CN103231425B - A kind of Large-specification recombination composite structural wood and manufacture method thereof - Google Patents
A kind of Large-specification recombination composite structural wood and manufacture method thereof Download PDFInfo
- Publication number
- CN103231425B CN103231425B CN201310146028.1A CN201310146028A CN103231425B CN 103231425 B CN103231425 B CN 103231425B CN 201310146028 A CN201310146028 A CN 201310146028A CN 103231425 B CN103231425 B CN 103231425B
- Authority
- CN
- China
- Prior art keywords
- recombinant material
- veneer
- adhesive
- layer
- composite structural
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention relates to a kind of Large-specification recombination composite structural wood, and provide manufacture method, with recombinant material, adhesive, veneer and cardboard are raw material, use Lengthwise joint, MULTILAYER COMPOSITE, optimize the methods such as glue interface structure, manufacture Large-specification recombination composite structural wood, the present invention solves recombinant material secondary gluing process and causes cracking because gluing is bad, come unglued, bonding strength is low, the physical mechanics property loss of energy is big waits the technical bottleneck hindering recombinant material for Large-specification recombination composite structural wood, Large-specification recombination composite structural wood may be used for being manufactured into beam, post, furniture and floor.
Description
Technical field
The invention belongs to the wood-based plate in industry of artificial boards and manufacturing technology field thereof, be particularly suited for mechanics
Performance requirement is high, building and the Engineered Wood Products such as beam, post, furniture and floor that specification is big.
Background technology
Recombinant material is a kind of novel building and Engineered Wood Products, including Recombined bamboo and Scrimber, is by bamboo
Bundle and wood bundle are fabricated by through operations such as impregnation, dry, assembly and gluings.At present, recombinant material
Production technology is broadly divided into two big classes: a class is cold forming, heat curing process, is called for short cold-press process;
Two is to use for reference wood-based plate conventional thermocompression technique, the recombinant material heat pressing process of formation.Due to by cold press and
The restriction of the specification of hot press device, at present, the specification of recombinant material is the least, as colded pressing
The specification (length × width x thickness) that the recombinant material square stock that method produces is conventional is: 193cm × 10.5cm
× 15.0cm and 200cm × 14.5cm × 15.0cm;The recombinant material stock size that heat pressing process produces is (long
× width x thickness) be: 244cm × 122cm × (1.5-4) cm, maximum breadth also can only achieve 500cm
× 120cm × 5cm (Yu Wenji, China's Recombined bamboo industry development present situation and trend analysis, timber industry,
2012,26 (1): 11-14).Such specification is difficult to meet structural wood such as beam, post, big
Type furniture and the specification requirement on big specification floor.
At present, the structural wood of big specification is generally used Lengthwise joint by the material of small dimension, laterally spells width,
Glued joint with MULTILAYER COMPOSITE and form.Glued joint bad meeting and cause the decline of plate property, glued joint common defect
Type includes: degumming, crack, space, bondline thickness variation, solidification not exclusively lack with surface preparation
Falling into, wherein, it is main that defect is prepared on degumming, crack and surface.Affect adhesive bonding of composites strong
The principal element of degree has: the material category of connected piece, the ratio of rigidity of connected piece and thermal coefficient of expansion
Etc. the impact of factor, make by the rigidity approximately equal of bonded part, thermal expansion and suction the most as far as possible
Hygral expansion close (benefit little Su, composite handbook, Chemical Industry Press, 2009).
Chinese patent 201010243351.7,201020279829.7,201020279815.5 provide
A kind of employing undersized log manufactures undersized log recombination structure material and manufacture method thereof by finger or mitered,
Adopt the recombination structure material that undersized log can be processed into big specification in this way.But this technique is two
The glue-line glue performance formed during secondary gluing is unstable, has certain variability, some sheet material glue-lines
It is likely to occur cracking, the phenomenon such as come unglued;Other sheet materials are deposited, and are likely to occur bonding strength low, physics
The problems such as mechanical property loss is big.By analyzing, the main cause causing above-mentioned phenomenon and problem is office
Portion's gluing is bad.
