CN103131358B - 一种应用于服装业代替线迹缝纫的反应型自催化粘合剂及其制备方法 - Google Patents

一种应用于服装业代替线迹缝纫的反应型自催化粘合剂及其制备方法 Download PDF

Info

Publication number
CN103131358B
CN103131358B CN201310045026.3A CN201310045026A CN103131358B CN 103131358 B CN103131358 B CN 103131358B CN 201310045026 A CN201310045026 A CN 201310045026A CN 103131358 B CN103131358 B CN 103131358B
Authority
CN
China
Prior art keywords
autocatalysis
tackiness agent
response type
stitching
rag trade
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
CN201310045026.3A
Other languages
English (en)
Other versions
CN103131358A (zh
Inventor
张瑞表
庄碧双
张翔
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
QUANZHOU DELI CHEMICAL CO Ltd
Original Assignee
QUANZHOU DELI CHEMICAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by QUANZHOU DELI CHEMICAL CO Ltd filed Critical QUANZHOU DELI CHEMICAL CO Ltd
Priority to CN201310045026.3A priority Critical patent/CN103131358B/zh
Publication of CN103131358A publication Critical patent/CN103131358A/zh
Application granted granted Critical
Publication of CN103131358B publication Critical patent/CN103131358B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种服装业代替线迹缝纫的反应型自催化粘合剂及其制备方法。所述反应型自催化粘合剂由乙烯基硅烷偶联剂，丙烯酸类和丙烯酸酯类单体的无规共聚物而成。本发明利用丙烯酸类的酸性可以催化乙烯基硅烷偶联剂与织物的羟基反应，快速形成稳定牢固的粘合作用。丙烯酸类和丙烯酸酯类可以提高跟织物的内聚力，增加相容性和粘合力。本发明采用无规共聚技术，制作方法，制作工艺简单，制备出一种粘合速度快，粘合牢固度高的服装业代替线迹缝纫的反应型自催化粘合剂。所述粘合剂自催化粘合，粘合速度快，粘结牢固，有优良的柔软性，透气性，无甲醛等有害气体，安全环保，无污染。

