CN103131302A - 一种含有羟丙基甲基纤维素的粉末涂料 - Google Patents

一种含有羟丙基甲基纤维素的粉末涂料 Download PDF

Info

Publication number
CN103131302A
CN103131302A CN2013100406468A CN201310040646A CN103131302A CN 103131302 A CN103131302 A CN 103131302A CN 2013100406468 A CN2013100406468 A CN 2013100406468A CN 201310040646 A CN201310040646 A CN 201310040646A CN 103131302 A CN103131302 A CN 103131302A
Authority
CN
China
Prior art keywords
parts
powder coating
powder
vltra tears
methyl cellulose
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN2013100406468A
Other languages
English (en)
Other versions
CN103131302B (zh
Inventor
倪进培
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Tianjin Rui Yuan Powder Coating Co., Ltd.
Original Assignee
倪进培
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 倪进培 filed Critical 倪进培
Priority to CN201310040646.8A priority Critical patent/CN103131302B/zh
Publication of CN103131302A publication Critical patent/CN103131302A/zh
Application granted granted Critical
Publication of CN103131302B publication Critical patent/CN103131302B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种含有羟丙基甲基纤维素的粉末涂料，是由下述重量份的原料制得：双酚A型环氧树脂90-95，聚酯树脂25-38，145松香树脂7-8，羟丙基甲基纤维素8-15，抗氧剂11350.3-0.5，抗氧剂BHT1-2,无机填料80-90，有机硅消泡剂1-2，安息香0.5-1.5，六偏磷酸钠0.3-0.5，三氧化二锑1-2，乙撑双硬脂酰胺3-4,钛白粉55-60，癸二酸二辛酯1-2，柠檬酸三丁酯0.6-0.8，四甲氧基甲基甘脲4-7，鳞片状锌粉3-5，微晶蜡3-5，硅烷偶联剂KH570 1-2。本发明绿色环保，机械强度高;既使用方便,又无毒无害阻燃，耐候性强。

Description

一种含有羟丙基甲基纤维素的粉末涂料
技术领域
本发明涉及涂料领域，确切地说是一种含有羟丙基甲基纤维素的粉末涂料。 
背景技术
    粉末涂料是一种新型的不含溶剂100%固体粉末状涂料。具有无溶剂、无污染、可回收、环保、节省能源和资源、减轻劳动强度和涂膜机械强度高等特点。粉末涂料是与一般涂料完全不同的形态，它是以微细粉末的状态存在的。由于不使用溶剂，所以称为粉末涂料。粉末涂料的主要特点有：具有无公害、高效率、节省资源的特点。 
发明内容
本发明的目的在于提供一种含有羟丙基甲基纤维素的粉末涂料。 
上述目的通过以下方案实现： 
一种含有羟丙基甲基纤维素的粉末涂料，其特征在于，是由下述重量份的原料制得：双酚A型环氧树脂 90-95，聚酯树脂25-38，145 松香树脂7-8，羟丙基甲基纤维素 8-15，抗氧剂1135 0.3-0.5，抗氧剂BHT 1-2,无机填料80-90，有机硅消泡剂 1-2，安息香 0.5-1.5，六偏磷酸钠0.3-0.5，三氧化二锑 1-2，乙撑双硬脂酰胺3-4,钛白粉55-60，癸二酸二辛酯1-2，柠檬酸三丁酯 0.6-0.8，四甲氧基甲基甘脲4-7，鳞片状锌粉 3-5，微晶蜡 3-5，硅烷偶联剂KH570  1-2。
   所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：所述的无机填料由下述重量份的原料组成：纳米碳酸钙20-30，滑石粉20-25、硅灰石粉40-50、改性纳米萤石矿渣10-15； 
    所述的改性纳米萤石矿渣的制备方法为：将萤石矿渣于700-800℃下煅烧4-6小时，冷却后，破碎，过100-200目筛，然后于8-10%的乙酸溶液中浸泡5-7小时后，取出，去离子水洗涤至中性，加入相当于萤石矿渣重量1-2%的氯化石蜡，1-2%的马来酸二辛酯，混匀后，烘干，研磨成纳米粉末，即得。
所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于： 
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于500-600转/分下搅拌混合3-4分钟，于2800-3000转/分下搅拌混合8-10分钟，后于400-500转/分下搅拌混合1-2分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在100-115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过100-200目筛，即得。
所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于： 
所述的有机硅消泡剂固含量为22%。
所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。 
本发明的有益效果为：本发明绿色环保，机械强度高;既使用方便,又无毒无害阻燃，耐候性强。 
具体实施方式
一种含有羟丙基甲基纤维素的粉末涂料，是由下述重量份（kg）的原料制得：双酚A型环氧树脂 95，聚酯树脂33，145 松香树脂8，羟丙基甲基纤维素 13，抗氧剂1135  0.5，抗氧剂BHT  1.7,无机填料83，有机硅消泡剂 1，安息香 1.2，六偏磷酸钠0.5，三氧化二锑 2，乙撑双硬脂酰胺4,钛白粉60，癸二酸二辛酯2，柠檬酸三丁酯 0.8，四甲氧基甲基甘脲6，鳞片状锌粉 3，微晶蜡 3，硅烷偶联剂KH570  1。 
   所述的无机填料由下述重量份的原料组成：纳米碳酸钙30，滑石粉25、硅灰石粉50、改性纳米萤石矿渣15； 
    所述的改性纳米萤石矿渣的制备方法为：将萤石矿渣于800℃下煅烧6小时，冷却后，破碎，过200目筛，然后于10%的乙酸溶液中浸泡7小时后，取出，去离子水洗涤至中性，加入相当于萤石矿渣重量2%的氯化石蜡，2%的马来酸二辛酯，混匀后，烘干，研磨成纳米粉末，即得。
所述的一种含有羟丙基甲基纤维素的粉末涂料， 
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于600转/分下搅拌混合4分钟，于3000转/分下搅拌混合10分钟，后于500转/分下搅拌混合1分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过180目筛，即得。
所述的有机硅消泡剂固含量为22%。 
所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。 
将本实施例所得涂料采用高压静电喷涂于铸件上，电压为60KV，平均膜厚为70-100微米，固化条件为180℃烘烤20分钟； 
性能指标如下：
按照GB/T1732测试，抗冲击性 ≥50kg.cm；
按照GB/T6739测试，铅笔硬度≥H级；
480h QUV-B加速光老化试验测试得，保光率达92%。
    所得涂层表面平整，无气泡，颗粒、缩孔、针孔。 

