CN106113163A - Solid wood veneer sheet texture thick china mildew-resistant technique and grain of wood lagging mildew-resistant goods - Google Patents
Solid wood veneer sheet texture thick china mildew-resistant technique and grain of wood lagging mildew-resistant goods Download PDFInfo
- Publication number
- CN106113163A CN106113163A CN201610446723.3A CN201610446723A CN106113163A CN 106113163 A CN106113163 A CN 106113163A CN 201610446723 A CN201610446723 A CN 201610446723A CN 106113163 A CN106113163 A CN 106113163A
- Authority
- CN
- China
- Prior art keywords
- mildew
- finished product
- semi
- resistant
- lagging
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention provides a kind of solid wood veneer sheet texture thick china mildew-resistant technique, selects base material to make white embryo semi-finished product through machining, controls the moisture content of described white embryo semi-finished product；When configuring glue, glue adds water mildow-proof auxiliary agent and stirs；Hot pressing lagging technique attaches epidermis and prepares lagging semi-finished product routinely；Semi-finished product are cooled down；When primer spray, add oiliness mildew-resistant auxiliary agent in primers and stir；It is sprayed at according to a conventional method on the semi-finished product after above-mentioned process successively；Drying and sanding, spray-applied primer again, drying and sanding；Spray paint, then dries.The present invention also provides for a kind of grain of wood lagging mildew-resistant goods, can play and stop artificial board and produce mildew, the grain of wood the most beautiful attractive in appearance, color is more lively, without flaw, improve and produce sheet material quality and quality.
Description
Technical field
The present invention relates to house decorative material technical field, relate to a kind of solid wood veneer sheet texture thick china mildew-resistant technique,
Particularly to a kind of grain of wood lagging mildew-resistant goods.
Background technology
In wooden boards field, along with the development of science and technology, common artificial decorative panel production technology and technical maturity
Improve constantly, artificial decoration panel products market occupy timber industry produce main flow, but artificial decoration plate production technology and
The emphasis of production development gradually changes, technology trends mainly restructuring, Composite, the application of Functionalization, product
The trend of development is to break through traditional wood-based plate scope and develop into the wood base composite material that has more broad sense.Function is artificial
Plate belongs to the functional composite material in new material technology, and it directly emphasizes the purposes of product, as to heat, electricity, light, magnetic, sound, mushroom etc.
The specific function shown.
The products such as existing stick-skin furniture are typically with wood or/and sheet material base material as an alternative, will substitute base material
Determine step routinely, method makes semi-finished product through preliminary working.Stick natural veneer at the outer surface of semi-finished product, inner surface thus
Make lagging semi-finished product.Lagging semi-finished product successively through polish such as spray paint, cloth art, packagings thus make stick-skin furniture become
Product.Select the veneer of different materials, i.e. can be made into all kinds of lagging product.But, prior art produced at artificial board
Cheng Zhong, it may appear that more mildew, such as: MDF, clamping plate etc..Cause producing sheet material and there is significant drawback in appearance.
Meanwhile, also sheet material quality is produced in impact.To this end, how to solve artificial board to produce mildew in producing, for the present invention
The problem of research.
Summary of the invention
In view of this, the present invention is directed to the deficiency that prior art exists, its objective is to provide a kind of solid wood veneer sheet texture
Thick china mildew-resistant technique, solves in prior art in artificial board production process, it may appear that more mildew, causes producing
Out there is significant drawback, and the problem that sheet material quality is produced in impact in sheet material in appearance.
In view of this, the present invention is directed to the deficiency that prior art exists, its another purpose is to provide a kind of grain of wood patch
Skin mildew-resistant goods, solve in prior art in artificial board production process, it may appear that more mildew, cause producing
There is significant drawback, and the problem that sheet material quality is produced in impact in appearance in sheet material.