According to previously research: form good splicing prerequisite and be adhesive molecule and gluedd joint material
(timber) can be fully contacted and effective wetting (Gu Jiyou, adhesive and coating, China Forest publication
Society, 1999).Recombinant material is a kind of porous natural material timber or bamboo wood (is colded pressing at bigger pressure
Method briquetting pressure about 60MPa, pressure sintering briquetting pressure 4~6MPa) effect compacted under, recombinant material
Density be generally higher than 1.0g/cm3, when environment temperature and humidity change, it may occur that easement, crosswise concaving,
Warpages etc. deform, and can produce the jumping phenomenon such as silk and cracking (Yu Wenji, China's Recombined bamboo industry time serious
Development status and trend is analyzed, timber industry, and 2012,26 (1): 11-14), even if in processing
Process uses sanding, it is also difficult to obtain smooth cemented surface;Secondly, in the manufacture process of recombinant material,
In order to make adhesive distribution more uniform, after generally using dipping method, bamboo bundle and wood bundle by impregnation,
One layer of adhesive has all been wrapped up on surface, after solidification, defines the glue-line of one layer of insoluble insoluble densification, table
Face wetability declines;Furthermore, recombinant material intensity is high, and hardness is big, it is difficult to compressed, but by tradition
Thinking affects, and when selecting bonded part, selects rigidity approximately equal, thermal expansion and moisture expantion phase as far as possible
Near material, does not generally take into account that the third material introduced in addition to adhesive, therefore, coarse table
Face, it is difficult to the splicing face compressed and bad wetability easily produces degumming in post forming process, splits
The recombinant material spot gluing of the adhesive defects, particularly high rigidity such as seam, space, bondline thickness variation is not
Good problem fails effectively to be solved all the time.
Summary of the invention
It is an object of the invention to improve the deficiency in existing technology, it is provided that big specification restructuring is compound
Structural wood so that it is physical and mechanical property meets the requirement of structural wood performance.
For achieving the above object, the present invention takes techniques below scheme:
The present invention provides Large-specification recombination composite structural wood to include recombinant material, veneer and adhesive, by
The recombinant material stacking of multilayer Lengthwise joint forms, and arranges one layer of veneer between every layer of recombinant material, described
The thickness of veneer is 0.1-1.5mm;Adhesive layer it is provided with between recombinant material and veneer, used
Adhesive is resorcinol gluing agent or aqueous solution acrylate resin;Described recombinant material is longitudinally
The composition surface of spreading is provided with adhesive layer, and adhesive used is resorcinol gluing agent or aqueous high score
Sub-isocyanates gluing agent;When described recombinant material manufactures adhesive used be impregnating phenolic resin or
Dipping Lauxite.
The recombinant material of described Lengthwise joint is provided with a layer paperboard between the composition surface of Lengthwise joint, restructuring
Being provided with adhesive layer between material and cardboard, adhesive used is resorcinol gluing agent or aqueous high score
Sub-isocyanates gluing agent.
Described recombinant material is Recombined bamboo or Scrimber.
Described spreading is finger spreading or mitered spreading.
Further object is that the manufacturer that described Large-specification recombination composite structural wood is provided
Method.
For achieving the above object, the present invention takes following process technology scheme:
The present invention provides Large-specification recombination composite structural wood manufacture method, including following workshop section: (one)
Raw material preparation, (two) Lengthwise joint, (three) MULTILAYER COMPOSITE, (four) later stage process,
(1) raw material prepares, and prepares and adhesive allotment including recombinant material preparation, veneer:
(1) recombinant material prepares, by discongesting, being dried, impregnation, dry, gluing, maintenance, sanction
Limit, saw cut and sanding workshop section, and bamboo wood or timber are processed into specification recombinant material;Used by impregnation operation
Adhesive be impregnating phenolic resin or dipping Lauxite;
(2) veneer prepares, and by rotary-cut, dry, cutting edge workshop section, timber is processed into thickness
Specification veneer for 0.1-1.5mm;
(3) adhesive allotment, by resorcinol gluing agent or aqueous solution acrylate resin
Host and curing agent according to 100: (10-20) ratio uniform mix;
(2) Lengthwise joint
Described specification recombinant material two ends are used and is machined into finger face or miter, then in finger face
Or miter coats the resorcinol gluing agent after allotment or aqueous solution acrylate resin, warp
Cross longitudinal finger or mitered and make the recombinant material of Lengthwise joint;
(3) MULTILAYER COMPOSITE
The recombinant material of described Lengthwise joint and/or the upper and lower surface of veneer are coated resorcinol gluing
Agent or aqueous solution acrylate resin, if pressing one by the recombinant material after dried layer gluing and veneer
Layer one layer of veneer through-thickness of recombinant material, by stacking gradually, makes to be provided with between every layer of recombinant material one layer
Veneer, then through Cold-press adhesion, form Large-specification recombination composite structural wood slab;
(4) later stage processes
By described Large-specification recombination composite structural wood slab, through workshop sections such as cutting edge, saw section, sandings,
It is processed into Large-specification recombination composite structural wood.
