CN103232184A - Quartz stone slab and preparation method thereof - Google Patents
Quartz stone slab and preparation method thereof Download PDFInfo
- Publication number
- CN103232184A CN103232184A CN 201310164645 CN201310164645A CN103232184A CN 103232184 A CN103232184 A CN 103232184A CN 201310164645 CN201310164645 CN 201310164645 CN 201310164645 A CN201310164645 A CN 201310164645A CN 103232184 A CN103232184 A CN 103232184A
- Authority
- CN
- China
- Prior art keywords
- stirring
- minutes
- auxiliary material
- aggregate
- weighing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a quartz stone slab and a preparation method thereof, relating to the technical field of quartz stone slabs. The preparation method comprises the following steps of: mixing and stirring quartz sand, quartz powder, resin, titanium dioxide, a coupling agent, a curing agent and an accelerant, then, screening, distributing, vacuumizing, pressing, vibrating, removing paper, checking, baking and cooling to obtain a finished product. The quartz stone slab is made of natural quartz sand and quartz powder, is nontoxic and nonradiative, and can not become old, combust or be scratched or polluted; and the finished product is large in density, strong in impermeability, easy to wash and long in service life.
Description
Technical field
The present invention relates to the technical field of quartzy slabstone, relate in particular to a kind of quartzy slabstone and preparation method thereof.
Background technology
Artificial quartz in lump has the lithotome incomparable advantage as novel artificial building materials: high strength, high rigidity, high temperature resistant, protection against corrosion, anti-aging, natural texture, easy to clean, anti-folding, wear-resisting, material is consummate, radiationless etc.As Nonrenewable resources exhausted today day by day, artificial quartz in lump is its best substitute at lithotome.These advantages allow artificial quartz in lump become the upstart of architectural decoration, are widely used ground, wall decoration and the home decoration industry of cabinet, bathroom, office and megastore.But now the quartzy slabstone that uses on the market is done the kitchen range table top, if water stain oil stain is arranged on the quartzite table top, is easy to penetrate in the quartzite table top, and very difficult clean is fallen.Thereby cause quartzite table top treatment of dirt not fall, the clean and tidy and health of influence, duration of service is short, and for some time will be changed.
Summary of the invention
Technical problem to be solved by this invention provides a kind of easy to clean, quartzy slabstone that impermeable ability is strong and preparation method thereof.
Technical problem to be solved by this invention realizes by the following technical solutions:
A kind of quartzy slabstone is characterized in that, comprises aggregate and auxiliary material, and described aggregate is quartz sand and silica powder, and described auxiliary material comprises resin, titanium dioxide, coupling agent, solidifying agent, promotor, and type and the weight proportion of described quartz sand and silica powder are as follows:
The weight proportion of described auxiliary material is as follows:
A kind of preparation method's step of quartzy slabstone is as follows:
The weighing and mix of a, aggregate and auxiliary material
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing machine of quartz sand mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished and put into little agitation vat and solidifying agent and promotor are added to agitation vat again and continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body falls outer cover, open vacuum pump after falling pressure head, it is vacuumized,, after vacuumizing, open vibration motor and shake, shake and stop after 3.30 minutes, make the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
Beneficial effect of the present invention is: the present invention adopts natural quartz sand and silica powder, nontoxic radiationless, with not old, combustion not, does not scrape and spends, dirt is not dyed, and the density of finished product is big, and material is evenly distributed, and impermeable ability is strong, clean easily, duration of service is of a specified duration, is not easy fracture.
Embodiment
For technique means, creation characteristic that the present invention is realized, reach purpose and effect is easy to understand, below in conjunction with the example of embodiment the present invention is described in further details.
A kind of quartzy slabstone comprises aggregate and auxiliary material, and aggregate is quartz sand and silica powder, and auxiliary material comprises resin, titanium dioxide, coupling agent, solidifying agent, promotor, and type and the weight proportion of quartz sand and silica powder are as follows:
The weight proportion of auxiliary material is as follows:
A kind of preparation method's step of quartzy slabstone is as follows:
The weighing and mix of a, aggregate and auxiliary material
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing of quartz sand mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished and put into little agitation vat and solidifying agent and promotor are added to agitation vat again and continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body puts down outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
Embodiment one
The weighing and mix of a, aggregate and auxiliary material
Take by weighing quartz sand and silica powder, the weight of each type is:
Quartz sand: 6-8 order 10kg, 8-16 order 5kg, 40-70 order 15kg, 70-100 order 10kg, silica powder: 200 order 10kg, 325 order 20kg, take by weighing each auxiliary material by weight ratio, resin 8kg, titanium dioxide 430g, coupling agent 100g, solidifying agent 80g, promotor 20g.
With all claim quartz sand and disposable the putting in the mixing machine of quartz sand mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side.Resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, stop after stirring stirring, churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes.
