243893 A CN 103243893A CN 2012100296872 A CN2012100296872 A CN 2012100296872A CN 201210029687 A CN201210029687 A CN 201210029687A CN 103243893 A CN103243893 A CN 103243893A
- Authority
- CN
- China
- Prior art keywords
- layer
- finished product
- tenon
- production method
- composite floor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
A production method for a six-layer environment-friendly composite floor comprises the following steps: allocating an environment-friendly layer, performing a first step of hot pressing, performing a second step of hot pressing to manufacture a semi-finished product plate; maintaining the pressed semi-finished product plate on a ventilating portion for a week; opening tenon heads and tenon tails, wherein the tenon heads and the tenon tails cannot be too tight; removing exposed wood parts on the upper surface and the lower surface, sealing wax on other parts, and ensuring the wax to be evenly coated on the surfaces of the tonon heads and the tenon tails; and adhering a foot feeling layer on the lower surface of a balancing layer to manufacture a finished product. The floor manufactured by the method is wear-resisting, impact resisting, fouling resisting, inflaming retarding, moistureproof, fadeless, easy and convenient to install, capable of neutralizing formaldehyde released from impregnated paper laminated floors and releasing anion, and capable of improving foot feelings and enabling users to feel better compared with solid wood floors in use.
Description
Technical field
The present invention relates to house ornamentation material technology field, particularly a kind of production method of six layers of environment Protection composite floor board.
Background technology
Impregnated-paper laminated wood floor claims laminated flooring again, is made up of wearing layer, decorative layer, high density substrate layer, balance (protection against the tide) layer.Impregnated-paper laminated wood floor is with one or more layers dedicated paper dipping thermoset amino resin, mats formation on artificial board substrate top layers such as shaving board, high density fiberboards, and the back side adds balance layer, and the front adds wearing layer, through the floor of hot pressing, moulding.
But existing impregnated-paper laminated wood floor has such shortcoming with respect to wooden floor on the market at present:
1, because high density fiberboard needs to use formaldehyde in process of production, this is not environmental protection, because indoor formaldehyde content is in case surpass certain standard human body is harmful to.
2, impregnated-paper laminated wood floor is to adopt bionic means to make, and the floor feel of producing does not have wooden floor good.
Summary of the invention
Technical problem to be solved by this invention provides a kind of production method of six layers of environment Protection composite floor board.
For solving the problems of the technologies described above, the present invention realizes as follows: a kind of production method of six layers of environment Protection composite floor board may further comprise the steps:
The allotment environmental protection layer;
One hot pressing;
Half-finished product plate is made in two road hot pressing;
The described half-finished product plate that pressing is gone out carries out health in the ventilation, conditioned time is a week;
Leave tenon tenon tail, tenon tenon tail can not be too tight;
Remove upper surface and soffit and expose the part of timber, other parts are carried out sealing wax, guarantee that wax can be coated in the surface of tenon tenon tail uniformly;
Below balance layer, stick the feel layer, make finished product.
Good effect of the present invention is: the base plate that the method for the invention is produced, not only wear-resisting, shock resistance, resistance to deformation, anti-pollution, fire-retardant, moistureproof, colour-fast, and simple installation, can the formaldehyde that impregnated-paper laminated wood floor discharges be neutralized, discharge anion.Can also improve the feel on floor, allow this floor use and have than the better feel of wooden floor.
Description of drawings
Fig. 1 is step schematic diagram of the present invention;
Fig. 2 is structural representation of the present invention
The specific embodiment
The present invention is further detailed explanation below in conjunction with the drawings and specific embodiments.
The present invention increases two-layer on the basis of traditional handicraft, become six layers of impregnated-paper laminated wood floor from four layers of impregnated-paper laminated wood floor.Will increase three process on operation, reach the purpose of the characteristic of improving this floor, the floor of this technology has environmental protection and the good characteristics of feel.The base plate of producing is respectively wearing layer, decorative layer, environmental protection layer, high-density fiberboard layer, balance layer, feel layer from top to bottom.
