CN103196764A - 薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法 - Google Patents

薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法 Download PDF

Info

Publication number
CN103196764A
CN103196764A CN2013101178473A CN201310117847A CN103196764A CN 103196764 A CN103196764 A CN 103196764A CN 2013101178473 A CN2013101178473 A CN 2013101178473A CN 201310117847 A CN201310117847 A CN 201310117847A CN 103196764 A CN103196764 A CN 103196764A
Authority
CN
China
Prior art keywords
hrb
stainless steel
steel plate
hardness
thin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101178473A
Other languages
English (en)
Inventor
张建生
任永秀
王竟东
王传东
赵建伟
王冰
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Shanxi Taigang Stainless Steel Co Ltd
Original Assignee
Shanxi Taigang Stainless Steel Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Shanxi Taigang Stainless Steel Co Ltd filed Critical Shanxi Taigang Stainless Steel Co Ltd
Priority to CN2013101178473A priority Critical patent/CN103196764A/zh
Publication of CN103196764A publication Critical patent/CN103196764A/zh
Pending legal-status Critical Current

Abstract

薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法，其特征包括（1）选择一个机组生产的两组产品，其中第一组是厚度＞1.50mm产品至少50块；第二组是厚度≤1.50mm产品至少50块；（2）对第一组产品按照《金属材料洛氏硬度试验方法》规定的方法进行测试，获得生产中硬度值HRB平均值；（3）对第二组产品按照《金属材料维氏硬度试验》测试，获得金属维氏硬度值HV平均值；（4）利用公式HRB=HV/1.98，进行判定：如果满足HRB=HV/1.98满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板合格；如果HRB=HV/1.98不满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板不合格。本发明解决了薄钢板HRB测试的难题。

Description

薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法
技术领域                                                                             
本发明主要用于厚度≤1.50mm的薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定。
背景技术
奥氏体不锈钢板的洛氏硬度（HRB）是美国市场客户需要的性能指标。但在生产中发现，对于厚度≤1.50mm的薄规格Cr-Ni系奥氏体不锈钢板（以下简称：薄钢板），由于下述原因而无法按照GB/T230.1-2009《金属材料 洛氏硬度试验 第1部分：试验方法》规定的方法进行HRB测试。 
第一，薄规格Cr-Ni系奥氏体不锈钢板在按照GB/T230规定的方法试验时，试样背面存在肉眼可见的变形痕迹，而GB/T230中6.3规定：除HR30Tm，试验后试样背面不应出现可见变形。可见GB/T230给出的试样最小厚度与HRB值的关系图不适用于薄钢板。 
对于薄钢板，生产中只能按照GB/T4340.1-2009 《金属材料 维氏硬度试验 第1部分：试验方法》测试金属维氏硬度值（HV），虽然可以满足国内客户的需求，但美国等国际市场不接受维氏硬度值（HV），必须提供HRB值，一定程度上给出口贸易带来不便。 
第二，GB/T1172《黑色金属硬度及强度换算值》中《碳钢硬度与强度换算值》，虽然给出了HV和HRB硬度换算对应表，但仅适用于低碳钢。生产中发现304不锈钢据此进行换算，HRB数值偏低。由于产品标准中有硬度上限的要求，如果数据偏低，一些情况下会产生“合标不合用”的情况，客户的满意度会降低。生产过程中大量数据证明，GB/T1172不适合Cr-Ni系奥氏体不锈钢板的硬度换算。 
发明内容
为了满足特定客户的要求的检验厚度≤1.50mm的薄钢板的HRB判定，本发明提供薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法。 
本发明的技术方案：
1、选择一个机组生产的两组产品，其中第一组是厚度＞1.50mm产品至少50块；第二组是厚度≤1.50mm产品至少50块；
2、对第一组产品按照GB/T230.1-2009《金属材料 洛氏硬度试验 第1部分：试验方法》规定的方法进行测试，获得生产中硬度值HRB平均值；
3、对第二组产品按照GB/T4340.1-2009 《金属材料 维氏硬度试验 第1部分：试验方法》测试，获得金属维氏硬度值HV平均值；
4、利用经验公式HRB =HV/1.98进行判定：如果满足HRB =HV/1.98满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板合格；如果HRB =HV/1.98不满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板不合格。
本发明的第一组产品和第二组产品的化学成分和性能相同；生产条件一致。 
在化学成分和生产条件相同，各种性能指标数据也是稳定的，不会随厚度规格的变化而产生大的变化。因此从理论上来讲第一组和第二组的同类型硬度值是相同的，通过经验规律找出HRB和HV之间的关系（HRB =HV/1.98）。 
本发明解决了薄钢板HRB测试的难题，为客户提供了较为准确的HRB硬度数据。                                                                                                                                                       具体实施方式
实施例：用于出口北美地区的不锈钢产品（执行美国标准），产品包括304、304L、316、316L等Cr-Ni系奥氏体不锈钢薄钢板（厚度≤1.50mm）。
实施例：2010年11月太钢供Ta Chen International,Inc. 合同。 
（1）供货标准ASTM A 240/240M，牌号304/304L，表面2B，规格18GA×60″×C，重量为12399磅，硬度HRB84.0（测量Hv166，则洛氏硬度B为166/1.98=83.8，按进位规则确定为HRB84.0）。 
（2）供货标准ASTM A 240/240M，牌号316/316L，表面2B，规格20GA×60″×C ，重量为15880磅，硬度HRB84.0（测量Hv165，则洛氏硬度B为165/1.98=83.3，按进位规则确定为HRB83.0。 
生产日期:某年7月，同一热处理机组、同一生产工艺、化学成分相同的牌号是304钢板，其厚度规格是:2mm～6mm。 
说明：本发明的经验公式的获得试验数据见下表： 
Figure 2013101178473100002DEST_PATH_IMAGE001
Figure 2013101178473100002DEST_PATH_IMAGE002
  
Figure 2013101178473100002DEST_PATH_IMAGE003

Claims (1)

1.薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法，其特征包括
（1）、选择一个机组生产的两组产品，第一组产品和第二组产品的化学成分和性能相同；生产条件一致；其中第一组是厚度＞1.50mm产品至少50块；第二组是厚度≤1.50mm产品至少50块；
（2）、对第一组产品按照GB/T230.1-2009《金属材料 洛氏硬度试验 第1部分：试验方法》规定的方法进行测试，获得生产中硬度值HRB平均值；
（3）、对第二组产品按照GB/T4340.1-2009 《金属材料 维氏硬度试验 第1部分：试验方法》测试，获得金属维氏硬度值HV平均值；
（4）、利用经验公式HRB =HV/1.98，进行判定：如果满足HRB =HV/1.98满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板合格；如果HRB =HV/1.98不满足订货标准要求，则判定薄规格Cr-Ni系奥氏体不锈钢板不合格。
CN2013101178473A 2013-04-07 2013-04-07 薄规格Cr-Ni系奥氏体不锈钢板的洛氏硬度判定方法 Pending CN103196764A (zh)