CN103159979A - Abs/ps废旧塑料的分离回收方法 - Google Patents

Abs/ps废旧塑料的分离回收方法 Download PDF

Info

Publication number
CN103159979A
CN103159979A CN2013101225169A CN201310122516A CN103159979A CN 103159979 A CN103159979 A CN 103159979A CN 2013101225169 A CN2013101225169 A CN 2013101225169A CN 201310122516 A CN201310122516 A CN 201310122516A CN 103159979 A CN103159979 A CN 103159979A
Authority
CN
China
Prior art keywords
abs
plastic
solvent
plastics
drying
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN2013101225169A
Other languages
English (en)
Inventor
王重庆
王晖
符剑刚
覃丽芝
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Central South University
Original Assignee
Central South University
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Central South University filed Critical Central South University
Priority to CN2013101225169A priority Critical patent/CN103159979A/zh
Publication of CN103159979A publication Critical patent/CN103159979A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种ABS/PS废旧塑料的分离回收方法，包括：将ABS/PS混合塑料破碎到4～40mm，加入到溶剂中，ABS/PS混合塑料与溶剂比为8～20g/ml，其中溶剂为二甲苯或者二硫化碳；在10～90℃搅拌溶解150～280分钟；对溶液进行过滤，过滤出的滤渣干燥，得ABS塑料；滤液在30～60℃温度下蒸发，将析出的溶质干燥得到PS塑料。采用上述方法可以简单高效地分离回收ABS/PS废旧塑料，ABS的回收率为92.7～95.4%，PS的回收率为91.2～95.4%。

Description

ABS/PS废旧塑料的分离回收方法
技术领域
本发明涉及一种ABS/PS废旧塑料的分离回收方法。
背景技术
由于塑料的大量生产、消费与较短的使用周期使得塑料废弃物的数量急剧增加。塑料的大量废弃不仅造成资源的巨大浪费，也给环境带来极大危害：污染土壤和海洋、焚烧处理产生大量有物质。在能源问题日益突出、环境问题日益严峻的新形势下，加强废旧塑料回收利用的研究引起了各国政府的高度重视。废旧塑料的回收包括三个阶段：收集、分选以及循环利用，现阶段制约废旧塑料回收的瓶颈环节在于塑料的分选。
丙烯腈-丁二烯-苯乙烯（ABS）树脂是五大合成树脂之一，由于其优良的性质广泛应用于机械、汽车、电子电器、仪器仪表、纺织和建筑等工业领域，是一种用途极广的热塑性工程塑料。聚苯乙烯（PS）具有良好的透光性被广泛应用于光学工业中，抗冲击PS的力学性能较好用于制作机械零件和部件。两种塑料有时应用同一领域，例如汽车、电冰箱等，两者的废旧塑料容易混杂到一起，由于两者物理性质相近，很难较好地分离。
文献报道废旧塑料分选的技术有很多：浮沉分选、风力分选、水力旋流器分选、浮选、选择性溶解分离等。由于不同种类的塑料具有相似的物理性质，这些分选技术对废旧塑料的分离适用性较差，很难达到高效分离的效果。例如，浮沉分选、风力分选和水力旋流器分选都是基于不同塑料的密度差异进行分离，由于塑料具有相近的密度，这些方法有很大局限性；塑料具有相似的表面性质，对塑料进行直接浮选分离很难有效。
发明内容
本发明的目的是提供一种能简单、高效地分离回收ABS/PS废旧塑料的方法。
为了达到上述目的，本发明包括：
①将ABS/PS混合塑料破碎到4～40mm，加入到溶剂中，ABS/PS混合塑料与溶剂比为8～20g/ml，其中溶剂为二甲苯或者二硫化碳；
②在10～90℃搅拌溶解150～280分钟；
③对溶液进行过滤，过滤出的滤渣干燥，得ABS塑料；滤液在30～60℃温度下蒸发，将析出的溶质干燥得到PS塑料。
优选地，步骤③中所述过滤是通过100～400目筛网。
采用上述方法可以简单高效地分离回收ABS/PS废旧塑料，ABS的回收率为92.7～95.4%，PS的回收率为91.2～95.4%。
具体实施方式
实施例一
将粒度4mm的ABS/PS混合塑料加入到二甲苯溶剂中，混合塑料与溶剂比为20g/ml。在90℃温度下，机械搅拌280min。对溶液用400目筛网过滤，过滤出的滤渣干燥，得ABS塑料；滤液在30℃温度下蒸发，将析出的溶质干燥得到PS塑料，蒸发出的二甲苯溶剂循环使用。ABS的回收率为92.7%，PS的回收率为90.8%。
实施例二
将粒度40mm的ABS/PS混合塑料加入到二甲苯溶剂中，混合塑料与溶剂比为8g/ml。在10℃温度下，机械搅拌150min。对溶液用100目筛网过滤，过滤出的滤渣干燥，得ABS塑料；滤液在60℃温度下蒸发，将析出的溶质干燥得到PS塑料，蒸发出的二甲苯溶剂循环使用。ABS的回收率为94.2%，PS的回收率为92.7%。
实施例三
将粒度25mm的ABS/PS混合塑料加入到二甲苯溶剂中，混合塑料与溶剂比为12g/ml。在30℃温度下，机械搅拌200min。对溶液用300目筛网过滤，过滤出的滤渣干燥，得ABS塑料；滤液在60℃温度下蒸发，将析出的溶质干燥得到PS塑料，蒸发出的二甲苯溶剂循环使用。ABS的回收率为93.8%，PS的回收率为93.6%。
实施例四
将粒度35mm的ABS/PS混合塑料加入到二硫化碳溶剂中，混合塑料与溶剂比为15g/ml。在50℃温度下，机械搅拌180min对溶液用200目筛网过滤，过滤出的滤渣干燥，得ABS塑料；滤液在40℃温度下蒸发，将析出的溶质干燥得到PS塑料，蒸发出的二硫化碳溶剂循环使用。ABS的回收率为94.6%，PS的回收率为91.2%。
实施例四
将粒度25mm的ABS/PS混合塑料加入到二硫化碳溶剂中，混合塑料与溶剂比为12g/ml。在40℃温度下，机械搅拌200min。对溶液用400目筛网过滤，过滤出的滤渣干燥，得ABS塑料；滤液在40℃温度下蒸发，将析出的溶质干燥得到PS塑料，蒸发出的二硫化碳溶剂循环使用。ABS的回收率为95.4%，PS的回收率为95.4%。

Claims (2)

1.一种ABS/PS废旧塑料的分离回收方法，其特征是，包括：
① 将ABS/PS混合塑料破碎到4～40mm，加入到溶剂中，ABS/PS混合塑料与溶剂比为8～20g/ml，其中溶剂为二甲苯或者二硫化碳；
②在10～90℃搅拌溶解150～280分钟；
③对溶液进行过滤，过滤出的滤渣干燥，得ABS塑料；滤液在30～60℃温度下蒸发，将析出的溶质干燥得到PS塑料。
2.根据权利要求1的ABS/PS废旧塑料的分离回收方法，其特征是，步骤③中所述过滤是通过100～400目筛网。
CN2013101225169A 2013-04-10 2013-04-10 Abs/ps废旧塑料的分离回收方法 Pending CN103159979A (zh)