CN103205868A - Method for fulling by detergent in embossing and printing of woolen sweaters - Google Patents
Method for fulling by detergent in embossing and printing of woolen sweaters Download PDFInfo
- Publication number
- CN103205868A CN103205868A CN 201310125011 CN201310125011A CN103205868A CN 103205868 A CN103205868 A CN 103205868A CN 201310125011 CN201310125011 CN 201310125011 CN 201310125011 A CN201310125011 A CN 201310125011A CN 103205868 A CN103205868 A CN 103205868A
- Authority
- CN
- China
- Prior art keywords
- embossing
- woollen sweater
- fulling milling
- fulling
- 20min
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
The invention discloses a method for fulling by detergent in embossing and printing of woolen sweaters. The method includes: dipping for 10-20min at the water temperature of 35-40 DEG C and with a bath ratio of 1:20-1:30; adding 0.5owf%-1.5owf% neutral detergent to adjust the pH value to be 7-7.5, and processing for 10-30min; cleaning twice, 2-3min for each time and at the temperature of 85-90 DEG C, and drying for 20-25min. By the method, embossing and printing effects of the woolen sweaters can be greatly improved, and fabric after being processed is excellent in appearance, full in hand feel, soft in texture and effective in heat insulating.
Description
Technical field
The invention belongs to the textile dyeing and finishing technical field, relate to the fulling process of woollen sweater, be specifically related to a kind of method of woollen sweater embossing washing agent fulling milling.
Background technology
The stamp of woollen sweater refers to directly stamp the technology of certain colour image on woollen sweater.The stamp woollen sweater has colored type and changes the characteristics many, bright in colour, that pattern is true to nature, soft, and jacquard weave sweater superiority that do not had or inaccessible arranged, therefore, the stamp sweater more and more is subjected to consumer's favor, and woollen sweater not only can carry out local stamp but also can carry out the whole body stamp.
The sweater stamp has two kinds of PLATE SCREAM PRINTING and ROTARY SCREAM PRINTING usually, and the former is suitable for the stamp of garment piece, and the latter then is suitable for successional stamp.In the sweater stamp, except sub-fraction adopted ROTARY SCREAM PRINTING, most of sweater products all adopted PLATE SCREAM PRINTING, in PLATE SCREAM PRINTING again based on manual platen stamp.Print edition decorative pattern manufacturing process is: after the design of flower type is determined, need to draw the black and white original text of each color separation flower type, by being coated with photoresists at screen cloth, after printing down, development and flower version are repaired, can use by stamp.The woollen sweater screen printing mainly can be divided into decatize stamp, COAT PRINTING, low temperature stamp and embossing four classes by the difference of concrete technology, for a long time, wool (suede) shirt almost be everyone, spring, autumn in winter requisite clothes.Because comfortable and easy to wear, warmth retention property is strong, matte is plentiful, soft, a kind of embossment woollen sweater is arranged especially, it is to have likeness in form embossment relief pattern, quality is plentiful, texture is dim, color is soft, contrast is strong under illumination, give eye-catching space pattern, the satiny appearance effect that forms uniqueness of feel, be subjected to liking of consumers in general deeply.
Sheep's wool common name wool is production raw material important in the textile industry.Wool is a kind of natural fabric of complexity, mainly comprises protein (97%) and lipoidis (1%), is the ideal basis pledge of several enzymes, as protease and lipase.Wool is made up of scale cell, cortex cell and cell membrane complexes.Feltability is the maximum feature of woollen sweater.The existence of feltability also is the reason that causes fabric size instability (washing sweater has later often diminished).Embossing has utilized the fulling milling principle of wool surface scale and has made successful.
