CN103159409A - Method for generating protective layer for etching forming of toughened glass cover plate - Google Patents
Method for generating protective layer for etching forming of toughened glass cover plate Download PDFInfo
- Publication number
- CN103159409A CN103159409A CN2013101006265A CN201310100626A CN103159409A CN 103159409 A CN103159409 A CN 103159409A CN 2013101006265 A CN2013101006265 A CN 2013101006265A CN 201310100626 A CN201310100626 A CN 201310100626A CN 103159409 A CN103159409 A CN 103159409A
- Authority
- CN
- China
- Prior art keywords
- protective layer
- hydrofluoric acid
- glass cover
- forming
- cover plate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for generating a protective layer for etching forming of a toughened glass cover plate. The protective layer generation method comprises the following steps: grinding and cutting PVC (polyvinyl chloride) films to obtain blanks; bonding the blanks on the two surfaces of substrate glass; etching with hydrofluoric acid; and rinsing, edging, polishing, and withdrawing to obtain an etching forming intermediate product. According to the method, touch screen glass cover plates can be simultaneously processed in large quantity, the processing efficiency and the nondefective rate are increased, the equipment investment cost is saved, the material consumption and the production cost are obviously reduced, obvious economic benefits can be achieved, and the technology gets ahead of the same industry and can form an enterprise standard. The hydrofluoric acid chemical forming and the protective layer generation involved in the invention belong to processing techniques which can be widely used in forming of capacitive touch screen glass cover plates.
Description
Technical field
The present invention relates to the forming technique of toughened glass cover plate (Cove rlens), particularly relate to the protective layer generation method of the hydrofluoric acid etch moulding of a kind of toughened glass cover plate (Cover lens).
Background technology
At present, the same industry all adopts physical method both at home and abroad, namely uses numerical control (CNC) cutting, punching, edging and polishing, processes the glass cover-plate of capacitive touch screen.Its defective is: the processing work efficiency of the machines such as numerically-controlled machine low (CNC of two statures can only process the Cove-lens200 sheet left and right of 3.5 inches every day), facility investment and factory building area occupied are all larger, cause depreciation, maintaining expense and financial expense all very high, and then cause production cost high.Work efficiency is high to adopt hydrofluoric acid etch moulding process processing Cover l ens, facility investment and factory building area occupied little (equal production capacity only is equivalent to the former 15% and 50% left and right), but thereby the decrease production cost, enhance productivity.Adopting the key technical problem of hydrofluoric acid etch moulding process processing capacitance plate glass cover-plate is the protective layer Generating Problems of substrate glass.
Summary of the invention
The purpose of the embodiment of the present invention is to provide a kind of protective layer generation method for toughened glass cover plate etch-forming, the problem that the protective layer when being intended to solve target converted products (abbreviation substrate glass) hydrofluoric acid etch moulding generates.
The embodiment of the present invention is achieved in that a kind of protective layer generation method for toughened glass cover plate etch-forming, and this protective layer generation method comprises the following steps:
PVC film mill is cut blank mark;
The blank mark of substrate glass double faced adhesive;
Hydrofluoric acid etch;
Flushing, edging, polishing, pull out sheet and namely get the etch-forming intermediates.
Further, select a kind of PVC self-adhesive plastic film material of hydrofluoric acid resistant to prepare required protective film, be processed into the shape consistent with target product (being called for short blank mark), and it is pasted two surfaces up and down of substrate glass symmetrically; Thereby the efficient part of substrate glass is protected, and invalid target is exposed in hydrofluoric acid, makes its corrosion that is subject to hydrofluoric acid and attenuation, change is broken and even eroded fully, finally obtains the intermediates consistent with the target product shape.
Further, through simultaneous test screening repeatedly, select the PVC self-adhesive plastic film as the protective film material, utilize punch press with cutting die, the PVC processing film to be become the blank mark consistent with target product Cover lens, with pneumatic chip mounter, two identical blank marks are pasted symmetrically two surfaces up and down of substrate glass; And then place it in the hydrofluoric acid of 5 to-5 ℃ of concentration 45-70%, temperature and soaked about 60 minutes; the efficient part of substrate glass is under blank target protection; invalid target is exposed to for some time in acid solution and is corroded; take out and rinse the intermediates that namely get desired shape; again to middle product carry out edging, polishing, pull out sheet, cleaning, tempering and silk-screen overlay film, namely get at last required Cover lens.
