CN103183965A - Inspection well and production method thereof - Google Patents
Inspection well and production method thereof Download PDFInfo
- Publication number
- CN103183965A CN103183965A CN2013101289870A CN201310128987A CN103183965A CN 103183965 A CN103183965 A CN 103183965A CN 2013101289870 A CN2013101289870 A CN 2013101289870A CN 201310128987 A CN201310128987 A CN 201310128987A CN 103183965 A CN103183965 A CN 103183965A
- Authority
- CN
- China
- Prior art keywords
- raw material
- inspection chamber
- production method
- mulch film
- chamber according
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the field of a pipeline building, and in particular relates to an inspection well and a production method thereof. The inspection well is prepared by the following raw materials in parts by weight: 5-7 parts of a waste mulching film, 3-4 parts of waste ore sand, 0.1-0.3 part of waste oil and 0.1-0.3 part of an anti-aging agent. The production method of the inspection well comprises the following steps: mixing the waste mulching film with the waste ore sand to obtain a mixing raw material; adding the waste oil and the anti-aging agent into the mixing raw material to obtain a raw material primary product; synthesizing the raw material primary product at 180-220 DEG C to obtain a raw material; and adding the raw material to be used in a die, and moulding to obtain a product. The inspection well provided by the invention is made from materials which are waste in daily production and life and are easy to collect, so that manufacturing cost of the inspection well is low.
Description
Technical field
The present invention relates to the pipeline building field, in particular to a kind of inspection chamber and production method thereof.
Background technology
Inspection chamber is widely used in water supply and drainage, telecommunication cable and the urban construction industry; Fiber glass reinforced plastics inspection well is a kind of inspection chamber commonly used, and this fiber glass reinforced plastics inspection well mainly is to be that raw material is made by glass fibre and vibrin.
But, this fiber glass reinforced plastics inspection well its mainly to make raw material be glass fibre or vibrin, also need to add some additives simultaneously, its price of glass fibre and vibrin is higher, therefore, the raw materials cost of fiber glass reinforced plastics inspection well is high.
Summary of the invention
The object of the present invention is to provide a kind of inspection chamber and production method, to solve the above problems.
A kind of inspection chamber is provided in the embodiments of the invention, according to the parts by weight meter, has comprised, useless mulch film 5-7 part, abandoned mine sand 3-4 part, used oil 0.1-0.3 part, antiaging agent 0.1-0.3 part.
A kind of production method of inspection chamber is provided in the embodiments of the invention, has comprised, will give up mulch film and abandoned mine sand mix, and obtain mixing raw material; Used oil and antiaging agent are added in the described mixing raw material, obtain the raw material first product; Described raw material first product is synthetic under 180-220 ℃ of temperature, obtain stand-by raw material; With the described stand-by raw material mould of packing into, and moulding, finished product obtained.
This inspection chamber that the embodiment of the invention provides, comprise useless mulch film 5-7 part, abandoned mine sand 3-4 part, used oil 0.1-0.3 part, antiaging agent 0.1-0.3 part, the making raw material of inspection chamber adopts the material of being discarded in the daily productive life, be by collecting the discarded mulch film after using as useless mulch film, equally, abandoned mine sand and used oil are all collected waste again and are obtained; Can be the discarded machine oil of having sneaked into the impurity such as metal-powder that moisture, dust, other assorted oil and component wear produce as used oil, also can be go bad gradually, generated the discarded machine oil of organic acid, colloid and bituminous substances; When various components are mixed, because useless mulch film belongs to a kind of of plastics, have plasticity-, when with after abandoned mine sand, used oil and antiaging agent mix, abandoned mine sand is as a kind of packing material, and the framework of whole inspection chamber is finalized the design has important supporting role; And the adding of used oil has increased flowability and the binding property of mixture; Antiaging agent then plays good anti-aging effect to the inspection chamber of moulding; Therefore, obtain inspection chamber after handling after these components mix and by predetermined condition, it all is to collect the waste that obtains that its raw material is formed, easily collecting, and the cost of manufacture of Zhi inspection chamber is low therefrom.
Description of drawings
Fig. 1 shows the making method schema of the inspection chamber of the embodiment of the invention 1.
Embodiment
Also by reference to the accompanying drawings the present invention is described in further detail below by specific embodiment.
In the description of the invention, need to prove that unless clear and definite regulation and restriction are arranged in addition, broad understanding should be done in term terms such as " connections ", for example, can be fixedly connected; Can be that dismounting connects; It also can be a connection; It can be direct connection; Can be to connect indirectly by intermediary, can make the connection of two element internals, for the ordinary skill in the art, can particular case understand above-mentioned term concrete implication in the present invention.