Woollen sweater can carry out fulling milling, and it is internal cause that the structure of animal fiber has feltability; And at a certain temperature and humidity conditions, being subjected to chemical assistant and external force effect is the external factor of impelling the wool fibre fulling milling.The wool surface is covered with by many scales, the free end of scale is the tip direction that points to wool fibre, so make wool fibre have rubbing, namely just big along the little and reverse coefficient of friction of scale coefficient of friction, the contrary and suitable coefficient difference (coefficient of friction of forbidden lamella sheet direction is always greater than the coefficient of friction along the scale direction when being fibre frictoin) that just exists between the two.Add and be subjected to the influence that the external world is damp and hot and chemical assistant (agent is received in contracting) exists, when woollen sweater is subjected to the effect that mechanical external force is rubbed repeatedly, just produced the trend of pointing to the one-way movement of fiber butt, adding wool has good extensibility, resilience and space and curls and to make wool fibre be easy to motion more, just make to intert mutually between the wool fibre and tangle, and produce the felting that interweaves, the hair end is exposed to fabric face gradually, make the fabric good appearance that becomes, feel is abundant, the quality softness possesses good warming effect.
Summary of the invention
The invention provides a kind of method of woollen sweater embossing washing agent fulling milling, to improve the effect of woollen sweater embossing.
The method of woollen sweater embossing washing agent fulling milling of the present invention comprises the steps:
1, woollen sweater soaks
35 ℃~40 ℃ of water temperatures, bath raio are under the condition of 1:20~1:30, dipping 10min~20min;
2, fulling milling
Add 0.5owf%~1.5owf% neutral detergent, regulate pH value 7~7.5, handle 10min~30min;
3, clean
Clean 2 times, each 2min~3min, under 85 ℃~90 ℃, 20min~25min is handled in oven dry.
Described bath raio was 1:25 when preferably, woollen sweater soaked.
Preferably, described neutral detergent addition is 1owf% during fulling milling.
Preferably, under 85 ℃, 20min is handled in oven dry during cleaning.
Technology of the present invention can improve the effect of woollen sweater embossing greatly, and the appearance of fabrics after the processing is good, and feel is abundant, and the quality softness possesses good warming effect.
The specific embodiment
Below in conjunction with embodiment the method for woollen sweater embossing washing agent fulling milling of the present invention is described in detail; thereby so that advantages and features of the invention can be easier to be it will be appreciated by those skilled in the art that protection scope of the present invention is made more explicit defining.
Embodiment 1
1, woollen sweater soaks
35 ℃~40 ℃ of water temperatures, bath raio are under the condition of 1:20, dipping 10min;
2, fulling milling
Add the 0.5owf% neutral detergent, regulate pH value 7~7.5, handle 30min;
3, clean
Clean 2 times, each 2min~3min, under 85 ℃, 25min is handled in oven dry.
Embodiment 2
1, woollen sweater soaks
35 ℃~40 ℃ of water temperatures, bath raio are under the condition of 1:30, dipping 20min;
2, fulling milling
Add the 1.5owf% neutral detergent, regulate pH value 7~7.5, handle 10min;
3, clean
Clean 2 times, each 2min~3min, under 90 ℃, 20min is handled in oven dry.
Embodiment 3
1, woollen sweater soaks
35 ℃~40 ℃ of water temperatures, bath raio are under the condition of 1:25, dipping 15min;
2, fulling milling
Add the 1owf% neutral detergent, regulate pH value 7~7.5, handle 20min;
3, clean
Clean 2 times, each 2min~3min, under 85 ℃, 20min is handled in oven dry.
Claims (4)
1. the method for a woollen sweater embossing washing agent fulling milling is characterized in that, may further comprise the steps:
(1), woollen sweater soaks
35 ℃~40 ℃ of water temperatures, bath raio are under the condition of 1:20~1:30, dipping 10min~20min;
(2), fulling milling
Add 0.5owf%~1.5owf% neutral detergent, regulate pH value 7~7.5, handle 10min~30min;
(3), clean
Clean 2 times, each 2min~3min, under 85 ℃~90 ℃, 20min~25min is handled in oven dry.
2. the method for woollen sweater embossing washing agent fulling milling according to claim 1, it is characterized in that: described bath raio was 1:25 when woollen sweater soaked.
3. the method for woollen sweater embossing washing agent fulling milling according to claim 2, it is characterized in that: described neutral detergent addition is 1owf% during fulling milling.
4. the method for woollen sweater embossing washing agent fulling milling according to claim 1 is characterized in that: under 85 ℃, dry and handle 20min during cleaning.