Description

一种应用于服装业代替线迹缝纫的反应型自催化粘合剂及其制备方法
技术领域
本发明属于高分子合成领域，特别涉及一种代替服装业线迹缝纫的反应型自催化粘合剂的制备方法，本反应型自催化粘合剂是由乙烯基硅烷偶联剂，丙烯酸类及丙烯酸酯类的无规共聚制得。 
背景技术
现今服装制造业，大都是使用线迹缝纫机，使用一种或者多种线迹一层或者多层布料，虽然现今的线迹缝纫机已经由手动到机械，由机械到电动，再发展到数字化，但是缝纫的原理没有多大变化，尽管缝纫机发展到了数字化，甚至可以变频工作，缝出的线迹美观整齐，平整牢固，缝纫速度也大有提高，但是不管是链式线迹还是锁式线迹都是缝纫机线迹的基本形式，都摆脱不了线迹的束缚，随着纺织科技的发展和人们对服装舒适和美观的追求，寻找新的，更舒适，更美观，更快捷的缝纫方法就非常有必要，一些企业已经在做各种尝试，未来缝纫方式一定是多样化，服装的功能款式也符合人们更舒适，更美观的追求，制造效率也会大有提高，其中就有企业使用代替缝纫线迹的粘合带。但是由于粘合带不太适合复杂形状的粘合，所以现在很多企业在探索一种新的粘合快速，稳定牢固的缝纫粘合剂。 
中国专利公开号CN102182080A介绍了一种涂料印花粘合剂及其合成方法：该发明利用硅丙共聚物乳液、水性聚氨酯、液体橡胶和乳化剂等合成。利用聚丙烯酸良好的成膜性，有机硅良好的透气性和液体橡胶的高弹性，该粘合剂既具有优良的手感，又具有优良的色牢固度，有害物质排放量低。中国专利公开号CN101784628A发明了一种用于衣服的粘合带，能够减少衣服的缝制部位并利用粘合带制成衣服的粘合带，其极力抑制了横向拉伸，且在纵向上具有伸缩性能。热融合弹力丝为热融合性聚氨酯弹力丝、弹力膜为聚氨酯膜。 
虽然有很多用于服装的粘合剂，但是大多数都是用于涂料印花的粘合剂，偏向粘结布料与染料，用于无缝缝制服装的粘合剂很少，也有在织物之间放粘性薄膜，通过热压将织物粘合，这种粘合带的复杂形状在粘合时也很有不便。用于服装业代替线迹缝纫的反应型自催化快速粘合的粘合剂更是未见报道。 
本发明旨在提供一种新的能代替服装业线迹缝纫的自催化粘合剂及其制备方法。这种粘合剂，粘合强度高，柔韧性好，透气性优良，环境友好，使用方便，自催化，粘合速度快。制备方法，生产工艺简单，各种单体均有市售，市场前景非常广阔。 
发明内容
本发明根据需求，针对代替服装业线迹缝纫的粘合剂产品稀少，产品性能不稳定，提供一种新的反应型自催化粘合剂，其优点在于粘合速度快，粘合强度高，粘合性能稳定，柔韧性好，透气性优良，环境友好，使用方便可代替服装业缝纫线迹的自催化粘合剂及其制备方法。 
一种可代替服装业线迹缝纫的反应型自催化粘合剂，所述反应型自催化粘合剂的份数均按重量分数。 
所述的反应型自催化粘合剂合成方法如下 
按一定的配比量取无水乙醇100ml、乙烯基硅烷偶联剂（20-50份）、丙烯酸类化合物（15-25份）、丙烯酸酯类化合物（20-40份）、引发剂（AIBN）（0.1-1份），加入配有冷凝管的两口烧瓶中，氮气保护下，在室温按一定的搅拌速度(100r/min)搅拌10-40分钟，然后慢慢升温到一定温度（40-80℃），回流反应2-5个小时，经提纯，最终得到自催化粘合剂。 
所述乙烯基硅烷偶联剂包含甲基乙烯基二乙氧基硅烷，乙烯基三乙氧基硅烷，乙烯基二甲基乙氧基硅烷等带乙烯基的硅烷偶联剂。 
所述丙烯酸类化合物，包括丙烯酸，异丁烯酸，反式丁烯酸，烯丙基乙酸等带乙烯基的有机酸。 
所述丙烯酸酯类化合物，包括丙烯酸丁酯，丙烯酸乙酯，丙烯酸甲酯，丙烯酸异辛酯，甲基丙烯酸甲酯。 
本发明的优点 
（1）本发明采取无规共聚，制作方法，制作工艺简单。 
（2）具有自催化性能，粘合速度快，聚合物中丙烯酸的酸性可以催化乙烯基硅烷偶联剂与织物上羟基的反应，反应速度快。 
（3）自催化粘合剂粘合强度高，一般粘合剂都是靠内聚力使物体粘合在一起，本发明自催化粘合剂不仅有强大的内聚力，更是具有稳固的化学键，粘合牢固度高，性能稳定。 
（4）具有优良的透气性和柔软性。 
（5）本发明无甲醛等有害物质，安全环保，物污染。 
本发明是一种代替服装业线迹缝纫的反应型自催化粘合剂及其制备方法，应用范围较广，因此通过实施案例对本发明作进一步详细说明。 
具体实施方式
下面通过具体实施例进一步说明。 
实施例1： 
（1）自催化粘合剂的合成：无水乙醇100ml，甲基乙烯基二乙氧基硅烷20g，丙烯酸25g，丙烯酸丁酯40g，偶氮二异丁氰0.1g，在室温下高速搅拌10分钟，搅拌速度为500转/min，然后慢慢升温，在温度为40度反应5个小时，得到预产物。 
（2）将混合物在室温下，抽真空脱除全部乙醇，加入丙酮调至需要粘度，制得反应型自催化粘合剂。 
实施例2 
（1）无水乙醇100ml，甲基乙烯基二乙氧基硅烷50g，异丁烯酸15g，丙烯酸乙酯20g，偶氮二异丁氰1g，在室温下高速搅拌20分钟，搅拌速度为500r/min，然后慢慢升温，在温度为80℃反应2个小时，得到预产物。 
（2）将混合物在室温下，抽真空脱除全部乙醇，加入丙酮调至需要粘度，制得反应型自催化粘合剂。 
实施例3 
（1）无水乙醇100ml，甲基乙烯基二乙氧基硅烷35g，反式丁烯酸20g，丙烯酸甲酯30g，偶氮二异丁氰0.5g，在室温下高速搅拌30分钟，搅拌速度为500r/min，然后慢慢升温，在温度为60℃的条件下反应4个小时，得到预产物。 
（2）将混合物在室温下，抽真空脱除全部乙醇，加入丙酮调至需要粘度，制得反应型自催化粘合剂。 
实施例4 
（1）无水乙醇100ml，乙烯基三乙氧基硅烷35g，烯丙基乙酸20g，丙烯酸异辛酯30g，偶氮二异丁氰0.5g，在室温下高速搅拌40分钟，搅拌速度为500r/min，然后慢慢升温，在温度为70℃的条件下反应3个小时，得到预产物。 
（2）将混合物在室温下，抽真空脱除全部乙醇，加入丙酮调至需要粘度，制得反应型自催化粘合剂。 
实施例5 
（1）无水乙醇100ml，乙烯基二甲基乙氧基硅烷35g，丙烯酸20g，甲基丙烯酸甲酯30g，偶氮二异丁氰0.5g，在室温下高速搅拌20分钟，搅拌速度为500r/min，然后慢慢升温，在温度为50℃的条件下反应4.5个小时，得到预产物。 
（2）将混合物在室温下，抽真空脱除全部乙醇，加入丙酮调至需要粘度，制得反应型自催化粘合剂。 

Claims (3)

1.一种可代替服装业线迹缝纫的反应型自催化粘合剂，其特征在于量取无水乙醇100ml、乙烯基硅烷偶联剂20-50克、丙烯酸类化合物15-25克、丙烯酸酯类化合物20-40克、引发剂AIBN0.1-1克，加入配有冷凝管的两口烧瓶中，氮气保护下，在室温按一定的搅拌速度100r/min搅拌10-40分钟，然后慢慢升温到一定温度40-80℃，回流反应2-5个小时，经提纯，最终得到自催化粘合剂。 
2.根据权利要求1所述的一种可代替服装业线迹缝纫的反应型自催化粘合剂，其特征在于所述乙烯基硅烷偶联剂是甲基乙烯基二乙氧基硅烷，乙烯基三乙氧基硅烷，乙烯基二甲基乙氧基硅烷或其它带乙烯基的硅烷偶联剂。 
3.根据权利要求1所述的一种可代替服装业线迹缝纫的反应型自催化粘合剂，其特征在于所述丙烯酸酯类化合物为丙烯酸丁酯，丙烯酸乙酯，丙烯酸甲酯，丙烯酸异辛酯，甲基丙烯酸甲酯的一种。 
CN201310045026.3A 2013-02-01 2013-02-01 一种应用于服装业代替线迹缝纫的反应型自催化粘合剂及其制备方法 Expired - Fee Related CN103131358B (zh)