The three process that increases is respectively:
1, the operation of pressing environmental protection layer, this environmental protection layer adopts spraying coating process, will cover into one deck by the mode of spraying except formaldehyde agent, anion produce agent, dispersant together, reaches the purpose of environmental protection, can remove formaldehyde and can discharge anion again.
The operation of 2, pressing feel layer, this feel layer are to adopt the cushion coat of the soft sense of one deck.
3, the sealing wax operation of the timber exposed portions serve of high density fiberboard reaches the purpose that improves feel and waterproof.
The production method of a kind of six layers of environment Protection composite floor board of the present invention may further comprise the steps:
S1: allotment environmental protection layer.Environmental protection layer is by producing agent, dispersing agent, thickener according to 2: 2: 1 except formaldehyde agent, anion: 1 ratio proportioning, the water system that adds 100 parts then is mixed and made into.
S2: one hot pressing.Pave balance layer 3, high-density fiberboard layer 5, environmental protection layer 2 in the spraying, overlay.Temperature remains on about 200 degrees centigrade, specifically according to circumstances adjusts, and the pressing time was at 5 seconds.
S3: two road hot pressing.On the basis of one heating platen, stick decorative layer 4 and wearing layer 1 successively, overlay, make half-finished product plate.Temperature remains on about 200 degrees centigrade, specifically according to circumstances adjusts, and the pressing time, it was fixed specifically to come according to the pressing effect about 30 seconds.
S4: the half-finished product plate that pressing is gone out carries out health in the ventilation, about one week of health.
S5: half-finished product plate is sawed plate, break into platelet.
S6: fluting.Leave tenon tenon tail, tenon tenon tail can not be too tight.
S7: sealing wax.Remove upper surface and soffit and expose the part of timber, other parts are carried out sealing wax, guarantee that wax can be coated in the surface of tenon tenon tail uniformly.
S8: below balance layer 3, stick feel layer 6, make finished product.
S9: finished product is packed overlay film.
S10: with finished product vanning warehouse-in.
The product that adopts the inventive method to make combines the advantage of consolidated floor and wooden floor fully:
1, environment protecting
2, discharge the anion fine-purification air
3, feel is comfortable
4, good water-proof effect
Claims (5)
1. the production method of six layers of environment Protection composite floor board is characterized in that, may further comprise the steps:
The allotment environmental protection layer;
One hot pressing;
Half-finished product plate is made in two road hot pressing;
The described half-finished product plate that pressing is gone out carries out health in the ventilation, conditioned time is a week;
Leave tenon tenon tail, tenon tenon tail can not be too tight;
Remove upper surface and soffit and expose the part of timber, other parts are carried out sealing wax, guarantee that wax can be coated in the surface of tenon tenon tail uniformly;
Below balance layer, stick the feel layer, make finished product.
2. the production method of a kind of six layers of environment Protection composite floor board according to claim 1, it is characterized in that, described allotment environmental protection layer refers to: will produce agent, dispersing agent, thickener according to 2: 2: 1 except formaldehyde agent, anion: 1 ratio proportioning, the water system that adds 100 parts then is mixed and made into described environmental protection layer.
3. the production method of a kind of six layers of environment Protection composite floor board according to claim 1, it is characterized in that, described one hot pressing refers to: paving the ground balance layer high-density fiberboard layer of mating formation, at the described environmental protection layer of described high-density fiberboard layer spraying, overlaying then; Temperature remains on 200 degrees centigrade, and the pressing time is 5 seconds.
4. the production method of a kind of six layers of environment Protection composite floor board according to claim 1, it is characterized in that, described two road hot pressing are made half-finished product plate and are referred to: stick decorative layer and wearing layer successively on the basis of described one heating platen, overlay then, make half-finished product plate; Temperature remains on 200 degrees centigrade, and the pressing time was at 30 seconds.
5. the production method of a kind of six layers of environment Protection composite floor board according to claim 1 is characterized in that, and is further comprising the steps of:
Described finished product is packed overlay film;
With described finished product vanning warehouse-in.