To achieve these goals, the present invention adopts the following technical scheme that
A kind of solid wood veneer sheet texture thick china mildew-resistant technique, passes sequentially through following steps and realizes: 1) select base material to pass through
Being processed into white embryo semi-finished product, the moisture content controlling described white embryo semi-finished product is 8%-12%；2) configuration glue, adds in glue
Adding water mildow-proof auxiliary agent, glue configures with water mildow-proof auxiliary agent 1000:5 in mass ratio, and stirs；3) step is used
The glue adding mildew-resistant auxiliary agent that the white embryo semi-finished product prepared in rapid 1 and step 2 prepare, hot pressing lagging technique is at white embryo routinely
Brushing glue attach solid wood veneer sheet on semi-finished product, prepares lagging semi-finished product；4) the lagging semi-finished product in step 3 are carried out cold
But；5) configuration priming paint, adds oiliness mildew-resistant auxiliary agent in primers, and priming paint enters according to mass ratio 1000:5 with oiliness mildew-resistant auxiliary agent
Row configuration, and stir；6) priming paint prepared in step 5 is used, according to a conventional method by basecoat paint in processing through step 4
After lagging semi-finished product on, then dry and sanding；7) again spray-applied primer in the outer surface of the lagging semi-finished product of step 6 gained
On, then dry and sanding；8) spray paint, then dries.
Preferably, in described step 1, the product of the white embryo semi-finished product standard scope beyond above-mentioned moisture content is carried out dehumidifier
Process so that the moisture content of white embryo semi-finished product is within 8%-12%.
Preferably, in described step 2, described glue employing urea formaldehyde glue: flour: firming agent: water is according to volume ratio 6:3:
2:2 allocates.
Preferably, in described step 4, cool time is 1-3 hour.
Preferably, in described step 6, priming paint uses the paint that penetration is strong, and drying temperature is 30 40 degree, drying time
It it is 68 hours.
Preferably, the drying temperature in described step 7 is 29 36 degree, and drying time is 9 18 hours.
Preferably, the drying temperature in described step 8 is 30 38 degree, and drying time is 6 12 hours.
A kind of grain of wood lagging mildew-resistant goods, it is characterised in that technique according to claim 1 prepares described wood
Texture lagging mildew-resistant goods.
Using technique scheme, solid wood veneer sheet texture thick china mildew-resistant technique of the present invention has the advantage that
The solid wood veneer sheet texture thick china mildew-resistant technique of the present invention, first passes through selection base material through being processed into white embryo
Semi-finished product, the moisture content of strict control of material during processing from base material to openpore, moisture control is within 8%-12%；
Prevent moisture content in white embryo semi-finished product too much, affect subsequent thermal and overlay skin.Secondly, by glue and according to mass ratio
1000:5 adds water mildow-proof auxiliary agent, and stirs；Brush the most again to white embryo semi-finished product, hot pressing lagging work routinely
Solid wood veneer sheet is attached to white embryo semi-finished product and prepares lagging semi-finished product by skill；Through necessary cooling, remove moisture removal and and glue
It is fully cured, in by priming paint, adds oiliness mildew-resistant auxiliary agent according to mass ratio 1000:5, and stir；And be sprayed at
As head layer priming paint on semi-finished product, through drying and sanding；In above-mentioned steps, priming paint must be the priming paint that penetration is good, paint
Just can penetrate into the effect strengthening mildew-resistant in sheet material.Finally, spray-applied primer and drying again, obtain the most beautiful lacquer painting, warp
Cross long-time grain of wood lagging of placing and also will not produce mildew.Therefore, the solid wood veneer sheet texture thick china using the present invention is prevented
Mould technique, can play and stop artificial board and produce mildew, and the most beautiful attractive in appearance, the color of the grain of wood is more lively, without flaw, carries
High produce sheet material quality and quality.
Using technique scheme, the present invention has a kind of grain of wood lagging mildew-resistant goods to have one solid wood veneer of the present invention
All excellent effect that sheet texture thick china mildew-resistant technique is brought.
Accompanying drawing explanation
Fig. 1 is the process flow diagram of the present invention.
Fig. 2 is embodiments of the invention one solid wood veneer sheet texture thick china mildrew resistant finish process flow diagrams.
Fig. 3 is embodiments of the invention two grain of wood lagging mildew-resistant goods FB(flow block)s.
Detailed description of the invention
The present invention is described further with specific embodiment below in conjunction with the accompanying drawings.
The products such as existing stick-skin furniture are typically with wood or/and sheet material base material as an alternative, will substitute base material
Determine step routinely, method makes semi-finished product through preliminary working.Stick natural veneer at the outer surface of semi-finished product, inner surface thus
Make lagging semi-finished product.Lagging semi-finished product successively through polish such as spray paint, cloth art, packagings thus make stick-skin furniture become
Product.Select the veneer of different materials, i.e. can be made into all kinds of lagging product.Such as: MDF, clamping plate etc..
