CN103214765B - A kind of matrix material for ceiling-fan blade and preparation method thereof - Google Patents
A kind of matrix material for ceiling-fan blade and preparation method thereof Download PDFInfo
- Publication number
- CN103214765B CN103214765B CN201310141810.4A CN201310141810A CN103214765B CN 103214765 B CN103214765 B CN 103214765B CN 201310141810 A CN201310141810 A CN 201310141810A CN 103214765 B CN103214765 B CN 103214765B
- Authority
- CN
- China
- Prior art keywords
- matrix material
- speed
- ceiling
- fan blade
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of matrix material for ceiling-fan blade and preparation method thereof, this matrix material: comprise following component by weight percentage: polyvinyl chloride 45-80%; Calcium carbonate 5-30%; Whipping agent 0.5-4%; Stabilizer 1-8%; ACR processing aid 1-6%; PVC foam mediator agent 3.5-12%; Titanium dioxide 1-10%; OPE wax 0.5-4%.This preparation method: each component is added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100-150 DEG C; Stirring at low speed is even, and is down to room temperature; The above-mentioned middle material through mixing is added extrusion plasticizing in forcing machine, and mold cools down is shaped, traction discharging.The object of the invention is to overcome weak point of the prior art, comprehensive existing various flabellum material advantages, providing a kind of formula rationally, advantage of lower cost, for the matrix material and preparation method thereof of ceiling-fan blade.
Description
Technical field
The present invention relates to a kind of matrix material for ceiling-fan blade, the invention still further relates to a kind of method preparing this matrix material.
Background technology
Existing ceiling-fan blade generally adopts clamping plate, MDF, metal, and the material such as plastics ABS or solid wood is made.Clamping plate, the materials such as MDF are in waterproof, dust-proof, intensity, and the aspects such as life-span all exist larger defect; The ratio of metallic substance is great, antirust, and decorate properties is poor; General plastics are as relatively high in its cost of ABS; Adopt solid wood to make not environmentally, processing performance is poor.
Summary of the invention
The object of the invention is to overcome weak point of the prior art, comprehensive existing various flabellum material advantages, provide a kind of formula rationally, advantage of lower cost, for the matrix material of ceiling-fan blade;
Another object of the present invention is to provide a kind of method preparing this matrix material.
In order to achieve the above object, the present invention adopts following scheme:
For a matrix material for ceiling-fan blade, it is characterized in that comprising following component by weight percentage:
As above for a matrix material for ceiling-fan blade, it is characterized in that comprising following component by weight percentage:
As above for a matrix material for ceiling-fan blade, it is characterized in that the stearic acid also including 0.05-0.15% by weight percentage.
As above for a matrix material for ceiling-fan blade, it is characterized in that composed of the following components by weight percentage:
As above for a matrix material for ceiling-fan blade, it is characterized in that the PA40 adding assistant also including 0.3-1.2% by weight percentage.
As above for a matrix material for ceiling-fan blade, it is characterized in that composed of the following components by weight percentage:
As above for a matrix material for ceiling-fan blade, it is characterized in that the toner also including 0.05-0.15% by weight percentage.
Any one matrix material for ceiling-fan blade, is characterized in that described stabilizer is the mixture of organotin stabilizer and calcium zinc stabilizer as mentioned above; Described whipping agent is Cellmic C 121; Described ACR processing aid is polyacrylate(s) processing aid; Described titanium dioxide is titanium dioxide; Described OPE wax is polyethylene wax.
The present invention is a kind of to be prepared as mentioned above for the method for the matrix material of ceiling-fan blade, it is characterized in that comprising the following steps:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100-150 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging.
Preparation method as above, it is characterized in that the barrel zone temperature of forcing machine in step C is 130-170 DEG C, mould temperature is 130-170 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Polyvinyl chloride described in the present invention is commercially available prod, can buy from LG Corp of South Korea.
Calcium carbonate described in the present invention is commercially available prod, can buy from Jiangxi Jiu Feng nano-calcium carbonate company limited.
Whipping agent described in the present invention is commercially available prod, can buy from Rui'an City Zhong Wei rubber and plastics auxiliaries company limited.
Stabilizer described in the present invention is commercially available prod, can buy from blue sky, Tai'an auxiliary agent company limited and Xin Di plastic material company limited of Xiamen City.
ACR processing aid described in the present invention is commercially available prod, sincere plastics Chemical Co., Ltd. can buy from Shunde District of Foshan City.
PVC foam mediator agent described in the present invention is commercially available prod, can buy from Rhom and Hass (U.S.) or Qingdao Xin Li macromolecular material company limited.
Titanium dioxide described in the present invention is commercially available prod, can buy from Landtek Chemical Co., Ltd. of Langfang in Hebei Province.
OPE wax described in the present invention is commercially available prod, can buy from Dongguan City Qi macromolecular material of a specified duration company limited.
PA40 processing aid described in the present invention is commercially available prod, can buy from Hangzhou Sai Le Chemical Co., Ltd..
In sum, beneficial effect of the present invention:
The present invention fills a prescription advantages of simple, and matrix material preparation of the present invention is simple, and quality is light, advantage of lower cost, is applicable to make electric fan.
Embodiment
Below in conjunction with embodiment, the present invention is described further:
Embodiment 1
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging,, wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 130 DEG C, engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 2
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 150 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging,, wherein the barrel zone temperature of forcing machine is 170 DEG C, and mould temperature is 170 DEG C, engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 3
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 130 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging,, wherein the barrel zone temperature of forcing machine is 150 DEG C, and mould temperature is 150 DEG C, engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 4
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 130 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 5
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 150 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 170 DEG C, and mould temperature is 170 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 6
The present invention is used for the matrix material of ceiling-fan blade, comprises following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 120 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 140 DEG C, and mould temperature is 150 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 7
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 130 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 8
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 140 DEG C;
A, stirring at low speed are even, and are down to room temperature;
B, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 170 DEG C, and mould temperature is 130 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 9
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 130 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 150 DEG C, and mould temperature is 130 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min
Embodiment 10
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 140 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 140 DEG C, and mould temperature is 170 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 11
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100-150 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 130-170 DEG C, and mould temperature is 130-170 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 12
The present invention is used for the matrix material of ceiling-fan blade, composed of the following components by weight percentage:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 170 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Embodiment 13
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging; Wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 130 DEG C, and engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.
Claims (1)
1., for a matrix material for ceiling-fan blade, it is characterized in that comprising following component by weight percentage:
Preparation method:
A, each component added in stirrer by proportioning and carries out high-speed stirring, and be warming up to 100 DEG C;
B, stirring at low speed are even, and are down to room temperature;
C, by step B through mixing material add extrusion plasticizing in forcing machine, mold cools down shape, traction discharging,, wherein the barrel zone temperature of forcing machine is 130 DEG C, and mould temperature is 130 DEG C, engine speed is 8-9r/min, and feeding rotating speed is 6-8r/min, and pulling speed is 0.5-0.8m/min.