CN103241987A - Floral white quartz stone slab and preparation method thereof - Google Patents
Floral white quartz stone slab and preparation method thereof Download PDFInfo
- Publication number
- CN103241987A CN103241987A CN 201310170125 CN201310170125A CN103241987A CN 103241987 A CN103241987 A CN 103241987A CN 201310170125 CN201310170125 CN 201310170125 CN 201310170125 A CN201310170125 A CN 201310170125A CN 103241987 A CN103241987 A CN 103241987A
- Authority
- CN
- China
- Prior art keywords
- minutes
- aggregate
- stirring
- auxiliary material
- order
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a floral white quartz stone slab and a preparation method thereof, relating to the technical field of quartz stone slabs. A finished product is prepared by mixing and stirring quartz sand, quartz powder, mirror glass, white glass, resin, titanium dioxide, a coupling agent, a curing agent and an accelerant and then carrying out sieving, distributing, vacuumizing, pressing, vibrating, paper removing, detecting, roasting and cooling processes. By adopting the natural quartz sand and quartz powder, the floral white quartz stone slab is non-toxic and nonradiative, is delicate in preparation process, is exquisite, has high hardness, good luminosity and good sunlight refracting power, is not easy to break, is cooler and has high comfort level.
Description
Technical field
The present invention relates to the technical field of quartzy slabstone, relate in particular to a kind of design of scattered small flowers and plants white quartz slabstone and preparation method thereof.
Background technology
Artificial quartz in lump has the lithotome incomparable advantage as novel artificial building materials: high strength, high rigidity, high temperature resistant, protection against corrosion, anti-aging, natural texture, easy to clean, anti-folding, wear-resisting, material is consummate, radiationless etc.As Nonrenewable resources exhausted today day by day, artificial quartz in lump is its best substitute at lithotome.These advantages allow artificial quartz in lump become the upstart of architectural decoration, are widely used ground, wall decoration and the home decoration industry of cabinet, bathroom, office and megastore.
Present synthetic quartz slabstone is of a great variety.But characteristics such as quartzy slabstone hardness of the prior art is low, anti-folding are poor, and color has and mixes.
Summary of the invention
Design of scattered small flowers and plants white quartz slabstone that technical problem to be solved by this invention provides a kind of exquisiteness, the high luminosity of hardness is good, the sunlight refracting power is good, relatively feel nice and cool and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of design of scattered small flowers and plants white quartz slabstone is characterized in that, comprises aggregate, auxiliary material, and described aggregate is quartz sand, silica powder, mirror glass and Bai Bo, and described auxiliary material comprises resin, titanium dioxide, coupling agent, solidifying agent, promotor,
Type and the weight proportion of described each aggregate are as follows:
Mirror glass: 8-16 order 2kg
16-30 order 3kg
White glass: 8-16 order 22kg
16-30 order 22kg
Quartz sand: 150 order 15kg
Silica powder: 200 order 14kg
325 order 25kg;
The weight proportion of described auxiliary material is as follows:
2, the method for the quartzy slabstone of a kind of Thassos of preparation, preparation process is as follows:
The weighing and mix of a, aggregate and auxiliary material
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing machine of silica powder mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body falls outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to cooling frame after check reaches requirement of strength, cooling frame is put in the cold water cooled off, and be 20 minutes cooling time;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
Beneficial effect of the present invention is: the present invention adopts natural quartz sand and silica powder, and nontoxic radiationless, manufacture craft is careful, the quartzy slabstone of the white shape of design of scattered small flowers and plants, and exquisiteness, the high luminosity of hardness is good, is not easy fracture, and the sunlight refracting power is good, and is more nice and cool, the comfort level height.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with the example of embodiment the present invention is described in further details.
The weighing and mix of a, aggregate and auxiliary material
Take by weighing quartz sand, silica powder, mirror glass and Bai Bo, the weight of each type is:
Mirror glass: 8-16 order 2kg, 16-30 order 3kg, white glass: 8-16 order 22kg, 16-30 order 22kg, quartz sand: 150 order 15kg, silica powder: 200 order 114kg, 325 order 24kg take by weighing each auxiliary material by weight ratio, resin 10.8kg, titanium dioxide 800g, coupling agent 150g, solidifying agent 150g, promotor 30g.
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing machine of silica powder mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body falls outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to cooling frame after check reaches requirement of strength, cooling frame is put in the cold water cooled off, and be 20 minutes cooling time;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
The quartzy slabstone of the Thassos that makes draws by extruding and irradiating and detecting that design of scattered small flowers and plants bittersweet slabstone color and luster of the present invention is single, very fine and smooth, the high luminosity of hardness is good, the sunlight refracting power is good, more nice and cool, real utility value height.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (2)
1. a design of scattered small flowers and plants white quartz slabstone is characterized in that, comprises aggregate, auxiliary material, and described aggregate is quartz sand, silica powder, mirror glass and Bai Bo, and described auxiliary material comprises resin, titanium dioxide, coupling agent, solidifying agent, promotor,
Type and the weight proportion of described each aggregate are as follows:
Mirror glass: 8-16 order 2kg
16-30 order 3kg
White glass: 8-16 order 22kg
16-30 order 22kg
Quartz sand: 150 order 15kg
Silica powder: 200 order 14kg
325 order 25kg;
The weight proportion of described auxiliary material is as follows:
2. prepare the method for the quartzy slabstone of a kind of Thassos as claimed in claim 1, it is characterized in that preparation process is as follows:
The weighing and mix of a, aggregate and auxiliary material
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing machine of silica powder mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body falls outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to cooling frame after check reaches requirement of strength, cooling frame is put in the cold water cooled off, and be 20 minutes cooling time;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.