Embodiment one
As illustrated in figs. 1 and 2, MDF, the clamping plate course of processing approximately as:
1, by selected solid wood raw material and sheet material raw material sawing sheet, it is processed into and is sized, the length and width that such as sets,
The multi-sheets of thickness, solid wood veneer sheet.
2, sheet material preliminary working
Panel preliminary working semi-finished product: a portion sheet material according to technique need successively through colding pressing, clear limit, wood edges,
Hot pressing, milling line, thus make panel preliminary working semi-finished product.Embryo semi-finished product i.e.: in vain.
3, moisture control:
The moisture content of strict control of material during processing from sheet material raw material to openpore, obtains required white embryo half and becomes
Product, and control its moisture content within 8%～12%.The moisture content of embryo semi-finished product white to part does beyond the product of critical field
Dehumidifier processes, and dehumidifier processes and includes baking the affected part after applying some drugs, air dry or air-cooled etc., it is ensured that the moisture content of product is within 8%～12%.
4, configuration glue
Employing urea formaldehyde glue: flour: firming agent: water carries out glue, wherein, firming agent according to the allotment of volume ratio 6:3:2:2
For modified firming agent, it is made up of formaldehyde catching agent+ammonium chloride.Mildew-resistant auxiliary agent uses water mildow-proof auxiliary agent, glue and water mildow-proof
Auxiliary agent configures with according to mass ratio 1000:5, then stirs.Wherein, also need configured glue is measured；
The viscosity of glue is 10 centipoises, or the 15 centipoises [viscosity unit of glue: 1 pool (P)=0.1 Pa Sec (Pa s), 1 centipoise
(CP.S)=0.001 Pa Sec (Pa.S)].Satisfactory glue is for the use of next process, to incongruent quality
Than the glue required, need to reconfigure.
5, lagging semi-finished product
Size according to white embryo semi-finished product cuts the solid wood veneer sheet with sheet material corresponding size, at white embryo semi-finished product
Brush equably on outer surface and carry out, according to mass ratio 1000:5, the glue that configures, then solid wood veneer sheet is attached to painting brushes glue
On the white embryo semi-finished product of water, then pass through hot-press equipment and the white embryo semi-finished product posting solid wood veneer sheet are carried out hot pressing, remove
Bubble so that lagging is more smooth, activates glue, promotes glue effective hyposmosis bonding, thus makes lagging semi-finished product.
6, glue curing is treated in cooling
After hot pressing, the cooling of lagging semi-finished product plate is placed about 2 hours, after glue is fully cured, through delivery platform,
Transferred on next process.Then the processed of subsequent processing is carried out.
7, configuration priming paint
Priming paint must be the priming paint that penetration is good, and paint just can penetrate into the effect strengthening mildew-resistant in sheet material.By base oil: oil
Oiliness mildew-resistant auxiliary agent is added in the priming paint intermixture mixed up by the ratio of property antifungus agent/1000:5.
8, lagging semi-finished product spray-applied primer and finish paint
The priming paint that will have prepared, according to a conventional method spray-applied primer on lagging semi-finished product, i.e. this layer priming paint is head
Degree priming paint, the viscosity of head degree priming paint is 8 seconds, or 7 seconds (viscosity unit of paint is the second, is expressed as S).Again through drying, sand
Light, wherein drying control temperature is in 30 40 degree, the 68 hours baking needed time so that the surface of head degree priming paint will not be produced
Angry bubble, discount degree priming paint is more transparent；To note here is that: before spray head degree priming paint, to first carry out dedusting and remove
Live together reason.In order to make lacquer painting more beautiful, conveniently the texture of solid wood veneer sheet is transmitted, mirror effect can be played, so
Spray-applied primer is in the lagging surface of semi-finished being jetted through one layer of priming paint again, is drying, and wherein dries temperature
Degree is 29 36 degree, and drying time is 9 18 hours.Carry out sanding, polishing the most again.
Finally, spray paint equably on the lagging semi-finished product sprayed twice priming paint, then carry out, into drying, drying
Dry temperature controls within 30 38, and required drying time is 6 12 hours.Thus obtain required MDF, clamping plate.
9, MDF, clamping plate finished product polish
MDF, clamping plate carry out cloth art, cut, assemble and packaging etc. thus make stick-skin furniture finished product, and put in storage.
Embodiment two
As described in Fig. 1 and Fig. 3, the grain of wood lagging mildew-resistant goods course of processing approximately as:
1, by selected solid wood raw material and sheet material raw material sawing sheet, wherein sheet material raw material is MDF or clamping plate.Add
Work becomes to be sized, the length and width such as set, thick multi-sheets, solid wood and solid wood veneer sheet.