Please refer to Fig. 1, the inspection chamber that the embodiment of the invention one provides according to the weight part number scale, comprising: useless mulch film 5-7 part, abandoned mine sand 3-4 part, used oil 0.1-0.3 part, antiaging agent 0.1-0.3 part.
The inspection chamber of the above embodiment of the present invention, in the process of using, the making raw material of inspection chamber adopts the material of being discarded in the daily productive life, is by collecting the discarded mulch film after using as useless mulch film, equally, abandoned mine sand and used oil are all collected waste again and are obtained; Can be the discarded machine oil of having sneaked into the impurity such as metal-powder that moisture, dust, other assorted oil and component wear produce as used oil, also can be go bad gradually, generated the discarded machine oil of organic acid, colloid and bituminous substances; When various components are mixed, because useless mulch film belongs to a kind of of plastics, have plasticity-, when with after abandoned mine sand, used oil and antiaging agent mix, abandoned mine sand is as a kind of packing material, and the framework of whole inspection chamber is finalized the design has important supporting role; And the adding of used oil has increased flowability and the binding property of mixture; Antiaging agent then plays good aging-resistant effect to the inspection chamber of moulding; Therefore, obtain inspection chamber after handling after these components mix and by predetermined condition, it all is to collect the waste that obtains that its raw material is formed, easily collecting, and the cost of manufacture of Zhi inspection chamber is low therefrom.
In addition, in an embodiment of the present invention, the main making raw material of the inspection chamber mulch film that gives up, it is a kind of common white pollution thing, by the utilization of present embodiment, the mulch film of can realizing giving up recycling, useless mulch film has obtained effective processing, when having solved the high problem of fiber glass reinforced plastics inspection well cost of manufacture, also realized effect in energy saving and environmental protection.
Simultaneously, with regard to the making raw material of present embodiment inspection chamber, because plastics and abandoned mine, sand self have good chemical resistance and thermotolerance; Its inspection chamber of making has the result of use same with fiber glass reinforced plastics inspection well, all can substitute the constructional difficulties of traditional " brick well " and the shortcoming that easily seeps water.
Preferably, according to the weight part number scale, comprising: 6 parts of useless mulch films, 3.7 parts in abandoned mine sand, 0.2 part of used oil, 0.1 part of antiaging agent.
In order to make that the inspection chamber of the embodiment of the invention one is better used, be applied to more easily in people's the activity in production, the present invention also provides embodiment two on the basis of above-described embodiment one, embodiment two is further restriction and increases of making on the basis of embodiment one, now does detailed elaboration and explanation:
Optionally, described antiaging agent is coumarone;
Coumarone indene resin generally presents faint yellow liquid to Vandyke brown solid or thickness, it is the resin that is made through condensation by coal tar or heavy benzene or carbolic oil, the yellow coumarone of solid also claims solid coumarone-indene resin, matter is hard and crisp, outward appearance is the spitting image of rosin, coumarone indene resin has thermoplasticity, be mainly used in replacing natural resin or fat rosin, with preparation insulation compound and rust proof paint, the tackiness agent of the tenderizer of rubber (the tackify enhancement is arranged) and pottery, and for ink oil felt processed and imitation leather, coating, composite and the tackiness agent of rubber, tire and rubber item, fields such as printing-ink, the Chang Zuowei material-mix is used; In the present embodiment, can select coumarone as antiaging agent, when coumarone indene resin and other material (as plastics) are composite, present good water tolerance, acid and alkali-resistance, antirust and electrical specification.
Optionally, the particulate state sand of described abandoned mine sand for filtering through the 65-90 eye mesh screen; Consider in the process of making inspection chamber, make the various making raw materials of inspection chamber to mix uniformly, so in the process of concrete operations, abandoned mine sand is the particulate state sand that filters by the 65-90 eye mesh screen.
It is to be noted simultaneously, in an embodiment of the present invention, described abandoned mine sand not merely is defined as ore in sand form, it can also be river sand or dust storm, as long as by after the predetermined screen cloth sieving, the size that satisfies particle gets final product, and, the cost of river sand and dust storm is little, and it is drawn materials easily, can well be applied in the prescription of the embodiment of the invention.
Optionally, described used oil is bavin machine oil or steam turbine oil.