Further; select the PVC self-adhesive plastic film as protective layer; with cutting die, PVC self-adhesive plastic film protective layer is processed into the blank mark consistent with the glass cover-plate target product with punch press; two identical blank marks are placed in symmetrically two surfaces up and down of base plate glass; use the pneumatic motor paster; the cover plate efficient part is under protective layer, and invalid target is as exposures such as four limits, circular hole and square holes.Paster glass is placed in the hydrofluoric acid of 45-70% concentration, soaks 60min, exposure portion is eroded fully, takes out paster glass, washs 1min with clear water.
further, employing thickness is 0.25mm, width is the PVC film of 236mm, process the blank mark of 200PCS with punch press and cutting die, with the pneumatic motor paster, two identical blank marks are pasted on symmetrically two surfaces up and down of 100PCS substrate glass, post in blank target substrate glass (being called for short paster glass) the PVC mould bases of packing into above-mentioned again, mould bases being placed in again and filling concentration is 75%, temperature is in the acid tank of hydrofluoric acid solution of-5 ℃, take out again mould bases after soaking 45min from acid tank, wash the 1min left and right with flushing with clean water, again paster glass is pulled down from mould bases, carry out again edging, polishing, plectrum, clean, tempering, silk-screen and overlay film, namely get required toughened glass cover plate.
Positively effect of the present invention: select the PVC self-adhesive plastic film as protective layer and be processed into the blank mark consistent with glass cover-plate target product shape; the method that is used for the hydrofluoric acid etch moulding; energy is disposable editing objective product (Cove-lens) in batch simultaneously; the processing work efficiency is more much higher than CNC moulding; therefore can significantly save facility investment and factory building area occupied; thereby significantly reduce depreciation, maintaining expense and financial expense, and then reduce production costs more than 20%.
Description of drawings
Fig. 1 is the schema of the protective layer generation method that is used for toughened glass cover plate etch-forming that provides of the embodiment of the present invention
Embodiment
In order to make purpose of the present invention, technical scheme and advantage clearer, below in conjunction with drawings and Examples, the present invention is further elaborated.Should be appreciated that specific embodiment described herein only in order to explain the present invention, is not intended to limit the present invention.
The present invention adopts hydrofluoric acid chemistry forming processes condenser type and resistive touch screen glass cover-plate first, has replaced the physical refining processes that working (machining) efficiency is low, good article rate is not high, the investment large, the maintaining expense is high.Its feature comprises that the hydrofluoric acid chemical process moulding of glass cover-plate and protective layer material are selected, shape processing and with the paster process of substrate glass, make that the cover plate efficient part is protected and invalid target is eroded fast.
As shown in Figure 1, the embodiment of the present invention is achieved in that a kind of protective layer generation method for toughened glass cover plate etch-forming, and this protective layer generation method comprises the following steps:
PVC film mill is cut blank mark;
The blank mark of substrate glass double faced adhesive;
Hydrofluoric acid etch;
Flushing, edging, polishing, pull out sheet and namely get the etch-forming intermediates.
In embodiments of the present invention; with punch press and cutting die, PET self-adhesive plastic film protective layer is processed into blank mark with the consistent shape of glass cover-plate target product; with pneumatic chip mounter, two identical blank marks are pasted on symmetrically two surfaces up and down of substrate glass; make its efficient part under protective layer, invalid target (four limits, circular hole and square hole etc.) exposes.With above-mentioned post blank target in batches glass cover-plate be placed in hydrofluoric acid, soak time 60min takes out the paster glass after acidleach, washs 1min with clear water, namely gets the just intermediates of one-step forming.