In described Lengthwise joint workshop section, the recombinant material of described Lengthwise joint is on the composition surface of Lengthwise joint
Between be provided with a layer paperboard, be provided with adhesive layer between recombinant material and cardboard, between adhesive used is
Benzenediol adhesive or aqueous solution acrylate resin.
In mitered operation, the thickness at mitered position and inclined-plane ratio are 1: 10-1: 20.
In finger operation, box pin joint parameter: the long 8mm-45mm of tooth, tooth top width 0.5mm-20mm, tooth
Away from 3mm-20mm, tooth refers to gradient 1/6-1/9.
The Large-specification recombination composite structural wood that the present invention provides is when MULTILAYER COMPOSITE, in hardness height, intensity
And arrange between the big recombinant material of rigidity one layer compressible, can deformation, thickness 0.1-1.5mm veneer
Veneer, this glue contact structure design, take full advantage of the good wetability of veneer, permeability,
Gluing and compressible and can the characteristic such as deformation, utilize thin wood veneer deformation behavior, can effectively fill out
Mend the gap formed between the recombinant material that hardness is high, strength and stiffness are big due to cemented surface injustice, from
And add effective cemented surface;Utilize wetability and gluing that thin wood veneer is good, can be with restructuring
Material forms good cemented surface, improves glue performance;When secondary gluing, utilize the infiltration of veneer
Property and compression performance, under the effect of applied pressure, make thin wood veneer compression compact, make meanwhile
Resorcinol gluing agent or aquosity polymer isocyanic ester gluing can penetrate into thin wood veneer fully
In, there is gluing reaction with thin wood veneer, thus form the compressed wood with recombinant material similar nature.This
Plant the design of glue contact structure, make use of the characteristic of recombinant material and thin wood veneer dexterously, after making gluing
Big specification recombinant material bonding layer meets the rigidity approximately equal of bonded part, and thermal expansion and moisture expantion are close
Traditional classical to glued joint face gluing theoretical, solve again recombinant material degumming, crack, space, glue-line thick
The adhesive defects such as degree variation.
The present invention provide Large-specification recombination composite structural wood when Lengthwise joint, connecing at Lengthwise joint
A layer paperboard it is provided with, cardboard acting on and the above-mentioned basic phase of thin wood veneer at weld between conjunction face
With, repeat no more here.Why when Lengthwise joint, selecting cardboard, reason is as follows: with veneer
Veneer is compared, except good wetability, permeability, gluing and compressible and can the spy such as deformation
Outside property, flexibility and the plasticity of cardboard are more preferable.It is often referred to junction and miter is special-shaped curved, cardboard
Can be designed according to the shape in finger face and miter, so that splicing face is more identical, can be maximum
Limit adhesive defects such as reducing degumming, crack, space, bondline thickness variation.
The Large-specification recombination composite structural wood that the present invention provides is in Lengthwise joint and MULTILAYER COMPOSITE process
In, use Cold-setting adhesives i.e. double-component isocyanate adhesive or resorcinol adhesive, permissible
Needs according to target product are recombinated compound in length and thickness direction, meet the large-sized rule of structural wood
Lattice requirement.
The Large-specification recombination composite structural wood that the present invention provides, in recombinant material manufacture process, selects leaching
Stain phenolic resin or dipping Lauxite, make bamboo bundle or wood bundle reach uniform impregnation, thus obtain
The recombinant material of stable performance.
The invention will be further described with specific embodiment below in conjunction with the accompanying drawings, not to the present invention's
Limit, the equivalent of every any this area carried out according to the disclosure of invention, belong to
Protection scope of the present invention.
