CN103206055A - 一种防潮墙纸的生产工艺 - Google Patents
一种防潮墙纸的生产工艺 Download PDFInfo
- Publication number
- CN103206055A CN103206055A CN 201310135449 CN201310135449A CN103206055A CN 103206055 A CN103206055 A CN 103206055A CN 201310135449 CN201310135449 CN 201310135449 CN 201310135449 A CN201310135449 A CN 201310135449A CN 103206055 A CN103206055 A CN 103206055A
- Authority
- CN
- China
- Prior art keywords
- finished product
- moistureproof
- production technology
- wallpaper
- production process
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种防潮墙纸的生产工艺，该生产工艺依次包括：步骤一：选取原材料，分别为硅橡胶、粘结剂；步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；步骤三:将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm-1mm；步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa-330MPa，温度为120℃-180℃；步骤五：冷却；步骤六：将所述冷却后的半成品放在压花机中压花；步骤七：将压花后的半成品表面涂上色彩，制成成品；步骤八：将所述成品晾干，收卷。本发明工艺简单、防潮、防霉。
Description
技术领域
本发明涉及一种墙纸的工艺，尤其涉及一种防潮墙纸的生产工艺。
背景技术
目前，随着时代的发展，追求生活质量和品位的人越来越多，如何将家装扮的更加温馨和时尚，是越来越多的人的需求，而墙纸正好能满足大众这样的一种要求，让个性十足无处不在。
而人们对墙纸的性能也要求的越来越多，比如是否具有印花或者是否可以防潮、防霉效果，而现有技术中的纸制品还不能满足上述要求。
发明内容
本发明所要解决的技术问题是提供一种工艺简单、防潮、防霉的墙纸的生产工艺。
为解决上述技术问题，本发明所采用的技术方案是：一种防潮墙纸的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为硅橡胶、粘结剂；
步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；
步骤三: 将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm-1mm；
步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa-330MPa，温度为120℃-180℃；
步骤五：冷却；
步骤六：将所述冷却后的半成品放在压花机中压花；
步骤七：将压花后的半成品表面涂上色彩，制成成品；
步骤八：将所述成品晾干，收卷。
所述颗粒直径为0.8mm。
所述压力为300MPa。
所述温度为150℃。
与现有技术相比，本发明的有益效果为：
由于本发明防潮墙纸的生产工艺采用了合理的原料及科学的工艺步骤及条件，所以能够制作出防潮、防霉的墙纸，适用于厨房和卫生间，且制作工序少、易操作，因此本发明工艺简单、防潮、防霉。
具体实施方式
以下结合具体实施方式详细说明本发明
一种防潮墙纸的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为硅橡胶、粘结剂；
步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；
步骤三: 将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm-1mm；
步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa-330MPa，温度为120℃-180℃；
步骤五：冷却；
步骤六：将所述冷却后的半成品放在压花机中压花；
步骤七：将压花后的半成品表面涂上色彩，制成成品；
步骤八：将所述成品晾干，收卷。
上述生产工艺采用了合理的原料及科学的工艺步骤及条件，所以能够制作出防潮、防霉的墙纸，且制作工序少、易操作。
实施例1：
一种防潮墙纸的生产工艺，该生产工艺依次包括：
步骤一：选取原材料，分别为硅橡胶、粘结剂；
步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；
步骤三: 将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.8mm；
步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为300MPa，温度为150℃；
步骤五：冷却；
步骤六：将所述冷却后的半成品放在压花机中压花；
步骤七：将压花后的半成品表面涂上色彩，制成成品；
步骤八：将所述成品晾干，收卷。
综上所述，本发明工艺简单、易操作。
以上所述仅为本发明的较佳实施方式，本发明的保护范围并不以上述实施方式为限，但凡本领域普通技术人员根据本发明所揭示内容所作的等效修饰或变化，皆应纳入权利要求书中记载的保护范围内。
Claims (4)
1.一种防潮墙纸的生产工艺，其特征在于：该生产工艺依次包括：
步骤一：选取原材料，分别为硅橡胶、粘结剂；
步骤二：将硅橡胶与粘结剂按照重量比为8：2的比例混合；
步骤三: 将上述混合物放在搅拌机中粉碎成颗粒大小，颗粒直径为0.5mm-1mm；
步骤四：将所述颗粒大小的混合物放在模具中挤压，制成半成品，所述压力为280MPa-330MPa，温度为120℃-180℃；
步骤五：冷却；
步骤六：将所述冷却后的半成品放在压花机中压花；
步骤七：将压花后的半成品表面涂上色彩，制成成品；
步骤八：将所述成品晾干，收卷。
2.根据权利要求1所述的一种防潮墙纸的生产工艺，其特征在于：所述颗粒直径为0.8mm。
3.根据权利要求1所述的一种防潮墙纸的生产工艺，其特征在于：所述压力为300MPa。
4.根据权利要求1所述的一种防潮墙纸的生产工艺，其特征在于：所述温度为150℃。