2, sheet material preliminary working
Panel preliminary working semi-finished product: a portion sheet material according to technique need successively through colding pressing, clear limit, wood edges,
Hot pressing, milling line, thus make panel preliminary working semi-finished product.Embryo semi-finished product i.e.: in vain.
(1), moisture control:
The moisture content of strict control of material during processing from sheet material raw material to openpore, obtains required white embryo half and becomes
Product, and control its moisture content within 8%～12%.The moisture content of embryo semi-finished product white to part must beyond the product of critical field
Must do dehumidifier to take care of health process, the wet process that takes care of health includes baking the affected part after applying some drugs, air dry or air-cooled etc., it is ensured that the moisture content of product 8%～
Within 12%.
(2), configuration glue
Glue uses urea-formaldehyde glue, and mildew-resistant auxiliary agent uses water mildow-proof auxiliary agent, urea-formaldehyde glue and water mildow-proof auxiliary agent and according to matter
Amount configures than 1000:5, then stirs.Wherein, also need configured glue is measured；The viscosity of glue is
10 centipoises, or the 15 centipoises [viscosity unit of glue: 1 pool (P)=0.1 Pa Sec (Pa s), 1 centipoise (CP.S)=0.001
Pa Sec (Pa.S)].Satisfactory glue for the use of next process, the glue that incongruent mass ratio is required,
Needs reconfigure.
(3), lagging semi-finished product
Size according to white embryo semi-finished product cuts the solid wood veneer sheet with sheet material corresponding size, at white embryo semi-finished product
Brush equably on outer surface and carry out, according to mass ratio 1000:5, the glue that configures, then solid wood veneer sheet is attached to painting brushes glue
On the white embryo semi-finished product of water, then pass through hot-press equipment and the white embryo semi-finished product posting solid wood veneer sheet are carried out hot pressing, remove
Bubble so that lagging is more smooth, activates glue, promotes glue effective hyposmosis bonding, thus makes lagging semi-finished product.
(4), glue curing is treated in cooling
After hot pressing, the cooling of lagging semi-finished product plate is placed about 2 hours, after glue is fully cured, through delivery platform,
Transferred on next process.Then the processed of subsequent processing is carried out.
(5), configuration priming paint
Priming paint must be the priming paint that penetration is good, and paint just can penetrate into the effect strengthening mildew-resistant in sheet material.By base oil: oil
Oiliness mildew-resistant auxiliary agent is added in the priming paint intermixture mixed up by the ratio of property antifungus agent/1000:5.
(6), lagging semi-finished product spraying
The priming paint that will have prepared, according to a conventional method spray-applied primer on lagging semi-finished product, i.e. this layer priming paint is head
Degree priming paint, the viscosity of head degree priming paint is 8 seconds, or 7 seconds (viscosity unit of paint is the second, is expressed as S).Again through drying, sand
Light, wherein drying control temperature is in 30 40 degree, the 68 hours baking needed time so that the surface of head degree priming paint will not be produced
Angry bubble, discount degree priming paint is more transparent；To note here is that: before spray head degree priming paint, to first carry out dedusting and remove
Live together reason.In order to make lacquer painting more beautiful, conveniently the texture of solid wood veneer sheet is transmitted, mirror effect can be played, so
Spray-applied primer is in the lagging surface of semi-finished being jetted through one layer of priming paint again, is drying, and wherein dries temperature
Degree is 29 36 degree, and drying time is 9 18 hours.Carry out sanding, polishing the most again.
Finally, the lagging semi-finished product sprayed twice priming paint spray lacquer painting equably, then carry out, into drying, drying
Dry temperature controls within 30 38, and required drying time is 6 12 hours.Thus obtain required MDF, clamping plate.
3, solid wood preliminary working
Solid wood column and solid wood crosspiece preliminary working: first solid wood carries out fixed length, then according to technique needs, a portion
The solid wood of fixed length becomes solid wood column and solid wood crosspiece through sanding post processing, and waits the assembling walked.
Solid-wood panels, solid wood foot, solid wood door plate, the preliminary working of solid wood side plate: the solid wood of another part fixed length is according to technique
Need successively through milling line, repair abnormity, sanding, carve and grind flower be processed into solid-wood panels, solid wood foot, solid wood door plate and solid wood side
Plate, and wait the assembling walked.