Accompanying drawing explanation
Fig. 1 recombinant material finger face
Fig. 2 cardboard finger face
Fig. 3 recombinant material finger spreading
Recombinant material after Fig. 4 finger spreading
Fig. 5 veneer
Fig. 6 big specification finger restructuring composite construction material
Fig. 7 recombinant material oblique section
Fig. 8 cardboard oblique section
Fig. 9 recombinant material mitered spreading
Recombinant material after Figure 10 mitered spreading
Figure 11 big specification mitered restructuring composite construction material
Detailed description of the invention
Embodiment 1: big specification finger restructuring composite construction material
The Large-specification recombination composite structural wood of exemplary embodiments of the present invention, it include Recombined bamboo (1),
Veneer (2), cardboard (3) and adhesive (not marking in figure), as shown in Figure 6, by multilayer
Recombined bamboo (1) stacking of longitudinal finger spreading forms, and arranges one layer of wood between every layer of Recombined bamboo (1)
Veneer (2), the thickness of veneer is 1.2mm;Adhesive layer it is provided with between Recombined bamboo and veneer
(not marking in figure), adhesive used is resorcinol gluing agent;The Recombined bamboo of Lengthwise joint exists
Be provided with between the composition surface of longitudinal finger a layer paperboard (3), Recombined bamboo (1) and cardboard (3) it
Between be provided with adhesive layer (not marking in figure), adhesive used is resorcinol gluing agent;Restructuring
Adhesive used during bamboo (1) manufacture is impregnating phenolic resin (not marking in figure).
It is as follows that Large-specification recombination composite structural wood manufacture method typical case of the present invention implements step:
1, by discongesting, being dried, impregnation, be dried, gluing, maintenance, cutting edge, saw cut and sanding
Workshop section, by bamboo processing one-tenth (length × width x thickness) be: the Recombined bamboo of 220cm × 30cm × 3.0cm;
It is impregnating phenolic resin at the adhesive used by impregnation operation, in hot pressing process, uses pressure sintering raw
Produce Recombined bamboo, belong to prior art;
2, above-mentioned Recombined bamboo is become finger joint teeth as shown in Figure 1 by tooth milling machine milling, the long 25mm of tooth,
Tooth top width 10mm, tooth pitch 20mm, tooth refers to gradient 1/8.
3, weigh resorcinol gluing agent host and curing agent according to 100: 15 ratios, mixing, through stirring
After mixing, form uniform host and curing agent uniform resorcinol gluing agent;
4, cardboard is processed into dentalation as shown in Figure 2, the long 25mm of tooth, tooth top width 10mm,
Tooth pitch 20mm, tooth refers to gradient 1/8.
5, resorcinol gluing agent after described allotment in finger topcoating, glue-spread is 300g/m2,
Or the area a m before processing according to cardboard2, use impregnation mode, cardboard finger entered in adhesive,
Impregnation resin content is (300 × a) g;By the Recombined bamboo finger-jointed plate after gluing according to assembly shown in Fig. 3, will
Sheet material after assembly uses two ends to overstock to centre, makes to combine closely at finger, the plate after finger spreading
Material is as shown in Figure 4.
6, by rotary-cut, dry, cutting edge workshop section, it is 30cm that timber is processed into width, and thickness is
The veneer bar of 1.0mm, as shown in Figure 5;
7, Recombined bamboo surface after longitudinal finger spreading or veneer coat allotment after resorcinol
Adhesive, glue-spread is 300g/m2;
8, if by thick by one layer of veneer edge of one layer of Recombined bamboo to the Recombined bamboo after dried layer gluing and veneer
Degree direction, by stacking gradually, makes to be provided with one layer of veneer between every layer of Recombined bamboo, then through Cold-press adhesion,
Form Large-specification recombination composite structural wood slab;
9, by described Large-specification recombination composite structural wood slab, through works such as cutting edge, saw section, sandings
Section, is processed into Large-specification recombination composite structural wood as shown in Figure 6.
The beam of exemplary embodiments of the present invention, post, furniture or floor, be by above-mentioned restructuring composite construction
Material is fabricated by.
Reference examples 1
Comparison exemplary embodiments does not use the Large-specification recombination composite structural wood of veneer and cardboard, and it includes
Recombined bamboo and adhesive, Large-specification recombination composite structural wood is by the Recombined bamboo heap of multilayer longitudinal direction finger spreading
Folding and form, be provided with adhesive layer between Recombined bamboo, adhesive used is resorcinol gluing agent or water
Property polymer isocyanic ester adhesive;It is provided with adhesive layer, institute between the Recombined bamboo of longitudinal finger spreading
Adhesive be resorcinol gluing agent or aqueous solution acrylate resin;Recombined bamboo manufactures
The adhesive of Shi Suoyong is impregnating phenolic resin or dipping Lauxite.
The Large-specification recombination composite structural wood exemplary manufacturing method not using veneer and cardboard of comparison 1,
In addition to without cardboard and veneer, other techniques are equal to embodiment 1.
