CN103205767A - 无磷双组份常温脱脂剂 - Google Patents
无磷双组份常温脱脂剂 Download PDFInfo
- Publication number
- CN103205767A CN103205767A CN2013100927075A CN201310092707A CN103205767A CN 103205767 A CN103205767 A CN 103205767A CN 2013100927075 A CN2013100927075 A CN 2013100927075A CN 201310092707 A CN201310092707 A CN 201310092707A CN 103205767 A CN103205767 A CN 103205767A
- Authority
- CN
- China
- Prior art keywords
- agent
- phosphate
- room temperature
- liquid
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种主要用于汽车及家电涂装前处理脱脂工序的无磷常温双组份脱脂剂,其特征是原料有以下重量百分比的物质:粉体A剂包括偏硅酸钠20~50%,葡萄糖酸钠1-4%,碱性盐20~60%;液体B剂包括表面活性剂11~26%,水余量;本发明提供的脱脂剂去污力强,且泡沫低,使用温度在18℃以上就能达到质量要求,并适用于浸渍、喷淋清洗。
Description
技术领域
本发明属于一种金属板材的脱脂剂,特别是一种用于涂装前各种板材进行脱脂处理的双组份常温脱脂剂,主要应用于家电及汽车车身涂装前进行常温脱脂处理。
背景技术
随着我国家电和汽车工业的迅速发展,对产品的外观和涂层质量要求越来越高,但现有使用的脱脂剂都是在升温的条件的下使用。目前一般的脱脂剂的使用温度都在40-55℃,能源使用量要比材料的费用还要高,尤其是在南方,为了生产还要在夏季使用能源,造成了成本上升,产品的竞争力下降。
本发明的目的是提供一种在常温使用下的无磷双组份脱脂剂,使用时容易控制技术要求,使用效果好,在常温的条件就可使用(>18℃即可)。脱脂剂产品稳定性好,B组份没有分层和结晶现象,去污力强、产生泡沫少,适合喷淋和浸渍的条件下使用,现场操作方便。
本发明提供的双组份常温脱脂剂,原料有以下重量百分比的物质:
粉体A剂
偏硅酸钠 20~50%,
葡萄糖酸钠 1-4%,
碱性盐 20~60%;
液体B剂
表面活性剂 11~26%,
水 余量;
其中,碱性盐为氢氧化钠、碳酸钠中的1-2种;表面活性剂包括下列物质:非离子表面活性剂DOWFAX20A64、DOWFAX20A612和Plura LF221;此三种原料在液体B剂中的重量比例分别为:7-12%:2-7%:2-7%。
上述脱脂剂的制备方法是:粉体A剂:在容器中按比例加入偏硅酸钠、葡萄糖酸钠及碱性盐,搅拌均匀即可。液体B剂:在容器内按比例加入水,并按比例和先后加入表面活性剂的各物质,充分搅拌至均匀无色为止即可。
使用方法:将粉体A剂和液体B剂按照重量比例溶解于水中,三者重量比例为13:10: 1000,在18℃以上进行工作,在工艺时间处理就可以达到质量要求。
本发明的优点是:使用时容易控制技术要求,使用效果好,脱脂剂产品稳定性好,没有分层和结晶现象,脱脂时去污力强、产生泡沫少,现场操作方便。使用温度低,节约能源。
具体实施方式
实施例1:
原料有以下重量百分比的物质:
粉体A剂:
偏硅酸钠 45%,
葡萄糖酸钠 2%,
氢氧化钠 10%,
碳酸钠 43%;
液体B剂:
20A64 11%,
LF-221 6%,
20A612 4%,
余量 水。
非离子表面活性剂DOWFAX20A64和DOWFAX20A612为上海康辽贸易有限公司代理销售的美国陶式化学产品,为市场公开销售的产品;非离子表面活性剂Plura LF221为上海泰今国际贸易有限公司代理销售的巴斯夫(中国)有限公司的化学产品,为市场公开销售的产品。
制备方法:粉体A剂:在容器中按比例加入偏硅酸钠、葡萄糖酸钠及碱性盐,搅拌均匀即可。液体B剂:在容器内按比例加入水,并按比例和先后加入表面活性剂的各物质,充分搅拌至均匀无色为止即可。
使用方法:将粉体A剂和液体B剂按照重量比例溶解于水中,三者重量比例为13:10: 1000,在18℃以上进行工作,在工艺时间处理就可以达到质量要求。
实施例2:
原料有以下重量百分比的物质:
粉体A剂:
偏硅酸钠 40%,
葡萄糖酸钠 1.5%,
氢氧化钠 15%,
碳酸钠 43.5%;
液体B剂:
20A64 10%,
LF-221 5%,
20A612 3%,
余量 水。
制备方法和使用方法同实施例1。
实施例3
原料有以下重量百分比的物质:
粉体A剂:
偏硅酸钠 38%,
葡萄糖酸钠 3%,
氢氧化钠 12%,
碳酸钠 47%;
液体B剂:
20A64 12%,
LF-221 4%,
20A612 6%,
余量 水。
制备方法和使用方法同实施例1。
实施例4
原料有以下重量百分比的物质:
粉体A剂:
偏硅酸钠 46%,
葡萄糖酸钠 1.8%,
氢氧化钠 9%,
碳酸钠 43.2%;
液体B剂:
20A64 11%,
LF-221 3%,
20A612 3%,
余量 水。
制备方法和使用方法同实施例1。
金属板材经过以上的产品进行处理后,脱脂能力可以达到98%以上,并且使用温度在18℃即可以使用,泡沫低,处理效果好。
Claims (1)
1.一种无磷常温双组份脱脂剂,其特征是原料有以下重量百分比的物质:
粉体A剂
偏硅酸钠 20~50%,
葡萄糖酸钠 1-4%,
碱性盐 20~60%;
液体B剂
表面活性剂 11~26%,
水 余量;
其中,碱性盐为氢氧化钠、碳酸钠中的1-2种;表面活性剂包括下列物质:非离子表面活性剂DOWFAX20A64、DOWFAX20A612和Plura LF221,此三种原料在液体B剂中的重量比分别为:7-12%:2-7%:2-7%。