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes.
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented.
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine.
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body puts down outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 1 hour;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
Embodiment two
The weighing and mix of a, aggregate and auxiliary material
Take by weighing quartz sand and silica powder, the weight of each type is:
Quartz sand: 6-8 order 12kg, 8-16 order 6kg, 40-70 order 16kg, 70-100 order 12kg, silica powder: 200 order 12kg, 325 order 25kg, take by weighing each auxiliary material by weight ratio, resin 10kg, titanium dioxide 510g, coupling agent 120g, solidifying agent 110g, promotor 23g.
With all claim quartz sand and disposable the putting in the mixing machine of quartz sand mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side.Resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, stop after stirring stirring, churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes.
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes.
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented.
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine.
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body puts down outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
Embodiment three
The weighing and mix of a, aggregate and auxiliary material
Take by weighing quartz sand and silica powder, the weight of each type is:
Quartz sand: 6-8 order 15kg, 8-16 order 8kg, 40-70 order 20kg, 70-100 order 15kg, silica powder: 200 order 15kg, 325 order 30kg, take by weighing each auxiliary material by weight ratio, resin 11.7kg, titanium dioxide 573g, coupling agent 200g, solidifying agent 150g, promotor 30g.
With all claim quartz sand and disposable the putting in the mixing machine of quartz sand mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side.Resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, stop after stirring stirring, churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes.
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes.
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented.
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine.
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body puts down outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.3 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.
The quartzy slabstone that above-mentioned three embodiment are made respectively cuts next piece size and detects and test for long 5cm, wide 5cm, high 1.5cm.With identical oil stain and water stain dropping in respectively on three quartzite plates.Detected result is as follows:
In sum, the time of the water stain oil stain infiltration in the present invention is longer, more is fit to be used in our life utility value height.
More than show and described ultimate principle of the present invention and principal character and advantage of the present invention.The technician of the industry should understand; the present invention is not restricted to the described embodiments; that describes in above-described embodiment and the specification sheets just illustrates principle of the present invention; without departing from the spirit and scope of the present invention; the present invention also has various changes and modifications, and these changes and improvements all fall in the claimed scope of the invention.The claimed scope of the present invention is defined by appending claims and equivalent thereof.
Claims (2)
1. a quartzy slabstone is characterized in that, comprises aggregate and auxiliary material, and described aggregate is quartz sand and silica powder, and described auxiliary material comprises resin, titanium dioxide, coupling agent, solidifying agent, promotor, and type and the weight proportion of described quartz sand and silica powder are as follows:
The weight proportion of described auxiliary material is as follows:
2. prepare the method for a kind of quartzy slabstone as claimed in claim 1, it is characterized in that, preparation process is as follows:
The weighing and mix of a, aggregate and auxiliary material
Proportion takes by weighing all types of quartz sand and silica powder by weight, with all claim quartz sand and disposable the putting in the mixing machine of silica powder mix, stop after mixing, the time of mixing is 20 minutes, and mixed aggregate taken out takes by weighing the spiral-plate aequum and be deposited in stirrer on one side;
Proportion takes by weighing auxiliary material by weight, and resin, titanium dioxide, coupling agent are put in the agitation vat and stirred, and stops after stirring stirring, and churning time is at least 30 minutes; Take by weighing the spiral-plate aequum after stirring is finished again and put into little agitation vat and solidifying agent and promotor are added to agitation vat continue to stir, the time of stirring is at least 2 minutes;
The aggregate that mixes and the auxiliary material that mixes put in the same stirrer stir, stirs after 2 minutes and shut down stirring once, stir the mixing stirring of finishing aggregate and auxiliary material after 3 minutes;
B, screen cloth are divided equally
The material that stirs is dropped into trommel screen through chute to be segmented;
C, material distributing machine
With the Sheet Steel Form of 3200*900 move to can the material distributing machine of forward and reverse motion on, will throw in to Sheet Steel Form through the material after the trommel screen segmentation, through manually evenly distributing after, cover paper again and treat the entrance pressure machine;
D, vacuumize, shake, suppress
The Sheet Steel Form of the good material of cloth moved in the press body falls outer cover, open vacuum pump after falling pressure head, it is vacuumized, until vacuum tightness reach-opening vibration motor behind the 0.01MPa shakes, and shakes to stop after 3.30 minutes, makes the blank version;
E, remove paper, check, advance baking oven
The blank flat that suppresses is shifted out press to sliding support, throw off the paper of covering and test, move to baking oven after reaching qualified requirement, through 110 ℃ of high bakes at least 2 hours;
F, go out baking oven and advance cooling frame
Blank flat after the baking moves to the cooling frame cooling after check reaches requirement of strength;
G, post-processed
, sanding and polishing thick with cutting edge on request after the cooled blank flat demoulding, deciding made finished product.