Table 1 Recombined bamboo and Large-specification recombination composite structural wood physical and mechanical property
As it can be seen from table 1 use the present invention big specification recombination structure material to manufacture its physical and mechanical property
The most not decaying compared with Recombined bamboo, and reference examples is compared, horizontal shear strength adds 37.1%,
MOR adds 68.2%, and stripping performance is greatly improved.
Embodiment 2 big specification mitered restructuring composite construction material
The Large-specification recombination composite structural wood of exemplary embodiments of the present invention, it include Scrimber (1),
Veneer (2), cardboard (3) and adhesive (not marking in figure), as shown in figure 11, by many
The Scrimber stacking of the longitudinal mitered spreading of layer forms, and arranges one layer of wood single between every layer of Scrimber (1)
Plate (3), the thickness of veneer is 0.8mm;It is provided with between Scrimber (1) and veneer (3)
Adhesive layer (does not marks in figure), and adhesive used is aqueous solution acrylate resin;
The Scrimber (1) of longitudinal mitered spreading is provided with a layer paperboard (2) between the composition surface of longitudinal mitered,
Adhesive layer (not marking in figure), gluing used it is provided with between Scrimber (1) and cardboard (2)
Agent is aqueous solution acrylate resin;Adhesive used during Scrimber (1) manufacture is leaching
Stain Lauxite (does not marks in figure).
It is as follows that Large-specification recombination composite structural wood manufacture method typical case of the present invention implements step:
1, by discongesting, being dried, impregnation, be dried, gluing, maintenance, cutting edge, saw cut and sanding
Workshop section, timber is processed into (length × width x thickness) is: the Scrimber of 180cm × 140cm × 4.5cm;It is dipping Lauxite at the adhesive used by impregnation operation, in gluing technique, uses cold
Platen press, belongs to prior art;
2, above-mentioned Scrimber is sawn into oblique section as shown in Figure 7, the thickness at mitered position and inclined-plane
Length ratio is 1: 10;
3, weigh emulsion polymer isocyanate adhesive according to 100: 18 ratios and stick host and the curing agent of agent, uniformly
Mixing and stirring;
4, by cardboard by being processed into ramp structure as shown in Figure 8, the thickness at mitered position is with oblique
Face length ratio is 1: 10;
5, the emulsion polymer isocyanate adhesive after miter coats described allotment sticks agent, and glue-spread is
250g/m2, or the area am according to cardboard miter2, use impregnation mode, cardboard immersed gluing
In agent, impregnation resin content is (250 × a) g;By the Scrimber after gluing according to assembly shown in Fig. 9, will
Sheet material after assembly uses two ends to overstock to centre, makes to combine closely at mitered, the plate after mitered spreading
Material is as shown in Figure 10.
6, by rotary-cut, dry, cutting edge workshop section, it is 14cm that timber is processed into width, and thickness is
The specification veneer of 0.8mm, as shown in Figure 5;
7, Scrimber surface after longitudinal mitered spreading or veneer coat allotment after aqueous isocyanide
Acid esters adhesive, glue-spread is 250g/m2;
8, if by thick by one layer of veneer edge of one layer of Scrimber to the Scrimber after dried layer gluing and veneer
Degree direction, by stacking gradually, makes to be provided with one layer of veneer between every layer of Scrimber, then through Cold-press adhesion,
Form Large-specification recombination composite structural wood slab;
9, by described Large-specification recombination composite structural wood slab, through works such as cutting edge, saw section, sandings
Section, is processed into Large-specification recombination composite structural wood as shown in figure 11.
The beam of exemplary embodiments of the present invention, post, furniture or floor, be by above-mentioned restructuring composite construction
Material is fabricated by.
Reference examples 2
Comparison exemplary embodiments does not use the Large-specification recombination composite structural wood of veneer and cardboard, and it includes
Scrimber and adhesive, Large-specification recombination composite structural wood is by the restructuring yard of multilayer longitudinal direction mitered spreading
Folding and form, be provided with adhesive layer between Scrimber, adhesive used is aquosity polymer isocyanic ester
Adhesive;Being provided with adhesive layer between the Scrimber of longitudinal mitered spreading, adhesive used is aqueous
Polymer isocyanic ester adhesive;Adhesive used during Scrimber manufacture is dipping Lauxite.
The Large-specification recombination composite structural wood exemplary manufacturing method not using veneer and cardboard of comparison 2,
In addition to without cardboard and veneer, other techniques are equal to embodiment 1.
