CN103157864A - 铝合金水、气分离器真空钎焊工艺 - Google Patents

铝合金水、气分离器真空钎焊工艺 Download PDF

Info

Publication number
CN103157864A
CN103157864A CN2011104101953A CN201110410195A CN103157864A CN 103157864 A CN103157864 A CN 103157864A CN 2011104101953 A CN2011104101953 A CN 2011104101953A CN 201110410195 A CN201110410195 A CN 201110410195A CN 103157864 A CN103157864 A CN 103157864A
Authority
CN
China
Prior art keywords
vacuum
minutes
brazing process
temperature
drying oven
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2011104101953A
Other languages
English (en)
Other versions
CN103157864B (zh
Inventor
涂勇
张剑波
姜国建
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guizhou Yonghong Aviation Machinery Co Ltd
Original Assignee
Guizhou Yonghong Aviation Machinery Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Guizhou Yonghong Aviation Machinery Co Ltd filed Critical Guizhou Yonghong Aviation Machinery Co Ltd
Priority to CN201110410195.3A priority Critical patent/CN103157864B/zh
Publication of CN103157864A publication Critical patent/CN103157864A/zh
Application granted granted Critical
Publication of CN103157864B publication Critical patent/CN103157864B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种铝合金水、气分离器真空钎焊工艺，属于真空钎焊工艺。其方案是：将工件放入真空炉中，在20-25min内加热至300-400℃，保温60-80min，控制真空度＞8×10-3Pa；在15-20min内升温至560-570℃，保温20-40min，控制真空度＞4×10-3Pa；在10-15min内升温至600-605℃，保温10-20min，控制真空度＞3×10-3Pa；在10-15min内降温至595-598℃，保温10-15min，断电降温。本发明缩短了钎焊工艺时间、提高了效率，消除了翅片容易变形，焊缝易溶蚀过烧、饱满度差等缺陷；是一种焊接铝合金水气分离器的方法。

Description

铝合金水、气分离器真空钎焊工艺
技术领域：本发明涉及一种铝合金真空钎焊工艺，尤其涉及一种铝合金水气分离器真空钎焊工艺。
背景技术：水气分离器是将空压机中的压缩空气进行水、气分离的一个重要部件。水气分离器具有体积小、结构复杂、焊接面分布广、尺寸进度要求高、加工难度大等特点，一直采用Nocolok钎焊工艺生产。该工艺方法为有钎剂钎焊，其缺点是增加喷涂钎剂和焊后处理工序，环保性差，钎焊质量不稳定。虽然近年来真空钎焊工艺方法在铝合金板翅式散热器制造中逐渐得到了广泛应用，但产品结构多为平面型、焊缝方向单一；而铝合金水气分离器铝结构复杂，产品焊接面多、分布广、存在多方向焊接部位，真空钎焊过程中翅片容易变形，因此很难生产出符合要求的水气分离器产品。
发明内容：针对现有技术中存在的上述缺陷，本发明旨在提供一种通过改变焊接工艺参数来大幅度提高产品钎焊质量的铝合金水、气分离器真空钎焊工艺。
为了实现上述目的，本发明采用以下技术方案：它包括真空钎焊；具体工艺参数如下：
1)将工件放入真空炉中，在20-25min内将真空炉加热至300-400℃，保温60-80min，控制真空度＞8×10-3Pa；
2)在15-20min内将真空炉升温至560-570℃，保温20-40min，控制真空度＞4×10-3Pa；
3)在10-15min内将真空炉升温至600-605℃，保温10-20min，控制真空度＞3×10-3Pa；
4)在10-15min内将真空炉降温至595-598℃，保温10-15min，然后断电；直至工件温度降至590-600℃。
与现有技术比较，本发明由于采用了上述技术方案，在常规真空钎焊工艺的基础上省略了180-200℃的烘干工序和480-530℃的加热段工序，因此不仅缩短了整个钎焊工艺过程的时间、提高了效率，而且也克服了翅片在常规真空钎焊工艺保温时间下容易变形，焊缝常常出现溶蚀过烧现象、难以达到饱满要求的缺陷；另外，600-605℃段的保温时间缩短为10-20min，既减少了高温段的焊接时间、又进一步提高了焊接效率。采用本发明工艺能够得到外观合格、焊缝微观组织和焊缝质量良好的产品。
从实际情况应用的情况来看，采用本发明工艺生产的铝合金水气分离器，其焊缝的钎着率得到了明显提高。以下是对采用本发明工艺生产的铝合金水气分离器(四批，共400套)在表1试验条件下进行的试验数据。
表1：试验条件
  温度   升温时间(min)   保温时间(min)   真空度(Pa)
  300-400℃   20   60-80   (9-8)×10-3
  560-570℃   15   10-20   (4-5)×10-3
  600-605℃   15   10-20   (5-3)×10-3
  595-598℃   10min(降温)   10-15   3×10-3
表2：产品泄漏试验
  批次   产品数量(套)   着钎合格数   布合格数   着钎合格率％
  1   30   28   2   93
  2   50   45   5   90
  3   20   19   1   95
  4   66   60   6   91
从上述试验结果可知，本发明工艺在完全满足产品各项性能指标的前提下，将产品的着钎合格率提高到了90％以上。
附图说明：
图1是本发明的温度曲线图。
具体实施方式：下面结合附图和具体的实施例对本发明作进一步说明：
将零件按常规方法清洗干净，将清洗好的零件放入恒温恒湿的干燥间进行成型装配、校正，然后按图1所示的工艺参数进行真空钎焊：
1)将工件竖立放入真空炉中，在20-25min内将真空炉加热至300-400℃，保温60-80min，控制真空度＞8×10-3Pa；
2)在15-20min内将真空炉升温至560-570℃，保温20-40min，控制真空度＞4×10-3Pa；
3)在10-15min内将真空炉升温至600-605℃，保温10-20min，控制真空度＞3×10-3Pa；
4)在10-15min内将真空炉降温至595-598℃，保温10-15min；然后断电，直至工件温度降至590-600℃，即可出炉。
在上述实施例中，将工件按竖立方式送入炉中的目的是使钎料熔化后在重力影响增强钎料流动性，从而保证钎料铺展到各个焊接处，并且有利于多余的钎料溢出，确保焊件外观质量。

Claims (1)

1.一种铝合金水、气分离器真空钎焊工艺，包括真空钎焊；其特征在于具体工艺参数如下：
1)将工件竖立放入真空炉中，在20-25min内将真空炉加热至300-400℃，保温60-80min，控制真空度＞8×10-3Pa；
2)在15-20min内将真空炉升温至560-570℃，保温20-40min，控制真空度＞4×10-3Pa；
3)在10-15min内将真空炉升温至600-605℃，保温10-20min，控制真空度＞3×10-3Pa；
4)在10-15min内将真空炉降温至595-598℃，保温10-15min，然后断电；直至工件温度降至590-600℃。
CN201110410195.3A 2011-12-12 2011-12-12 铝合金水、气分离器真空钎焊工艺 Active CN103157864B (zh)