The present invention is further illustrated below in conjunction with specific embodiment.
embodiment 1: employing thickness is 0.25mm, width is the PVC film of 236mm, process the blank mark of 200PCS (long 190mm * wide 116mm) with punch press and cutting die, with the pneumatic motor paster, two identical blank marks are pasted on symmetrically two surfaces up and down of 100PCS substrate glass (long 191mm * wide 117mm * thick 0.7mm), again above-mentioned paster glass is packed in the etching basket, the etching basket being placed in again and filling concentration is 75%, temperature is in the acid tank of hydrofluoric acid solution of-5 ℃, take out again the etching basket after soaking 45min from acid tank, wash the 1min left and right with flushing with clean water, again paster glass is taken out from the etching basket, rinse, edging, polishing, plectrum namely gets the etch-forming intermediates.Namely get toughened glass cover plate (Cover-lens) by cleaning, tempering, silk-screen, overlay film again.
The above is only preferred embodiment of the present invention, not in order to limiting the present invention, all any modifications of doing within the spirit and principles in the present invention, is equal to and replaces and improvement etc., within all should being included in protection scope of the present invention.
Claims (5)
1. a protective layer generation method that is used for toughened glass cover plate etch-forming, is characterized in that, this protective layer generation method comprises the following steps:
PVC film mill is cut blank mark;
The blank mark of substrate glass double faced adhesive;
Hydrofluoric acid etch;
Flushing, edging, polishing, pull out sheet and namely get the etch-forming intermediates.
2. the protective layer generation method for toughened glass cover plate etch-forming as claimed in claim 1, it is characterized in that, select a kind of PVC self-adhesive plastic film material of hydrofluoric acid resistant to prepare required protective film, be processed into the shape consistent with target product, and it is pasted two surfaces up and down of substrate glass symmetrically; Thereby the efficient part of substrate glass is protected, and invalid target is exposed in hydrofluoric acid, makes its corrosion that is subject to hydrofluoric acid and attenuation, change is broken and even eroded fully, finally obtains the intermediates consistent with the target product shape.
3. the protective layer generation method for toughened glass cover plate etch-forming as claimed in claim 1, it is characterized in that, through simultaneous test screening repeatedly, select the PVC self-adhesive plastic film as the protective film material, utilize punch press with cutting die, the PVC processing film to be become the shape consistent with target product Cover lens, use pneumatic chip mounter, two identical blank marks are pasted symmetrically two surfaces up and down of substrate glass; And then place it in the hydrofluoric acid of 5 to-5 ℃ of concentration 45-70%, temperature and soaked about 60 minutes; the efficient part of substrate glass is under blank target protection; invalid target is exposed to for some time in acid solution and is corroded; take out and rinse the intermediates that namely get desired shape; again to middle product carry out edging, polishing, pull out sheet, cleaning, tempering and silk-screen overlay film, namely get at last required Cover lens.
4. the protective layer generation method for toughened glass cover plate etch-forming as claimed in claim 1, it is characterized in that, select the PVC self-adhesive plastic film as protective layer, with cutting die, PVC self-adhesive plastic film protective layer is processed into the shape consistent with the glass cover-plate target product with punch press, with pneumatic chip mounter, two identical blank marks are pasted on symmetrically two surfaces up and down of substrate glass, the substrate glass efficient part is under protective layer, invalid target is as four limits, the exposure such as circular hole and square hole, to post blank target substrate glass and be placed in the hydrofluoric acid of 45-70% concentration, soak 60min, exposure portion is eroded fully, take out paster glass, wash 1min with clear water.
5. the protective layer generation method for toughened glass cover plate etch-forming as claimed in claim 1, it is characterized in that, employing thickness is 0.25mm, width is the PVC film of 236mm, process the blank mark of 200PCS with punch press and cutting die, with the pneumatic motor paster, two identical blank marks are pasted on symmetrically two surfaces up and down of 100PCS substrate glass, again paster glass is packed in the PVC mould bases, mould bases being placed in again and filling concentration is 75%, temperature is in the acid tank of hydrofluoric acid solution of-5 ℃, take out again mould bases after soaking 45min from acid tank, wash the 1min left and right with flushing with clean water, again paster glass is pulled down from mould bases, carry out again edging, polishing, plectrum, clean, tempering, silk-screen and overlay film, namely get required toughened glass cover plate.