Table 1 Scrimber and Large-specification recombination composite structural wood physical and mechanical property
As it can be seen from table 1 use the present invention big specification recombination structure material to manufacture its physical and mechanical property
The most not decaying compared with Scrimber, and reference examples is compared, horizontal shear strength adds 26.91%,
The improvement that stripping performance has obtained, horizontal shear strength is directly related with glue performance with stripping performance,
Therefore, the glue performance of restructuring composite construction material is significantly improved by the present invention.
Claims (6)
1. a Large-specification recombination composite structural wood, it includes recombinant material, veneer, cardboard and glue
Glutinous agent, is characterized in that: is stacked by the recombinant material of multilayer Lengthwise joint and forms, sets between every layer of recombinant material
Putting one layer of veneer, the thickness of described veneer is 0.1-1.5mm;Set between recombinant material and veneer
Having adhesive layer, adhesive used is resorcinol gluing agent or aquosity polymer isocyanic ester gluing
Agent;The composition surface of described recombinant material Lengthwise joint is provided with adhesive layer, and adhesive used is isophthalic two
Phenol adhesive or aqueous solution acrylate resin;The adhesive that described recombinant material is used when manufacturing
It is impregnating phenolic resin or dipping Lauxite;The recombinant material of described Lengthwise joint is at Lengthwise joint
Composition surface between be provided with a layer paperboard, be provided with adhesive layer, glue used between recombinant material and cardboard
Glutinous agent is resorcinol gluing agent or aqueous solution acrylate resin.
The most according to claim 1, Large-specification recombination composite structural wood, is characterized in that: described heavy
Group material is Recombined bamboo or Scrimber.
The most according to claim 1, Large-specification recombination composite structural wood, is characterized in that: described in connect
A length of finger spreading or mitered spreading.
4. a manufacture method for Large-specification recombination composite structural wood, including following workshop section: (one)
Raw material preparation, (two) Lengthwise joint, (three) MULTILAYER COMPOSITE, (four) later stage process, its feature
It is:
(1) raw material prepares, and prepares and adhesive allotment including recombinant material preparation, veneer:
(1) recombinant material prepares, by discongesting, being dried, impregnation, dry, gluing, maintenance, sanction
Limit, saw cut and sanding workshop section, and bamboo wood or timber are processed into specification recombinant material;Used by impregnation operation
Adhesive be impregnating phenolic resin or dipping Lauxite;
(2) veneer prepares, and by rotary-cut, dry, cutting edge workshop section, timber is processed into thickness is
The specification veneer of 0.1-1.5mm;
(3) adhesive allotment, by resorcinol gluing agent or aqueous solution acrylate resin
Host and curing agent are according to 100: (10-20) ratio uniform mixes;
(2) Lengthwise joint
Described specification recombinant material two ends are used and is machined into finger face or miter, then in finger face
Or miter coats the resorcinol gluing agent after allotment or aqueous solution acrylate resin, warp
Cross longitudinal finger or mitered makes the recombinant material of Lengthwise joint;In described Lengthwise joint workshop section, described
The recombinant material of Lengthwise joint is provided with a layer paperboard, recombinant material and cardboard between the composition surface of Lengthwise joint
Between be provided with adhesive layer, adhesive used is resorcinol gluing agent or aqueous high molecular isocyanic acid
Ester adhesive;
(3) MULTILAYER COMPOSITE
The recombinant material of described Lengthwise joint and/or the upper and lower surface of veneer are coated resorcinol gluing
Agent or aqueous solution acrylate resin, if pressing one by the recombinant material after dried layer gluing and veneer
Layer one layer of veneer through-thickness of recombinant material, by stacking gradually, makes to be provided with between every layer of recombinant material one layer
Veneer, then through Cold-press adhesion, form Large-specification recombination composite structural wood slab;
(4) later stage processes
By described Large-specification recombination composite structural wood slab, through cutting edge, saw section, sanding workshop section,
It is processed into Large-specification recombination composite structural wood.
The manufacture method of Large-specification recombination composite structural wood the most according to claim 4, its feature
Being: in mitered operation, the thickness at mitered position and chamfer length ratio are 1: 10-1: 20.
The manufacture method of Large-specification recombination composite structural wood the most according to claim 4, it is special
Levy and be: in finger operation, box pin joint parameter: the long 8mm-45mm of tooth, tooth top width 0.5mm-20mm,
Tooth pitch 3mm-20mm, tooth refers to gradient 1/6-1/9.