In addition, the selection of used oil also is various, concrete, used oil can be the discarded machine oil of having sneaked into the impurity such as metal-powder of moisture, dust, other assorted oil and component wear generation, also can be to go bad gradually, generated the discarded machine oil of organic acid, colloid and bituminous substances, certainly, it is pointed out that used oil is except the above-mentioned example of lifting, also can comprise some other discarded machinery oil, as discarded lubricated wet goods.
In addition, in order to make the making processes of the inspection chamber that the embodiment of the invention provides can realize smoothly that present embodiment also provides a kind of making method of inspection chamber, comprising:
Step 101: will give up mulch film and abandoned mine sand mix, and obtain mixing raw material;
After mixing, useless mulch film and abandoned mine sand namely obtains mixing raw material; certainly in concrete operation; useless mulch film should carry out removal of impurities; remove its dust that contains and straw; pulverize again afterwards; and abandoned mine sand is the grains of sand through selecting in advance, will obtain mixing raw material after mixing with the useless mulch film after pulverizing with through the grains of sand of selecting in advance.
Step 102: used oil and antiaging agent are added in the described mixing raw material, obtain the raw material first product;
Used oil and the ageing-resistant mixing raw material that joins obtain afterwards, and the raw material first product is used for follow-up synthesis step, preferably, need abundant mixing after used oil and antiaging agent joined mixing raw material, the process of mixing can realize by stirring machine, also can be by manually realizing.
Step 103: described raw material first product is synthetic under 165-250 ℃ of temperature, obtain stand-by raw material;
Synthetic step is the process of 4 kinds of raw materials being closed with fixed attention by predetermined temperature, after synthetic, will form the stand-by raw material of solid-state shape; Preferably, He Cheng temperature is preferably 200 ℃.
Step 104: with the described stand-by raw material mould of packing into, and moulding, obtain finished product.
In the process of concrete operations, the selection of mould is decided according to the shape of the required inspection chamber of people, and different moulds can form difform inspection chamber, and preferred, in the process of moulding, molding time is elected 8-15 minute as; With 10 minutes the bests, the mold pressing of moulding was the 25-35 MPa, was the best with 30 MPas.
The above is the preferred embodiments of the present invention only, is not limited to the present invention, and for a person skilled in the art, the present invention can have various changes and variation.Within the spirit and principles in the present invention all, any modification of doing, be equal to replacement, improvement etc., all should be included within protection scope of the present invention.
Claims (10)
1. an inspection chamber is characterized in that, its preparation raw material comprises according to the parts by weight meter, useless mulch film 5-7 part, abandoned mine sand 3-4 part, used oil 0.1-0.3 part and antiaging agent 0.1-0.3 part.
2. inspection chamber according to claim 1 is characterized in that, its preparation raw material comprises, according to the parts by weight meter, comprising: 6 parts of useless mulch films, 3.7 parts in abandoned mine sand, 0.2 part of used oil, 0.1 part of antiaging agent.
3. inspection chamber according to claim 2 is characterized in that, described antiaging agent is coumarone.
4. inspection chamber according to claim 3 is characterized in that, the particulate state sand of described abandoned mine sand for filtering through the 65-90 eye mesh screen.
5. inspection chamber according to claim 4 is characterized in that, described used oil is bavin machine oil or steam turbine oil.
6. the production method according to the described inspection chamber of claim 1-5 is characterized in that, comprising:
To give up mulch film and abandoned mine sand mixes, and obtains mixing raw material;
Used oil and antiaging agent are added in the described mixing raw material, obtain the raw material first product;
Described raw material first product is synthetic under 180-220 ℃ of temperature, obtain stand-by raw material;
With the described stand-by raw material mould of packing into, and moulding, finished product obtained.
7. the production method of inspection chamber according to claim 6 is characterized in that, in described will give up mulch film and the mixing of abandoned mine sand, obtains also comprising before the step of mixing raw material:
To described useless mulch film removal of impurities, described removal of impurities comprises dust and the straw of removing in the described useless mulch film;
Useless mulch film after the described removal of impurities is pulverized.
8. the production method of inspection chamber according to claim 7 is characterized in that, described that described raw material first product is synthetic under 165-250 ℃ of temperature, obtains in the step of stand-by raw material;
Described synthesis temperature is 200 ℃.
9. the production method of inspection chamber according to claim 8 is characterized in that, with the described stand-by raw material mould of packing into, and moulding obtains in the step of finished product described:
The pressure of described moulding is the 25-35 MPa.
10. the production method of inspection chamber according to claim 9 is characterized in that, the time of described moulding is: 8-15 minute.