Claims (5)

1.一种含有羟丙基甲基纤维素的粉末涂料，其特征在于，是由下述重量份的原料制得：双酚A型环氧树脂 90-95，聚酯树脂25-38，145 松香树脂7-8，羟丙基甲基纤维素 8-15，抗氧剂1135 0.3-0.5，抗氧剂BHT 1-2,无机填料80-90，有机硅消泡剂 1-2，安息香 0.5-1.5，六偏磷酸钠0.3-0.5，三氧化二锑 1-2，乙撑双硬脂酰胺3-4,钛白粉55-60，癸二酸二辛酯1-2，柠檬酸三丁酯 0.6-0.8，四甲氧基甲基甘脲4-7，鳞片状锌粉 3-5，微晶蜡 3-5，硅烷偶联剂KH570  1-2。
2.根据权利要求1所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：所述的无机填料由下述重量份的原料组成：纳米碳酸钙20-30，滑石粉20-25、硅灰石粉40-50、改性纳米萤石矿渣10-15；
    所述的改性纳米萤石矿渣的制备方法为：将萤石矿渣于700-800℃下煅烧4-6小时，冷却后，破碎，过100-200目筛，然后于8-10%的乙酸溶液中浸泡5-7小时后，取出，去离子水洗涤至中性，加入相当于萤石矿渣重量1-2%的氯化石蜡，1-2%的马来酸二辛酯，混匀后，烘干，研磨成纳米粉末，即得。
3.根据权利要求1所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：
制备方法包括以下步骤：
（1）、按所述重量份精确称量各原料，先于500-600转/分下搅拌混合3-4分钟，于2800-3000转/分下搅拌混合8-10分钟，后于400-500转/分下搅拌混合1-2分钟，停止搅拌，得混合物料；
（2）、将混合物料用挤出机在100-115℃的温度下挤出，得挤出料；
（3）、挤出料粉碎后过100-200目筛，即得。
4.根据权利要求1所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：
所述的有机硅消泡剂固含量为22%。
5.根据权利要求1所述的一种含有羟丙基甲基纤维素的粉末涂料，其特征在于：所述的聚酯树脂为羟基型聚酯，酸值 30-40mk KOH/g， 粘度 5000-7000mPa.S， 固化温度 180-200℃。
CN201310040646.8A 2013-02-03 2013-02-03 一种含有羟丙基甲基纤维素的粉末涂料 Active CN103131302B (zh)