4, assemble
By through the MDF made of preliminary working, clamping plate preliminary working semi-finished product, solid-wood panels, solid wood foot, solid wood door plate and
Solid wood side plate fits together according to the shape of finished product thus makes semi-finished product.
5, lagging semi-finished product polish
Lagging semi-finished product after spraying are carried out cloth art, packaging etc. thus makes stick-skin furniture finished product, and put in storage.
In the present invention, the transparent priming of head degree priming paint PU or PE.If selecting PU, also need to spray twice, if selected
PE also needs to spray once.The viscosity of head degree priming paint is 8 seconds, or 7 seconds (concentration unit of paint is the second).
Drying with barn, cross rifle sprays, and spraying second layer priming paint viscosity is 8 seconds 12 seconds, and coating thickness is 51 59
Micromillimetre.Drying temperature is 30 40 degree, or 28-38 degree, and drying time is 68 hours.After drying, with model be 320 or
The paper sand of 400 carries out light weight sand, and light weight sand rear surface is smooth, smooth.
In the present invention, need to further illustrate: one is to need spraying protective layer before spraying last finish paint.Spray
Stopping off: spraying protective layer, drying and light weight sand successively on the MDF of spray-applied primer again, the outer surface of clamping plate.Spraying
Protective layer is to protect color.The clear finish of spraying protective layer PU or PE.Coating thickness 6-8 micromillimetre.Dry with barn
Dry, dry, carry out light weight sand with the paper sand that model is 600.Two is spray paint after above-mentioned spraying protective layer: in spraying
Spray paint on the MDF of protective layer, clamping plate outer surface, then dries.Spray paint PU clear finish.Coating thickness is about
40 50 micromillimetres.Viscosity is the 7-8 second, and the brightness after spraying is with reference to colour table.Drying with barn, drying temperature is 29 36 degree,
Drying time is 9 18 hours.
Above in conjunction with accompanying drawing, the present invention is described in detail, but embodiments of the present invention are not limited in above-mentioned
Embodiment, the present invention can be made various deformation according to prior art, belong to the guarantor of the present invention by those skilled in the art
Protect scope.
Claims (8)
1. a solid wood veneer sheet texture thick china mildew-resistant technique, it is characterised in that pass sequentially through following steps and realize:
1) selecting base material through being processed into white embryo semi-finished product, the moisture content controlling described white embryo semi-finished product is 8%-12%；
2) configuration glue, adds water mildow-proof auxiliary agent in glue, and glue is carried out with water mildow-proof auxiliary agent 1000:5 in mass ratio
Configuration, and stir；
3) glue adding mildew-resistant auxiliary agent that the white embryo semi-finished product prepared in step 1 and step 2 prepare, routinely hot pressing patch are used
Skin technique brushing glue attach solid wood veneer sheet on white embryo semi-finished product, prepares lagging semi-finished product；
4) the lagging semi-finished product in step 3 are cooled down；
5) configuration priming paint, adds oiliness mildew-resistant auxiliary agent in primers, and priming paint and oiliness mildew-resistant auxiliary agent are according to mass ratio 1000:5
Configure, and stir；
6) priming paint prepared in step 5 is used, according to a conventional method by basecoat paint lagging semi-finished product after processing through step 4
On, then dry and sanding；
7) again spray-applied primer on the outer surface of the lagging semi-finished product of step 6 gained, then dry and sanding；
8) spray paint, then dries.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
In 1, the product of the white embryo semi-finished product standard scope beyond above-mentioned moisture content is carried out dehumidifier process so that containing of white embryo semi-finished product
Water rate is within 8%-12%.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
In 2, described glue employing urea formaldehyde glue: flour: firming agent: water is allocated according to volume ratio 6:3:2:2.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
In 4, cool time is 1-3 hour.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
In 6, priming paint uses the paint that penetration is strong, and drying temperature is 30 40 degree, and drying time is 68 hours.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
Drying temperature in 7 is 29 36 degree, and drying time is 9 18 hours.
A kind of solid wood veneer sheet texture thick china mildew-resistant technique the most according to claim 1, it is characterised in that: described step
Drying temperature in 8 is 30 38 degree, and drying time is 6 12 hours.
8. a grain of wood lagging mildew-resistant goods, it is characterised in that technique according to claim 1 prepares described wood grain
Reason lagging mildew-resistant goods.