CN103232770B - 汽车广告液体隔离膜 - Google Patents

汽车广告液体隔离膜 Download PDF

Info

Publication number
CN103232770B
CN103232770B CN201310121282.6A CN201310121282A CN103232770B CN 103232770 B CN103232770 B CN 103232770B CN 201310121282 A CN201310121282 A CN 201310121282A CN 103232770 B CN103232770 B CN 103232770B
Authority
CN
China
Prior art keywords
isolation film
automobile
liquid isolation
advertisement
film
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310121282.6A
Other languages
English (en)
Other versions
CN103232770A (zh
Inventor
罗守金
罗飞
罗丽娟
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Individual
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310121282.6A priority Critical patent/CN103232770B/zh
Publication of CN103232770A publication Critical patent/CN103232770A/zh
Application granted granted Critical
Publication of CN103232770B publication Critical patent/CN103232770B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种汽车广告液体隔离膜,它是由聚苯乙烯5~20%、C9石油树脂2~8%、环氧树脂0.8~4%、快干醇酸树脂0.5~5%、乙基纤维素2~10%、线型热塑丁苯橡胶2~10%、尼龙酸甲酯5~20%、混合苯50~70%组成的。本发明还公开了所述汽车广告液体隔离膜的制备方法。将本发明涂在车身上以后,可以在车身油漆和广告膜之间形成一层隔膜,从而保护了车身油漆,同时使广告膜能很容易地从车身上取下,缩短了广告膜更换的时间,提高了工作效率。

Description

汽车广告液体隔离膜
技术领域
本发明属于油漆化工领域,具体涉及一种汽车广告液体隔离膜及其制备方法。
背景技术
贴在汽车特别是公交车身上的广告膜由于日晒雨淋,广告膜及其反面的粘胶很容易与车身上的油漆溶为一体,这样一来,在取下或者更换广告膜时,广告膜或者粘胶就会不容易从车身上除掉,要么将车身上的油漆一起拉掉,要么部分广告膜或者粘胶滞留在车身上,影响车身的美观。
目前还没有很好的办法解决以上问题,通常的做法是在取下广告膜后给车身重新刷一遍油漆。这样一来不仅造成了资源浪费,而且工时较长,很容易耽误发车时间。
发明内容
本发明的目的就是针对上述缺陷,提供一种汽车广告液体隔离膜,将该液体隔离膜涂在车身上以后,可以在车身油漆和广告膜之间形成一层隔膜,从而保护车身油漆,使广告膜能很容易地从车身上取下。
上述目的是通过采用以下技术方案实现的:
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
优选地,所述的汽车广告液体隔离膜由下述重量百分比的成分组成:
最佳地,所述的汽车广告液体隔离膜由下述重量百分比的成分组成:
其中:所述环氧树脂的平均环氧值为0.44。
本发明进一步提供所述汽车广告液体隔离膜的制备方法,该方法是:
首先将混合苯和尼龙酸甲酯,聚苯乙烯,乙基纤维素按比例投进反应釜,开启搅拌,在120℃条件下反应2h,再加入线型热塑丁苯橡胶,在100℃条件下反应2h,然后降温至40℃以下放料,在室温条件下加入环氧树脂、快干醇酸树脂、C9石油树脂,混合均匀,即得。
本发明的有益效果是:
1)本发明与车身油漆不互相溶,稳定性好,本发明涂在车身以后,会在车身油漆外形成一层薄膜,该薄膜的附着力适中,它小于车身油漆的附着力,但又不是太小,这样就不仅使广告膜能很容易地随隔离膜一起除掉,又能保证广告膜不会从车身上脱落。
2)本发明的液体隔离膜溶剂挥发速度快,膜干得快,因此不损坏车身油漆的光泽度,同时还可缩短广告膜更换的时间。
3)本发明所采用的材料均不溶于水,因此即使车身经常被雨淋或清洗,也能保持清洁和鲜亮。
4)采用本发明很好地解决了汽车更换广告膜时对车身油漆损坏的难题,缩短了广告膜更换的时间,提高了工作效率,减少了对环境的白色污染,具有较大的经济和社会效益。
具体实施方式
下面结合实施例对本发明进行详细说明。
实施例1
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
所述环氧树脂的平均环氧值为0.44。
所述混合苯为甲苯、对二甲苯、苯酚、氯苯的混合物,它们的重量比为任意比,本实施例中它们的重量比依次为5:1:1:1。
所述尼龙酸甲酯是一种高沸点环保溶剂,商品名为MDBE,它是由三种二价酸酯组成的混合物,即琥珀酸(丁二酸)二甲酯CH3OOC(CH22COOCH3,戊二酸二甲酯CH3OOC(CH23COOCH3和已二酸二甲酯CH3OOC(CH24COOCH三种溶剂的组合。
所述汽车广告液体隔离膜的制备方法是:首先将混合苯和尼龙酸甲酯,聚苯乙烯,乙基纤维素按比例投进反应釜,开启搅拌,在120℃条件下反应2h,再加入线型热塑丁苯橡胶,在100℃条件下反应2h,然后降温至40℃以下放料,在室温条件下加入环氧树脂、快干醇酸树脂、C9石油树脂,混合均匀,即得。
使用时,先将本发明刷涂在车身油漆上,15分钟后再将广告膜粘在隔离膜上,本发明外观为桔色,涂在车身上像清漆一样,可增加车身的光亮,本发明的固含量达30%以上。
实施例2
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
所述混合苯为:间二甲苯、苯甲酸,它们的重量比为任意比,本实施例中它们的重量比为10:1。
所述汽车广告液体隔离膜的制备方法与实施例1相同。
实施例3
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
所述混合苯为:二甲苯、苯乙酮、溴苯。
所述汽车广告液体隔离膜的制备方法与实施例1相同。
实施例4
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
所述混合苯为:甲苯、氯苯。
所述汽车广告液体隔离膜的制备方法与实施例1相同。
实施例5
一种汽车广告液体隔离膜,它是由下述重量百分比的成分组成的:
所述混合苯为:甲苯、邻二甲苯、苯乙酮。
所述汽车广告液体隔离膜的制备方法与实施例1相同。
实施例1~5的检测结果见表1。
表1汽车广告液体隔离膜的质量检测结果

Claims (4)

1.一种汽车广告液体隔离膜,其特征在于它是由下述重量百分比的成分组成的:
所述环氧树脂的平均环氧值为0.44。
2.根据权利要求1所述的汽车广告液体隔离膜,其特征在于它是由下述重量百分比的成分组成的:
3.根据权利要求1所述的汽车广告液体隔离膜,其特征在于它是由下述重量百分比的成分组成的:
4.根据权利要求1~3任何一项所述的汽车广告液体隔离膜的制备方法,其特征在于:首先将混合苯和尼龙酸甲酯,聚苯乙烯,乙基纤维素按比例投进反应釜,开启搅拌,在120℃条件下反应2h,再加入线型热塑丁苯橡胶,在100℃条件下反应2h,然后降温至40℃以下放料,在室温条件下加入环氧树脂、快干醇酸树脂、C9石油树脂,混合均匀。
CN201310121282.6A 2013-04-09 2013-04-09 汽车广告液体隔离膜 Expired - Fee Related CN103232770B (zh)